CN104693616A - 一种耐高温、耐腐蚀衬里及其制备方式 - Google Patents
一种耐高温、耐腐蚀衬里及其制备方式 Download PDFInfo
- Publication number
- CN104693616A CN104693616A CN201310669876.0A CN201310669876A CN104693616A CN 104693616 A CN104693616 A CN 104693616A CN 201310669876 A CN201310669876 A CN 201310669876A CN 104693616 A CN104693616 A CN 104693616A
- Authority
- CN
- China
- Prior art keywords
- lining
- corrosion resistant
- rubber
- high temperature
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种耐高温、耐腐蚀衬里及其制备方式，它由三元乙丙橡胶、丁苯橡胶、硫化剂、硬脂酸、白炭黑、硫磺、促进剂、防老剂、填充剂、软化剂组成。将所述一种耐高温、耐腐蚀衬里的各组分混炼得混炼胶料，再将所得混炼胶料过滤后通过冷喂料压出成型制得防腐橡胶胶板；将上一步骤所得胶板通过热烙法进行衬贴得衬胶；将上步所得衬胶进行硫化即得乙丙橡胶耐腐蚀衬里。本发明可用于耐酸、耐碱、耐氨、耐氯及耐氧化剂等的罐的衬里材料，使用温度可达100℃。
Description
技术领域
本发明涉及化工防腐材料领域，具体涉及一种耐高温、耐腐蚀衬里及其制备方式。
背景技术
20世纪80年代，国内引进了多条粘胶生产线，其中十一级闪蒸装置体现出了高效、节能及稳定性，给国内粘胶行业带来了新的技术突破。但进口设备价格高昂，成为限制国内粘胶业发展的瓶颈。因此，寻求十一级闪蒸装置的国产化成为当务之急。与之相配套的防腐橡胶衬里的开发也作为关键因素之一被提上日程。
目前市场上销售的橡胶防腐衬里，如天然橡胶衬里，氯丁橡胶衬里、丁基橡胶衬里，在工艺上除了采用传统的高压热硫化生产工艺之外，还出现了常压热硫化，直接常压蒸汽硫化机自动化等新工艺橡胶衬里。虽然这些衬里材料都极大地满足了化工防腐需要耐高温、耐腐蚀性介质，如硫酸、盐酸、磷酸、烧碱等酸碱介质对钢铁设备的腐蚀要求。但是，在实际应用中，由于介质往往不是单一的，有时混有溶剂油，如环保行业的水处理设备，而在石油设备及食品加工等设备中的介质中常常使用造成了极大的危险，使衬里材料溶胀损坏，致使橡胶衬里不耐腐蚀，使用寿命短，防腐不够安全可靠。
发明内容
本发明的目的是提供的一种耐高温、耐腐蚀衬里及其制备方式。
为解决上述技术问题，本发明所采用的技术方案如下：
（1）将所述一种耐高温、耐腐蚀衬里的各组分混炼得混炼胶料，再将所得混炼胶料过滤后通过冷喂料压出成型制得防腐橡胶胶板；
（2）将步骤（1）所得胶板通过热烙法进行衬贴得衬胶；
（3）将步骤（2）所得衬胶进行硫化即得一种耐高温、耐腐蚀衬里。
本发明的有益效果：
（1）本发明与国内同类产品相比，耐热性显著提高；与国外同类产品相比，实际使用温度也有一定的提高；同时兼有良好的韧性与耐低温性，降低了硬质橡胶衬里产品对于贮运的要求，提高了经济效益。
（2）本发明通过特定的组分及用量，改善了现有硬质橡胶的性能，由所述组合物制得的一种耐高温、耐腐蚀衬里，耐热性能良好，在酸液中实际使用温度可达110℃，在饱和蒸汽中实际使用温度可达130℃；在真空度达-900KPa的条件下可长期使用。所得防腐橡胶衬里同时具有良好的耐化学介质腐蚀性。此外，耐低温性也有一定的提高，达到了半硬质橡胶衬里 的低温性能（-5℃），处于国内领先水平，达到了国外同类产品的先进水平。
具体实施例
以下实施例用于说明本发明，但不用来限制本发明的范围。
实施例1：
其制备方式为：将所述一种耐高温、耐腐蚀衬里的各组分混炼得混炼胶料，再将所得混炼胶料过滤后通过冷喂料压出成型制得防腐橡胶胶板；将上一步骤所得胶板通过热烙法进行衬贴得衬胶；将上步所得衬胶进行硫化即得乙丙橡胶耐腐蚀衬里。
本发明与国内同类产品相比，耐热性显著提高；同时兼有良好的韧性与耐化学介质腐蚀性。
实施例2：
制备方式同上。
耐低温性有一定的提高，达到了半硬质橡胶衬里的低温性能（-5℃），处于国内领先水平，达到了国外同类产品的先进水平。
实施例3：
制备方式同上。
本发明通过特定的组分及用量，改善了现有硬质橡胶的性能，由所述组合物制得的一种耐高温、耐腐蚀衬里，耐热性能良好，在酸液中实际使用温度可达110℃，在饱和蒸汽中实际使用温度可达130℃；在真空度达-900KPa的条件下可长期使用。所得防腐橡胶衬里同时具有良好的耐化学介质腐蚀性。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种耐高温、耐腐蚀衬里及其制备方式，其特征在于，它由三元乙丙橡胶、丁苯橡胶、硫化剂、硬脂酸、白炭黑、硫磺、促进剂、防老剂、填充剂、软化剂组成。
2.根据权利要求1，所述的一种耐高温、耐腐蚀衬里及其制备方式，其特征在于，所述的硫化剂是二氧化铅。
3.根据权利要求1，所述的一种耐高温、耐腐蚀衬里及其制备方式，其特征在于，所述的促进剂为对醌二肟。
4.根据权利要求1至3，所述的一种耐高温、耐腐蚀衬里及其制备方式，其特征在于，其各组分按重量份数比为：三元乙丙橡胶70～95份、丁苯橡胶65～80份、硫化剂20～35份、硬脂酸50～65份、白炭黑40～58份、硫磺30～45份、促进剂10～25份、防老剂15～30份、填充剂10～20份、软化剂5～18份。
5.根据权利要求1至4，所述的一种耐高温、耐腐蚀衬里及其制备方式，其特征在于，其制备方式是：
（1）将所述乙丙橡胶耐腐蚀衬里的各组分混炼得混炼胶料，再将所得混炼胶料过滤后通过冷喂料压出成型制得防腐橡胶胶板；
（2）将步骤（1）所得胶板通过热烙法进行衬贴得衬胶；
（3）将步骤（2）所得衬胶进行硫化即得乙丙橡胶耐腐蚀衬里。