CN104480583A - Abrasion-resistant steel wire ring - Google Patents
Abrasion-resistant steel wire ring Download PDFInfo
- Publication number
- CN104480583A CN104480583A CN201410661524.5A CN201410661524A CN104480583A CN 104480583 A CN104480583 A CN 104480583A CN 201410661524 A CN201410661524 A CN 201410661524A CN 104480583 A CN104480583 A CN 104480583A
- Authority
- CN
- China
- Prior art keywords
- wear
- steel
- resistant
- abrasion
- steel wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an abrasion-resistant steel wire ring which comprises an iron steel core substrate. Abrasion-resistant alloy layers coat the inner surface and the outer surface of the iron steel core substrate, and abrasion-resistant alloy materials are formed on the inner surface of the steel wire ring by the aid of hot spraying technology. The abrasion resistance of the steel wire ring in high-speed running can be remarkably improved by the aid of alloy layers, the service life of the steel wire ring is prolonged, and the alloy materials are reasonably matched, rich in source, low in production cost, simple in coating technology and high in practicability.
Description
Technical field
The invention belongs to field of textile equipment, particularly, what the present invention relates to is a kind of wear-resistant bead ring.
Background technology
Steel traveler is one of crucial equipment of Weaving device, it directly affects the twist of Weaving device yarn, package density and broken end, filoplume value and cotton balls quantity, use the steel traveler of high-quality can promote the quality scale of yarn, improve the output of resultant yarn, reduce lap waste, reduce costs, improve Economic returns.
Because steel traveler is frequent and between steel construction, and contact with between yarn, therefore, the contact surface of steel traveler all bears high wearing and tearing.And in order to improve yarn output, steel traveler must be risen to the higher speed of service, this just has higher requirement to the ABRASION RESISTANCE of steel traveler and intensity.In existing technology, by applying suitable material on steel traveler, the service behaviour of steel traveler has been made greatly to promote, but, for the steel traveler of high-speed cruising, the performance of its ABRASION RESISTANCE aspect also cannot reach instructions for use completely, and its production technology cost is higher, and Practical Performance is restricted.
Summary of the invention
For the deficiency that prior art exists, the invention provides a kind of wear-resistant bead ring, the equal plating of its surfaces externally and internally has wear-resistant alloy layer, effectively can promote the anti-wear performance of steel traveler in high-speed cruising, improves the service life of steel traveler.
To achieve these goals, the present invention realizes by the following technical solutions:
A kind of wear-resistant bead ring, it comprises irony steel core matrix, it is characterized in that, the equal plating of surfaces externally and internally of described irony steel core matrix has wear-resistant alloy layer, and described wear resistant alloy material takes shape in steel traveler inner surface by hot-spraying technique.
Further, the thickness of described irony steel core matrix is 0.45-0.55mm.
Further, described antifriction alloy layer thickness is 45-55um.
Further, the hardness of described wear-resistant alloy layer can reach 60-70HRC.
Further, the material of described irony steel core matrix can be 72B carbon steel, 82B carbon steel, 45 steel, 40Cr, 65Mn or 20CrMnTi.
Compared with prior art, the invention has the beneficial effects as follows:
Wear-resistant bead ring provided by the invention, this steel traveler passes through at its irony steel core matrix surfaces externally and internally equal plating one wear-resistant alloy layer, and this laminated gold significantly can promote the anti-wear performance of steel traveler in high-speed cruising, improves the service life of steel traveler; And rationally, abundance, production cost is lower, and plating technic is easy, and Practical Performance is higher in this laminated gold copper-base alloy collocation.
Accompanying drawing explanation
The present invention is described in detail below in conjunction with the drawings and specific embodiments;
Fig. 1 is structural representation of the present invention.
The Reference numeral that in figure, each component names is corresponding is: 1-irony steel core matrix; 2-wear-resistant alloy layer.
Detailed description of the invention
The technological means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with detailed description of the invention, setting forth the present invention further.
Embodiment 1:
A kind of wear-resistant bead ring disclosed in this invention, it comprises irony steel core matrix 1, and the equal plating of surfaces externally and internally of described irony steel core matrix has wear-resistant alloy layer 2, and described wear resistant alloy material takes shape in steel traveler inner surface by hot-spraying technique.The thickness of described irony steel core matrix is 0.45-0.55mm.Described antifriction alloy layer thickness is 45-55um.The hardness of described wear-resistant alloy layer can reach 60-70HRC.The material of described irony steel core matrix can be 72B carbon steel, 82B carbon steel, 45 steel, 40Cr, 65Mn or 20CrMnTi.
Wear-resistant bead ring provided by the invention, this steel traveler passes through at its irony steel core matrix surfaces externally and internally equal plating one wear-resistant alloy layer, and this laminated gold significantly can promote the anti-wear performance of steel traveler in high-speed cruising, improves the service life of steel traveler; And rationally, raw material sources enriches, and production cost is lower, and plating technic is easy, and Practical Performance is higher in this laminated gold copper-base alloy collocation.
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (5)
1. a wear-resistant bead ring, it comprises irony steel core matrix (1), it is characterized in that, the equal plating of surfaces externally and internally of described irony steel core matrix (1) has wear-resistant alloy layer (2), and described wear-resistant alloy layer (2) material takes shape in steel traveler inner surface by hot-spraying technique.
2. wear-resistant bead ring according to claim 1, is characterized in that, the thickness of described irony steel core matrix (1) is 0.45-0.55mm.
3. wear-resistant bead ring according to claim 1, is characterized in that, described wear-resistant alloy layer (2) thickness is 45-55um.
4. wear-resistant bead ring according to claim 1, is characterized in that, the hardness of described wear-resistant alloy layer (2) can reach 60-70HRC.
5. wear-resistant bead ring according to claim 1, is characterized in that, the material of described irony steel core matrix (1) can be 72B carbon steel, 82B carbon steel, 45 steel, 40Cr, 65Mn or 20CrMnTi.