CN104388839B - Alloy for steam turbine rotor - Google Patents

Alloy for steam turbine rotor Download PDF

Info

Publication number
CN104388839B
CN104388839B CN201410615152.2A CN201410615152A CN104388839B CN 104388839 B CN104388839 B CN 104388839B CN 201410615152 A CN201410615152 A CN 201410615152A CN 104388839 B CN104388839 B CN 104388839B
Authority
CN
China
Prior art keywords
turbine rotor
alloy
steam turbine
present
balance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410615152.2A
Other languages
Chinese (zh)
Other versions
CN104388839A (en
Inventor
金照宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Othea Jianyang Carbon Black Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410615152.2A priority Critical patent/CN104388839B/en
Publication of CN104388839A publication Critical patent/CN104388839A/en
Application granted granted Critical
Publication of CN104388839B publication Critical patent/CN104388839B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses an alloy for a steam turbine rotor. The alloy for the steam turbine rotor comprises the following elements: 5-8% of Ni, 1-1.5% of Mo, 0.1-0.3% of Pb, 0.2-0.5% of Co, 0.7-1% of Mn, 0.2-0.3% of V, 0.25-0.35% of C, less than or equal to 0.1% of Si and the balance of Fe. Compared with the existing alloy steel, the alloy for the steam turbine rotor can be used for obviously improving impact energy of a material for the steam turbine rotor and improving toughness of the material, so that the alloy for the steam turbine rotor especially can serve as a material for a high temperature steam turbine rotor.

Description

A kind of turbine rotor alloy
Technical field
The invention belongs to field of alloy material is and in particular to a kind of turbine rotor alloy.
Background technology
Turbine rotor is the important core part of steam turbine, rigors because of its working environment, rotor alloy material is needed to have good elevated temperature strength, typically select steel alloy, as 30cr1mo1v, but the toughness of this steel alloy is relatively poor so that its range of application is limited to it is impossible to meet the demand of high-temperature steam turbine rotor.
Content of the invention
The technical problem to be solved in the present invention is to overcome existing defect, there is provided a kind of turbine rotor alloy.
In order to solve above-mentioned technical problem, the invention provides following technical scheme:
A kind of turbine rotor alloy, alloying element and percentage composition are as follows: ni 5-8, mo 1-1.5, pb 0.1-0.3, co 0.2-0.5, mn 0.7-1, v 0.2-0.3, c 0.25-0.35, si≤0.1, balance of fe.
Contain the impurity such as inevitable p, s in alloy, but impurity content is more few better.
The turbine rotor alloy of the present invention, compared with existing steel alloy, can significantly improve the ballistic work of existing turbine rotor material, improve the toughness of material, be particularly well suited as the material of high-temperature steam turbine rotor.
Specific embodiment
Below in conjunction with preferred embodiment, the present invention will be described it will be appreciated that preferred embodiment described herein is merely to illustrate and explains the present invention, is not intended to limit the present invention.
Embodiment 1
The percentage by weight of turbine rotor alloy each element is: ni 8, mo 1, pb 0.3, co 0.3, mn 1, v 0.3, c 0.30, si0.07, balance of fe, smelts according to a conventional method and obtains.The yield strength of alloy: 720mpa, elongation percentage: 17%, the contraction percentage of area: 65.0%, ballistic work akv:180j.
Embodiment 2
The percentage by weight of turbine rotor alloy each element is: ni 5, mo 1.5, pb 0.1, co 0.2, mn 1, v 0.2, c 0.25, si0.07, balance of fe, smelts according to a conventional method and obtains.The yield strength of alloy: 680mpa, elongation percentage: 23%, the contraction percentage of area: 72.0%, ballistic work akv:175j.
Embodiment 3
The percentage by weight of turbine rotor alloy each element is: ni 6, mo 1.1, pb 0.3, co 0.5, mn 0.7, v 0.3, c 0.35, si0.06, balance of fe, smelts according to a conventional method and obtains.The yield strength of alloy: 710mpa, elongation percentage: 19%, the contraction percentage of area: 68.2%, ballistic work akv:167j.
Finally it is noted that the foregoing is only the preferred embodiments of the present invention, it is not limited to the present invention, although being described in detail to the present invention with reference to the foregoing embodiments, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent to wherein some technical characteristics.All any modification, equivalent substitution and improvement within the spirit and principles in the present invention, made etc., should be included within the scope of the present invention.

Claims (2)

1. a kind of turbine rotor alloy, alloying element and weight percentage are as follows: ni 5-8, mo 1-1.5, pb 0.1-0.3, co 0.2-0.5, mn 0.7-1, v 0.2-0.3, c 0.25-0.35, si≤0.1, balance of fe.
2. turbine rotor alloy according to claim 1 is it is characterised in that described alloying element and weight percentage are as follows: ni 8, mo 1-1.5, pb 0.3, co 0.2-0.5, mn 0.7-1, v 0.2-0.3, c 0.25-0.35, si≤0.1, balance of fe.
CN201410615152.2A 2014-11-05 2014-11-05 Alloy for steam turbine rotor Active CN104388839B (en)