CN104356806A - Flexible moisture-resistant water-based anticorrosive paint for bamboo-weaved rattan chairs - Google Patents
Flexible moisture-resistant water-based anticorrosive paint for bamboo-weaved rattan chairs Download PDFInfo
- Publication number
- CN104356806A CN104356806A CN201410596693.5A CN201410596693A CN104356806A CN 104356806 A CN104356806 A CN 104356806A CN 201410596693 A CN201410596693 A CN 201410596693A CN 104356806 A CN104356806 A CN 104356806A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- anticorrosive paint
- deionized water
- bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of anticorrosive paint and in particular relates to flexible moisture-resistant water-based anticorrosive paint for bamboo-weaved rattan chairs. The anticorrosive paint is prepared from the following raw materials in parts by weight: 2-3 parts of sodium methacrylate, 0.01-0.02 part of disodium stannous citrate, 4-5 parts of aminosilane, 20-40 parts of acrylic emulsion with the solid content of 40%-50%, 18-24 parts of a waterborne polyurethane dispersoid with the solid content of 30%-40%, 0.5-0.8 part of a wetting agent, 1-2 parts of coco fatty acid diethanol amide, 12-18 parts of de-ionized water and 1-2 parts of an assistant. According to the anticorrosive paint, the acrylic emulsion is compounded with the polyurethane dispersoid, and aminosilane is added for modification, so that the paint is excellent in flexibility and environmental corrosion resistance, and a paint film is good in adhesion and resistant to heat and water; in combination with the materials such as the assistant with auxiliary film forming and drying effects, the wetting agent and disodium stannous citrate, the paint forms the dense and bright paint film on the surface of a bamboo material and is free of bad odor, environment-friendly and safe, and the mildew and rot phenomena of the rattan chairs are effectively improved.
Description
Technical field
The present invention relates to antifouling paint field, be specifically related to the pliable and tough moisture resistance aqueous anticorrosion paint of a kind of bamboo weaving rattan chair.
Background technology
In recent years, with the various product of the natural materials hand wovens such as rattan, wicker, bamboo cane, all kinds of stalks, there is the wide market space, this series products is many as indoor furniture, goods of furniture for display rather than for use and daily living article, because it has the advantage of nature, environmental protection, pole is liked by human consumer, and a lot of product is sold abroad.Because fabric natural material is in use affected by environment, very easily damage by worms rotten, make moist mouldy, thus serious reduction work-ing life and use properties, therefore, need at product surface spray coating antifouling paste in actual production process, require that this kind of antifouling paste in conjunction with material feature, not only will will possess good antiseptic property simultaneously, also will have the feature of environmental protection of height and lower production cost.
Summary of the invention
The object of the invention is to, provide a kind of bamboo weaving rattan chair pliable and tough moisture resistance aqueous anticorrosion paint, in order to achieve the above object, the technical solution used in the present invention is as follows:
The pliable and tough moisture resistance aqueous anticorrosion paint of a kind of bamboo weaving rattan chair, it is characterized in that, this antifouling paste is made up of the raw material of following weight part: sodium methacrylate 2-3, distannous citrate 0.01-0.02, aminosilane 4-5, solid content are the ACRYLIC EMULSION 20-40 of 40-50%, the aqueous polyurethane dispersion 18-24 of solid content 30-40%, wetting agent 0.5-0.8, lauric acid amide of ethanol 1-2, deionized water 12-18, auxiliary agent 1-2;
Auxiliary agent is made up of the raw material of following weight part: nano zine oxide 3-5, ethylene glycol phenyl ether 1-2, cm-chitosan 1-2, nano rare earth cerium colloidal sol 1-2, deionized water 10-12, polymine 1-3, preparation method is: be first dissolved in deionized water by cm-chitosan, polymine, again other leftover materials are added in mixing solutions, and stir with the speed of 500-600 rev/min, after material dispersion is even, under 60-80 DEG C of condition, mixture is condensed into paste, after being cooled to room temperature and get final product.
The described pliable and tough moisture resistance aqueous anticorrosion paint of a kind of bamboo weaving rattan chair, its preparation method is as follows:
(1) after first ACRYLIC EMULSION, aqueous polyurethane dispersion being mixed, be heated to 40-50 DEG C, then add aminosilane, after dispersed with stirring 20-30min, insulation leaves standstill 20-30min, and be cooled to room temperature subsequently, gained material is for subsequent use;
(2) sodium methacrylate, distannous citrate, lauric acid amide of ethanol are added in deionized water, be stirred to after complete material dissolves completely, slowly add step (1) gained material uniformly, and do not stop to stir simultaneously, after treating that step (1) material adds, add other remaining component again, continue to be uniformly mixed 40-50min, to obtain final product.
Compared with prior art, antifouling paste advantage of the present invention is: by ACRYLIC EMULSION and the composite use of polyurethane dispersions, improve snappiness and the environment resistant corrosive power of paint film, compound resin emulsion is through amino silane modified postadhesion power, heat-resisting, water-resistant capacity is improved, distannous citrate is a kind of safe sanitas, can delay to paint deterioration by oxidation, be combined with auxiliary film forming again, the compositions such as the auxiliary agent of dry effect and wetting agent, the present invention is painted with bamboo epidermis face well attached, become paint film coherent light bright, without unpleasant odor, Environmental Safety, Waterproof corrosion, effectively improve the mouldy rotten phenomenon of rattan chair.
Embodiment
Embodiment
The antifouling paste of the present embodiment is made up of the raw material of following weight part: sodium methacrylate 2, distannous citrate 0.01, aminosilane 4, solid content are ACRYLIC EMULSION 35, the aqueous polyurethane dispersion 20 of solid content 30%, wetting agent 0.5, lauric acid amide of ethanol 1, deionized water 15, the auxiliary agent 1 of 40%;
Auxiliary agent is made up of the raw material of following weight part: nano zine oxide 5, ethylene glycol phenyl ether 2, cm-chitosan 1, nano rare earth cerium colloidal sol 1, deionized water 10, polymine 2, preparation method is: be first dissolved in deionized water by cm-chitosan, polymine, again other leftover materials are added in mixing solutions, and stir with the speed of 600 revs/min, after material dispersion is even, under 60-80 DEG C of condition, mixture is condensed into paste, after being cooled to room temperature and get final product.
The preparation method of this antifouling paste is as follows:
(1) after first ACRYLIC EMULSION, aqueous polyurethane dispersion being mixed, be heated to 40-50 DEG C, then add aminosilane, after dispersed with stirring 20min, insulation leaves standstill 30min, and be cooled to room temperature subsequently, gained material is for subsequent use;
(2) sodium methacrylate, distannous citrate, lauric acid amide of ethanol are added in deionized water, be stirred to after complete material dissolves completely, slowly add step (1) gained material uniformly, and do not stop to stir simultaneously, after treating that step (1) material adds, add other remaining component again, continue to be uniformly mixed 50min, to obtain final product.
After the allotment of the present embodiment antifouling paste, after being applied to bamboo weaving rattan chair surface complete drying, its performance test results is:
| Test event | Technical indicator |
| Outward appearance | Smooth, bright, plentiful |
| Hardness of paint film (shore D) | 65±3 |
| Sticking power grade | ≥4B |
| Resistance to salt water (3% salt solution, room temperature 30d) | Non-foaming, not stratified, nondiscoloration |
| Water tolerance (30d) | Unchanged |
| Weathering resistance (1 year) | Unchanged |
Above-mentioned test is all followed relevant criterion and is carried out.
Claims (2)
1. the pliable and tough moisture resistance aqueous anticorrosion paint of bamboo weaving rattan chair, it is characterized in that, this antifouling paste is made up of the raw material of following weight part: sodium methacrylate 2-3, distannous citrate 0.01-0.02, aminosilane 0.5-1, solid content are the ACRYLIC EMULSION 20-40 of 40-50%, the aqueous polyurethane dispersion 18-24 of solid content 30-40%, wetting agent 0.5-0.8, lauric acid amide of ethanol 1-2, deionized water 12-18, auxiliary agent 1-2;
The component that described auxiliary agent comprises and weight part thereof are: nano zine oxide 3-5, ethylene glycol phenyl ether 1-2, cm-chitosan 1-2, nano rare earth cerium colloidal sol 1-2, deionized water 10-12, polymine 1-3, preparation method is: be first dissolved in deionized water by cm-chitosan, polymine, again other leftover materials are added in mixing solutions, and stir with the speed of 500-600 rev/min, after material dispersion is even, under 60-80 DEG C of condition, mixture is condensed into paste, after being cooled to room temperature and get final product.
2. the pliable and tough moisture resistance aqueous anticorrosion paint of a kind of bamboo weaving rattan chair as claimed in claim 1, its preparation method is as follows:
(1) after first ACRYLIC EMULSION, aqueous polyurethane dispersion being mixed, be heated to 40-50 DEG C, then add aminosilane, after dispersed with stirring 20-30min, insulation leaves standstill 20-30min, and be cooled to room temperature subsequently, gained material is for subsequent use;
(2) sodium methacrylate, distannous citrate, lauric acid amide of ethanol are added in deionized water, be stirred to after complete material dissolves completely, slowly add step (1) gained material uniformly, and do not stop to stir simultaneously, after treating that step (1) material adds, add other remaining component again, continue to be uniformly mixed 40-50min, to obtain final product.