CN104312513B - 一种双组分环氧电子灌封硅胶 - Google Patents

一种双组分环氧电子灌封硅胶 Download PDF

Info

Publication number
CN104312513B
CN104312513B CN201410655287.1A CN201410655287A CN104312513B CN 104312513 B CN104312513 B CN 104312513B CN 201410655287 A CN201410655287 A CN 201410655287A CN 104312513 B CN104312513 B CN 104312513B
Authority
CN
China
Prior art keywords
component
silica gel
embedding silica
component epoxy
epoxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410655287.1A
Other languages
English (en)
Other versions
CN104312513A (zh
Inventor
王博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Abner New Materials Co ltd
Original Assignee
Nanjing Abnen Sealing Technology Stock Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Abnen Sealing Technology Stock Co Ltd filed Critical Nanjing Abnen Sealing Technology Stock Co Ltd
Priority to CN201410655287.1A priority Critical patent/CN104312513B/zh
Publication of CN104312513A publication Critical patent/CN104312513A/zh
Application granted granted Critical
Publication of CN104312513B publication Critical patent/CN104312513B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种双组分环氧电子灌封硅胶，胶粘剂为AB双组分，以质量百分数计，A组分包括以下组分及配比：端羟基聚二甲基硅氧烷20～30％，环氧树脂30～40％，二甲基硅油3.5～10％，甲基肟基硅烷1～5％，乙烯基肟基硅烷1～5％，气相二氧化硅2.45～4.45％，碳酸钙粉10～13％，氢氧化铝粉10～15％，硅微粉10～20％，二月桂酸二丁基锡0.05％；以质量百分数计，B组分包括以下组分及配比：直链脂肪族胺15～25％、脂环胺10～20％、低分子量聚酰胺3～10％、助剂0.5～1％和填料39～46％和偶联剂5～10％。

Description

一种双组分环氧电子灌封硅胶
技术领域
本发明涉及一种双组分环氧电子灌封硅胶，广泛应用于电子零组件如：电子变压器、负离子发生器、模块电源、高压包、水族水泵、继电器、电容、点火线圈、互感器、AC/DC模块、LED、LED模组、AC电容、(立式、卧式、盒式、薄膜)电容、灯饰、电器等各类电子元器件的绝缘灌注、防潮封填等，属于化工领域。
背景技术
本专利涉及一种双组分环氧电子灌封硅胶，具体应用于电子零组件，达到粘结、密封、绝缘之作用，保证电子零组件使用寿命。不仅如此，而本身所具备的硅胶特性也能够在生产生活中使用。如它的耐酸碱性能好、耐大气老化、绝缘，抗压，防潮防震等。
发明内容
本发明的目的在于提供了一种环保阻燃型环氧树脂灌封AB胶，粘度低、流动性好、容易渗透进产品的间隙中，散热性好；可常温或中温固化，固化速度适中；固化后无气泡、表面平整、有光泽、硬度高；固化物耐酸碱性能好，防潮防水防尘性能佳，耐湿热和大气老化；固化物具有良好的绝缘、抗压、粘接强度高等物理特性。
实现本发明目的的技术解决方案为：一种双组分环氧电子灌封硅胶，胶粘剂为AB双组分，以质量百分数计，A组分包括以下组分及配比：端羟基聚二甲基硅氧烷20～30％，环氧树脂30～40％，二甲基硅油3.5～10％，甲基肟基硅烷1～5％，乙烯基肟基硅烷1～5％，气相二氧化硅2.45～4.45％，碳酸钙粉10～13％，氢氧化铝粉10～15％，硅微粉10～20％，二月桂酸二丁基锡0.05％；以质量百分数计，B组分包括以下组分及配比：直链脂肪族胺15～25％、脂环胺10～20％、低分子量聚酰胺3～10％、助剂0.5～1％和填料39～46％和偶联剂5～10％。
其中，环氧树脂选自E51或E44中的一种或两种；直链脂肪族胺选自二乙烯三胺、三乙烯四胺、四乙烯五胺或羟乙基乙二胺中的一种或几种；脂环胺选自N-氨乙基哌嗪、羟乙基哌嗪、异佛尔酮二胺、双(4-氨基-3-甲基环己基)甲烷或双(4-氨基环己基)-甲烷中的一种或几种；低分子量聚酰胺为低分子量聚酰胺65；偶联剂选自KH550、KH560或KH792中的一种或者几种组合。
本发明技术方案带来的有益效果：
一、具有阻燃性，等级为UL94-HB级。
二、低粘度、流动性、自排泡性较方便的灌封复杂的电子部件，可浇注到细微之处。
三、具有可拆性密封后的元器件可取出进行修理和更换,然后用本灌封胶进行修补可不留痕迹。
四、胶料在常温条件下混合后存放时间较长，但在加热条件下可快速固化，利于自动生产线上的使用。
五、固化过程中不收缩，具有更优的防水防潮和抗老化性能。
具体实施方式
实施例1
本实施例的双组分环氧电子灌封硅胶，胶粘剂为AB双组分，以质量百分数计，A组分配比：端羟基聚二甲基硅氧烷20～30％，环氧树脂30～40％，二甲基硅油3.5～10％，甲基肟基硅烷1～5％，乙烯基肟基硅烷1～5％，气相二氧化硅2.45～4.45％，碳酸钙粉10～13％，氢氧化铝粉10～15％，硅微粉10～20％，二月桂酸二丁基锡0.05％；以质量百分数计，B组分包括以下组分及配比：直链脂肪族胺15～25％、脂环胺10～20％、低分子量聚酰胺3～10％、助剂0.5～1％和填料39～46％和偶联剂5～10％。
其中，环氧树脂选自E51或E44中的一种或两种；直链脂肪族胺选自二乙烯三胺、三乙烯四胺、四乙烯五胺或羟乙基乙二胺中的一种或几种；脂环胺选自N-氨乙基哌嗪、羟乙基哌嗪、异佛尔酮二胺、双(4-氨基-3-甲基环己基)甲烷或双(4-氨基环己基)-甲烷中的一种或几种；低分子量聚酰胺为低分子量聚酰胺65；偶联剂选自KH550、KH560或KH792中的一种或者几种组合。
本实施例的双组分环氧灌封硅胶，各项性能优越，粘度低、流动性好、容易渗透进产品的间隙中，散热性好；可常温或中温固化，固化速度适中；固化后无气泡、表面平整、有光泽、硬度高；固化物耐酸碱性能好，防潮防水防尘性能佳，耐湿热和大气老化；固化物具有良好的绝缘、抗压、粘接强度高等物理特性。广泛应用于电子零组件。
实施例2
与实施例1基本相同，本实施例的双组分环氧电子灌封硅胶，A组分配比：端羟基聚二甲基硅氧烷20％，环氧树脂30％，二甲基硅油3.5％，甲基肟基硅烷1％，乙烯基肟基硅烷1％，气相二氧化硅2.45％，碳酸钙粉13％，氢氧化铝粉13％，硅微粉16％，二月桂酸二丁基锡0.05％；B组分配比：直链脂肪族胺15％、脂环胺20％、低分子量聚酰胺9％、助剂0.5％和填料46％和偶联剂9.5％。
实施例3
与实施例1基本相同，本实施例的双组分环氧电子灌封硅胶，A组分配比：端羟基聚二甲基硅氧烷30％，环氧树脂30％，二甲基硅油4.95％，甲基肟基硅烷1％，乙烯基肟基硅烷1％，气相二氧化硅3％，碳酸钙粉10％，氢氧化铝粉10％，硅微粉10％，二月桂酸二丁基锡0.05％；B组分配比：直链脂肪族胺25％、脂环胺20％、低分子量聚酰胺10％、助剂0.5％和填料39％和偶联剂5.5％。
实施例4
与实施例1基本相同，本实施例的双组分环氧电子灌封硅胶，A组分配比：端羟基聚二甲基硅氧烷21％，环氧树脂31％，二甲基硅油4％，甲基肟基硅烷3％，乙烯基肟基硅烷2％，气相二氧化硅2.95％，碳酸钙粉12％，氢氧化铝粉12％，硅微粉12％，二月桂酸二丁基锡0.05％；B组分配比：直链脂肪族胺20％、脂环胺20％、低分子量聚酰胺10％、助剂1％和填料40％和偶联剂9％。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，例如各组分的增加或减少，若该种改动没有意想不到的效果，则都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。

Claims (6)

1.一种双组分环氧电子灌封硅胶，其特征在于：所述的胶粘剂为AB双组分，以质量百分数计，A组分包括以下组分及配比：端羟基聚二甲基硅氧烷20～30％，环氧树脂30～40％，二甲基硅油3.5～10％，甲基肟基硅烷1～5％，乙烯基肟基硅烷1～5％，气相二氧化硅2.45～4.45％，碳酸钙粉10～13％，氢氧化铝粉10～15％，硅微粉10～20％，二月桂酸二丁基锡0.05％；以质量百分数计，B组分包括以下组分及配比：直链脂肪族胺15～25％、脂环胺10～20％、低分子量聚酰胺3～10％、助剂0.5～1％和填料39～46％和偶联剂5～10％。
2.根据权利要求1所述的双组分环氧电子灌封硅胶，其特征在于：所述环氧树脂选自E51或E44中的一种或两种。
3.根据权利要求1所述的双组分环氧电子灌封硅胶，其特征在于：所述直链脂肪族胺选自二乙烯三胺、三乙烯四胺、四乙烯五胺或羟乙基乙二胺中的一种或几种。
4.根据权利要求1所述的双组分环氧电子灌封硅胶，其特征在于：所述脂环胺选自N-氨乙基哌嗪、羟乙基哌嗪、异佛尔酮二胺、双(4-氨基-3-甲基环己基)甲烷或双(4-氨基环己基)-甲烷中的一种或几种。
5.根据权利要求1所述的双组分环氧电子灌封硅胶，其特征在于：所述低分子量聚酰胺为低分子量聚酰胺65。
6.根据权利要求1所述的双组分环氧电子灌封硅胶，其特征在于：所述偶联剂选自KH550、KH560或KH792中的一种或者几种组合。
CN201410655287.1A 2014-11-17 2014-11-17 一种双组分环氧电子灌封硅胶 Active CN104312513B (zh)