CN104312444B - 一种水玻璃基多效木材胶黏剂及其制备方法 - Google Patents
一种水玻璃基多效木材胶黏剂及其制备方法 Download PDFInfo
- Publication number
- CN104312444B CN104312444B CN201410535934.5A CN201410535934A CN104312444B CN 104312444 B CN104312444 B CN 104312444B CN 201410535934 A CN201410535934 A CN 201410535934A CN 104312444 B CN104312444 B CN 104312444B
- Authority
- CN
- China
- Prior art keywords
- parts
- silica
- water
- waterglass
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种水玻璃基多效木材胶黏剂及其制备方法，该胶黏剂的配方组成（按重量份）为：水玻璃100份；铵盐改性丙烯酸酯乳液10-20份；豆蔻酸镁4-8份；硅烷偶联剂1-2份；四针状氧化锌晶须5-10份；黄原胶1-3份；二氧化硅包覆聚磷酸铵3-8份；氧化钼3-5份；水10-30份；硅微粉6-12份。制备时包括二氧化硅包覆聚磷酸铵和水玻璃基胶黏剂制备两个步骤。本发明的木材胶黏剂环保无毒，兼具阻燃、抑烟、抗菌、吸声、防腐和耐水等功能，制备工艺简便，易工业化。
Description
技术领域
本发明涉及木材胶黏剂领域，具体为一种水玻璃基多效木材胶黏剂及其制备方法。
背景技术
传统木材胶黏剂通常只具有粘接功能，导致功能化木质复合材料的制备往往需要首先对木材进行阻燃、防腐等多重处理，工艺繁琐，效果微弱。现代人造板工业的日益发展使其对胶黏剂的要求越来越高，除了具有高粘接性能以外，具有无醛、阻燃、抗菌、防腐等性能的多效木材胶黏剂正受到更多的关注。
发明内容
本发明所解决的技术问题是在于提供一种水玻璃基多效木材胶黏剂，以解决上述背景技术中的缺点。
本发明所解决的技术问题采用以下技术方案来实现：
一种水玻璃基多效木材胶黏剂，包括以下重量份的原料：
水玻璃：100份；
铵盐改性丙烯酸酯乳液：10-20份；
豆蔻酸镁：4-8份；
硅烷偶联剂：1-2份；
四针状氧化锌晶须：5-10份；
黄原胶：1-3份；
二氧化硅包覆聚磷酸铵：3-8份；
氧化钼：3-5份；
水：10-30份；
硅微粉：6-12份；
其具体制备方法步骤为：
1）首先制备二氧化硅包覆聚磷酸铵：将聚磷酸铵粉末浸入硅溶胶中24h，然后将混合物干燥、粉碎、磨细，就得到所述二氧化硅包覆聚磷酸铵。
2）将10-20份铵盐改性丙烯酸酯乳液缓慢加入到100份水玻璃中，手动搅拌使二者混合均匀。接着依次加入4-8份豆蔻酸镁、1-2份硅烷偶联剂、5-10份四针状氧化锌晶须，在转速为800r/min转速下搅拌均匀后，再加入1-3份黄原胶、3-8份二氧化硅包覆聚磷酸铵、3-5份氧化钼和10-30份水，在转速为800r/min转速下搅拌分散30-60min。最后加入6-12份硅微粉，搅拌均匀即可。
本发明的技术原理在于：铵盐改性丙烯酸酯乳液具有柔韧性高、附着力好的特点，将其与水玻璃混合，可以实现降低水玻璃胶的脆性和增强胶接力的目的；四针状氧化锌晶须具有耐磨、增强、降噪、吸波、抗静电、抗菌、抗老化等突出性能；硅微粉具有耐火、防腐、防水、抗渗等功能；氧化钼和二氧化硅包覆聚磷酸铵具有抑烟阻燃功效，而且二氧化硅包覆聚磷酸铵可以防止阻燃剂在使用过程中流失，起到长久的阻燃效果；豆蔻酸镁是一种高级脂肪酸盐，可以夺取水玻璃中的钠离子，起到增强胶黏剂耐水性能的作用；同时，硅、镁、磷、钼、锌等离子之间会产生协同效应，进一步提高胶黏剂的阻燃防火性能；黄原胶具有乳化、增稠、稳定的作用，有助于体系的浸润和稳定。因而，以上组合体系可以得到具有环保无醛、阻燃、抑烟、抗菌、吸声、防腐、耐水等多功效于一体的木材胶黏剂。
有益效果：本发明所用主要组分水玻璃、丙烯酸酯乳液、硅微粉、四针状氧化锌晶须、豆蔻酸镁、黄原胶等均来源丰富、性能优良、无毒无害，保证了胶黏剂的高性能和环保无醛。本发明中木材胶黏剂兼具环保、阻燃、抑烟、抗菌、吸声、防腐、耐水等功效，而且制备工艺简单，易工业化、清洁无污染。使用本发明的多效木材胶黏剂可一步实现具有多功能的各类人造板产品制造。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
首先制备二氧化硅包覆聚磷酸铵：将聚磷酸铵粉末浸入硅溶胶中24h，然后将混合物干燥、粉碎、磨细，就得到二氧化硅包覆聚磷酸铵。
将10份铵盐改性丙烯酸酯乳液缓慢加入到100份水玻璃中，手动搅拌使二者混合均匀。接着依次加入4份豆蔻酸镁、1份硅烷偶联剂、5份四针状氧化锌晶须，在转速为800r/min转速下搅拌均匀后，再加入1份黄原胶、3份二氧化硅包覆聚磷酸铵、3份氧化钼和10份水，在转速为800r/min转速下搅拌分散30min。最后加入6份硅微粉，搅拌均匀即可。
实施例2
将15份铵盐改性丙烯酸酯乳液缓慢加入到100份水玻璃中，手动搅拌使二者混合均匀。接着依次加入6份豆蔻酸镁、1.5份硅烷偶联剂、7.5份四针状氧化锌晶须，在转速为800r/min转速下搅拌均匀后，再加入2份黄原胶、5.5份二氧化硅包覆聚磷酸铵、4份氧化钼和20份水，在转速为800r/min转速下搅拌分散45min。最后加入9份硅微粉，搅拌均匀即可。
实施例3
将20份铵盐改性丙烯酸酯乳液缓慢加入到100份水玻璃中，手动搅拌使二者混合均匀。接着依次加入8份豆蔻酸镁、2份硅烷偶联剂、10份四针状氧化锌晶须，在转速为800r/min转速下搅拌均匀后，再加入3份黄原胶、8份二氧化硅包覆聚磷酸铵、5份氧化钼和30份水，在转速为800r/min转速下搅拌分散60min。最后加入12份硅微粉，搅拌均匀即可。
以上显示和描述了本发明的基本原理和主要特征及本发明的优点，本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内，本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (1)
1.一种水玻璃基多效木材胶黏剂，其特征在于，包括以下重量份的组分：
水玻璃：100份；
铵盐改性丙烯酸酯乳液：10-20份；
豆蔻酸镁：4-8份；
硅烷偶联剂：1-2份；
四针状氧化锌晶须：5-10份；
黄原胶：1-3份；
二氧化硅包覆聚磷酸铵：3-8份；
氧化钼：3-5份；
水：10-30份；
硅微粉：6-12份；
其制备步骤为：
1）首先将聚磷酸铵粉末浸入硅溶胶中24h，然后将混合物干燥、粉碎、磨细，就得到所述的二氧化硅包覆聚磷酸铵；
2）将10-20份铵盐改性丙烯酸酯乳液缓慢加入到100份水玻璃中，手动搅拌使二者混合均匀；接着依次加入4-8份豆蔻酸镁、1-2份硅烷偶联剂、5-10份四针状氧化锌晶须，在转速为800r/min转速下搅拌均匀后，再加入1-3份黄原胶、3-8份二氧化硅包覆聚磷酸铵、3-5份氧化钼和10-30份水，在转速为800r/min转速下搅拌分散30-60min；最后加入6-12份硅微粉，搅拌均匀即可。