CN104277630A - Fireproof waterproof coating material for packaging shells and preparation method thereof - Google Patents
Fireproof waterproof coating material for packaging shells and preparation method thereof Download PDFInfo
- Publication number
- CN104277630A CN104277630A CN201410491978.2A CN201410491978A CN104277630A CN 104277630 A CN104277630 A CN 104277630A CN 201410491978 A CN201410491978 A CN 201410491978A CN 104277630 A CN104277630 A CN 104277630A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- proof
- water
- covering material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a material, particularly a fireproof waterproof coating material for packaging shells and a preparation method thereof. The material is prepared from the following components in parts by weight: 30-40 parts of acrylic acid emulsion, 30-40 parts of film formation assistant, 30-40 parts of surfactant, 20-30 parts of dispersing agent, 20-30 parts of flame retardant, 20-30 parts of defoaming agent, 50-80 parts of deionized water, 50-90 parts of PVC (polyvinyl chloride) resin, 4-10 parts of stabilizer, 40-80 parts of plasticizer, 1-5 parts of ultraviolet absorbent, 5-10 parts of composite antioxidant and 3-12 parts of calcium carbonate. The fireproof waterproof coating material can effectively enhance the fireproof and waterproof quality of the packaging shells, effectively protects the safety of the product in the packaging shell, changes the single decoration function of the traditional packaging shell surface coating, and greatly enhances the reutilization quality of the packaging shell.
Description
Technical field
The present invention relates to a kind of covering material, be specifically related to a kind of fire-proof and water-proof covering material for Package casing and preparation method thereof.
Background technology
Overlay film (laminating), also known as " cross mould ", " mounting glue ", " pad pasting " etc., refers to and posts printed matter surface with transparent plastic film by hot pressing, play protection and increase gloss.Overlay film has been widely used in the front cover of books and periodicals, picture album, autograph book, postcard, product description, and wall calendar and map etc. carry out surperficial binding and layout and protection.At present, common overlay film wrapped product has carton, carton, handbag, fertilizer bag, seed packet, adhesive label etc.
Overlay film is for a skim is sticked in the outer packaging of product, makes the outward appearance of product more beautiful, glossy, and bears dirty, and needs the product adopting this technique a lot, as the outer packaging, autograph book, picture album etc. of books and periodicals.Overlay film is indispensable one technique of printing industry.
Plastics film conventional in current coating technique has: polyvinyl chloride (PVC), polypropylene (BOPP) and polyester (PET) film etc.Wherein BOPP film (15 ~ 20pm) is pliable and tough, nontoxic and transparency is high, low price, is comparatively ideal matrix material in coating technique.
Covering material of the prior art is the effect of a kind of decoration and foundation to protect mostly; still good fire prevention and water resistance is not possessed; the product of or moisture-sensitive inflammable for some; safe protection cannot be realized; therefore inventing a kind of Package casing covering material of waterproof fireproofing, is the blank of prior art.
Summary of the invention
The object of the invention is the defect for above-mentioned prior art; provide a kind of fire-proof and water-proof covering material for Package casing and preparation method thereof; this covering material effectively can improve fire prevention and the water resistance of Package casing; the safety of product in available protecting Package casing; change the single decoration function of Traditional Packing case surface covering material, substantially increase the quality of Package casing second stage employ.
Object of the present invention can be achieved through the following technical solutions:
For a fire-proof and water-proof covering material for Package casing, described covering material is formulated according to shown weight ratio scope by following component: ACRYLIC EMULSION 30-40 part, film coalescence aid 30-40 part, tensio-active agent 30-40 part, dispersion agent 20-30 part, fire retardant 20-30 part, defoamer 20-30 part, deionized water 50-80 part, polyvinyl chloride resin 50-90 part, stablizer 4-10 part, softening agent 40-80 part, UV light absorber 1-5 part, composite antioxidant 5-10 part, calcium carbonate 3-12 part.
As a further improvement on the present invention, the weight of this covering material is optimized for further: ACRYLIC EMULSION 30-35 part, film coalescence aid 35-40 part, tensio-active agent 35-40 part, dispersion agent 25-30 part, fire retardant 20-25 part, defoamer 20-28 part, deionized water 50-70 part, polyvinyl chloride resin 50-80 part, stablizer 4-8 part, softening agent 40-60 part, UV light absorber 2-5 part, composite antioxidant 5-8 part, calcium carbonate 3-10 part.
As further optimization of the present invention, this overlay film is coated with in material: ACRYLIC EMULSION is TRC-15 emulsion; Film coalescence aid is Lauryl Alcohol ester; Tensio-active agent is PE-100 wetting agent; Dispersion agent is LWJ-5040 dispersion agent; Fire retardant is antimonous oxide; Defoamer is silicone antifoam agent; Water reducer is PC-1016 high performance water reducing agent of polyocarboxy acid; Stablizer is Arizona bacilli zinc complexes or dibasic lead phosphite; UV light absorber is salol.
The invention also discloses a kind of preparation method of the fire-proof and water-proof covering material for outer cover packaging, comprise the following steps:
(1) by following weight ratio scope preparation raw material: ACRYLIC EMULSION 30-40 part, film coalescence aid 30-40 part, tensio-active agent 30-40 part, dispersion agent 20-30 part, fire retardant 20-30 part, defoamer 20-30 part, deionized water 50-80 part, polyvinyl chloride resin 50-90 part, stablizer 4-10 part, softening agent 40-80 part, UV light absorber 1-5 part, composite antioxidant 5-10 part, calcium carbonate 3-12 part;
(2) taken ACRYLIC EMULSION, film coalescence aid, tensio-active agent, dispersion agent, fire retardant, defoamer, deionized water, polyvinyl chloride resin, stablizer, softening agent, UV light absorber, composite antioxidant, calcium carbonate are added in stirrer, 25-40min is stirred under low whipping speed 180-220r/min, then taken silicate solutions is added, 50-70min is stirred under low whipping speed 450-550r/min, by order number > 120 object silk screen filter, barrelling.
The present invention effectively can improve fire prevention and the water resistance of Package casing, and in available protecting Package casing, the safety of product, changes the single decoration function of Traditional Packing shell covering material, substantially increase the quality of Package casing second stage employ.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described in further detail:
Embodiment 1
For a preparation method for the fire-proof and water-proof covering material of outer cover packaging, comprise the following steps:
(1) by following weight ratio scope preparation raw material: ACRYLIC EMULSION 30 parts, film coalescence aid 30 parts, 30 parts, tensio-active agent, dispersion agent 20 parts, fire retardant 20 parts, defoamer 20 parts, deionized water 50 parts, polyvinyl chloride resin 50 parts, stablizer 4 parts, 40 parts, softening agent, UV light absorber 1 part, composite antioxidant 5 parts, 3 parts, calcium carbonate;
(2) taken ACRYLIC EMULSION, film coalescence aid, tensio-active agent, dispersion agent, fire retardant, defoamer, deionized water, polyvinyl chloride resin, stablizer, softening agent, UV light absorber, composite antioxidant, calcium carbonate are added in stirrer, 25min is stirred under low whipping speed 180r/min, then taken silicate solutions is added, 50min is stirred under low whipping speed 450r/min, by order number 130 object silk screen filter, barrelling.
Embodiment 2
The invention also discloses a kind of preparation method of the fire-proof and water-proof covering material for outer cover packaging, comprise the following steps:
(1) by following weight ratio scope preparation raw material: ACRYLIC EMULSION 35 parts, film coalescence aid 36 parts, 37 parts, tensio-active agent, dispersion agent 25 parts, fire retardant 28 parts, defoamer 22 parts, deionized water 65 parts, polyvinyl chloride resin 80 parts, stablizer 6 parts, 50 parts, softening agent, UV light absorber 3 parts, composite antioxidant 8 parts, 10 parts, calcium carbonate;
(2) taken ACRYLIC EMULSION, film coalescence aid, tensio-active agent, dispersion agent, fire retardant, defoamer, deionized water, polyvinyl chloride resin, stablizer, softening agent, UV light absorber, composite antioxidant, calcium carbonate are added in stirrer, 30min is stirred under low whipping speed 200r/min, then taken silicate solutions is added, 60min is stirred under low whipping speed 500r/min, by order number 140 object silk screen filter, barrelling.
Embodiment 3
The invention also discloses a kind of preparation method of the fire-proof and water-proof covering material for outer cover packaging, comprise the following steps:
(1) by following weight ratio scope preparation raw material: ACRYLIC EMULSION 40 parts, film coalescence aid 40 parts, 40 parts, tensio-active agent, dispersion agent 30 parts, fire retardant 30 parts, defoamer 30 parts, deionized water 80 parts, polyvinyl chloride resin 90 parts, stablizer 10 parts, 80 parts, softening agent, UV light absorber 5 parts, composite antioxidant 10 parts, 12 parts, calcium carbonate;
(2) taken ACRYLIC EMULSION, film coalescence aid, tensio-active agent, dispersion agent, fire retardant, defoamer, deionized water, polyvinyl chloride resin, stablizer, softening agent, UV light absorber, composite antioxidant, calcium carbonate are added in stirrer, 40min is stirred under low whipping speed 220r/min, then taken silicate solutions is added, 70min is stirred under low whipping speed 550r/min, by order number 130 object silk screen filter, barrelling.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technology people of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (4)
1. for a fire-proof and water-proof covering material for Package casing, it is characterized in that: described covering material is formulated according to shown weight ratio scope by following component: ACRYLIC EMULSION 30-40 part, film coalescence aid 30-40 part, tensio-active agent 30-40 part, dispersion agent 20-30 part, fire retardant 20-30 part, defoamer 20-30 part, deionized water 50-80 part, polyvinyl chloride resin 50-90 part, stablizer 4-10 part, softening agent 40-80 part, UV light absorber 1-5 part, composite antioxidant 5-10 part, calcium carbonate 3-12 part.
2. a kind of fire-proof and water-proof covering material for outer cover packaging according to claim 1, is characterized in that: the weight of described covering material is optimized for further: ACRYLIC EMULSION 30-35 part, film coalescence aid 35-40 part, tensio-active agent 35-40 part, dispersion agent 25-30 part, fire retardant 20-25 part, defoamer 20-28 part, deionized water 50-70 part, polyvinyl chloride resin 50-80 part, stablizer 4-8 part, softening agent 40-60 part, UV light absorber 2-5 part, composite antioxidant 5-8 part, calcium carbonate 3-10 part.
3., according to a kind of fire-proof and water-proof covering material for outer cover packaging according to claim 1 or claim 2, it is characterized in that: described ACRYLIC EMULSION is TRC-15 emulsion; Described film coalescence aid for tensio-active agent described in Lauryl Alcohol ester be PE-100 wetting agent; Described dispersion agent is LWJ-5040 dispersion agent; Described fire retardant is antimonous oxide; Described defoamer is silicone antifoam agent; Described water reducer is PC-1016 high performance water reducing agent of polyocarboxy acid; Described stablizer is Arizona bacilli zinc complexes or dibasic lead phosphite; Described UV light absorber is salol.
4., according to the preparation method of any described in claim 1-3 for the fire-proof and water-proof covering material of outer cover packaging, it is characterized in that, comprise the following steps:
(1) by following weight ratio scope preparation raw material: ACRYLIC EMULSION 30-40 part, film coalescence aid 30-40 part, tensio-active agent 30-40 part, dispersion agent 20-30 part, fire retardant 20-30 part, defoamer 20-30 part, deionized water 50-80 part, polyvinyl chloride resin 50-90 part, stablizer 4-10 part, softening agent 40-80 part, UV light absorber 1-5 part, composite antioxidant 5-10 part, calcium carbonate 3-12 part;
(2) taken ACRYLIC EMULSION, film coalescence aid, tensio-active agent, dispersion agent, fire retardant, defoamer, deionized water, polyvinyl chloride resin, stablizer, softening agent, UV light absorber, composite antioxidant, calcium carbonate are added in stirrer, 25-40min is stirred under low whipping speed 180-220r/min, then taken silicate solutions is added, 50-70min is stirred under low whipping speed 450-550r/min, by order number > 120 object silk screen filter, barrelling.