CN104211302B - 一种光伏玻璃板及其制备方法 - Google Patents

一种光伏玻璃板及其制备方法 Download PDF

Info

Publication number
CN104211302B
CN104211302B CN201410442688.9A CN201410442688A CN104211302B CN 104211302 B CN104211302 B CN 104211302B CN 201410442688 A CN201410442688 A CN 201410442688A CN 104211302 B CN104211302 B CN 104211302B
Authority
CN
China
Prior art keywords
parts
glass plate
oxide
heat
raw materials
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410442688.9A
Other languages
English (en)
Other versions
CN104211302A (zh
Inventor
江秀友
郭昌林
冯尚庆
魏飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Weifang Energy Technology Co ltd
Original Assignee
Electric Co Of Guo Wang Yishui Shandong County
State Grid Corp of China SGCC
Linyi Power Supply Co of State Grid Shandong Electric Power Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Electric Co Of Guo Wang Yishui Shandong County, State Grid Corp of China SGCC, Linyi Power Supply Co of State Grid Shandong Electric Power Co Ltd filed Critical Electric Co Of Guo Wang Yishui Shandong County
Priority to CN201410442688.9A priority Critical patent/CN104211302B/zh
Publication of CN104211302A publication Critical patent/CN104211302A/zh
Application granted granted Critical
Publication of CN104211302B publication Critical patent/CN104211302B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于玻璃制造领域，尤其涉及一种光伏玻璃板，其由如下重量份的原料制备而成：石英砂，氧化铝，方解石，芒硝，高岭土，氧化钡，氧化钇，氧化钐以及碳酸锶。本发明还公开了上述光伏玻璃板的制备方法。本发明玻璃板具备较好的透光性，并且机械性能以及热稳定好等优点，具备较好的应用前景。

Description

一种光伏玻璃板及其制备方法
技术领域
本发明属于玻璃制造领域，尤其涉及一种光伏玻璃板及其制备方法。
背景技术
光伏是通过光电效应或者光化学效应直接把光能转化成电能的装置。以光电效应工作的薄膜式太阳能电池为主流，而以光化学效应工作的实施光伏已经处于走出实验室进行市场的阶段。随着光伏产业的发展，对光伏玻璃板玻璃品种的要求越来越广，因此不同新品种的玻璃逐渐被研制出来，如专利申请号为2007100545499的申请中，公开了一种光学玻璃，这种玻璃具备较好的透光率，但是硬度、可熔性及可加工性不够；法国圣戈班公司和美国PPG公司生产了高透光度玻璃：但其透光率只能达到89％，且价格很高，如3.2mm厚的玻璃每平方米售价为120元。现有技术需要我们开发一种透光率好，机械性能以及热稳定性能高的光伏玻璃板。
发明内容
本发明的目的是解决现有技术中光伏玻璃板的诸多缺陷，经过大量试验和探索，改变现有的原料组成及制备工艺，提供一种光伏玻璃板，该玻璃板具备较好的透光性，并且机械性能以及热稳定好等优点；本发明还公开了上述光伏玻璃板的制备方法。
为了实现上述目的，本发明的技术方案通过如下方式来实现的：
一种光伏玻璃板，其由如下重量份的原料制备而成：石英砂100-150份，氧化铝12-15份，方解石8-10份，芒硝7-9份，高岭土4-5份，氧化钡1-2份，氧化钇0.2-0.3份，氧化钐0.2-0.3份，碳酸锶0.1-0.2份。
所述玻璃板按照如下方法制备而成：
步骤1）按照上述重量份称取各原料备用；
步骤2）首先将刚玉坩埚置于硅钼棒炉中，以20℃/min的速度升温至1300℃，然后将原料依次添加到刚玉坩埚中，保温反应60min，然后以15℃/min的速度升温至1500℃，保温30min，将熔化好的玻璃液浇铸到石墨模具内，成形后立即转入箱式电阻炉中退火，退火温度600℃，然后降温自然冷却，即得。
优选地，玻璃板的厚度为3.2mm。
本发明取得有益效果主要包括：本发明制备的玻璃板提高了太阳光透射比和可见光透射比，降低了紫外线透射比，大大提高光伏电池的光电转换效率；本发明制备的玻璃板热稳定性能耗，机械强度高，不易破碎；本发明原料选择合理，制备方法简单，适合大规模工业化生产。
具体实施方式
为了使本技术领域的人员更好地理解本申请中的技术方案，下面将结合本申请具体实施例，对本发明进行更加清楚、完整地描述，显然，所描述的实施例仅仅是本申请一部分实施例，而不是全部的实施例。基于本申请中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都应当属于本发明保护的范围。
实施例1
一种光伏玻璃板，其由如下重量份的原料制备而成：石英砂100份，氧化铝12份，方解石8份，芒硝7份，高岭土4份，氧化钡1份，氧化钇0.2份，氧化钐0.2份，碳酸锶0.1份。
所述玻璃板按照如下方法制备而成：
步骤1）按照上述重量份称取各原料备用；
步骤2）首先将刚玉坩埚置于硅钼棒炉中，以20℃/min的速度升温至1300℃，然后将原料依次添加到刚玉坩埚中，保温反应60min，然后以15℃/min的速度升温至1500℃，保温30min，将熔化好的玻璃液浇铸到石墨模具内，成形后立即转入箱式电阻炉中退火，退火温度600℃，然后降温自然冷却，即得。
实施例2
一种光伏玻璃板，其由如下重量份的原料制备而成：石英砂150份，氧化铝15份，方解石10份，芒硝9份，高岭土5份，氧化钡2份，氧化钇0.3份，氧化钐0.3份，碳酸锶0.2份。
所述玻璃板按照如下方法制备而成：
步骤1）按照上述重量份称取各原料备用；
步骤2）首先将刚玉坩埚置于硅钼棒炉中，以20℃/min的速度升温至1300℃，然后将原料依次添加到刚玉坩埚中，保温反应60min，然后以15℃/min的速度升温至1500℃，保温30min，将熔化好的玻璃液浇铸到石墨模具内，成形后立即转入箱式电阻炉中退火，退火温度600℃，然后降温自然冷却，即得。
实施例3
本发明实施例1-2制备的玻璃板的性能测试：
一、玻璃板厚度均为3.2mm；热膨胀系数是显示样品对原长度的相对膨胀率的值，根据DIN51045标准来测定；抗折强度采用陶瓷试验机测定；显微维氏硬度采用数显显微硬度仪，利用维氏压头，载荷为100g，时间为30s。具体见表1：
表1
组别 维氏硬度（HV 0.1/30） 热膨胀系数(×10-7/K) 抗折强度Gpa
实施例1 513 71.0 84.6
实施例2 509 71.5 85.1
二、以3.2mm样品为例，经Cary500型分光光度计测试结果如下表2：
表2
组别 可见光透射比% 太阳能透射比% 紫外线透射比%
实施例1 94.9 96.2 80.4
实施例2 94.8 95.7 81.0
结论：本发明实施例1-2制备的光伏玻璃板提高了太阳光透射比和可见光透射比，降低了紫外线透射比，并且热稳定性能耗，机械强度高，不易破碎，各种性能均优于市场同类产品。
上面结合具体实施例对本发明进行了示例性的描述，显然本发明的实现并不受上述方式的限制，只要采用了本发明的方法构思和技术方案进行的各种改进，或未经改进将本发明的构思和技术方案直接应用于其它场合的，均在本发明的保护范围内。

Claims (2)

1.一种光伏玻璃板，其特征在于，所述玻璃板由如下重量份的原料制备而成：石英砂100-150份，氧化铝12-15份，方解石8-10份，芒硝7-9份，高岭土4-5份，氧化钡1-2份，氧化钇0.2-0.3份，氧化钐0.2-0.3份，碳酸锶0.1-0.2份；
所述玻璃板按照如下方法制备而成：
步骤1）按照重量份称取各原料备用；
步骤2）首先将刚玉坩埚置于硅钼棒炉中，以20℃/min的速度升温至1300℃，然后将原料依次添加到刚玉坩埚中，保温反应60min，然后以15℃/min的速度升温至1500℃，保温30min，将熔化好的玻璃液浇铸到石墨模具内，成形后立即转入箱式电阻炉中退火，退火温度600℃，然后降温自然冷却，即得。
2.如权利要求1所述的玻璃板在光伏中的应用。
CN201410442688.9A 2014-09-02 2014-09-02 一种光伏玻璃板及其制备方法 Active CN104211302B (zh)