CN104163652A - GRC (glass fiber reinforced cement) partition plate and manufacturing technique thereof - Google Patents
GRC (glass fiber reinforced cement) partition plate and manufacturing technique thereof Download PDFInfo
- Publication number
- CN104163652A CN104163652A CN201410402050.2A CN201410402050A CN104163652A CN 104163652 A CN104163652 A CN 104163652A CN 201410402050 A CN201410402050 A CN 201410402050A CN 104163652 A CN104163652 A CN 104163652A
- Authority
- CN
- China
- Prior art keywords
- parts
- partition plate
- grc
- water
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a GRC (glass fiber reinforced cement) partition plate which is prepared from the following raw materials in parts by weight: 90 parts of polyphenylene particle, 1 part of water 108 adhesive powder, 200 parts of calcium silicate board, 700 parts of ordinary Portland cement, 1 part of foaming agent and 210 parts of water. The light-weight partition plate is mainly prepared from a GRC material and uses the specific formula and technique, and thus, the strength, transparency and other properties of the partition plate can be greatly enhanced.
Description
Technical field
The present invention relates to GRC partition plate and manufacture field thereof, particularly relate to a kind of GRC partition plate and manufacturing process thereof.
Background technology
GRC material is also glass fiber reinforced concrete, and it is to take the fiber cement composite material that alkali resistant glass fibre is body material as strongthener, sand-cement slurry, and light cellular partition board is that a kind of innovative panellised wall material has been widely used in various construction works.
Summary of the invention
For above problem, the present invention designs a kind of GRC partition plate and manufacturing process thereof, the main employing GRC material of its light cellular partition board makes use, have and use specific formula and technique, thereby can significantly improve the partition plate intensity transparency and various aspects of performance, for reaching this object, the invention provides a kind of GRC partition plate, the weight proportion of its each feed composition is as follows, comprises 90 parts of granular polystyrenes, 1 part of water 108 rubber powder, 200 parts of calcium silicate boards, 700 parts of ordinary Portland cements, 1 part of whipping agent, 210 parts, water.
Manufacturing process of the present invention is as follows: 90 kilograms of granular polystyrenes are dropped in blender and twist and mix, 210 kilograms, water reinjects, drop into again 1 kilogram of whipping agent, 1 kilogram of water 108 rubber powder, then drop into 700 kilograms of ordinary Portland cements, with mould, spray mold oil, put into calcium silicate board, strand is mixed after 2 minutes and is poured into slip, modifies die face depanning in two hours, seven days packings of maintenance.
The invention provides a kind of GRC partition plate and manufacturing process thereof, this partition plate adopts granular polystyrene, water 108 rubber powders, calcium silicate board, ordinary Portland cement, whipping agent and water to make, thereby and adopt special process can significantly improve partition plate performance, and the gained GRC partition plate transparency and various aspects of performance are all largely increased.
?
Embodiment
Below in conjunction with embodiment, invention is described in detail:
The present invention designs a kind of GRC partition plate and manufacturing process thereof, and the main employing GRC material of its light cellular partition board makes use, has and uses specific formula and technique, thereby can significantly improve the partition plate intensity transparency and various aspects of performance.
As an embodiment of the present invention, the invention provides a kind of GRC partition plate, the weight proportion of its each feed composition is as follows, comprises 90 parts of granular polystyrenes, 1 part of water 108 rubber powder, 200 parts of calcium silicate boards, 700 parts of ordinary Portland cements, 1 part of whipping agent, 210 parts, water.
Manufacturing process of the present invention is as follows: 90 kilograms of granular polystyrenes are dropped in blender and twist and mix, 210 kilograms, water reinjects, drop into again 1 kilogram of whipping agent, 1 kilogram of water 108 rubber powder, then drop into 700 kilograms of ordinary Portland cements, with mould, spray mold oil, put into calcium silicate board, strand is mixed after 2 minutes and is poured into slip, modifies die face depanning in two hours, seven days packings of maintenance.
The above, be only preferred embodiment of the present invention, is not the present invention to be done to the restriction of any other form, and according to any modification or equivalent variations that technical spirit of the present invention is done, still belongs to the present invention's scope required for protection.
Claims (2)
1. a GRC partition plate, the weight proportion of its each feed composition is as follows, it is characterized in that: comprise 90 parts of granular polystyrenes, 1 part of water 108 rubber powder, 200 parts of calcium silicate boards, 700 parts of ordinary Portland cements, 1 part of whipping agent, 210 parts, water.
2. its manufacturing process of GRC partition plate according to claim 1, it is characterized in that: 90 kilograms of granular polystyrenes are dropped in blender and twist and mix, reinject 210 kilograms, water, then drop into 1 kilogram of whipping agent, 1 kilogram of water 108 rubber powder, drop into again 700 kilograms of ordinary Portland cements, with mould, spray mold oil, put into calcium silicate board, strand is mixed after 2 minutes and is poured into slip, modify die face depanning in two hours, seven days packings of maintenance.