CN104119743A - 一种高粘度多彩涂料 - Google Patents
一种高粘度多彩涂料 Download PDFInfo
- Publication number
- CN104119743A CN104119743A CN201410374168.9A CN201410374168A CN104119743A CN 104119743 A CN104119743 A CN 104119743A CN 201410374168 A CN201410374168 A CN 201410374168A CN 104119743 A CN104119743 A CN 104119743A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- high viscosity
- multicolor finish
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种高粘度多彩涂料，其原料按重量份数配比如下：聚乙烯醇100份；瓜尔胶5-15份；钛白粉10-20份；氨水50-60份；碳酸钙35-45份；膨润土45-55份；去离子水80-90份；蓖麻油30-40份；颜料10-20份；石蜡油25-35份；丙烯酸乳液20-30份；二甲苯30-40份；增塑剂4-10份；甲苯15-35份；松香20-40份；硅胶5-25份；产品搅拌后呈均匀状态，无硬块，涂膜耐擦洗2000-4000次；在水中浸泡10-20d后无掉粉、皱皮、起泡和脱落现象；实干8-10h，表干0.5-1.5h；涂膜色彩鲜艳、外观平整光洁，可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域，尤其涉及一种高粘度多彩涂料。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或碳酸钙配制而成的粘稠液体。中国涂料界比较权威的《涂料工艺》一书是这样定义的：“涂料是一种材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。”涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧保护膜的物料，称为涂料。涂料与油漆是同一概念。油漆是人们沿用已久的习惯名称，引进我国后，就一直利用在建筑行业。涂料的作用可以概括为三个方面：保护作用，装饰作用，特殊功能作用。涂料的一般组成：包含成膜物质、颜填料、溶剂、助剂。
涂料是指应用于物体表面而能结成坚韧保护膜的物料的总称，建筑涂料是涂料中的一个重要类别，在我国，一般将用于建筑物内墙，外墙，顶棚，地面，卫生间的涂料称为建筑涂料。聚乙烯醇，有机化合物，白色片状、絮状或粉末状固体，无味。溶于水，不溶于汽油、煤油、植物油、苯、甲苯、二氯乙烷、四氯化碳、丙酮、醋酸乙酯、甲醇、乙二醇等。微溶于二甲基亚砜。聚乙烯醇是重要的化工原料，用于制造聚乙烯醇缩醛、耐汽油管道和维尼纶合成纤维、织物处理剂、乳化剂、纸张涂层、粘合剂等。
所谓高粘度多彩涂料是由不相容的两相成分组成，其中一相分散介质为连续相，另一相为分散相，涂装时，通过一次性喷涂，便可得到豪华、美观、高粘度多彩的图案。而随着人性化理念的普及，及新型和谐社会的构成，设计一种耐水性、耐擦洗性及干燥时间短的高粘度多彩涂料是非常必要的。
发明内容
解决的技术问题：
本申请针对上述技术问题，提供一种高粘度多彩涂料，解决现有高粘度多彩涂料耐水性和耐擦洗性差、干燥时间长等技术问题。
技术方案：
一种高粘度多彩涂料，所述高粘度多彩涂料的原料按重量份数配比如下：聚乙烯醇100份；瓜尔胶5-15份；钛白粉10-20份；氨水50-60份；碳酸钙35-45份；膨润土45-55份；去离子水80-90份；蓖麻油30-40份；颜料10-20份；石蜡油25-35份；丙烯酸乳液20-30份；二甲苯30-40份；增塑剂4-10份；甲苯15-35份；松香20-40份；硅胶5-25份。
作为本发明的一种优选技术方案：所述高粘度多彩涂料的原料按重量份数配比如下：聚乙烯醇100份；瓜尔胶10份；钛白粉15份；氨水55份；碳酸钙40份；膨润土50份；去离子水85份；蓖麻油35份；颜料15份；石蜡油30份；丙烯酸乳液25份；二甲苯35份；增塑剂7份；甲苯25份；松香30份；硅胶15份。
作为本发明的一种优选技术方案：所述颜料采用氧化铁红、氧化铁绿或氧化铁黄。
作为本发明的一种优选技术方案：所述增塑剂采用邻苯二甲酸二丁酯。
有益效果：
本发明所述一种高粘度多彩涂料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品搅拌后呈均匀状态，无硬块，涂膜耐擦洗2000-4000次；2、在水中浸泡10-20d后无掉粉、皱皮、起泡和脱落现象；3、实干8-10h，表干0.5-1.5h；4、涂膜色彩鲜艳、外观平整光洁，可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种高粘度多彩涂料，其原料按重量份数配比如下：聚乙烯醇100份；瓜尔胶15份；钛白粉20份；氨水60份；碳酸钙45份；膨润土55份；去离子水90份；蓖麻油40份；氧化铁黄20份；石蜡油35份；丙烯酸乳液30份；二甲苯40份；邻苯二甲酸二丁酯10份；甲苯35份；松香40份；硅胶25份。
将聚乙烯醇、钛白粉、氨水、碳酸钙和膨润土加入去离子水中，加热至40℃搅拌3h，加入蓖麻油、石蜡油、丙烯酸乳液、二甲苯、松香和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入瓜尔胶和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜耐擦洗3000次；在水中浸泡15d后无掉粉、皱皮、起泡和脱落现象；实干9h，表干1h。
实施例2:
一种高粘度多彩涂料，其原料按重量份数配比如下：聚乙烯醇100份；瓜尔胶5份；钛白粉10份；氨水50份；碳酸钙35份；膨润土45份；去离子水80份；蓖麻油30份；氧化铁绿10份；石蜡油25份；丙烯酸乳液20份；二甲苯30份；邻苯二甲酸二丁酯4份；甲苯15份；松香20份；硅胶5份。
将聚乙烯醇、钛白粉、氨水、碳酸钙和膨润土加入去离子水中，加热至40℃搅拌3h，加入蓖麻油、石蜡油、丙烯酸乳液、二甲苯、松香和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入瓜尔胶和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜耐擦洗2000次；在水中浸泡10d后无掉粉、皱皮、起泡和脱落现象；实干10h，表干1.5h。
实施例3:
一种高粘度多彩涂料，其原料按重量份数配比如下：聚乙烯醇100份；瓜尔胶10份；钛白粉15份；氨水55份；碳酸钙40份；膨润土50份；去离子水85份；蓖麻油35份；氧化铁红15份；石蜡油30份；丙烯酸乳液25份；二甲苯35份；邻苯二甲酸二丁酯7份；甲苯25份；松香30份；硅胶15份。
将聚乙烯醇、钛白粉、氨水、碳酸钙和膨润土加入去离子水中，加热至40℃搅拌3h，加入蓖麻油、石蜡油、丙烯酸乳液、二甲苯、松香和邻苯二甲酸二丁酯，升温至50℃用球磨机球磨10min，加入瓜尔胶和剩余原料，升温至60℃搅拌10h后既得成品。
涂膜耐擦洗4000次；在水中浸泡20d后无掉粉、皱皮、起泡和脱落现象；实干8h，表干0.5h。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。
Claims (4)
1.一种高粘度多彩涂料，其特征在于所述高粘度多彩涂料的原料按重量份数配比如下：聚乙烯醇100份；瓜尔胶5-15份；钛白粉10-20份；氨水50-60份；碳酸钙35-45份；膨润土45-55份；去离子水80-90份；蓖麻油30-40份；颜料10-20份；石蜡油25-35份；丙烯酸乳液20-30份；二甲苯30-40份；增塑剂4-10份；甲苯15-35份；松香20-40份；硅胶5-25份。
2.根据权利要求1所述的一种高粘度多彩涂料，其特征在于所述高粘度多彩涂料的原料按重量份数配比如下：聚乙烯醇100份；瓜尔胶10份；钛白粉15份；氨水55份；碳酸钙40份；膨润土50份；去离子水85份；蓖麻油35份；颜料15份；石蜡油30份；丙烯酸乳液25份；二甲苯35份；增塑剂7份；甲苯25份；松香30份；硅胶15份。
3.根据权利要求1所述的一种高粘度多彩涂料，其特征在于：所述颜料采用氧化铁红、氧化铁绿或氧化铁黄。
4.根据权利要求1所述的一种高粘度多彩涂料，其特征在于：所述增塑剂采用邻苯二甲酸二丁酯。