CN104109303A - 一种耐热105℃聚氯乙烯电缆料及其制备方法 - Google Patents

一种耐热105℃聚氯乙烯电缆料及其制备方法 Download PDF

Info

Publication number
CN104109303A
CN104109303A CN201410284164.1A CN201410284164A CN104109303A CN 104109303 A CN104109303 A CN 104109303A CN 201410284164 A CN201410284164 A CN 201410284164A CN 104109303 A CN104109303 A CN 104109303A
Authority
CN
China
Prior art keywords
parts
polyvinyl chloride
pvc
cable material
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410284164.1A
Other languages
English (en)
Inventor
谷道荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI RONGJIU OPTICAL FIBER COMMUNICATION Co Ltd
Original Assignee
ANHUI RONGJIU OPTICAL FIBER COMMUNICATION Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI RONGJIU OPTICAL FIBER COMMUNICATION Co Ltd filed Critical ANHUI RONGJIU OPTICAL FIBER COMMUNICATION Co Ltd
Priority to CN201410284164.1A priority Critical patent/CN104109303A/zh
Publication of CN104109303A publication Critical patent/CN104109303A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐热105℃聚氯乙烯电缆料及其制备方法，由下列重量份的原料制成：SG-3聚氯乙烯树脂100、双酚A型聚碳酸酯15-20、氯化聚乙烯8-12、偏苯三酸三辛酯25-35、邻苯二甲酸二异癸酯10-15、季戊四醇硬脂酸酯5-10、硫酸钡10-15、纳米硅灰石5-10、复合填料4-8、苯胺甲基三乙氧基硅烷1-2、钙锌复合稳定剂5-8、硬脂酸钡1-2、乙撑双硬脂酰胺1-2、硼酸锌10-15、十溴二苯醚5-10、抗氧剂10350.5-1；本发明电缆料具有优良的机械强度、热稳定性、耐候耐老化、耐磨等性能，且阻燃效果好，火焰消失后火苗能迅速熄灭，不会延然其它材料，燃烧时发烟量少，可在105℃下长期使用，提高电线电缆的使用寿命。

Description

一种耐热105℃聚氯乙烯电缆料及其制备方法
技术领域
本发明涉及一种电缆料及其制备方法，具体涉及一种耐热105℃电缆料及其制备方法。
背景技术
聚氯乙烯(PVC)由于具有难燃、耐油、耐电晕、耐化学腐蚀和良好的耐水性能和加工性能，因此广泛应用于电线电缆的护层材料。但是现有的聚氯乙烯电缆料很难在高温下长期使用，容易失效，造成极大地经济损失。
发明内容
本发明的目的在于针对现有技术的不足，提供一种一种耐热105℃电缆料及其制备方法。
本发明采用的技术方案如下：
一种耐热105℃聚氯乙烯电缆料，由下列重量份的原料制成：SG-3聚氯乙烯树脂100、双酚A型聚碳酸酯15-20、氯化聚乙烯8-12、偏苯三酸三辛酯25-35、邻苯二甲酸二异癸酯10-15、季戊四醇硬脂酸酯5-10、硫酸钡10-15、纳米硅灰石5-10、复合填料4-8、苯胺甲基三乙氧基硅烷1-2、钙锌复合稳定剂5-8、硬脂酸钡1-2、乙撑双硬脂酰胺1-2、硼酸锌10-15、十溴二苯醚5-10、抗氧剂10350.5-1；
所述复合填料的制备方法如下：a.取下列重量份的原料：高岭石10-15、叶腊石5-10、沸石粉4-8、粉煤灰3-6、硬脂酸2-3、异丙基二硬脂酰氧基铝酸酯1-2、木质素磺酸钙3-5、环氧亚麻油10-15、纳米氧化锆2-4、纳米玉石粉4-8、异辛酸铈1-2、异辛酸钕0.5-1；b、将高岭石、叶腊石在520-540℃下煅烧3-5h，冷却至室温后放入浓度为10-15％的盐酸溶液中，70-80℃水浴加热1-2h，取出用蒸馏水洗涤至中性，烘干，粉碎至粒度为0.1-0.2mm，然后加入硬脂酸、异丙基二硬脂酰氧基铝酸酯、沸石粉、粉煤灰、木质素磺酸钙，4000-5000rpm高速研磨10-15min，烘干，粉碎，过300-400目筛，c、将过筛后的粉末与其余原料混合，1500-2000rpm高速搅拌5-10min即可。
耐热105℃聚氯乙烯电缆料的制备方法，包括以下步骤：
(1)将SG-3聚氯乙烯树脂、偏苯三酸三辛酯、季戊四醇硬脂酸酯、硫酸钡、纳米硅灰石、钙锌复合稳定剂、硼酸锌、乙撑双硬脂酰胺、抗氧剂1035投入高速捏合机内，在90-100℃下高速捏合8-12min；
(2)将双酚A型聚碳酸酯、氯化聚乙烯、邻苯二甲酸二异癸酯、复合填料、苯胺甲基三乙氧基硅烷、硬脂酸钡、十溴二苯醚投入开炼机内，控制辊温95-105℃，辊距0.3-0.5mm，混炼5-10min，而后经平板切粒机切成母料粒子；
(3)将步骤(1)捏合好的PVC投入开炼机中塑炼，辊温控制在145-165℃，待PVC塑化包辊后，将辊温降至100-110℃，加入步骤(2)制得的母料粒子合炼，采用高剪切的方法，塑炼15-25min，均匀后挤塑造粒即可。
本发明的有益效果：
本发明电缆料具有优良的机械强度、热稳定性、耐候耐老化、耐磨等性能，且阻燃效果好，火焰消失后火苗能迅速熄灭，不会延然其它材料，燃烧时发烟量少，可在105℃下长期使用，提高电线电缆的使用寿命。
具体实施方式
一种耐热105℃聚氯乙烯电缆料，由下列重量(kg)的原料制成：SG-3聚氯乙烯树脂100、双酚A型聚碳酸酯15、氯化聚乙烯10、偏苯三酸三辛酯30、邻苯二甲酸二异癸酯15、季戊四醇硬脂酸酯7、硫酸钡15、纳米硅灰石8、复合填料6、苯胺甲基三乙氧基硅烷1.5、钙锌复合稳定剂6、硬脂酸钡1.5、乙撑双硬脂酰胺2、硼酸锌15、十溴二苯醚6、抗氧剂10350.6；
所述复合填料的制备方法如下：a.取下列重量(kg)的原料：高岭石10、叶腊石10、沸石粉6、粉煤灰4、硬脂酸2、异丙基二硬脂酰氧基铝酸酯1.5、木质素磺酸钙4、环氧亚麻油10、纳米氧化锆3、纳米玉石粉6、异辛酸铈1.5、异辛酸钕0.5；b、将高岭石、叶腊石在540℃下煅烧3h，冷却至室温后放入浓度为12％的盐酸溶液中，75℃水浴加热1.5h，取出用蒸馏水洗涤至中性，烘干，粉碎至粒度为0.1mm，然后加入硬脂酸、异丙基二硬脂酰氧基铝酸酯、沸石粉、粉煤灰、木质素磺酸钙，5000rpm高速研磨10min，烘干，粉碎，过400目筛，c、将过筛后的粉末与其余原料混合，1500rpm高速搅拌8min即可。
耐热105℃聚氯乙烯电缆料的制备方法，包括以下步骤：
(1)将SG-3聚氯乙烯树脂、偏苯三酸三辛酯、季戊四醇硬脂酸酯、硫酸钡、纳米硅灰石、钙锌复合稳定剂、硼酸锌、乙撑双硬脂酰胺、抗氧剂1035投入高速捏合机内，在98℃下高速捏合10min；
(2)将双酚A型聚碳酸酯、氯化聚乙烯、邻苯二甲酸二异癸酯、复合填料、苯胺甲基三乙氧基硅烷、硬脂酸钡、十溴二苯醚投入开炼机内，控制辊温102℃，辊距0.3mm，混炼6min，而后经平板切粒机切成母料粒子；
(3)将步骤(1)捏合好的PVC投入开炼机中塑炼，辊温为155℃，待PVC塑化包辊后，将辊温降至105℃，加入步骤(2)制得的母料粒子合炼，采用高剪切的方法，塑炼25min，均匀后挤塑造粒即可。
制得的电缆料的性能测试结果如下：

Claims (2)

1.一种耐热105℃聚氯乙烯电缆料，其特征在于，由下列重量份的原料制成：SG-3聚氯乙烯树脂 100、双酚A型聚碳酸酯15-20、氯化聚乙烯8-12、偏苯三酸三辛酯25-35、邻苯二甲酸二异癸酯10-15、季戊四醇硬脂酸酯5-10、硫酸钡10-15、纳米硅灰石5-10、复合填料4-8、苯胺甲基三乙氧基硅烷1-2、钙锌复合稳定剂5-8、硬脂酸钡1-2、乙撑双硬脂酰胺1-2、硼酸锌10-15、十溴二苯醚5-10、抗氧剂1035 0.5-1；
    所述复合填料的制备方法如下：a.取下列重量份的原料：高岭石10-15、叶腊石5-10、沸石粉4-8、粉煤灰3-6、硬脂酸2-3、异丙基二硬脂酰氧基铝酸酯 1-2、木质素磺酸钙3-5、环氧亚麻油10-15、纳米氧化锆2-4、纳米玉石粉4-8、异辛酸铈1-2、异辛酸钕0.5-1；b、将高岭石、叶腊石在520-540℃下煅烧3-5h，冷却至室温后放入浓度为10-15%的盐酸溶液中，70-80℃水浴加热1-2h，取出用蒸馏水洗涤至中性，烘干，粉碎至粒度为0.1-0.2mm，然后加入硬脂酸、异丙基二硬脂酰氧基铝酸酯、沸石粉、粉煤灰、木质素磺酸钙，4000-5000rpm高速研磨10-15min，烘干，粉碎，过300-400目筛，c、将过筛后的粉末与其余原料混合，1500-2000rpm高速搅拌5-10min即可。
2.如权利要求1所述的耐热105℃聚氯乙烯电缆料的制备方法，其特征在于包括以下步骤：
（1）将SG-3聚氯乙烯树脂 、偏苯三酸三辛酯、季戊四醇硬脂酸酯、硫酸钡、纳米硅灰石、钙锌复合稳定剂、硼酸锌、乙撑双硬脂酰胺、抗氧剂1035投入高速捏合机内，在90-100℃下高速捏合8-12min；
(2)将双酚A型聚碳酸酯、氯化聚乙烯、邻苯二甲酸二异癸酯、复合填料、苯胺甲基三乙氧基硅烷、硬脂酸钡、十溴二苯醚投入开炼机内，控制辊温95-105℃，辊距0.3-0.5mm，混炼5-10min，而后经平板切粒机切成母料粒子；
将步骤（1）捏合好的PVC投入开炼机中塑炼，辊温控制在145-165℃，待PVC塑化包辊后，将辊温降至100-110℃，加入步骤（2）制得的母料粒子合炼，采用高剪切的方法，塑炼15-25min，均匀后挤塑造粒即可。
CN201410284164.1A 2014-06-23 2014-06-23 一种耐热105℃聚氯乙烯电缆料及其制备方法 Pending CN104109303A (zh)