CN104108898A - Concrete waterproof agent - Google Patents
Concrete waterproof agent Download PDFInfo
- Publication number
- CN104108898A CN104108898A CN201410293335.7A CN201410293335A CN104108898A CN 104108898 A CN104108898 A CN 104108898A CN 201410293335 A CN201410293335 A CN 201410293335A CN 104108898 A CN104108898 A CN 104108898A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- concrete
- waterproof agent
- acid ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a concrete waterproof agent, which comprises the following raw materials by weight: 18-26 parts of hydrophobic gas phase silica, 10-15 parts of zeolite powder, 6-12 parts of slag micro powder, 4.5-6.5 parts of 2-phosphonic acid butane-1,2,4-tricarboxylic acid, 9-18 parts of earthy graphite powder, 20-30 parts of AF-2 type high efficiency water reducer, 5-10 parts of qercetin, 7-14 parts of methyl silanol sodium, 4-9 parts of butyl stearate, 10-15 parts of hydrophobic perlite, 5-10 parts of tall oil asphalt sulfonate, 8-16 parts of polymethyltriethoxysilan, 3-5 parts of sorbose calcium, 2.5-4.5 parts of dicyclohexyl amine nitrite, 3-5 parts of ethoxylated lanolin and 4-7 parts of auxiliary agent. The concrete waterproof agent can effectively improve the capillary structure, block the capillary channel in the concrete, and obviously increase the anti-permeability and water resistance functions; the anti-permeability level can reach more than P25, and the concrete waterproof agent has enhancement, water reduction and crack resistance efficacy and can improve the workability of the concrete, the water seepage rate is less, working performance of the concrete can be obviously improved, and the concrete waterproof agent is suitable for water resistance of flat roof as well as anti-permeability and moisture resistance engineering of building ground.
Description
Technical field
The present invention relates to a kind of concrete waterproofer, belong to concrete admixture field.
Background technology
Concrete admixture, is called for short admixture, refers to before mixing concrete mixing or in mix process, mixes to improve the material of concrete performance.Because admixture can improve concrete performance effectively, and have good economic benefit, be all widely used in many countries, the application in engineering more and more comes into one's own, and becomes material indispensable in concrete.Wherein water-resisting agent is the one in concrete admixture, and it can improve concrete impervious water-proof function.Along with developing rapidly of Concrete Industry, the impervious water resistance of the water-resisting agent that used in the market cannot meet the requirement of high performance concrete.
Summary of the invention
To the object of the invention is the defect existing in prior art in order solving, a kind of concrete waterproofer of high effect leakage proof waterproof to be provided.
For achieving the above object, the technical solution used in the present invention is as follows:
A kind of concrete waterproofer, raw material by following weight part mixes: hydrophobicity aerosil 18-26, zeolite powder 10-15, slag micropowder 6-12,2-phosphonic acids butane-1,2,4-tricarboxylic acid 4.5-6.5, amorphous graphite powder 9-18, AF-2 type high efficiency water reducing agent 20-30, Folium Nelumbinis essenc 5-10, methyl silicon sodium alcoholate 7-14, butyl stearate 4-9, hydrophobic pearlite 10-15, tall oil-asphalt sodium sulfonate 5-10, poly-Union carbide A-162 8-16, sorbose calcium 3-5, dicyclohexyl amine nitrite 2.5-4.5, ethoxylation lanolin 3-5, auxiliary agent 4-7;
Described auxiliary agent is made up of the raw material of following weight part: graphene oxide 16-22, trees ashes 10-15, refuse clay brick powder 8-12, octadecylamine 4-7, cumene sodium sulfonate 3-5, cryolite powder 10-15, polyester powder 5-10, aliphatic alcohol polyether acid amides 3-6, octyl group Dodecyl Polyglucosides 2-4, isooctyl alcohol phosphoric acid ester 4.5-6.5, crystal aluminum chloride 7-11, Rhizoma amorphophalli powder 4-8, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 1-2, sodium alginate 2.5-4.5;
Refuse clay brick powder, cryolite powder, trees ashes are mixed, then add aliphatic alcohol polyether acid amides, octyl group Dodecyl Polyglucosides, isooctyl alcohol phosphoric acid ester, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester and sodium alginate, under 50-60 DEG C of bath temperature, stir 8-12min, be cooled to normal temperature, after oven dry, add remaining raw material, stir, obtain described auxiliary agent.
Beneficial effect of the present invention:
Concrete waterproofer of the present invention can be imitated and be improved concrete capillary structure, stop up inside concrete capillary porosity duct, significantly improve concrete impervious water-proof function, more than impervious grade can reach P25, there is the effects such as enhancing, diminishing, cracking resistance simultaneously, and can improve the workability of fresh concrete, Qinshui rate is little, significantly improves concrete workability, is applicable to flat roof waterproof and building ground antiseepage tidal defense engineering.
Embodiment
A kind of concrete waterproofer, raw material by following weight (kg) mixes: hydrophobicity aerosil 22, zeolite powder 12, slag micropowder 10,2-phosphonic acids butane-1,2,4-tricarboxylic acid 6, amorphous graphite powder 14, AF-2 type high efficiency water reducing agent 25, Folium Nelumbinis essenc 8, methyl silicon sodium alcoholate 11, butyl stearate 6, hydrophobic pearlite 12, tall oil-asphalt sodium sulfonate 8, poly-Union carbide A-162 12, sorbose calcium 4, dicyclohexyl amine nitrite 3.5, ethoxylation lanolin 4, auxiliary agent 5;
Described auxiliary agent is made up of the raw material of following weight (kg): graphene oxide 20, trees ashes 10, refuse clay brick powder 12, octadecylamine 6, cumene sodium sulfonate 4, cryolite powder 12, polyester powder 8, aliphatic alcohol polyether acid amides 5, octyl group Dodecyl Polyglucosides 3.5, isooctyl alcohol phosphoric acid ester 5.5, crystal aluminum chloride 9, Rhizoma amorphophalli powder 6, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 1.5, sodium alginate 3.5;
Refuse clay brick powder, cryolite powder, trees ashes are mixed, then add aliphatic alcohol polyether acid amides, octyl group Dodecyl Polyglucosides, isooctyl alcohol phosphoric acid ester, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester and sodium alginate, under 55 DEG C of bath temperatures, stir 10min, be cooled to normal temperature, after oven dry, add remaining raw material, stir, obtain described auxiliary agent.
It is as shown in the table that the above-mentioned concrete waterproofer making mixes salient features detected result in concrete:
Claims (1)
1. a concrete waterproofer, it is characterized in that, raw material by following weight part mixes: hydrophobicity aerosil 18-26, zeolite powder 10-15, slag micropowder 6-12, 2-phosphonic acids butane-1, 2, 4-tricarboxylic acid 4.5-6.5, amorphous graphite powder 9-18, AF-2 type high efficiency water reducing agent 20-30, Folium Nelumbinis essenc 5-10, methyl silicon sodium alcoholate 7-14, butyl stearate 4-9, hydrophobic pearlite 10-15, tall oil-asphalt sodium sulfonate 5-10, poly-Union carbide A-162 8-16, sorbose calcium 3-5, dicyclohexyl amine nitrite 2.5-4.5, ethoxylation lanolin 3-5, auxiliary agent 4-7,
Described auxiliary agent is made up of the raw material of following weight part: graphene oxide 16-22, trees ashes 10-15, refuse clay brick powder 8-12, octadecylamine 4-7, cumene sodium sulfonate 3-5, cryolite powder 10-15, polyester powder 5-10, aliphatic alcohol polyether acid amides 3-6, octyl group Dodecyl Polyglucosides 2-4, isooctyl alcohol phosphoric acid ester 4.5-6.5, crystal aluminum chloride 7-11, Rhizoma amorphophalli powder 4-8, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 1-2, sodium alginate 2.5-4.5;
Refuse clay brick powder, cryolite powder, trees ashes are mixed, then add aliphatic alcohol polyether acid amides, octyl group Dodecyl Polyglucosides, isooctyl alcohol phosphoric acid ester, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester and sodium alginate, under 50-60 DEG C of bath temperature, stir 8-12min, be cooled to normal temperature, after oven dry, add remaining raw material, stir, obtain described auxiliary agent.