CN104087221A - 一种耐水脲醛树脂胶黏剂的制备方法 - Google Patents
一种耐水脲醛树脂胶黏剂的制备方法 Download PDFInfo
- Publication number
- CN104087221A CN104087221A CN201410279922.0A CN201410279922A CN104087221A CN 104087221 A CN104087221 A CN 104087221A CN 201410279922 A CN201410279922 A CN 201410279922A CN 104087221 A CN104087221 A CN 104087221A
- Authority
- CN
- China
- Prior art keywords
- raw material
- urea
- resin adhesive
- formaldehyde resin
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种耐水脲醛树脂胶黏剂的制备方法，涉及涉及化工技术领域，由以下重量份的原料组成，甲醛85-95份、尿素95-105份、六亚甲基四胺6.2-6.4份、三聚氰胺1.4-1.6份、聚乙烯醇1.8-2.0份、氢氧化钠25-35份、硫脲5.7-5.9份。本发明的有益效果是：本发明制备方便简单，环保无污染，原料易得，设备投资少，纯度高，便于操作，制备的耐水脲醛树脂胶黏剂使用效果好，耐高温性强，黏度适应，安全可靠。
Description
技术领域
本发明涉及化工技术领域，具体涉及一种耐水脲醛树脂胶黏剂的制备方法。
背景技术
胶黏剂是现代工业发展和人类生活水平提高必不可少的重要材料，胶黏剂及粘接技术以其他连接方式无法比拟的特种工艺，在现代经济、现代国防、现代科技中发挥着重大作用。如现代航天航空的各种飞行器中几乎没有不采用胶黏剂和粘接技术的，可以说，哪里有人类’哪里就少不了胶黏剂产品与粘接技术，它为工业提供了新颖实用的工艺'为人类营造了多姿多彩的生活。胶黏剂与塑料、合成橡胶、合成纤维涂料并称为五大合成材料，其生产与应用涉及多学科的高度综合’包括高分子化学、材料学、有机化学、无机化学、分析化学、高分子物理、物理学、流变学、生物学等学科,胶黏剂的种类有很多种，每种胶黏剂的适用范围也有与之最相匹配的行业使用，脲醛树脂胶黏剂一种比较新型的胶黏剂，由于其制作的工艺及其制作方便都很传统，一般市面上的这种脲醛树脂胶黏剂的存在量并不大。
发明内容
本发明所要解决的技术问题在于提供一种黏度适宜，制备工艺简单的一种耐水脲醛树脂胶黏剂的制备方法。
本发明所要解决的技术问题采用以下技术方案来实现：
一种耐水脲醛树脂胶黏剂，其特征在于：由以下组分的原料组成：
各原料的优选重量为：
所述的氢氧化钠的浓度为30％。
本发明的另一目的是制备本发明一种耐水脲醛树脂胶黏剂的方法，其特征在于：包括以下工艺步骤，
a.选取反应釜，所述的反应釜配备夹套和搅拌器。
b.按照配方量将原料中的甲醛、六亚甲基四胺加入步骤a中选取的反应釜中，开启搅拌直至溶解。
c.待上述步骤b中反应物全部溶解后，将原料中的尿素总量的50％和全部的三聚氰胺加入步骤b中的反应釜中，而后将内部温度升至92℃，开始反应。
d.再次称取原料中剩下的50％的尿素和原料中所有的聚乙烯醇，继续反应，直至测试反应物的pH值为4.8，反应结束。
e.将上述步骤d中反应釜内的温度降至40℃，按照配方量将原料中所有的氢氧化钠加入其中，调节pH值为7.5后，降幅内抽真空。
f.按照配方量称取原料中所有的硫脲，加入步骤e中抽硫脲后反应釜中，升高温度至80℃，反应40-45min。
g.待上述步骤f内反应物反应结束后，对釜内温度进行降温至25-30℃，而后进行出料，得到的产物即为本发明所要制备的耐水脲醛树脂胶黏剂成品，包装，入库。
本发明的有益效果是：本发明制备方便简单，环保无污染，原料易得， 设备投资少，纯度高，便于操作，制备的耐水脲醛树脂胶黏剂使用效果好，耐高温性强，黏度适应，安全可靠。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
一种耐水脲醛树脂胶黏剂，其特征在于：由以下组分的原料组成：
本发明的另一目的是制备本发明耐水脲醛树脂胶黏剂的方法，包括以下工艺步骤，
a.选取反应釜，所述的反应釜配备夹套和搅拌器。
b.按照配方量将原料中的甲醛、六亚甲基四胺加入步骤a中选取的反应釜中，开启搅拌直至溶解。
c.待上述步骤b中反应物全部溶解后，将原料中的尿素总量的50％和全部的三聚氰胺加入步骤b中的反应釜中，而后将内部温度升至92℃，开始反应。
d.再次称取原料中剩下的50％的尿素和原料中所有的聚乙烯醇，继续反应，直至测试反应物的pH值为4.8，反应结束。
e.将上述步骤d中反应釜内的温度降至40℃，按照配方量将原料中所有的浓度为30％的氢氧化钠加入其中，调节pH值为7.5后，降幅内抽真空。
f.按照配方量称取原料中所有的硫脲，加入步骤e中抽硫脲后反应釜中，升高温度至80℃，反应40-45min。
g.待上述步骤f内反应物反应结束后，对釜内温度进行降温至25-30℃， 而后进行出料，得到的产物即为本发明所要制备的耐水脲醛树脂胶黏剂成品，包装，入库。
实施例2
一种耐水脲醛树脂胶黏剂，其特征在于：由以下组分的原料组成：
本发明的另一目的是制备本发明耐水脲醛树脂胶黏剂的方法，包括以下工艺步骤，
a.选取反应釜，所述的反应釜配备夹套和搅拌器。
b.按照配方量将原料中的甲醛、六亚甲基四胺加入步骤a中选取的反应釜中，开启搅拌直至溶解。
c.待上述步骤b中反应物全部溶解后，将原料中的尿素总量的50％和全部的三聚氰胺加入步骤b中的反应釜中，而后将内部温度升至92℃，开始反应。
d.再次称取原料中剩下的50％的尿素和原料中所有的聚乙烯醇，继续反应，直至测试反应物的pH值为4.8，反应结束。
e.将上述步骤d中反应釜内的温度降至40℃，按照配方量将原料中所有的浓度为30％的氢氧化钠加入其中，调节pH值为7.5后，降幅内抽真空。
f.按照配方量称取原料中所有的硫脲，加入步骤e中抽硫脲后反应釜中，升高温度至80℃，反应40-45min。
g.待上述步骤f内反应物反应结束后，对釜内温度进行降温至25-30℃，而后进行出料，得到的产物即为本发明所要制备的耐水脲醛树脂胶黏剂成品，包装，入库。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明 书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种耐水脲醛树脂胶黏剂，其特征在于：由以下组分的原料组成：
。
2.根据权利要求1所述的一种耐水脲醛树脂胶黏剂，其特征在于：优选的组合物由以下重量的原料组成，
。
3.根据权利要求1所述的一种耐水脲醛树脂胶黏剂，其特征在于：所述的氢氧化钠的浓度为30％。
4.一种制备权利要求1-2任一项所述的一种耐水脲醛树脂胶黏剂制备方法，其特征在于：包括以下步骤，
a.选取反应釜，所述的反应釜配备夹套和搅拌器。
b.按照配方量将原料中的甲醛、六亚甲基四胺加入步骤a中选取的反应釜中，开启搅拌直至溶解。
c.待上述步骤b中反应物全部溶解后，将原料中的尿素总量的50％和全部的三聚氰胺加入步骤b中的反应釜中，而后将内部温度升至92℃，开始反应。
d.再次称取原料中剩下的50％的尿素和原料中所有的聚乙烯醇，继续反应，直至测试反应物的pH值为4.8，反应结束。
e.将上述步骤d中反应釜内的温度降至40℃，按照配方量将原料中所有的氢氧化钠加入其中，调节pH值为7.5后，降幅内抽真空。
f.按照配方量称取原料中所有的硫脲，加入步骤e中抽硫脲后反应釜中，升高温度至80℃，反应40-45min。
g.待上述步骤f内反应物反应结束后，对釜内温度进行降温至25-30℃，而后进行出料，得到的产物即为本发明所要制备的耐水脲醛树脂胶黏剂成品，包装，入库。