CN104046149A - 一种水性带锈涂料及其制备方法 - Google Patents

一种水性带锈涂料及其制备方法 Download PDF

Info

Publication number
CN104046149A
CN104046149A CN201410310828.7A CN201410310828A CN104046149A CN 104046149 A CN104046149 A CN 104046149A CN 201410310828 A CN201410310828 A CN 201410310828A CN 104046149 A CN104046149 A CN 104046149A
Authority
CN
China
Prior art keywords
weight
parts
weight part
rust
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410310828.7A
Other languages
English (en)
Other versions
CN104046149B (zh
Inventor
曹建梅
王学刚
李辛庚
岳增武
王晓明
樊志彬
郭凯
闫风洁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
State Grid Corp of China SGCC
Electric Power Research Institute of State Grid Shandong Electric Power Co Ltd
Original Assignee
State Grid Corp of China SGCC
Electric Power Research Institute of State Grid Shandong Electric Power Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by State Grid Corp of China SGCC, Electric Power Research Institute of State Grid Shandong Electric Power Co Ltd filed Critical State Grid Corp of China SGCC
Priority to CN201410310828.7A priority Critical patent/CN104046149B/zh
Publication of CN104046149A publication Critical patent/CN104046149A/zh
Application granted granted Critical
Publication of CN104046149B publication Critical patent/CN104046149B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种涂料，特别涉及一种水性带锈涂料，包括以下成分：苯丙乳液30-40重量份，转化剂8-10重量份，转化促进剂8-10重量份，防锈颜料5-10重量份，填料8-10重量份，消泡剂0.5-1重量份，成膜助剂0.5-0.8重量份，增稠剂0.5-0.8重量份，缓蚀剂0.5-1重量份，防霉剂0.5-1重量份，水20-30重量份。本发明的有效果是，不含磷酸、不含有毒颜料及锌盐防锈颜料，涂层附着力高，涂层质量好，是一种较好的带锈的环保型水性带锈涂料。

Description

一种水性带锈涂料及其制备方法
技术领域
本发明涉及一种涂料，特别涉及一种水性带锈涂料及其制备方法。
背景技术
使用传统防腐涂料对基材进行涂装前必须进行严格的表面处理。而对大型和结构复杂的钢铁构件来说，严格的表面处理常常不能实现。低的基材表面处理水平造成涂层附着力低，涂层质量差。带锈涂料可在一定锈蚀程度的钢铁表面直接施工且具有较好防护效果。水性带锈涂料由于具有环境友好、节约有机资源、不燃等突出优点得到了大力推广。目前的水性带锈涂料中多含锌铬黄等有毒防锈颜料。不含锌铬黄等有毒防锈颜料的水性带锈涂料多以磷酸锌等锌盐作为防锈颜料。但是无毒与环保是两个不同的概念，根据欧美相关环保规定，含锌的防锈颜料不属于环保型防锈颜料的范畴。
发明内容
本发明旨在克服现有技术中存在的不足，提供一种不含磷酸、不含有毒颜料及锌盐防锈颜料的环保型水性带锈涂料。
本发明技术方案如下：
一种水性带锈涂料，其特征在于，包括以下成分：苯丙乳液30-40重量份，转化剂8-10重量份，转化促进剂8-10重量份，防锈颜料5-10重量份，填料8-10重量份，消泡剂0.5-1重量份，成膜助剂0.5-0.8重量份，增稠剂0.5-0.8重量份，缓蚀剂0.5-1重量份，防霉剂0.5-1重量份，水20-30重量份；
     所述转化剂为草酸、植酸和单宁酸中的一种或几种；所述转化促进剂为苯三酚或邻苯二酚；所述防锈颜料为离子交换型颜料Ca/SiO2、三聚磷酸铝、磷酸钙、磷酸锶、偏硼酸钙和氧化铁红中的一种或几种；所述填料为硫酸钡和滑石粉中的一种或两种；所述消泡剂为破泡型硅烷消泡剂；所述成膜助剂为乙二醇丙醚或乙二醇丁醚；所述增稠剂为琼脂、海藻酸盐或聚丙烯酸盐；所述缓蚀剂为硫脲；所述防霉剂为苯甲酸钠或亚硝酸钠。
上述所述的水性带锈涂料，优选的，所这的防锈颜料采用以下重量配比：离子交换型颜料Ca/SiO2、三聚磷酸铝、偏硼酸钙和氧化铁红的比为2：2：1：2。
     本发明还公开了上述水性带锈涂料的制备方法，其特征在于采用以下步骤：
(1)将防锈颜料与8-12重量份水混合并研磨分散至细度为20-60微米；
(2)将转化剂、转化促进剂、5-8重量份的水、成膜助剂搅拌混合均匀；
(3)在转速为400-600rpm的搅拌条件下，将（2）所得混合物加入苯丙乳液中，搅拌0.5-1h，混合均匀；
(4)在转速为1500-2000 rpm的搅拌条件下，在（3）得到的混合物中加入（1）所得混合物，加入消泡剂、缓蚀剂、防霉剂、增稠剂和余量水，搅拌均匀，即得水性带锈涂料。
本发明的有效果是，不含磷酸、不含有毒颜料及锌盐防锈颜料，涂层附着力高，涂层质量好，是一种较好的带锈的环保型水性带锈涂料。
具体实施方式
实施例1
 本实施例的环保型水性带锈涂料，包括以下成分：苯丙乳液32重量份，转化剂8重量份，转化促进剂10重量份，防锈颜料6重量份，填料8重量份，消泡剂0.5重量份，成膜助剂0.8重量份，增稠剂0.5重量份，缓蚀剂0.8重量份，防霉剂0.8重量份，水25重量份；
     所述转化剂为3重量份的草酸和5重量份的植酸；所述转化促进剂为苯三酚；所述防锈颜料为2重量份的三聚磷酸铝、1重量份的磷酸钙和3重量份的氧化铁红；所述填料为硫酸钡；所述消泡剂为破泡型硅烷消泡剂；所述成膜助剂为乙二醇丁醚；所述增稠剂为海藻酸盐；所述缓蚀剂为硫脲；所述防霉剂为苯甲酸钠。
其制备方法为：
步骤一，将防锈颜料与8重量份水混合并研磨分散至细度为50微米；
步骤二，将转化剂、转化促进剂、5重量份的水、成膜助剂搅拌混合均匀；
步骤三，在转速为500rpm的搅拌条件下，将步骤二所得混合物加入苯丙乳液中，搅拌1h，混合均匀；
在转速为2000 rpm的搅拌条件下，在步骤三得到的混合物中加入步骤一所得混合物，加入消泡剂、缓蚀剂、防霉剂、增稠剂和余量水，搅拌均匀，即得水性带锈涂料。
实施例2
一种环保型水性带锈涂料，包括以下成分：苯丙乳液38重量份，转化剂10重量份，转化促进剂8重量份，防锈颜料10重量份，填料10重量份，消泡剂0.8重量份，成膜助剂0.5重量份，增稠剂0.8重量份，缓蚀剂0.5重量份，防霉剂0.5重量份，水30重量份；
     所述转化剂为草酸；所述转化促进剂为邻苯二酚；所述防锈颜料为2重量份的离子交换型颜料Ca/SiO2、2重量份的三聚磷酸铝、1重量份的偏硼酸钙和2重量份的氧化铁红；所述填料为滑石粉；所述消泡剂为破泡型硅烷消泡剂；所述成膜助剂为乙二醇丙醚；所述增稠剂为聚丙烯酸盐；所述缓蚀剂为硫脲；所述防霉剂为亚硝酸钠。
其制备方法为：
步骤一，将防锈颜料与10重量份水混合并研磨分散至细度为30微米；
步骤二，将转化剂、转化促进剂、8重量份的水、成膜助剂搅拌混合均匀；
步骤三，在转速为500rpm的搅拌条件下，将步骤二所得混合物加入苯丙乳液中，搅拌1h，混合均匀；
在转速为1600 rpm的搅拌条件下，在步骤三得到的混合物中加入步骤一所得混合物，加入消泡剂、缓蚀剂、防霉剂、增稠剂和余量水，搅拌均匀，即得水性带锈涂料。
 
测试结果：
  将上述实施例的涂料，进行检测，具体结果如下: 

Claims (3)

1.一种水性带锈涂料，其特征在于，包括以下重量份的成分：苯丙乳液30-40重量份，转化剂8-10重量份，转化促进剂8-10重量份，防锈颜料5-10重量份，填料8-10重量份，消泡剂0.5-1重量份，成膜助剂0.5-0.8重量份，增稠剂0.5-0.8重量份，缓蚀剂0.5-1重量份，防霉剂0.5-1重量份，水20-30重量份；
     所述转化剂为草酸、植酸和单宁酸中的一种或几种；所述转化促进剂为苯三酚或邻苯二酚；所述防锈颜料为离子交换型颜料Ca/SiO2、三聚磷酸铝、磷酸钙、磷酸锶、偏硼酸钙和氧化铁红中的一种或几种；所述填料为硫酸钡和滑石粉中的一种或两种；所述消泡剂为破泡型硅烷消泡剂；所述成膜助剂为乙二醇丙醚或乙二醇丁醚；所述增稠剂为琼脂、海藻酸盐或聚丙烯酸盐；所述缓蚀剂为硫脲；所述防霉剂为苯甲酸钠或亚硝酸钠。
2.根据权利要求1所述的水性带锈涂料，其特征在在于：所这的防锈颜料采用以下重量配比：离子交换型颜料Ca/SiO2、三聚磷酸铝、偏硼酸钙和氧化铁红的比为2：2：1：2。
3.一种权利要求1或2所述的水性带锈涂料的制备方法，其特征在于采用以下步骤：
(1)将防锈颜料与8-12重量份水混合并研磨分散至细度为20-60微米；
(2)将转化剂、转化促进剂、5-8重量份的水、成膜助剂搅拌混合均匀；
(3)在转速为400-600rpm的搅拌条件下，将（2）所得混合物加入苯丙乳液中，搅拌0.5-1h，混合均匀；
(4)在转速为1500-2000 rpm的搅拌条件下，在（3）得到的混合物中加入（1）所得混合物，加入消泡剂、缓蚀剂、防霉剂、增稠剂和余量水，搅拌均匀，即得水性带锈涂料。
CN201410310828.7A 2014-07-01 2014-07-01 一种水性带锈涂料及其制备方法 Active CN104046149B (zh)