CN103834247A - Aluminium powder paint, spraying method of aluminium powder paint and product sprayed by the method - Google Patents
Aluminium powder paint, spraying method of aluminium powder paint and product sprayed by the method Download PDFInfo
- Publication number
- CN103834247A CN103834247A CN201210479370.9A CN201210479370A CN103834247A CN 103834247 A CN103834247 A CN 103834247A CN 201210479370 A CN201210479370 A CN 201210479370A CN 103834247 A CN103834247 A CN 103834247A
- Authority
- CN
- China
- Prior art keywords
- powder paint
- aluminium powder
- aluminum powder
- paint
- spraying method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明揭示一种铝粉漆、铝粉漆的喷涂方法及其喷涂产品。该铝粉漆包括按照质量分数计算的下列组分：热塑性型丙烯酸酯树脂30～40%；醋酸丁酸纤维素10～20%；漆膜流平剂0.1～0.5%；醋酸丁酯10～20%；乙二醇丁醚5～10%；二甲苯5～15%；铝粉浆8～10%。所述喷涂方法包括如下步骤：取所述铝粉漆与稀释剂按照一定的质量分数搅拌均匀；采用喷涂的方式将稀释后的铝粉漆喷涂于产品表面；在常温或50～60℃下烘烤干燥。所述喷涂产品为采用所述铝粉漆的喷涂方法得到的产品。相较于现有技术，本发明的铝粉漆、铝粉漆的喷涂方法及其喷涂产品，所述铝粉漆具有优异的硬度、耐酒精性，可以遮蔽塑胶产品表面的应力痕或结合线。The invention discloses an aluminum powder paint, a spraying method of the aluminum powder paint and a sprayed product thereof. The aluminum powder paint includes the following components calculated by mass fraction: 30-40% of thermoplastic acrylate resin; 10-20% of cellulose acetate butyrate; 0.1-0.5% of paint film leveling agent; 10-20% of butyl acetate %; Ethylene glycol butyl ether 5-10%; Xylene 5-15%; Aluminum powder paste 8-10%. The spraying method includes the following steps: taking the aluminum powder paint and diluent and stirring evenly according to a certain mass fraction; spraying the diluted aluminum powder paint on the surface of the product by spraying; drying at room temperature or at 50-60°C Roast dry. The sprayed product is a product obtained by adopting the spraying method of the aluminum powder paint. Compared with the prior art, the aluminum powder paint of the present invention, the spraying method of aluminum powder paint and its sprayed products, the aluminum powder paint has excellent hardness and alcohol resistance, and can cover stress marks or joint lines on the surface of plastic products .
Description
[technical field]
The present invention relates to a kind of aluminium powder paint, be specifically related to spraying method and the sprayed product thereof of a kind of aluminium powder paint, aluminium powder paint.
[background technology]
Due to problems such as die design, condition of molding restrictions, plastic cement products, in the time of moulding, usually has joint line or stress trace to exist, and affects quality and the outward appearance of product, and these bad methods such as polishing, spraying priming paint that conventionally need solve.
But, do not have at present a kind of aluminium powder paint of high-quality, not only there is excellent hardness, alcohol resistance, and can cover stress trace or the joint line of surface of plastic product.
In view of this, be necessary to provide in fact spraying method and the sprayed product thereof of a kind of aluminium powder paint, aluminium powder paint, to address the above problem.
[summary of the invention]
In view of above problem, the object of this invention is to provide spraying method and the sprayed product thereof of a kind of aluminium powder paint, aluminium powder paint, cannot have excellent hardness, alcohol resistance concurrently to solve prior art aluminium powder paint, can cover the stress trace of surface of plastic product or the problem of joint line.
In order to achieve the above object, the invention provides a kind of aluminium powder paint, it comprises the following component of calculating according to massfraction:
Thermoplastic type acrylate resin 30～40%;
Cellulose acetate butyrate 10～20%;
Paint film flow agent 0.1～0.5%;
N-BUTYL ACETATE 10～20%;
Butyl glycol ether 5～10%;
Dimethylbenzene 5～15%;
Aluminum paste 8～10%.
Optionally, described thermoplastic acrylic ester resin is K2560.
Optionally, described cellulose acetate butyrate is CAB381-2 solution, and the massfraction of described CAB381-2 is 20%.
Optionally, described paint film flow agent is BYK333 solution.
Optionally, in described aluminum paste, the massfraction of aluminium powder is 40%.
The present invention also provides a kind of spraying method of described aluminium powder paint, and it comprises the steps:
Getting described aluminium powder paint and thinner stirs according to certain massfraction;
Adopt the mode of spraying that the aluminium powder paint after dilution is sprayed to product surface;
At normal temperature or 50～60 ℃, baking is dry.
Optionally, described thinner comprises the following component of calculating according to massfraction:
Vinyl acetic monomer: 70～80%
Ritalin: 10～15%
Virahol: 10～15%
Optionally, the mass ratio of described aluminium powder paint and described thinner is 1:1～1:1.5.
The present invention also provides a kind of sprayed product that adopts the spraying method of described aluminium powder paint to obtain.
Compared to prior art, the spraying method of aluminium powder paint of the present invention, aluminium powder paint and sprayed product thereof, described aluminium powder paint has excellent hardness, alcohol resistance, and can cover stress trace or the joint line of surface of plastic product.
[embodiment]
For object of the present invention, method steps and function are had to further understanding, be described in detail as follows:
In order to achieve the above object, the invention provides a kind of aluminium powder paint, it comprises the following component of calculating according to massfraction:
Thermoplastic type acrylate resin 30～40%;
Cellulose acetate butyrate 10～20%;
Paint film flow agent 0.1～0.5%;
N-BUTYL ACETATE 10～20%;
Butyl glycol ether 5～10%;
Dimethylbenzene 5～15%;
Aluminum paste 8～10%.
Wherein, described thermoplastic acrylic ester resin can be K2560.
Wherein, described cellulose acetate butyrate can be CAB381-2 solution, and in described CAB381-2 solution solution, the massfraction of CAB381-2 can be 20%.CAB-381-2 has comprehensive preferably, as: solvability, Combination, water tolerance, excellent surface hardness and higher coating strength.
Wherein, described paint film flow agent can be BYK333 solution.
Wherein, in described aluminum paste, the massfraction of aluminium powder can be 40%.
Embodiment 1:
Described aluminium powder paint, it comprises the following component of calculating according to massfraction:
K2560 40%；
20% CAB381-2 solution 20%;
BYK333 0.5%；
N-BUTYL ACETATE 15%;
Butyl glycol ether 5%;
Dimethylbenzene 9.5%;
40% aluminum paste 10%.
The making method of described aluminium powder paint is for example, take 40g thermoplastic type acrylate resin K2560, after adding 15g N-BUTYL ACETATE and 5g butyl glycol ether to dissolve, add 20%(massfraction) CAB381-2 solution and the BYK333 of 0.5g, stir, add again 40%(massfraction) aluminum paste, add 9.5g dimethylbenzene mixing and stirring.
Embodiment 2:
Described aluminium powder paint, it comprises the following component of calculating according to massfraction:
K2560 30%；
20% CAB381-2 solution 18%;
BYK333 0.5%；
N-BUTYL ACETATE 18.5%;
Butyl glycol ether 10%;
Dimethylbenzene 15%;
40% aluminum paste 8%.
The making method of embodiment 2 is similar to Example 1, repeats no more.
Embodiment 3:
Described aluminium powder paint, it comprises the following component of calculating according to massfraction:
K2560 38.5%；
20% CAB381-2 solution 10%;
BYK333 0.5%；
N-BUTYL ACETATE 20%;
Butyl glycol ether 8%;
Dimethylbenzene 14%;
40% aluminum paste 9%.
The making method of embodiment 3 is similar to Example 1, repeats no more.
The present invention also provides a kind of spraying method of described aluminium powder paint, and it comprises the steps:
Getting described aluminium powder paint and thinner stirs according to certain massfraction;
Adopt the mode of spraying that the aluminium powder paint after dilution is sprayed to product surface;
At normal temperature or 50～60 ℃, baking is dry.
Wherein, described thinner can be to comprise the following component of calculating according to massfraction:
Vinyl acetic monomer: 70～80%
Ritalin: 10～15%
Virahol: 10～15%
Wherein, described thinner is for example to comprise the following component of calculating according to massfraction:
Vinyl acetic monomer: 70%
Ritalin: 15%
Virahol: 15%
Wherein, the mass ratio of described aluminium powder paint and described thinner is 1:1～1:1.5.The mass ratio of described aluminium powder paint and described thinner is for example 1:1.
The present invention also provides a kind of sprayed product that adopts the spraying method of described aluminium powder paint to obtain.Described sprayed product is plastic cement products, after described product is sprayed to described aluminium powder paint 24 hours, described product is carried out to performance test, and test result is as shown in the table:
Compared to prior art, the spraying method of aluminium powder paint of the present invention, aluminium powder paint and sprayed product thereof, described aluminium powder paint has excellent hardness, alcohol resistance, and can cover stress trace or the joint line of surface of plastic product.
Be pointed out that, the invention is not restricted to above-mentioned embodiment, any simple modification, equivalent variations and modification that any those skilled in the art do above-described embodiment based on technical solution of the present invention, all fall within the scope of protection of the present invention.
Claims (10)
1. an aluminium powder paint, is characterized in that, it comprises the following component of calculating according to massfraction:
Thermoplastic type acrylate resin 30～40%;
Cellulose acetate butyrate 10～20%;
Paint film flow agent 0.1～0.5%;
N-BUTYL ACETATE 10～20%;
Butyl glycol ether 5～10%;
Dimethylbenzene 5～15%;
Aluminum paste 8～10%.
2. aluminium powder paint as claimed in claim 1, is characterized in that, described thermoplastic acrylic ester resin is K2560.
3. aluminium powder paint as claimed in claim 1, is characterized in that, described cellulose acetate butyrate is CAB381-2 solution.
4. aluminium powder paint as claimed in claim 3, is characterized in that, in described CAB381-2 solution, the massfraction of CAB381-2 is 20%.
5. aluminium powder paint as claimed in claim 1, is characterized in that, described paint film flow agent is BYK333 solution.
6. aluminium powder paint as claimed in claim 1, is characterized in that, in described aluminum paste, the massfraction of aluminium powder is 40%.
7. a spraying method for aluminium powder paint as described in any one in claim 1-6, is characterized in that, it comprises the steps:
Getting described aluminium powder paint and thinner stirs according to certain massfraction;
Adopt the mode of spraying that the aluminium powder paint after dilution is sprayed to product surface;
At normal temperature or 50～60 ℃, baking is dry.
8. the spraying method of aluminium powder paint as claimed in claim 7, is characterized in that, described thinner comprises the following component of calculating according to massfraction:
Vinyl acetic monomer: 70～80%
Ritalin: 10～15%
Virahol: 10～15%.
9. the spraying method of aluminium powder paint as claimed in claim 8, is characterized in that, the mass ratio of described aluminium powder paint and described thinner is 1:1～1:1.5.
10. the sprayed product that the spraying method of employing aluminium powder paint as described in any one in claim 7～9 obtains.