CN103589042A - 一种抑菌复合塑料薄膜及其制备方法 - Google Patents

一种抑菌复合塑料薄膜及其制备方法 Download PDF

Info

Publication number
CN103589042A
CN103589042A CN201310550227.9A CN201310550227A CN103589042A CN 103589042 A CN103589042 A CN 103589042A CN 201310550227 A CN201310550227 A CN 201310550227A CN 103589042 A CN103589042 A CN 103589042A
Authority
CN
China
Prior art keywords
plastic film
plastics
antibacterial
parts
modified nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310550227.9A
Other languages
English (en)
Inventor
王欣南
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Xinying Special Material Technologies Co Ltd
Original Assignee
Suzhou Xinying Special Material Technologies Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Xinying Special Material Technologies Co Ltd filed Critical Suzhou Xinying Special Material Technologies Co Ltd
Priority to CN201310550227.9A priority Critical patent/CN103589042A/zh
Publication of CN103589042A publication Critical patent/CN103589042A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种抑菌复合塑料薄膜及其制备方法，它是由下述重量份数的物质制成：塑料40-60份、抗氧化剂10-15份、聚对苯二甲酸丁二醇酯5-20份、抑菌复合物25-30份，氧化铁5-15份，1,4-丁烯二醇5-10份。本发明燃烧释放烟气少，使用寿命长，较广泛的应用于建筑、室内装潢等领域。

Description

一种抑菌复合塑料薄膜及其制备方法
技术领域
本发明涉及高分子材料技术领域，尤其涉及一种抑菌复合塑料薄膜及其制备方法。
背景技术
随着工业的不断发展，塑料得到越来越广泛的应用。聚乙烯、聚丙烯、PTT聚酯、ABS等等大量使用在节水灌溉、建筑、室内装潢、家具、电力、运输等行业。但是塑料中的碳、氢两种元素含量很高，所以极容易燃烧，因而限制了塑料的使用。一般使用塑料时都需进行阻燃处理。目前阻燃主要以外添加阻燃剂为主。采用外添加阻燃剂方式对材料进行阻燃处理， 其阻燃效率高，技术成熟，价格便宜，但添加的阻燃剂一般卤素含量较高，燃烧时，塑料受热释放出含卤烟气，具有毒性，会危害人体的健康，甚至造成人员死亡；阻燃剂添加量大，对材料本身的后期加工影响较大，且阻燃剂易析出不能长久保持阻燃性，缩短了使用寿命。
发明内容
为了实现本发明的目的，本发明提供一种抑菌复合塑料薄膜，其特征在于：它是由下述重量份数的物质制成：塑料40-60份、抗氧化剂 10-15份、聚对苯二甲酸丁二醇酯5-20份、氧化铁5-15份，1,4-丁烯二醇5-10份、抑菌复合物   20-25份;所述的抑菌复合物的制备方法为：将黄顶菊、飞机草、五爪金龙、胜红蓟、高良姜、大蒜、香芹、水按照20-25：15-20：10-15 ：10-15：8-10：8-10： 5-7：10-20的质量份数配比混合，加入（10份的活力单位为100U）的纤维素酶进行酶解，酶解反应温度为30℃，酶解反应时间为1小时，过滤得到中草药液；去渣后再加入浓度为50%～70%的乙醇水溶液，再将固液混合物超声波辅助提取，超声波提取条件：超声温度为45～56℃、超声频率为20～30kHz、超声提取时间为1～2个小时，然后将固液混合物在20～30kPa真空条件下抽滤，取滤液在15～25kPa真空、45～50℃条件下减压蒸馏得抑菌复合物。
抗氧化剂为酚类，包括：单酚、双酚、多酚、对苯二酚、二苯胺、对苯二胺中的一种或几种。
所述塑料为高压低密度聚乙烯、低压高密度聚乙烯、高低压复合聚乙烯、乙烯- 醋酸乙烯共聚物中的一种或几种。
所述改性纳米塑料中还包括氧化锑5-8份。
所述改性纳米塑料中还包括硼酸锌5-8份。
所述的一种抑菌复合塑料薄膜的制备方法，其特征在于：其步骤为：
称重，将各成分按照比例称量好；
搅拌，把上述各成分放入在40-60℃下真空搅拌10-30分钟；
混合，将上述混合好的各成分在双辊开炼机上熔融混合，温度为120-160℃； 
成型，采用塑料吹膜机挤出吹膜，即得产品；
所述的吹膜机料筒后段温度分四段控制，分别控制在180～200℃，料筒前段温度分四段控制，分别控制在210～230℃，机头温度分两段控制，分别控制在220～240℃，吹胀比为1.5～2.0，螺杆转速20～40r/min，牵引速度10～50m/min。
有益效果：本发明采用的组分混合后，能够较好的阻燃，而且受热放出烟气较少，对人体损害小；阻燃剂不易析出，使用寿命长。具有杀菌效果的薄膜材料、绿色环保并且具有抑菌效果；对人、畜无害。另外，本发明配方合理，制备方法简单。
具体实施方式
下面结合具体实施方式对本发明作进一步详细的描述：
实施例1：
   一种抑菌复合塑料薄膜，其特征在于：它是由下述重量份数的物质制成：塑料40 份、抗氧化剂 10 份、聚对苯二甲酸丁二醇酯5 份、氧化铁5 份，1,4-丁烯二醇5 份、抑菌复合物   20 份;所述的抑菌复合物的制备方法为：将黄顶菊、飞机草、五爪金龙、胜红蓟、高良姜、大蒜、香芹、水按照20-25：15-20：10-15 ：10-15：8-10：8-10： 5-7：10-20的质量份数配比混合，加入（10份的活力单位为100U）的纤维素酶进行酶解，酶解反应温度为30℃，酶解反应时间为1小时，过滤得到中草药液；去渣后再加入浓度为50%～70%的乙醇水溶液，再将固液混合物超声波辅助提取，超声波提取条件：超声温度为45～56℃、超声频率为20～30kHz、超声提取时间为1～2个小时，然后将固液混合物在20～30kPa真空条件下抽滤，取滤液在15～25kPa真空、45～50℃条件下减压蒸馏得抑菌复合物。
抗氧化剂为酚类，包括：单酚、双酚、多酚、对苯二酚、二苯胺、对苯二胺中的一种或几种。
所述塑料为高压低密度聚乙烯、低压高密度聚乙烯、高低压复合聚乙烯、乙烯- 醋酸乙烯共聚物中的一种或几种。
所述改性纳米塑料中还包括氧化锑5-8份。
所述改性纳米塑料中还包括硼酸锌5-8份。
所述的一种抑菌复合塑料薄膜的制备方法，其特征在于：其步骤为：
称重，将各成分按照比例称量好；
搅拌，把上述各成分放入在40-60℃下真空搅拌10-30分钟；
混合，将上述混合好的各成分在双辊开炼机上熔融混合，温度为120-160℃； 
成型，采用塑料吹膜机挤出吹膜，即得产品；
所述的吹膜机料筒后段温度分四段控制，分别控制在180～200℃，料筒前段温度分四段控制，分别控制在210～230℃，机头温度分两段控制，分别控制在220～240℃，吹胀比为1.5～2.0，螺杆转速20～40r/min，牵引速度10～50m/min。.
实施例2：
   一种抑菌复合塑料薄膜，其特征在于：它是由下述重量份数的物质制成：塑料 60份、抗氧化剂  15份、聚对苯二甲酸丁二醇酯 20份、氧化铁 15份，1,4-丁烯二醇 10份、抑菌复合物  25份;所述的抑菌复合物的制备方法为：将黄顶菊、飞机草、五爪金龙、胜红蓟、高良姜、大蒜、香芹、水按照20-25：15-20：10-15 ：10-15：8-10：8-10： 5-7：10-20的质量份数配比混合，加入（10份的活力单位为100U）的纤维素酶进行酶解，酶解反应温度为30℃，酶解反应时间为1小时，过滤得到中草药液；去渣后再加入浓度为50%～70%的乙醇水溶液，再将固液混合物超声波辅助提取，超声波提取条件：超声温度为45～56℃、超声频率为20～30kHz、超声提取时间为1～2个小时，然后将固液混合物在20～30kPa真空条件下抽滤，取滤液在15～25kPa真空、45～50℃条件下减压蒸馏得抑菌复合物。
抗氧化剂为酚类，包括：单酚、双酚、多酚、对苯二酚、二苯胺、对苯二胺中的一种或几种。
所述塑料为高压低密度聚乙烯、低压高密度聚乙烯、高低压复合聚乙烯、乙烯- 醋酸乙烯共聚物中的一种或几种。
所述改性纳米塑料中还包括氧化锑5-8份。
所述改性纳米塑料中还包括硼酸锌5-8份。
所述的一种抑菌复合塑料薄膜的制备方法，其特征在于：其步骤为：
称重，将各成分按照比例称量好；
搅拌，把上述各成分放入在40-60℃下真空搅拌10-30分钟；
混合，将上述混合好的各成分在双辊开炼机上熔融混合，温度为120-160℃； 
成型，采用塑料吹膜机挤出吹膜，即得产品；
所述的吹膜机料筒后段温度分四段控制，分别控制在180～200℃，料筒前段温度分四段控制，分别控制在210～230℃，机头温度分两段控制，分别控制在220～240℃，吹胀比为1.5～2.0，螺杆转速20～40r/min，牵引速度10～50m/min。
具有杀菌效果的薄膜材料、绿色环保并且具有抑菌效果；对人、畜无害。另外，本发明配方合理，制备方法简单。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (6)

1.一种抑菌复合塑料薄膜，其特征在于：它是由下述重量份数的物质制成：塑料40-60份、抗氧化剂 10-15份、聚对苯二甲酸丁二醇酯5-20份、氧化铁5-15份，1,4-丁烯二醇5-10份、抑菌复合物   20-25份;所述的抑菌复合物的制备方法为：将黄顶菊、飞机草、五爪金龙、胜红蓟、高良姜、大蒜、香芹、水按照20-25：15-20：10-15 ：10-15：8-10：8-10： 5-7：10-20的质量份数配比混合，加入（10份的活力单位为100U）的纤维素酶进行酶解，酶解反应温度为30℃，酶解反应时间为1小时，过滤得到中草药液；去渣后再加入浓度为50%～70%的乙醇水溶液，再将固液混合物超声波辅助提取，超声波提取条件：超声温度为45～56℃、超声频率为20～30kHz、超声提取时间为1～2个小时，然后将固液混合物在20～30kPa真空条件下抽滤，取滤液在15～25kPa真空、45～50℃条件下减压蒸馏得抑菌复合物。
2.根据权利要求1所述的改性纳米塑料，其特征在于：抗氧化剂为酚类，包括：单酚、双酚、多酚、对苯二酚、二苯胺、对苯二胺中的一种或几种。
3.根据权利要求3或4所述的改性纳米塑料，其特征在于：所述塑料为高压低密度聚乙烯、低压高密度聚乙烯、高低压复合聚乙烯、乙烯- 醋酸乙烯共聚物中的一种或几种。
4.根据权利要求5所述的改性纳米塑料，其特征在于：所述改性纳米塑料中还包括氧化锑5-8份。
5.根据权利要求5所述的改性纳米塑料，其特征在于：所述改性纳米塑料中还包括硼酸锌5-8份。
6.根据权利要求1所述的一种抑菌复合塑料薄膜的制备方法，其特征在于：其步骤为：
称重，将各成分按照比例称量好；
搅拌，把上述各成分放入在40-60℃下真空搅拌10-30分钟；
混合，将上述混合好的各成分在双辊开炼机上熔融混合，温度为120-160℃； 
成型，采用塑料吹膜机挤出吹膜，即得产品；
所述的吹膜机料筒后段温度分四段控制，分别控制在180～200℃，料筒前段温度分四段控制，分别控制在210～230℃，机头温度分两段控制，分别控制在220～240℃，吹胀比为1.5～2.0，螺杆转速20～40r/min，牵引速度10～50m/min。
CN201310550227.9A 2013-11-08 2013-11-08 一种抑菌复合塑料薄膜及其制备方法 Pending CN103589042A (zh)