CN103571304B - A kind of flame retardant epoxy floor coatings - Google Patents
A kind of flame retardant epoxy floor coatings Download PDFInfo
- Publication number
- CN103571304B CN103571304B CN201310496511.2A CN201310496511A CN103571304B CN 103571304 B CN103571304 B CN 103571304B CN 201310496511 A CN201310496511 A CN 201310496511A CN 103571304 B CN103571304 B CN 103571304B
- Authority
- CN
- China
- Prior art keywords
- byk
- toner
- flame retardant
- floor coatings
- host
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of flame retardant epoxy floor coatings.Flame retardant epoxy floor coatings is made up of according to the ratio mixing match of weight ratio 100:20 100:30 host and firming agent, wherein said host is made up of the raw material of following weight: epoxy resin 40 70%, diluent 2 10%, fire retardant 30 50%, dispersant 0.01 2%, defoamer 0.01 2%, levelling agent 0.01 2%, toner 1 5%, firming agent forms: polyetheramine 30 90%, property amine 10 70%, accelerator 1 10%.This flame retardant epoxy floor coatings prepares the product being different from the market of fire-retardant terrace, can reach UL94V0 fire-protection rating, and after product construction, appearance looks elegant is generous, and easy construction, it is easy to operation, low volatilization or non-volatile.
Description
Technical field
The present invention relates to a kind of building chemical coating, be specifically related to a kind of flame retardant epoxy floor coatings.
Background technology
Epoxy flooring coating is a kind of high intensity, floor wear-resistant, attractive in appearance, has seamless, quality
The advantages such as solid, resistance to chemical reagents is good, and anticorrosion is waterproof, dust-proof, easy maintenance, and maintenance cost is cheap.
Design kinds of schemes can be required according to different purposes, as 0.3--0.5mm epoxy thin coating floor,
0.6--0.8mm epoxy thickness be coated with terrace, epoxy self-leveling ground thick for 1-5mm, anti-skid wearable application,
Mortar type application, antistatic, corrosion-proof coating etc..
Epoxy flooring coating is from the outset for functional terrace: such as anticorrosion, wear-resisting, anti-skidding, develops into
General general industry terrace；Except having functional requirement, also there is ornamental effect.In work
On the basis of the acquisition of industry terrace is wide variety of, along with improving constantly of people's living standard, in family
Decoration is able to popularization and application.Epoxy industry ground slab has become one of China's industry with the fastest developing speed,
Cause the attention of everybody.It can realize factorial praluction as cement products, and prospect is more considerable.
Floor paint is when normally using, general it is emphasised that wearability and pressure-proof and impact resistance energy, also has portion
Divide and require to produce into the different requirements such as anticorrosion type, have the customer requirement floor paint of only a few to have heatproof
Performance or fire resistance, if any food factory because having baking box etc. or Electronics Factory to heat or part
Factory has baking vanish requirement, general heat resistance to require to reach more than 100 degree, according to this situation, and can
To use the floor paint that the good heat-resisting quantity of pliability is strong to produce.Require that the places such as high place such as amusement and recreation are wanted
Ask floor paint to have certain resistance to cigarette end to burn performance because cigarette end when glowing extreme temperatures plus shadows such as tar
Ring, often produce the problems such as Huang of burning.
Epoxy flooring coating in the market not only volatilizees pungent abnormal smells from the patient also non-refractory, therefore produces
Environmental protection the most attractive in appearance but also resistance to high epoxy flooring coating are extremely urgent.
Summary of the invention
The purpose of present invention is to solve above-mentioned the deficiencies in the prior art, it is provided that one can reach
After the construction of UL94V0 fire-protection rating, product, appearance looks elegant is generous, easy construction, volatilization easily operated, low
Or non-volatile coating.
The present invention is realized by techniques below means:
A kind of flame retardant epoxy floor coatings, it is characterised in that by host and firming agent according to weight ratio
The ratio mixing match composition of 100:20 100:30, wherein,
Described host is made up of the raw material of following weight: epoxy resin 40-70 part, diluent
2-10 part, fire retardant 30-50 part, dispersant 0.01-2 part, defoamer 0.01-2 part, levelling agent
0.01-2 part and toner 1-5 part；
Described firming agent is made up of the raw material of following weight: polyetheramine 30-90 part, modified amine
10-70 part and accelerator 1-10 part.
In described host, the selection of various dispensings is as follows:
Epoxy resin is selected from E-51, one or more in E-44, E-20；
Diluent is selected from AGE, BGE, benzyl alcohol, dimethylbenzene, isobutanol, one or more in butanone；
Fire retardant is selected from aluminium hydroxide, magnesium hydroxide, antimony oxide, tetrabromobisphenol A, poly-described phosphorus
Acid ammonium, MAP, Diammonium phosphate (DAP), ammonium chloride, boric acid, TCPP, TDCPP, IPPP, DMMP, phosphorus
Triphenyl phosphate ester, one or more in TDE；
Dispersant is selected from polyether modified siloxane, and BYK-111, BYK-110, in polydimethylsiloxane
One or more；
Defoamer is selected from polyether modified siloxane, dimethyl siloxane, in BYK-A530, BYK-525
Kind or more than；
Levelling agent is selected from polyether modified siloxane, and polydimethylsiloxane, in BYK-315, BYK-320
One or more；
Toner is selected from corresponding inorganic toner or organic toner；
In described firming agent, the selection of various dispensings is as follows:
Polyetheramine is selected from D-230, the one in D-400, T-403；
Modified amine is modified selected from IPDA, the one in MXDA modification；
Accelerator is selected from DMP-30, K-54, benzyl dimethylamine, the one in triethylamine
Beneficial effects of the present invention: the flame retardant epoxy floor coatings of the present invention is different from product on the market,
Can reach UL94V0 fire-protection rating, after product construction, appearance looks elegant is generous, and easy construction, easily
In operation, low volatilization or non-volatile.
Detailed description of the invention
Embodiment 1
By weight:
By mixing cured according to the ratio of weight ratio 100:20 to host and firming agent, make thick 3 mm wides
13 millimeters, 3, the sample of long 125 millimeters, samples vertical is placed, and installs；Sample is made the when of installation
The blue flame at relatively low distance combustion tube top, one end 3/8 " being 3/4 height " is placed on sample lower end
Centre, burn 10 seconds, then remove flame 8 seconds and extinguish, i.e. can be made into flame retardant epoxy terrace
Coating.
Embodiment 2
By weight:
By mixing cured according to the ratio (weight ratio) of 100:30 to host and firming agent, make thick 3 millis
Rice is wide 13 millimeters, 3, the sample of long 125 millimeters, and samples vertical is placed, and installs；The when of installation
The blue flame making the relatively low distance combustion tube top 3/8, one end " being 3/4 height " of sample is placed on sample
The centre of lower end, burns 10 seconds, then removes flame and extinguishes for 5 seconds, i.e. can be made into fire-retardant ring
Oxygen floor coatings.
Embodiment 3
By weight:
By mixing cured according to the ratio (weight ratio) of 100:25 to host and firming agent, make thick 3 millis
Rice is wide 13 millimeters, 3, the sample of long 125 millimeters, and samples vertical is placed, and installs；The when of installation
The blue flame making the relatively low distance combustion tube top 3/8, one end " being 3/4 height " of sample is placed on sample
The centre of lower end, burns 10 seconds, then removes flame and extinguishes for 3 seconds, i.e. can be made into fire-retardant ring
Oxygen floor coatings.
Embodiment 4
By weight:
By mixing cured according to the ratio (weight ratio) of 100:20 to host and firming agent, make thick 3 millis
Rice is wide 13 millimeters, 3, the sample of long 125 millimeters, and samples vertical is placed, and installs；The when of installation
The blue flame making the relatively low distance combustion tube top 3/8, one end " being 3/4 height " of sample is placed on sample
The centre of lower end, burns 10 seconds, then removes flame and extinguishes for 6 seconds, i.e. can be made into fire-retardant ring
Oxygen floor coatings.
Embodiment 5
By weight:
By mixing cured according to the ratio (weight ratio) of 100:20 to host and firming agent, make thick 3 millis
Rice is wide 13 millimeters, 3, the sample of long 125 millimeters, and samples vertical is placed, and installs；The when of installation
The blue flame making the relatively low distance combustion tube top 3/8, one end " being 3/4 height " of sample is placed on sample
The centre of lower end, burns 10 seconds, then removes flame and extinguishes for 7 seconds, i.e. can be made into fire-retardant ring
Oxygen floor coatings.
The embodiment of the present invention, through test, all obtains splendid coating performance, and its test result is average such as
Under:
Claims (1)
1. a flame retardant epoxy floor coatings, it is characterised in that be made up of according to the ratio mixing match of weight ratio 100:20 100:30 host and firming agent, wherein,
Described host is made up of the raw material of following weight: epoxy resin 40-70 part, diluent 2-10 part, fire retardant 30-50 part, dispersant 0.01-2 part, defoamer 0.01-2 part, levelling agent 0.01-2 part and toner 1-5 part；
Described firming agent is made up of the raw material of following weight: polyetheramine 30-90 part, modified amine 10-70 part and accelerator 1-10 part,
Described epoxy resin is selected from E-51, one or more in E-44, E-20,
Described diluent is selected from AGE, BGE, benzyl alcohol, dimethylbenzene, isobutanol, one or more in butanone,
Described fire retardant is selected from aluminium hydroxide, magnesium hydroxide, antimony oxide, tetrabromobisphenol A, APP, MAP, Diammonium phosphate (DAP), ammonium chloride, boric acid, TCPP, TDCPP, IPPP, DMMP, triphenyl phosphate, one or more in TDE,
Described dispersant is selected from polyether modified siloxane, BYK-111, BYK-110, one or more in polydimethylsiloxane,
Described defoamer is selected from polyether modified siloxane, dimethyl siloxane, one or more in BYK-A530, BYK-525,
Described levelling agent is selected from polyether modified siloxane, polydimethylsiloxane, one or more in BYK-315, BYK-320,
Described toner is selected from corresponding inorganic toner or organic toner,
In described firming agent, various components are as follows:
Described polyetheramine be selected from D-230, the one in D-400, T-403,
Described modified amine is modified selected from IPDA, the one in MXDA modification,
Described accelerator is selected from DMP-30, K-54, benzyl dimethylamine, the one in triethylamine.