CN103525279A - 一种铁红防锈底漆 - Google Patents
一种铁红防锈底漆 Download PDFInfo
- Publication number
- CN103525279A CN103525279A CN201310466751.8A CN201310466751A CN103525279A CN 103525279 A CN103525279 A CN 103525279A CN 201310466751 A CN201310466751 A CN 201310466751A CN 103525279 A CN103525279 A CN 103525279A
- Authority
- CN
- China
- Prior art keywords
- parts
- iron oxide
- oxide red
- proofing primer
- red rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及油漆领域，特别是一种铁红防锈底漆，其质量份组成为：改性醇酸树脂25～35份、醋酸纤维素20～30份、单宁酸5～8份、铁红20～25份、滑石粉3～5份、云母粉3～6份、鞣酸2～5份、流平剂0.5～1.5份、消泡剂0.2～1.2份、丁醇20～30份、环己酮15～20份、异丙醇10～15份。采用本发明的技术方案的有益效果是：本发明的铁红防锈底漆具有良好的附着力，具有良好的化学品质，耐盐雾、耐水性、耐油性较好。而且其机械性能好、填充性强，尤其适用于各类金属制品、车辆机械、船舶等防锈打底，施工过程无污染，安全环保，生产过程简单，无须特殊设备，性价比高。
Description
技术领域
本发明涉及油漆领域，特别是一种铁红防锈底漆。
背景技术
铁红防锈漆是一种可保护金属表面免受大气、海水等的化学或电化学腐蚀的涂料。由改性醇酸树脂、防锈颜料、体质颜料、催干剂，有机溶剂等组成。
防锈底漆的防锈功能主要通过防锈颜料发挥作用，因此通常以防锈颜料的作用和名称分类命名。以防锈颜料的防锈作用机理来看，大致归纳为四种类型：物理作用防锈底漆、化学作用防锈底漆、电化学作用防锈底漆及综合作用防锈底漆，其中化学作用防锈底漆一般为化学防锈涂料、磷化底涂和带锈涂料。结合使用效果又可分为普通防锈漆和特种防锈漆，普通防锈漆分为物理、和一般化学防锈涂料，特种防锈漆分为：磷化底漆、富锌底漆和锈面涂料。
传统防锈油漆，虽有其优点，但需要以破坏环境为代价，来获取自身效益。如红丹防锈漆，虽然防锈质量比较好，但由于铅含量高，在施工和铲除旧的红丹漆及焊接时易产生毒物，对施工人员伤害大，且难以治愈。被铲下的红丹漆或喷出洒落在地上的红丹漆，渗透在地里或流到江河里会污染水质，且对人的身体不好。
发明内容
本发明的目的是：克服现有技术中防锈底漆中含有铅等有害物质，对人体和环境造成影响的技术不足，提供一种成本低、安全无污染的铁红防锈底漆。
为实现本发明的目的，本发明采用的技术方案如下：
一种铁红防锈底漆，其质量份组成为：改性醇酸树脂25～35份、醋酸纤维素20～30份、单宁酸5～8份、铁红20～25份、滑石粉3～5份、云母粉3～6份、鞣酸2～5份、流平剂0.5～1.5份、消泡剂0.2～1.2份、丁醇20～30份、环己酮15～20份、异丙醇10～15份。
进一步的，所述改性醇酸树脂选自：松香改性醇酸树脂、苯乙烯改性醇酸树脂、苯甲酸改性醇酸树脂中的至少一种。
进一步的，所述流平剂选自：平滑流平剂、快速破泡剂、溶剂型涂料用脱泡剂中的至少一种。
进一步的，所述消泡剂选自：乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯中的至少一种。
进一步的，所述消泡剂为高碳醇脂肪酸酯复合物。
进一步的，一种铁红防锈底漆，其质量份组成为：改性醇酸树脂30份、醋酸纤维素25份、单宁酸6份、铁红22份、滑石粉4份、云母粉4份、鞣酸3.5份、流平剂1份、消泡剂0.7份、丁醇25份、环己酮17份、异丙醇12份。
本发明添加高碳醇脂肪酸酯复合物的目的是：无腐蚀性，不易燃，不易爆，不挥发，性质稳定，1%水溶液pH为8～9，相对密度0.78～0.88，室温下及加热时易流动，-25～-30℃时粘度增大，流动性差，用作消泡剂安全可靠。
采用本发明的技术方案的有益效果是：本发明的铁红防锈底漆具有良好的附着力，具有良好的化学品质，耐盐雾、耐水性、耐油性较好。而且其机械性能好、填充性强，尤其适用于各类金属制品、车辆机械、船舶等防锈打底，施工过程无污染，安全环保，生产过程简单，无须特殊设备，性价比高。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
实施例1
一种铁红防锈底漆，其质量份组成为：松香改性醇酸树脂、苯甲酸改性醇酸树脂25份，醋酸纤维素20份，单宁酸5份，铁红20份，滑石粉3份，云母粉3份，鞣酸2份，平滑流平剂0.5份，乳化硅油，高碳醇脂肪酸酯复合物0.2份，丁醇20份，环己酮15份，异丙醇10份。
实施例2
一种铁红防锈底漆，其质量份组成为：松香改性醇酸树脂、苯乙烯改性醇酸树脂30份，醋酸纤维素25份，单宁酸6份，铁红22份，滑石粉4份，云母粉4份，鞣酸3.5份，平滑流平剂、快速破泡剂1份，高碳醇脂肪酸酯复合物0.7份，丁醇25份，环己酮17份，异丙醇12份。
实施例3
一种铁红防锈底漆，其质量份组成为：苯甲酸改性醇酸树脂35份，醋酸纤维素30份，单宁酸8份，铁红25份，滑石粉5份，云母粉6份，鞣酸5份，溶剂型涂料用脱泡剂1.5份，聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯1.2份，丁醇30份，环己酮20份，异丙醇15份。
本发明添加高碳醇脂肪酸酯复合物的目的是：无腐蚀性，不易燃，不易爆，不挥发，性质稳定，1%水溶液pH为8～9，相对密度0.78～0.88，室温下及加热时易流动，-25～-30℃时粘度增大，流动性差，用作消泡剂安全可靠。
本发明采用苯甲酸改性醇酸树脂的目的：苯甲酸改性醇酸树脂是用苯甲酸或对叔丁基苯甲酸代替部分脂肪酸制成的改性醇酸树脂。苯甲酸是一元酸，分子量较小，而且有一个苯环结构，引入醇酸树脂结构中可使漆膜快干，光泽好，硬度大，耐水性、耐盐雾性、保光性、耐候性均好，耐溶剂性比苯乙烯改性的醇酸树脂好，不怕咬起；但较脆，耐冲击性与弯曲性比未改性者差，与其他醇酸树脂或氨基树脂的混溶性也很好，可以并用。
尽管上述实施例已对本发明的技术方案进行了详细地描述，但是本发明的技术方案并不限于以上实施例，在不脱离本发明的思想和宗旨的情况下，对本发明的技术方案所做的任何改动都将落入本发明的权利要求书所限定的范围。
Claims (6)
1.一种铁红防锈底漆，其特征在于，其质量份组成为：改性醇酸树脂25～35份、醋酸纤维素20～30份、单宁酸5～8份、铁红20～25份、滑石粉3～5份、云母粉3～6份、鞣酸2～5份、流平剂0.5～1.5份、消泡剂0.2～1.2份、丁醇20～30份、环己酮15～20份、异丙醇10～15份。
2.根据权利要求1所述的一种铁红防锈底漆，其特征在于，所述改性醇酸树脂选自：松香改性醇酸树脂、苯乙烯改性醇酸树脂、苯甲酸改性醇酸树脂中的至少一种。
3.根据权利要求1所述的一种铁红防锈底漆，其特征在于，所述流平剂选自：平滑流平剂、快速破泡剂、溶剂型涂料用脱泡剂中的至少一种。
4.根据权利要求1所述的一种铁红防锈底漆，其特征在于，所述消泡剂选自：乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯中的至少一种。
5.根据权利要求1所述的一种铁红防锈底漆，其特征在于，所述消泡剂为高碳醇脂肪酸酯复合物。
6.根据权利要求1所述的一种铁红防锈底漆，其特征在于，其质量份组成为：改性醇酸树脂30份、醋酸纤维素25份、单宁酸6份、铁红22份、滑石粉4份、云母粉4份、鞣酸3.5份、流平剂1份、消泡剂0.7份、丁醇25份、环己酮17份、异丙醇12份。