CN103525186A - UV (Ultraviolet) offset halogen-free printing ink and preparation method thereof - Google Patents
UV (Ultraviolet) offset halogen-free printing ink and preparation method thereof Download PDFInfo
- Publication number
- CN103525186A CN103525186A CN201310484399.0A CN201310484399A CN103525186A CN 103525186 A CN103525186 A CN 103525186A CN 201310484399 A CN201310484399 A CN 201310484399A CN 103525186 A CN103525186 A CN 103525186A
- Authority
- CN
- China
- Prior art keywords
- acrylate
- offset printing
- printing ink
- ink
- phenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to UV (Ultraviolet) printing ink, and specifically relates to UV offset halogen-free printing ink and a preparation method thereof. The UV printing ink formula consists of the following components in percentage by weight: 30-50% of resin, 10-20% of polyfunctional acrylate, 1-4% of assistant, 5-18% of photoinitiator, 3-6% of filler, 10-45% of pigments and 0.5-1.5% of phosphate, wherein the resin is a mixture of polyhydric alcohol-modified acrylate, amido-modified epoxy acrylate and urethane acrylate with high functional groups. The printing ink does not contain any halogens and generate cancerogenic substances such as dioxin after combination, is less in influence on the environment and a human body and is environment-friendly. In addition, the printing ink further has the advantages of fast curing speed, stable performance, strong adhesive force, strong storage stability, good compound dispersibility with various pigments and the like, and is applicable to high-speed production and is high in production efficiency. The printing ink can be fully dried and fixed on the surface of a matrix within a short time.
Description
Technical field
The present invention relates to a kind of UV ink, be specifically related to a kind of UV offset printing Halogen ink and preparation method thereof.
Background technology
UV offset printing Halogen ink, is to utilize ultraviolet light wave photosensitization, makes black film forming and dry.UV China ink mechanism dry and film forming is a kind of variation of chemistry.Utilize different ultraviolet spectrograms, produce different energy and by different prepolymers and different monomers, aggregate into polymkeric substance.So the look film of UV ink, has good mechanicalness and chemical.
UV offset printing Halogen ink is comprised of pigment, pre-(together) polymers, reactive thinner, light trigger and auxiliary agent conventionally, have curing speed soon, containing volatile solvent, odorless, the advantage such as non-stimulated, levelling good, not network blocking, water tolerance are strong, resistance to solvent scouring, be applicable to the printing of the materials such as metal foil paper, synthetic paper, compound gold and silver paperboard, compound laser paper, polychlorovinyl sheet material, polyester sheet, crystalline p p sheet, polyethylene sheets, iron plate.
In offset printing, use UV Halogen ink; can remove the color separation of dusting from; be conducive to the clean of printing environment; protection operator's health, has also avoided the trouble brought to post-press finishing owing to dusting, as the impact on glazing, overlay film; and can carry out line processing; improve operating environment, enhance productivity, shorten the time of delivery.
UV offset printing Halogen ink just solidifies and integrates after UV light source irradiates; pre-irradiation skinning not in ink tank not, can be not dry and hard in seal machine or version yet, and these characteristics can prevent the generation of ink skinning; solve trouble and worry when offset press is shut down, greatly reduced the waste of ink.
In addition, UV offset printing Halogen ink is in existing flexographic ink formula materials, to filter out not halogen-containing starting material as the material of formula.This has got rid of the existence of halogen ink from source.In some European ink standards, regulation demonstration can not contain halogen.From environmental angle, UV offset printing Halogen ink is mainly used in the printing of packing, environmentally friendly.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, a kind of UV offset printing Halogen ink is provided, this ink, containing any halogen, can not produce the carcinogenic substances such as Dioxins after burning yet, few, environmentally friendly on environment and human body impact.It is fast that this ink also has curing speed in addition, stable performance, and strong adhesion, stability in storage is strong, with the advantage such as the composite good dispersity of various pigment, is applicable to high-speed production, and production efficiency is high, only needs the extremely short time to anchor at substrate surface by complete drying.
Another object of the present invention is to provide the preparation method of above-mentioned a kind of UV offset printing Halogen ink.
Technical problem to be solved by this invention is achieved by the following technical programs:
An offset printing Halogen ink, this ink formulations is comprised of each component of following weight percent:
Resin 30 ~ 50%, this resin is the mixture of polyalcohol modified acrylate, amino modified epoxy acrylate, high functional polyurethane acrylate.Polyalcohol modified acrylate can produce the solidified coating of high crosslink density, also can increase solidification rate, and it can also improve glossiness, hardness and wear resistance in addition, and polyhydric character contributes to the dispersed of pigment; Amino modified epoxy acrylate contributes to improve the water tolerance of coating; And high functional polyurethane acrylate utilizes the characteristic of its high functionality, can effectively mix and disperse above-mentioned two kinds of resins, be also conducive to increase sticking power and hardness; Therefore, the feature of the comprehensive above-mentioned three kinds of resins of the present invention, gives this resin good characteristic.
Polyfunctional group acrylate monomer 10 ~ 20%; Monomer used selects those skilled in the art's conventional monomer that does not contain the polyfunctionality of phenyl ring when carrying out UV Printing ink producing all can realize the present invention, for example: at least one in tripropylene glycol double methacrylate, Viscoat 295, ethoxylated trimethylolpropane triacrylate, propoxylation Viscoat 295, double pentaerythritol methacrylate.Therefore the monomer structure resin-phase of these high functionalities seemingly, not only contributes to the dispersed of resin, is also conducive to sticking power, the hardness of coating, the further reinforcement of water tolerance.
Auxiliary agent 1 ~ 4%, according to the needs of formula, selects those skilled in the art's conventional auxiliary agent when carrying out UV Printing ink producing, as: utilize stopper to prevent that pigment from reuniting and hyper-dispersant help pigment effectively disperses.
Light trigger 5 ~ 18%, monomer used selects those skilled in the art's conventional light trigger when carrying out UV Printing ink producing all can realize the present invention, for example: sec.-propyl thia anthraquinone, 4-dimethylamino-ethyl benzoate, 2, 4-diethyl thioxanthone, 1-hydroxyl-cyclohexyl-phenyl ketone, 2-methyl isophthalic acid-[4-methylthio group phenyl]-2-morpholinyl-1-acetone, 2, 4, 6 (trimethylbenzoyl) diphenyl phosphine oxide, 2-phenyl benzyl-2-dimethyl amine-1-(4-morpholine benzyl phenyl) butanone, at least one in 4-phenyl benzophenone, these light triggers all have good consistency with monomer and resin, toxicity is little.
Filler 3 ~ 6%, monomer used selects those skilled in the art's conventional filler when carrying out UV Printing ink producing all can realize the present invention; Such as: at least one in talcum powder, wilkinite, calcium carbonate etc.
Pigment 10 ~ 45%, needs for required color, can adopt the pigment of distinct colors; Phosphoesterase 30 .5 ~ 1.5%, phosphoric acid ester, as adhesion promoter, can effectively increase the bonding force of resin and bottom in the present invention.
The preparation method of above-mentioned UV offset printing Halogen ink, specifically can adopt following working method:
(1) light trigger and polyfunctionality Acrylic Acid Monomer are mixed, polyfunctionality Acrylic Acid Monomer and initiator fully mix and obtain mixed solution 1;
(2) after high functional polyurethane acrylate, amino modified epoxy acrylate and polyalcohol modified acrylate being mixed evenly, add dispersion agent, under the state stirring, add successively pigment, filler and stopper, with 600 ~ 1200rpm, stir again, when temperature is elevated to 50 ℃, continue again to stir within 30 minutes, to obtain mixed solution 2;
(3) under whipped state, in mixed solution 2, add successively mixed solution 1 and phosphoric acid ester, in stirring tank, stir;
(4) ink stirring is placed on after grinding 2 ~ 6 times on three-roll grinder and obtains UV offset printing Halogen ink.
Further each constituent optimization of described formula is:
Polyalcohol modified acrylate 15 ~ 25%;
Amino modified epoxy acrylate 10 ~ 15%;
High functional polyurethane acrylate 5 ~ 10%;
Polyfunctional group acrylate monomer 10 ~ 20%;
Auxiliary agent 1 ~ 4%;
Light trigger 8 ~ 15%;
Filler 3 ~ 6%;
Pigment 10 ~ 30%;
Phosphoric acid ester 1 ~ 1.5%.
The present invention has following beneficial effect:
The first, UV curing speed is fast, stable performance, and transfer performance is good, is applicable to very much high-speed production, and production efficiency is high;
The second, do not contain the halogenss such as fluorine, chlorine, bromine, iodine, few on environment and human body impact, meet environmental requirement; Containing organic volatile, not little to human body skin pungency, be beneficial to ink and printing work personnel's health, be also beneficial to and continue to improve environment and prevent from polluting;
Three, stability in storage is strong, and hardness is high, has well water-fast, oil resistant, antifouling property;
Four, there is good adhesion property, be applicable to metal foil paper, synthetic paper, compound gold and silver paperboard, compound laser paper, transfer paper, polychlorovinyl sheet material, polyester sheet, the material printings such as crystalline p p sheet, polyethylene sheets, iron plate.
Embodiment
Below in conjunction with embodiment, the present invention will be described in detail, and embodiment is only the preferred embodiment of the present invention, is not limitation of the invention.
Embodiment 1:
Polyalcohol modified acrylate 25%;
Amino modified epoxy acrylate 14%;
High functional polyurethane acrylate 8%;
Tripropylene glycol double methacrylate 7%;
Propoxylation Viscoat 295 8%;
Stopper 1%;
Dispersion agent 1%;
4-phenyl benzophenone 4%;
2,4,6 (trimethylbenzoyl) diphenyl phosphine oxide 6%;
Filler 5%;
Phthalocyanine blue 20%;
Phosphoric acid ester 1%.
Embodiment 2
Polyalcohol modified acrylate 23%;
Amino modified epoxy acrylate 12%;
High functional polyurethane acrylate 10%;
Viscoat 295 10%;
Ethoxylated trimethylolpropane triacrylate 5%;
Stopper 1%;
Dispersion agent 2%;
Sec.-propyl thia anthraquinone 3%;
2-phenyl benzyl-2-dimethyl amine-1-(4-morpholine benzyl phenyl) butanone 6%;
Filler 5%;
Permanent bordeaux 22%;
Phosphoric acid ester 1%.
Embodiment 3
Polyalcohol modified acrylate 22%;
Amino modified epoxy acrylate 15%;
High functional polyurethane acrylate 10%;
Viscoat 295 6%;
Double pentaerythritol methacrylate 7%;
Stopper 2%;
Dispersion agent 2%;
4-dimethylamino-ethyl benzoate 7%;
1-hydroxyl-cyclohexyl-phenyl ketone 6%;
Filler 5%;
Diarylide yellow 17%;
Phosphoric acid ester 1%.
Embodiment 4:
Polyalcohol modified acrylate 21%;
Amino modified epoxy acrylate 10%;
High functional polyurethane acrylate 10%;
Ethoxylated trimethylolpropane triacrylate 8%;
Propoxylation Viscoat 295 9%;
Stopper 2%;
Dispersion agent 1%;
2-methyl isophthalic acid-[4-methylthio group phenyl]-2-morpholinyl-1-acetone 5%;
1-hydroxyl-cyclohexyl-phenyl ketone 8%;
Filler 5%;
Carbon black 11%;
Phthalocyanine blue 3%;
Penetrate light indigo plant 4%;
Permanent violet 2%;
Phosphoric acid ester 1%.
Upper table is the performance test of corresponding embodiment
The above embodiment has only expressed embodiments of the present invention; it describes comparatively concrete and detailed; but can not therefore be interpreted as the restriction to the scope of the claims of the present invention; as long as employing is equal to the technical scheme that the form of replacement or equivalent transformation obtains, within all should dropping on protection scope of the present invention.
Claims (7)
1. a UV offset printing Halogen ink, is characterized in that ink formulations is comprised of each component of following weight percent:
Resin 30 ~ 50%;
Polyfunctional group acrylate monomer 10 ~ 20%;
Auxiliary agent 1 ~ 4%;
Light trigger 5 ~ 18%;
Filler 3 ~ 6%;
Pigment 10 ~ 45%;
Phosphoesterase 30 .5 ~ 1.5%;
Described resin is the mixture of polyalcohol modified acrylate, amino modified epoxy acrylate, high functional polyurethane acrylate.
2. a kind of UV offset printing Halogen ink according to claim 1, it is characterized in that, described polyfunctional group acrylate monomer is at least one in tripropylene glycol double methacrylate, Viscoat 295, ethoxylated trimethylolpropane triacrylate, propoxylation Viscoat 295, double pentaerythritol methacrylate.
3. a kind of UV offset printing Halogen ink according to claim 1, is characterized in that, described filler is at least one in talcum powder, wilkinite, calcium carbonate etc.
4. a kind of UV offset printing Halogen ink according to claim 1, is characterized in that, described auxiliary agent is stopper and hyper-dispersant.
5. a kind of UV offset printing Halogen ink according to claim 1; it is characterized in that; described light trigger is sec.-propyl thia anthraquinone, 4-dimethylamino-ethyl benzoate, 2; 4-diethyl thioxanthone, 1-hydroxyl-cyclohexyl-phenyl ketone, 2-methyl isophthalic acid-[4-methylthio group phenyl]-2-morpholinyl-1-acetone, 2; 4; 6 (trimethylbenzoyl) diphenyl phosphine oxide, 2-phenyl benzyl-2-dimethyl amine-1-(4-morpholine benzyl phenyl) butanone, phenyl two (2; 4,6-trimethylbenzoyl) at least one in phosphine oxide, 4-phenyl benzophenone.
6. a preparation method for UV offset printing Halogen ink described in claim 1, is characterized in that comprising the steps:
(1) light trigger and polyfunctionality Acrylic Acid Monomer are mixed, polyfunctionality Acrylic Acid Monomer and initiator fully mix and obtain mixed solution 1;
(2) after high functional polyurethane acrylate, amino modified epoxy acrylate and polyalcohol modified acrylate being mixed evenly, add dispersion agent, under the state stirring, add successively pigment, filler and stopper, with 600 ~ 1200rpm, stir again, when temperature is elevated to 50 ℃, continue again to stir within 30 minutes, to obtain mixed solution 2;
(3) under whipped state, in mixed solution 2, add successively mixed solution 1 and phosphoric acid ester, in stirring tank, stir;
(4) ink stirring is placed on after grinding 2 ~ 6 times on three-roll grinder and obtains UV offset printing Halogen ink.
7. a kind of UV offset printing Halogen ink according to claim 1, is characterized in that, each constituent optimization of described formula is:
Polyalcohol modified acrylate 15 ~ 25%;
Amino modified epoxy acrylate 10 ~ 15%;
High functional polyurethane acrylate 5 ~ 10%;
Polyfunctional group acrylate monomer 10 ~ 20%;
Auxiliary agent 1 ~ 4%;
Light trigger 8 ~ 15%;
Filler 3 ~ 6%;
Pigment 10 ~ 30%;
Phosphoric acid ester 1 ~ 1.5%.