CN103508706A - 一种提高混凝土管桩轴向承载力的配方 - Google Patents
一种提高混凝土管桩轴向承载力的配方 Download PDFInfo
- Publication number
- CN103508706A CN103508706A CN201310404592.9A CN201310404592A CN103508706A CN 103508706 A CN103508706 A CN 103508706A CN 201310404592 A CN201310404592 A CN 201310404592A CN 103508706 A CN103508706 A CN 103508706A
- Authority
- CN
- China
- Prior art keywords
- formula
- tubular pile
- concrete tubular
- bearing capacity
- axial bearing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：铝酸钠5%～8%、砂30%～35%、石25%～30%、陶粒10%～15%、木质素磺酸钙4%～8%、水泥12%～20%、水3%～7%。本发明具有材料搭配合理、方便制造和制造成本低等优点，能提高混凝土管桩轴向承载力进而缩小管桩体积，节省了生产制造的成本，为混凝土管桩的运输以及施工提供了方便。
Description
技术领域
本发明涉及管桩制造技术领域，具体的说是一种提高混凝土管桩轴向承载力的配方。
背景技术
在当今的大城市里，经常会看到造型独特的建筑。这些建筑本身对于其地基的牢固程度要求较高，如有的要求有高的抗裂弯矩，有的要求能够承受较高的轴向压力，有的要求有效预应力要达到一定值等等，尤其是对于轴向压力要求较高的混凝土管桩，致使混凝土管桩的体积不得不随着要求的提高而变大，这样给管桩的运输以及施工都带来了极大的麻烦。
发明内容
本发明所要解决的技术问题在于提供一种材料搭配合理的、方便制造的、制造成本低的，能提高混凝土管桩轴向承载力进而缩小管桩体积的配方，即一种提高混凝土管桩轴向承载力的配方。
本发明所要解决的技术问题采用以下技术方案来实现：
一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
所述各组分所占的最佳质量百分比如下：
相关组分的性能及作用如下：
铝酸钠：性质：白色、无臭、无味，呈强碱性的固体，高温熔融产物为白色粉末，溶于水，不溶于乙醇，在空气中易吸收水份和二氧化碳，水中溶解后易析出氢氧化铝沉淀，氢氧化铝溶于氢氧化钠溶液也生成偏铝酸钠溶液。用作纺织品的媒染剂、纸的填料、水的净化剂等。可用氧化铝与固态氢氧化钠或碳酸钠共熔制得。主要用于土木工程方面，本品与水玻璃混合用于施工中的堵漏；造纸行业，本品与硫酸铝混合使用是一种良好的填充剂；水处理方面，可做净水剂助剂，可做为水泥速凝剂；在石油化工、制药、橡胶、印染、纺织、催化剂生产中也有较广泛的应用。
陶粒：具有密度小、质轻、保温、隔热、耐火性优异、抗震性好、抗渗性优异等特性，能够提高混凝土管桩的结构强度，起到隔震、抗震的作用，对混凝土管桩起到保护作用。
木质素磺酸钙：溶于水，微酸性，稳定性良好。有以下用途：1、用作混凝土减水剂：掺水泥量的0.25～0.3%，可以减少用水量10～14以上，改善混凝土和易性，提高工程质量，夏季使用，可抑制坍落度损失，一般都与高效减水剂复配使用；2、用作矿粘结剂：冶炼业，用木质素磺酸钙与矿粉混合，制成矿粉球，干燥后放入窑中，可大幅度提高冶炼回收率；3、耐火材料：制造耐火材料砖瓦时，使用木质素磺酸钙做分散剂和粘合剂，能显著改善操作性能，并有减水、增强、防止龟裂等良好效果；4、陶瓷：木质素磺酸钙用于陶瓷制品，可以降低碳含量增加生坯强度，减少塑性粘土用量，泥浆流动性好，提高成品率70-90%，烧结速度由70分钟减少为40分钟；5、用作饲料粘合剂，可提高家畜和家禽的喜食性，颗粒强度好，减少饲料的微粉量，减少粉料反回率，降低成本。模的损失减少，生产能力提高10-20%，美国与加拿大在饲料中允许掺量为4.0%；6、其它：木质素磺酸钙还可用于精炼助剂、铸造、农药可湿性粉剂加工、型煤压制、采矿、选矿业的选矿剂，道路、土壤、粉尘的控制、制革鞣革填料、炭黑造粒等方面。
本发明的有益效果是：本发明具有材料搭配合理、方便制造和制造成本低等优点，能提高混凝土管桩轴向承载力进而缩小管桩体积，节省了生产制造的成本，为混凝土管桩的运输以及施工提供了方便。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面对本发明进一步阐述。
实施例一：
一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
实施例二：
一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
实施例三：
一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种提高混凝土管桩轴向承载力的配方，其特征在于：该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
2.根据权利要求1所述的一种提高混凝土管桩轴向承载力的配方，其特征在于：所述各组分所占的最佳质量百分比如下：