CN103483989A - 一种耐水煮粉末涂料 - Google Patents
一种耐水煮粉末涂料 Download PDFInfo
- Publication number
- CN103483989A CN103483989A CN201310393220.0A CN201310393220A CN103483989A CN 103483989 A CN103483989 A CN 103483989A CN 201310393220 A CN201310393220 A CN 201310393220A CN 103483989 A CN103483989 A CN 103483989A
- Authority
- CN
- China
- Prior art keywords
- parts
- boiling
- water
- hours
- resistant powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐水煮粉末涂料，它是由下述重量份的原料组成的：二酚基丙烷型环氧树脂50-60、P9335聚酯树脂10-20、聚甲基苯基硅氧烷液体1-2、二甲基咪唑2-3、红金粉1.8-2.2、中空玻璃微珠6-8、焦宝石粉2-3、煅烧红柱石颗粒2-3、磷酸三丁酯1-2、复合填料10-20；本发明的涂料具有下列优势：1.耐水煮性能从常规粉末涂料的60度10小时提升到95度25小时，长期水煮测试涂层表面仍无变化。2.在耐候性测试方面可以将常规粉的500小时提升至1200小时，涂层仍无褪色老化现象。
Description
技术领域
本发明主要涉及一种涂料，尤其涉及一种耐水煮粉末涂料。
背景技术
热固型粉末涂料是指以热固性树脂作为成膜物质，加入起交联反应的固化剂经加热后能形成不溶不熔的质地坚硬涂层。温度再高该涂层也不会像热塑性涂层那样软化，而只能发生分解。由于热固性粉末涂料所采用的树脂为聚合度较低的预聚物，分子量较低，所以涂层的流平性较好，具有较好的装饰性，而且低分子量的预聚物经固化后，能形成网状交联的大分子，因而涂层具有较好防腐性和机械性能。故热固性粉末涂料发展尤为迅速，而为了提高传统粉末的整体性能，通过加入新的复合填料等来改善其性能是很有必要的。
发明内容
本发明目的就是为了提供一种耐水煮粉末涂料。
本发明是通过以下技术方案实现的：
一种耐水煮粉末涂料，其特征在于它是由下述重量份的原料组成的：
聚酯树脂脂P9335 60-70、高岭土10-20、干性油醇酸树脂3-5、聚乙烯醚3.5-5.5、间苯二酚1-2、肌醇六磷酸酯2-3、硫酸钡4-6、氨乙基哌嗪5-10、醋酸钠1-2、复合填料10-20；
所述的复合填料是由下述重量份的原料组成的：
红土50-60、骨粉4-6、铁矿渣粉10-13、硅灰石粉5-7、三聚磷酸钠1-2、十二烷基三甲基氯化铵2-3、桉树油1-2；
将上述红土、铁矿渣粉、硅灰石粉混合，在600-800℃下煅烧3-4小时，冷却出料，加入桉树油，混合均匀，得预混料，将三聚磷酸钠加入到15-20倍水中，搅拌均匀后加入十二烷基三甲基氯化铵，升高温度为60-80℃，与上述预混料混合研磨，烘干，过80-100目筛，即得所述复合填料。
一种耐水煮粉末涂料的制备方法，包括以下步骤：
将上述各原料放入高速混合机中进行预混，然后送入到高速挤出机中混炼挤出，然后压片破碎后，再经过ACM 微粉碎机粉碎、过筛，即得所述耐水煮粉末涂料。
本发明的优点是：
本发明的涂料具有下列优势：1.耐水煮性能从常规粉末涂料的60度10小时提升到95度25小时，长期水煮测试涂层表面仍无变化。2.在耐候性测试方面可以将常规粉的500小时提升至1200小时，涂层仍无褪色老化现象。
具体实施方式
实施例1，
一种耐水煮粉末涂料，它是由下述重量份（公斤）的原料组成的：
聚酯树脂脂P9335 70、高岭土10、干性油醇酸树脂5、聚乙烯醚5.5、间苯二酚2、肌醇六磷酸酯2、硫酸钡6、氨乙基哌嗪10、醋酸钠1、复合填料20；
所述的复合填料是由下述重量份的原料组成的：
红土60、骨粉4、铁矿渣粉13、硅灰石粉7、三聚磷酸钠2、十二烷基三甲基氯化铵2、桉树油2；
将上述红土、铁矿渣粉、硅灰石粉混合，在800℃下煅烧3小时，冷却出料，加入桉树油，混合均匀，得预混料，将三聚磷酸钠加入到20倍水中，搅拌均匀后加入十二烷基三甲基氯化铵，升高温度为80℃，与上述预混料混合研磨，烘干，过100目筛，即得所述复合填料。
一种耐水煮粉末涂料的制备方法，包括以下步骤：
将上述各原料放入高速混合机中进行预混，然后送入到高速挤出机中混炼挤出，然后压片破碎后，再经过ACM 微粉碎机粉碎、过筛，即得所述耐水煮粉末涂料。
性能测试：
1.耐水煮性能从常规粉末涂料的60度10小时提升到95度25小时，长期水煮测试涂层表面仍无变化；
2.在耐候性测试方面可以将常规粉的500小时提升至1200小时，涂层仍五褪色老化现象。
Claims (2)
1.一种耐水煮粉末涂料，其特征在于它是由下述重量份的原料组成的：
聚酯树脂脂P9335 60-70、高岭土10-20、干性油醇酸树脂3-5、聚乙烯醚3.5-5.5、间苯二酚1-2、肌醇六磷酸酯2-3、硫酸钡4-6、氨乙基哌嗪5-10、醋酸钠1-2、复合填料10-20；
所述的复合填料是由下述重量份的原料组成的：
红土50-60、骨粉4-6、铁矿渣粉10-13、硅灰石粉5-7、三聚磷酸钠1-2、十二烷基三甲基氯化铵2-3、桉树油1-2；
将上述红土、铁矿渣粉、硅灰石粉混合，在600-800℃下煅烧3-4小时，冷却出料，加入桉树油，混合均匀，得预混料，将三聚磷酸钠加入到15-20倍水中，搅拌均匀后加入十二烷基三甲基氯化铵，升高温度为60-80℃，与上述预混料混合研磨，烘干，过80-100目筛，即得所述复合填料。
2.一种如权利要求1所述的耐水煮粉末涂料的制备方法，其特征在于包括以下步骤：
将上述各原料放入高速混合机中进行预混，然后送入到高速挤出机中混炼挤出，然后压片破碎后，再经过ACM 微粉碎机粉碎、过筛，即得所述耐水煮粉末涂料。