CN103320068A - Flame-retardant adhesive - Google Patents
Flame-retardant adhesive Download PDFInfo
- Publication number
- CN103320068A CN103320068A CN2013102607616A CN201310260761A CN103320068A CN 103320068 A CN103320068 A CN 103320068A CN 2013102607616 A CN2013102607616 A CN 2013102607616A CN 201310260761 A CN201310260761 A CN 201310260761A CN 103320068 A CN103320068 A CN 103320068A
- Authority
- CN
- China
- Prior art keywords
- flame
- agent
- flaming viscose
- hardener
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardant adhesive. The flame-retardant adhesive comprises the following ingredients in percentage by weight: 20-60% of amino resin, 8-16% of melamine, 5-12% of polyether polyol, 1-3% of adhesive force improver, 3-6% of silicon dioxide, 10-15% of epoxy hardener and 13-28% of flame retardant. The flame-retardant adhesive provided by the invention simultaneously has good adhesion and flame resistance and can avoid the potential safety hazard.
Description
Technical field
The present invention relates to the glue paste field, particularly relate to a kind of anti-flaming viscose agent.
Background technology
For a long time, can carry out combination by the mode of glue paste between the surface of variant production, the typical surface that combines by the glue paste mode comprises paper surface and paperboard surface.But, glue paste brand and of a great variety, of many uses, be difficult to select.
At present, the glue paste on the market, viscosity is not enough, if the accident of simultaneously presence of fire, glue paste will be good combustion-supporting product, accelerate spreading of fire, cause the generation of potential safety hazard.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of anti-flaming viscose agent, has good cementability, has simultaneously good flame retardant effect, has avoided the generation of potential safety hazard.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of anti-flaming viscose agent is provided, it is characterized in that, moiety and the weight ratio thereof of described anti-flaming viscose agent comprise:
Aminoresin 20-60%
Trimeric cyanamide 8-16%
Polyether glycol 5-12%
Adhesion promoter 1-3%
Silicon-dioxide 3-6%
Epoxy hardener 10-15%
Fire retardant 13-28%.
In a preferred embodiment of the present invention, described epoxy hardener is polyamide curing agent, amine hardener, amine additives modified firming agent, polyisocyanate curing agent or pnenolic aldehyde amine hardener.
In a preferred embodiment of the present invention, described fire retardant is red phosphorus.
The invention has the beneficial effects as follows: anti-flaming viscose agent of the present invention, have good cementability, have simultaneously good flame retardant resistance, avoided the generation of potential safety hazard.
Embodiment
The below is described in detail preferred embodiment of the present invention, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
The invention provides a kind of anti-flaming viscose agent, it is characterized in that, moiety and the weight ratio thereof of described anti-flaming viscose agent comprise:
Aminoresin 20-60%
Trimeric cyanamide 8-16%
Polyether glycol 5-12%
Adhesion promoter 1-3%
Silicon-dioxide 3-6%
Epoxy hardener 10-15%
Fire retardant 13-28%.
In above-mentioned, described adhesion promoter is the adhesion-promoting auxiliary agent of complementary metal, has increased adherence and the ductility of tackiness agent on metal works, has guaranteed adhesive attachment power, difficult drop-off.
Described epoxy hardener is polyamide curing agent, amine hardener, amine additives modified firming agent, polyisocyanate curing agent or pnenolic aldehyde amine hardener.
Among the present invention, described fire retardant is red phosphorus.Red phosphorus, nontoxic odorlessness, red phosphorus will could burn about 240 ℃, has well fire-retardant.
The anti-flaming viscose agent that the present invention discloses has good cementability, has simultaneously good flame retardant resistance, has avoided the generation of potential safety hazard.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (3)
1. an anti-flaming viscose agent is characterized in that, moiety and the weight ratio thereof of described anti-flaming viscose agent comprise:
Aminoresin 20-60%
Trimeric cyanamide 8-16%
Polyether glycol 5-12%
Adhesion promoter 1-3%
Silicon-dioxide 3-6%
Epoxy hardener 10-15%
Fire retardant 13-28%.
2. anti-flaming viscose agent according to claim 1 is characterized in that, described epoxy hardener is polyamide curing agent, amine hardener, amine additives modified firming agent, polyisocyanate curing agent or pnenolic aldehyde amine hardener.
3. anti-flaming viscose agent according to claim 1 is characterized in that, described fire retardant is red phosphorus.