CN103320023A - Fluorescent adhesive - Google Patents
Fluorescent adhesive Download PDFInfo
- Publication number
- CN103320023A CN103320023A CN2013102607565A CN201310260756A CN103320023A CN 103320023 A CN103320023 A CN 103320023A CN 2013102607565 A CN2013102607565 A CN 2013102607565A CN 201310260756 A CN201310260756 A CN 201310260756A CN 103320023 A CN103320023 A CN 103320023A
- Authority
- CN
- China
- Prior art keywords
- glue paste
- fluorescence glue
- fluorescent agent
- fluorescent adhesive
- sodium bicarbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fluorescent adhesive, comprising the components by weight percent: 15-55% of epoxy modified acrylate, 6-18% of vinyl acetate 10-20% of stannous octoate, 0.3-1.8% of plastic powder, 0.7-2.3% of sodium bicarbonate, 3-5% of carboxylated styrene butadiene latex, and 26-27% of fluorescer. In the manner, the fluorescent adhesive provided by the invention contains the carboxylated styrene butadiene latex and the fluorescer, so that the fluorescent adhesive has good adhesion, and simultaneously has the effect of glowing at night; and the beautiful degree is increased.
Description
Technical field
The present invention relates to the glue paste field, particularly relate to a kind of fluorescence glue paste.
Background technology
For a long time, can carry out combination by the mode of glue paste between the surface of variant production, the typical surface that combines by the glue paste mode comprises paper surface and paperboard surface.But, glue paste brand and of a great variety, of many uses, be difficult to select.
At present, the glue paste on the market, the viscosity deficiency comes off easily, and along with people are also more and more higher to the requirement of tackiness agent to the pursuit of fashion.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of fluorescence glue paste, has good cementability, has simultaneously in noctilucent effect, has increased aesthetics.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of fluorescence glue paste is provided, and moiety and the weight ratio thereof of described fluorescence glue paste comprise:
Epoxy modification acrylate 15-55%
Vinyl acetate between to for plastic 6-18%
Stannous octoate 10-20%
Mould cosmetics 0.3-1.8%
Sodium bicarbonate 0.7-2.3%
Carboxyl styrene-butadiene emulsion 3-5%
Fluorescent agent 26-27%.
In a preferred embodiment of the present invention, moiety and the weight ratio thereof of described fluorescence glue paste comprise:
Epoxy modification acrylate 45%
Vinyl acetate between to for plastic 12%
Stannous octoate 15%
Mould cosmetics 1.5%
Sodium bicarbonate 2.0%
Carboxyl styrene-butadiene emulsion 4%
Fluorescent agent 20.5%.
In a preferred embodiment of the present invention, the pH value of described fluorescent agent is 6.
The invention has the beneficial effects as follows: fluorescence glue paste of the present invention, contain carboxyl styrene-butadiene emulsion and fluorescent agent, make it have good cementability, have simultaneously in noctilucent effect, increased aesthetics.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
The invention provides a kind of fluorescence glue paste, moiety and the weight ratio thereof of described fluorescence glue paste comprise:
Epoxy modification acrylate 15-55%
Vinyl acetate between to for plastic 6-18%
Stannous octoate 10-20%
Mould cosmetics 0.3-1.8%
Sodium bicarbonate 0.7-2.3%
Carboxyl styrene-butadiene emulsion 3-5%
Fluorescent agent 26-27%.
Embodiment:
Moiety and the weight ratio thereof of described fluorescence glue paste comprise:
Epoxy modification acrylate 45%
Vinyl acetate between to for plastic 12%
Stannous octoate 15%
Mould cosmetics 1.5%
Sodium bicarbonate 2.0%
Carboxyl styrene-butadiene emulsion 4%
Fluorescent agent 20.5%.
In above-mentioned, described carboxylic styrene butadiene latex is to add a small amount of carboxylic acid and other auxiliary agent with divinyl, vinylbenzene, by the multipolymer that letex polymerization generates, is a kind of oyster white water dispersion that has bluish voilet gloss.Advantages such as the combined styrene ratio is higher, has higher cohesive force and conjunctiva intensity, and machinery and chemical stability are good, and is mobile, that package stability is all good, and loading level is big.
Described fluorescent agent is a kind of fluorescence dye, or is called white dyestuff, also is a kind of organic compound of complexity.Its characteristic is to excite incident beam to produce fluorescence, make dye the sparkling effect that material obtains similar fluorite, the material that naked eyes are seen is very white, reaches the effect that brightens.Its effect is that the sightless ultraviolet radiation that goods absorb is transformed into indigo fluorescent radiation, with original gold-tinted radiation each other complementary color become white light, improve the whiteness of product under daylight.Wherein, the pH value of described fluorescent agent is 6, and the size of pH value is determining the brightness of fluorescent agent.
The fluorescence glue paste that the present invention discloses contains carboxyl styrene-butadiene emulsion and fluorescent agent, makes it have good cementability, has simultaneously in noctilucent effect, has increased aesthetics.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (3)
1. a fluorescence glue paste is characterized in that, moiety and the weight ratio thereof of described fluorescence glue paste comprise:
Epoxy modification acrylate 15-55%
Vinyl acetate between to for plastic 6-18%
Stannous octoate 10-20%
Mould cosmetics 0.3-1.8%
Sodium bicarbonate 0.7-2.3%
Carboxyl styrene-butadiene emulsion 3-5%
Fluorescent agent 26-27%.
2. fluorescence glue paste according to claim 1 is characterized in that, moiety and the weight ratio thereof of described fluorescence glue paste comprise:
Epoxy modification acrylate 45%
Vinyl acetate between to for plastic 12%
Stannous octoate 15%
Mould cosmetics 1.5%
Sodium bicarbonate 2.0%
Carboxyl styrene-butadiene emulsion 4%
Fluorescent agent 20.5%.
3. fluorescence glue paste according to claim 1 is characterized in that, the pH value of described fluorescent agent is 6.