CN103319130B - A kind of light lath for building partition wall board attapulgite binder - Google Patents
A kind of light lath for building partition wall board attapulgite binder Download PDFInfo
- Publication number
- CN103319130B CN103319130B CN201310212037.6A CN201310212037A CN103319130B CN 103319130 B CN103319130 B CN 103319130B CN 201310212037 A CN201310212037 A CN 201310212037A CN 103319130 B CN103319130 B CN 103319130B
- Authority
- CN
- China
- Prior art keywords
- attapulgite
- partition wall
- wall board
- building partition
- light lath
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of light lath for building partition wall board attapulgite binder, be made up of the raw material of following weight part: 32.5 fast hard aluminum sulfate salt cement 120-150, pure-acrylic emulsion 40-50, polyvinyl alcohol 4-6, glycol ether 3-4, hydroxyethylmethyl-cellulose 2-3, quartz sand 100-150, vegetable fibre 4-6, alum stone flour 3-5, benzol sulfohydrazide 4-8, ground dolomite 5-10, attapulgite 10-15, pulverized slag 4-8, borax 1-2, trolamine 5-8,3-aminopropyl trimethoxysilane 0.5-1.Light lath for building partition wall board attapulgite binder cohesive force of the present invention is strong, the chance reducing layering and peel off, and ensures construction quality, avoids the hollowing after life-time service, problems of crack, thus improves weather resistance.
Description
Technical field
The present invention relates to a kind of material of construction binding agent, be specifically related to a kind of light lath for building partition wall board attapulgite binder.
Background technology
Light lath for building partition wall take ordinary Portland cement as gelling material, with light-weight aggregates such as haydite, pearlstone, industrial residues for main raw material, and the porous air core type batten produced by extrusion molding.A certain amount of binding agent is needed to fix during its construction and installation.But existing binding agent exists that operating efficiency is low, cementability is poor, useful life longevity is poor and the shortcoming such as poor stability, can not meet the bonding requirement of light lath for building partition wall.Therefore, a kind of brand-new high performance light lath for building partition wall tackiness agent of research and development is badly in need of.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, provide that a kind of cohesive strength is high, good endurance, construction are simple, the light lath for building partition wall board attapulgite binder of safety non-toxic evil.
The technical solution used in the present invention is as follows:
A kind of light lath for building partition wall board attapulgite binder, is made up of the raw material of following weight part:
32.5 fast hard aluminum sulfate salt cement 120-150
Pure-acrylic emulsion 40-50
Polyvinyl alcohol 4-6
Glycol ether 3-4
Hydroxyethylmethyl-cellulose 2-3
Quartz sand 100-150
Vegetable fibre 4-6
Alum stone flour 3-5
Benzol sulfohydrazide 4-8
Ground dolomite 5-10
Attapulgite 10-15
Pulverized slag 4-8
Borax 1-2
Trolamine 5-8
3-aminopropyl trimethoxysilane 0.5-1.
Preferably, a kind of light lath for building partition wall board attapulgite binder, is made up of the raw material of following weight part:
32.5 fast hard aluminum sulfate salt cement 120
Pure-acrylic emulsion 45
Polyvinyl alcohol 5
Glycol ether 3
Hydroxyethylmethyl-cellulose 2
Quartz sand 140
Vegetable fibre 5
Alum stone flour 4
Benzol sulfohydrazide 6
Ground dolomite 8
Attapulgite 10
Pulverized slag 6
Borax 1.5
Trolamine 6
3-aminopropyl trimethoxysilane 0.8.
A preparation method for light lath for building partition wall board attapulgite binder, comprises the following steps:
(1) ground dolomite and attapulgite mixed add in shredder, then add borax,
Trolamine and 3-aminopropyl trimethoxysilane, 2000-3000rpm speed lapping 10-15 minute, takes out and dries, and pulverizes porphyrize, crosses 50-100 mesh sieve, obtains rhombspar/attapulgite mixed powder, stand-by;
(2) pure-acrylic emulsion is joined in reactor, heating in water bath is to 80-90 DEG C, under agitation add polyvinyl alcohol, glycol ether and hydroxyethylmethyl-cellulose, stir 20-30 minute, add above-mentioned obtained rhombspar/attapulgite mixed powder again to continue to stir 10-15 minute, emulsion is carried out spraying dry under the hot gas flow of 250-280 DEG C, obtains rubber powder;
(3) surplus stock and above-mentioned obtained rubber powder dry mixing is even, ball milling 1-2 hour, crosses 200-300 mesh sieve, packs.
Beneficial effect of the present invention:
Light lath for building partition wall board attapulgite binder cohesive force of the present invention is strong, the chance reducing layering and peel off, and ensures construction quality, avoids the hollowing after life-time service, problems of crack, thus improves weather resistance; Invention adhesive dry mixing in advance mixes, and steady quality, adds the stirring of suitable quantity of water during use, construct simple and convenient; The present invention effectively utilizes the waste materials such as pulverized slag, without poisonous and harmful additive, meets environmental requirement completely, safety non-pollution.
Embodiment
A kind of light lath for building partition wall board attapulgite binder, is made up of the raw material of following weight part (kilogram):
32.5 fast hard aluminum sulfate salt cement 120
Pure-acrylic emulsion 45
Polyvinyl alcohol 5
Glycol ether 3
Hydroxyethylmethyl-cellulose 2
Quartz sand 140
Vegetable fibre 5
Alum stone flour 4
Benzol sulfohydrazide 6
Ground dolomite 8
Attapulgite 10
Pulverized slag 6
Borax 1.5
Trolamine 6
3-aminopropyl trimethoxysilane 0.8.
A preparation method for light lath for building partition wall board attapulgite binder, comprises the following steps:
(1) ground dolomite and attapulgite mixed add in shredder, then add borax,
Trolamine and 3-aminopropyl trimethoxysilane, 3000rpm speed lapping 15 minutes, takes out and dries, and pulverizes porphyrize, crosses 80 mesh sieves, obtains rhombspar/attapulgite mixed powder, stand-by;
(2) pure-acrylic emulsion is joined in reactor, heating in water bath to 85 DEG C, under agitation add polyvinyl alcohol, glycol ether and hydroxyethylmethyl-cellulose, stir 25 minutes, add above-mentioned obtained rhombspar/attapulgite mixed powder again and continue stirring 15 minutes, emulsion is carried out spraying dry under the hot gas flow of 260 DEG C, obtains rubber powder;
(3) surplus stock and above-mentioned obtained rubber powder dry mixing is even, ball milling 1.5 hours, crosses 200 mesh sieves, packs.
Binding agent Specifeca tion speeification of the present invention is as follows:
Tensile bond strength (Mpa): 1.1
Tensile bond strength (Mpa) after immersion: 0.9
Tensile bond strength (Mpa) after thermal ageing: 0.8
Tensile bond strength (Mpa) after freeze-thaw cycle: 0.6.
Claims (3)
1. a light lath for building partition wall board attapulgite binder, is characterized in that, is made up of the raw material of following weight part:
32.5 fast hard aluminum sulfate salt cement 120-150
Pure-acrylic emulsion 40-50
Polyvinyl alcohol 4-6
Glycol ether 3-4
Hydroxyethylmethyl-cellulose 2-3
Quartz sand 100-150
Vegetable fibre 4-6
Alum stone flour 3-5
Benzol sulfohydrazide 4-8
Ground dolomite 5-10
Attapulgite 10-15
Pulverized slag 4-8
Borax 1-2
Trolamine 5-8
3-aminopropyl trimethoxysilane 0.5-1.
2. a kind of light lath for building partition wall board attapulgite binder according to claim 1, is characterized in that, be made up of the raw material of following weight part:
32.5 fast hard aluminum sulfate salt cement 120
Pure-acrylic emulsion 45
Polyvinyl alcohol 5
Glycol ether 3
Hydroxyethylmethyl-cellulose 2
Quartz sand 140
Vegetable fibre 5
Alum stone flour 4
Benzol sulfohydrazide 6
Ground dolomite 8
Attapulgite 10
Pulverized slag 6
Borax 1.5
Trolamine 6
3-aminopropyl trimethoxysilane 0.8.
3. a preparation method for light lath for building partition wall board attapulgite binder as claimed in claim 1 or 2, is characterized in that comprising the following steps:
(1) ground dolomite and attapulgite mixed add in shredder, then add borax,
Trolamine and 3-aminopropyl trimethoxysilane, 2000-3000rpm speed lapping 10-15 minute, takes out and dries, and pulverizes porphyrize, crosses 50-100 mesh sieve, obtains rhombspar/attapulgite mixed powder, stand-by;
(2) pure-acrylic emulsion is joined in reactor, heating in water bath is to 80-90 DEG C, under agitation add polyvinyl alcohol, glycol ether and hydroxyethylmethyl-cellulose, stir 20-30 minute, add above-mentioned obtained rhombspar/attapulgite mixed powder again to continue to stir 10-15 minute, emulsion is carried out spraying dry under the hot gas flow of 250-280 DEG C, obtains rubber powder;
(3) surplus stock and above-mentioned obtained rubber powder dry mixing is even, ball milling 1-2 hour, crosses 200-300 mesh sieve, packs.