CN102976624A - Pattern coating glass and preparation method thereof - Google Patents
Pattern coating glass and preparation method thereof Download PDFInfo
- Publication number
- CN102976624A CN102976624A CN2012105264810A CN201210526481A CN102976624A CN 102976624 A CN102976624 A CN 102976624A CN 2012105264810 A CN2012105264810 A CN 2012105264810A CN 201210526481 A CN201210526481 A CN 201210526481A CN 102976624 A CN102976624 A CN 102976624A
- Authority
- CN
- China
- Prior art keywords
- glass
- pattern
- plated film
- coated glass
- rete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a pattern coating glass and a preparation method thereof, and belongs to the technical field of glasses. The pattern coating glass is characterized in that coating layers are covered on partial surface of the glass, and patterns formed by the coating layers are arranged as arrays. The preparation method comprises the process routes of cutting, edging, coating colored glaze, coating, tempering and carrying out combined machining. The coating glass has the characteristic that the patterns can be selected at random, so that different demands can be met; and the coating glass can be used in a form of single glass and also can be processed into hollow sandwich composite glasses. LOW-E coating can be carried out based on pattern coating, thus the low radiation performance is brought to the glass as well as higher metal gloss, and the requirement on appearance in special environments is met.
Description
Technical field
The invention belongs to the glass technology field, particularly a kind of pattern coated glass and preparation method thereof.
Background technology
Coated glass (Reflective glass) also claim reflecting glass.Coated glass is at one or more layers metal of glass surface coating, alloy or metal compound film, to change the optical property of glass, satisfies certain particular requirement.
Coated glass is along with the development of vacuum magnetic-control sputtering, the lifting of low emissivity glass performance has reduced the heat transfer loss that glass causes because of thermal radiation, improved the heat insulating ability of glass port, cooperate double glazing to use, can the isolation glass conduction, convection current, three kinds of heat transfer paths of radiation, be a kind of energy saving environmental protection product that has very much practical value, application market is very extensive.But the coating technique that adopts at present can only be finished the justifying plated film, and the glass space of a whole page can only keep solid colour.Can not satisfying the market growing for the both artistic and practical diversified requirement of glass.
Summary of the invention
Be directed to high-end customer for the particular requirement of glass aesthetic property for high-quality coated glass product can be provided, improve the use range of coated glass.The invention provides a kind of coated glass and preparation method thereof.
Pattern coated glass provided by the invention is characterized in that: the part covers the plated film rete on glass surface, and is arranged with array way by the pattern that the plated film rete forms.
In the above-mentioned coated glass, have the arbitrary graphic pattern selectivity characteristic, for example: pattern is circular, rectangle, trilateral, the shape such as trapezoidal.
Described plated film rete is anti-oxidant rete, is nitride, the silicon nitride of metal, NI-G such as material, the composite film of zinc oxide, aluminum oxide, silver-colored NI-G nitride etc.
Described coated glass can be single-glass, composite intermediate layer glass or double glazing.
The present invention gives the preparation method of above-mentioned pattern coated glass, adopts following process program finishing patterns plated film.
According to the figure of product, carry out half tone and make.Glass carries out first the colored glaze printing after cutting the edging processing, uses glaze to be the organism glaze, then carries out glass coating, can require arrange the plated film trade mark according to color.Can only process anti-oxidant rete, carry out tempering after finishing, utilize annealing furnace high temperature to make organic glaze perfect combustion, keep the plated film rete, form pattern.Also can on pattern plated film basis, carry out again LOW-E processing, make glass possess low radiance.This product can be used for the processing of various compound glasses to be used.
Operational path is: cutting-edging-colored glaze-plated film-tempering-Compound Machining.
In the aforesaid method, preferably use organic glaze of black, the organic glaze endothermic effect of black is better, helps perfect combustion when being heated.
Beneficial effect of the present invention is:
Coated glass provided by the invention has following characteristic:
1, has the arbitrary graphic pattern selectivity characteristic.Applicable to various different demands.
2, can use with single product glass form, also can be processed as the compound glasses such as hollow sandwich.
3, carry out the LOW-E plated film on the pattern plated film basis again, make glass have low radiance.
4, better metalluster is arranged, satisfy the appearance requirement under the particular surroundings.
5, coated glass provided by the invention, the Application Areas of the coated glass of expansion.
Description of drawings
Fig. 1 is single-glass pattern plated film finished product schematic perspective view;
Fig. 2 is single-glass pattern plated film finished product front view;
Fig. 3 is pattern coated hollow finished product schematic perspective view;
Fig. 4 is pattern coated hollow finished product side-view;
Fig. 5 is pattern plated film composite finished product schematic perspective view.
Fig. 6 is pattern plated film composite finished product side-view.
Number in the figure: 1-pattern plated film rete.
Embodiment
The following examples can make those skilled in the art more fully understand the present invention, but do not limit the present invention in any way.
A kind of pattern coated glass, the part covers the plated film rete on glass surface, and is arranged with array way by the pattern that the plated film rete forms.
Described pattern is circular, as shown in Figure 1.
Described plated film rete is anti-oxidant rete, and material is SnO
2Or SiN
X
Described coated glass is single-glass (as shown in Figure 1, 2), composite intermediate layer glass (shown in Fig. 5,6) or double glazing (shown in Fig. 3,4).
The specific embodiments of this invention is as follows:
1. according to figure and glass size, desired pattern is made the required half tone of silk screen printing.Organic glaze (glaze item number RAL5010) of buying black, the organic glaze endothermic effect of black is better, helps perfect combustion when being heated.
2. glass is carried out processing treatment, change and be cut to the needed size shape of engineering.
3. finishing polish can be done by limit section, and corase grind or chamfered edge are processed.
4. use preprepared silk screen, use the organic glaze of black to carry out silk screen printing.Print out the pattern of drawing requirement.Dry after finishing printing.Use cork mat(t) to isolate, do not touch the position that needs plated film, prevent that backing from polluting glass surface, cause the plated film decrease in yield.
5. must not adopt the acid-basicity scavenging solution that glass is cleaned at filming process.Prevent from corroding organic glaze.Carry out plated film processing after the cleaning.Select oxidation-resistance rete (SnO
2Or SiN
X), monolithic uses behind the plated film.Also can select low radiation LOW-E rete to cooperate hollow product to use.
6. after plated film is finished, use cork mat(t) as backing, liner is on glass colored glaze position.Then be transported to the tempering operation and carry out tempering processing.Utilize the organic glaze of tempering high-temp combustion, obtain at last the plated film pattern.
7. after pattern coated glass tempering is finished, can cooperate hollow sandwich etc. to be made as the compound glass of high configuration.
After using the pattern plated film to carry out the Compound Machining of double glazing, the LOW-E rete of thermodynamical coordinate and its collocation is complementary.Concrete thermodynamical coordinate need to be take actual measurement as main.
The above; only for the better embodiment of the present invention, but protection scope of the present invention is not limited to this, anyly is familiar with those skilled in the art in the technical scope that the present invention discloses; the variation that can expect easily or replacement all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain of claim.
Claims (9)
1. pattern coated glass is characterized in that: locally on glass surface cover the plated film rete, and arranged with array way by the pattern that the plated film rete forms.
2. pattern coated glass according to claim 1 is characterized in that: described pattern is circular, rectangle, trilateral or trapezoidal.
3. pattern coated glass according to claim 1, it is characterized in that: described plated film rete is anti-oxidant rete.
4. pattern coated glass according to claim 3 is characterized in that: the composite film of nitride, silicon nitride, zinc oxide, aluminum oxide or silver-colored NI-G nitride that described plated film rete material is metal, NI-G.
5. pattern coated glass according to claim 1, it is characterized in that: described pattern coated glass is single-glass, composite intermediate layer glass or double glazing.
6. the preparation method of the described pattern coated glass of any one claim of claim 1 to 5, it is characterized in that: according to the figure of product, carry out half tone and make, after glass cuts the edging processing, carry out first the colored glaze printing, use glaze to be the organism glaze, then carry out glass coating, the anti-oxidant rete of plating, carry out tempering after finishing, utilize annealing furnace high temperature to make organic glaze perfect combustion, keep the plated film rete, form pattern.
7. method according to claim 6 is characterized in that: the organic glaze that uses black.
8. method according to claim 6 is characterized in that: carry out LOW-E processing again on pattern plated film basis, make glass possess low radiance.
9. method according to claim 6, it is characterized in that: the pattern coated glass by gained is made various compound glasses.