CN102817150A - Large chemical-fiber polyester-cotton ring-spun abrasive-belt base cloth - Google Patents
Large chemical-fiber polyester-cotton ring-spun abrasive-belt base cloth Download PDFInfo
- Publication number
- CN102817150A CN102817150A CN2012102913833A CN201210291383A CN102817150A CN 102817150 A CN102817150 A CN 102817150A CN 2012102913833 A CN2012102913833 A CN 2012102913833A CN 201210291383 A CN201210291383 A CN 201210291383A CN 102817150 A CN102817150 A CN 102817150A
- Authority
- CN
- China
- Prior art keywords
- chemical fibre
- big chemical
- base cloth
- fibre polyester
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a piece of large chemical-fiber polyester-cotton ring-spun abrasive=belt base cloth, which comprises a plurality of large chemical-fiber polyester-cotton fiber warp yarns, wherein the large chemical-fiber polyester-cotton fiber warp yarns are interwoven with a plurality of large chemical-fiber polyester-cotton weft yarns, the large chemical-fiber polyester-cotton warp yarns are interwoven with the large chemical-fiber polyester-cotton weft yarns to form twill weave, and the twill weave is formed by two upper twill and one lower twill; and the density of the base cloth in the warp direction is 83 to 108 yarns per 10cm, and the density of the base cloth in the weft direction is 45 to 58 yarns per 10cm. The large chemical-fiber polyester-cotton ring-spun abrasive-belt base cloth is few in impurities, little in hairiness, uniform in strength, flat in surface and good in viscosity; and three channels of composite drawing is adopted, so that the yarns and the cloth are reasonable in proportion, and the strength is uniform.
Description
[technical field]
The weaving technology field that the present invention relates to spin particularly relates to a kind of big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth.
[background technology]
Scientific and technical innovation, autonomous innovation is fabricated onto China from China and creates, and is the most important thing in the economic work during 12, and scientific and technical innovation, autonomous innovation at first will be carried out intellectual property protection, and protection of Intellectual Property Rights, unique channel are applied for national international monopoly exactly.
Coated abrasive tool, this industry before more than ten years for strange vocabulary of general Chinese Lai Shuoshi; Even the past, there was this respect product demand in some units; Also to rely on import; Because the at that time few of top-grade furniture of common people and the high-grade automobile of China, let alone high standard, high request and high bright and clean luxury goods.Through our industry people unremitting effort during the last ten years, grow out of nothing and expand from small to large, from having to excellent, uninterruptedly researches and develops new product together, not only satisfy domestic demand now, and 20% products export arrives some developed countries in addition, for country strives foreign exchange and honor.Particularly during the 11th Five-Year and after getting into 12.Can use high speed development, swift and violent expansion is represented.
Improving constantly of Along with people's living standard; With people the live closely bound up various service for life articles for use and the various products of all trades and professions, little inside and outside surface finally all needs grinding, cutting and polishing from each parts to entire equipment to train, automobile, aircraft, artillery, guided missile, rocket, artificial satellite, airship, warship, aircraft carrier etc. greatly to family expenses soup ladle, chopsticks.Metal material as; Gold, silver, copper, iron, tin, aluminium, lead etc., alloy material as; Steel alloys such as manganese, nickel, chromium, cobalt, tungsten, nonmetallic materials as; Furniture, wall, leather, glass, stone material, timber, diamond, jewel, diamond, crystal product, oily seven goods or the like all need just can reach accuracy and fineness standard after grinding, cutting and the polishing; And for example each parts is in contact with one another face; Without high-precision grinding, cutting and polishing; Be the accuracy that can't reach desirable, otherwise be not gas leakage, to leak be exactly leakage of oil, can't guarantee normally using and running well of machinery.And cut, grinding, polishing; Understand fully that at first what requirement is the workpiece material that needs to cut, grind, polish have and then select the abrasive band of corresponding cutting, grinding, polishing material, specification, institutional framework and standard to suit the remedy to the case according to the flintiness of material, standard-required; Carry out processed, could realize expected effect and QUALITY STANDARD.
Decision abrasive band quality and standard depend primarily on the technology manufacturing in abrasive band base material and abrasive band.And the base material in abrasive band generally is made up of four major parts, and promptly matrix, binding agent, abrasive material (sand grains) and structure are formed.In the manufacture process in abrasive band, base cloth is one of crucial base material, and its thickness, thin and thick, tearing power, density, intensity, flatness be decisive role all; Base cloth is the foundation in abrasive band, is the supporting body of abrasive band adhesive and abrasive material, also is the supporter in grinding, cutting, the polishing process; Therefore must possess certain TENSILE STRENGTH; Well scratch resistance, less retractility, its performance guarantee the important preceding topic of abrasive band grinding tool quality.
Big chemical fibre: Chemical Fiber is to spin or the staple fibre of fused mass directly spinning with the PET section, and its characteristics do, color and luster is good, and lot number is big, and powerful stable, fault is few, good spinnability." big chemical fibre " general larger chemical fiber factory is with cut into slices the preferably fiber of Direct Production of quality, and technology is more advanced, and mostly equipment is import, and product quality indicator is more satisfactory, and stable, and spinning property is than higher." big chemical fibre " product refers to superior relatively import and homemade production equipment, adopts polyester fondant direct fabrics method or polyester slice indirect spinning method and the polyester staple fiber that spins out.Because the raw material that " big chemical fibre " product uses all is qualified grade article basically, thereby each item quality index of its regular product is superior." big chemical fibre " polyester staple fiber is the leading raw material of cotton spinning industry." big chemical fibre " production equipment is an equipment of eating " flour and rice ".Big chemical fibre is that oil is a raw material, is regardless of lot number, and the terylene chemical fibre of producing with appearance Zheng chemical fibre factory is big chemical fibre.Polyester-cotton blend is meant the general designation of terylene and cotton BLENDED FABRIC, and the textiles that adopts the cotton mixed yarn of 65-67% terylene and 33%-35% to be made into is commonly called as cotton dacron terylene.Polyester-cotton blend had not only been given prominence to the style of terylene but also the strong point of COTTON FABRIC had been arranged, do, elasticity and ABRASION RESISTANCE are all better under the wet situation, dimensionally stable, washing shrinkage is little, have tall and straight, be difficult for fold, be prone to the characteristics of washing, doing soon, can not use the immersion of hot iron and boiling water.
According to the characteristic of big chemical fibre polyester fiber, big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth should have free from admixture, steady quality, shrinkage factor is little, filoplume is few, bar is done advantages such as even, that cloth cover is smooth, cohesiveness is strong.But, do not see the announcement of Related product and production Technology both at home and abroad as yet.
[summary of the invention]
One of them technical problem to be solved by this invention provides the big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth that a kind of impurity is few, filoplume is few, brute force is even, cloth cover is smooth, cohesive is good.
A kind of big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth, it comprises:
A plurality of big chemical fibre polyester fiber warp thread, said a plurality of big chemical fibre polyester fiber warp thread and a plurality of big chemical fibre polyester fiber weft yarns interweave,
Said big chemical fibre polyester fiber warp thread and said big chemical fibre polyester fiber weft yarn are woven into twill-weave,
Said twill-weave is twill once on two;
Its warp-wise density is 83-108/10cm, 45-58/10cm of latitudinal density.
As a kind of preferred version of big chemical fibre polyester-cotton blend RING SPINNING according to the invention abrasive band base cloth, wherein said big chemical fibre polyester fiber warp thread and said big chemical fibre polyester fiber weft yarn are woven into the angle that interweaves of certain angle.
As a kind of preferred version of big chemical fibre polyester-cotton blend RING SPINNING according to the invention abrasive band base cloth, the angle that interweaves of wherein said certain angle is 30 °～60 °.
A kind of preferred version as big chemical fibre polyester-cotton blend RING SPINNING according to the invention abrasive band base cloth; Wherein said big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth; Said big chemical fibre polyester fiber warp thread and said big chemical fibre polyester fiber weft yarn are woven into twill-weave, and said twill-weave is florentine drill.
The big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth that the present invention adopts big chemical fibre polyester fiber to carry out processing has the incomparable advantage of other types base cloth: impurity is few, filoplume is few, brute force is even, cloth cover is smooth, cohesive is good, and it adopts the compound drafting in three roads to make yarn, cloth reasonable mixture ratio, evenly powerful.This invention is applied widely, is metal material, alloy material, hard alloy material, the grinding of high-grade stone product, cutting, the desirable selection of polishing.The present invention has filled up domestic and international blank, has solved the U.S. and European Union's high-tech product and such base cloth product restricted problem to China's outlet, has effectively improved high-end product occupation rate of market and international competitiveness at home.
[description of drawings]
Fig. 1 be big chemical fibre polyester-cotton blend RING SPINNING according to the invention abrasive band base cloth two on once the twill base cloth organize sketch map.
Fig. 2 be big chemical fibre polyester-cotton blend RING SPINNING according to the invention abrasive band base cloth two on the cross-sectional view of twill base cloth once.
[specific embodiment]
Below in conjunction with concrete embodiment production method according to the invention is elaborated.
Like Fig. 1～shown in Figure 2, among the figure, 1, warp thread; 1a, through interlacing point; 2, weft yarn; 3, the angle that interweaves.
Alleged here " embodiment " or " embodiment " are meant special characteristic, structure or the characteristic that can be contained at least one implementation of the present invention.Different in this manual local " in one embodiment " that occur not are all to refer to same embodiment, neither be independent or optionally mutually exclusive with other embodiment embodiment.
As shown in Figure 1, Fig. 1 for big chemical fibre polyester-cotton blend RING SPINNING according to the invention abrasive band base cloth two on once the twill base cloth organize sketch map.In this embodiment; This big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth comprises a plurality of big chemical fibre polyester fiber warp thread 1; Said a plurality of big chemical fibre polyester fiber warp thread 1 interweave with a plurality of big chemical fibre polyester fiber weft yarns 2; Said big chemical fibre polyester fiber warp thread 1 is woven into twill-weave with said big chemical fibre polyester fiber weft yarn 2, when big chemical fibre polyester fiber warp thread 1 is on big chemical fiber weft yarn 2, is through interlacing point 1a, and this twill-weave is twill once on two; Its warp-wise density is 83-108/10cm, 45-58/10cm of latitudinal density.
As shown in Figure 2, Fig. 2 is the cross-sectional view of big chemical fibre polyester-cotton blend RING SPINNING according to the invention abrasive band base cloth.In this embodiment, big chemical fibre polyester fiber warp thread 1 and said big chemical fibre polyester fiber weft yarn 2 are woven on two twill-weave once, and big chemical fibre polyester fiber warp thread 1 and said big chemical fibre polyester fiber weft yarn 2 are woven into the angle 3 that interweaves of certain angle.
Preferably, big chemical fibre polyester fiber warp thread 1 and said big chemical fibre polyester fiber weft yarn 2 are woven into 30 °～60 ° the angle 3 that interweaves.
In another embodiment, said big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth, said big chemical fibre polyester fiber warp thread and said big chemical fibre polyester fiber weft yarn are woven into twill-weave, and said twill-weave is florentine drill.
Method for simplifying flow process in its actual production is: the cotton vanning, and----------------------------------------weave cotton cloth--checking and accepting packing--supplies to make the production abrasive band to sizing to warping to spun yarn to rove to drafting three to drafting two to drafting one to blowing to blowing to go up axle to wear palm fibre in the winder packing in comb and parallel cotton fibers prior to spinning in comb and parallel cotton fibers prior to spinning+big chemical fibre terylene short fiber vanning.
The main specifications of the big chemical fibre polyester-cotton blend of this kind RING SPINNING abrasive band base cloth is in the actual production:
Wherein, T is big: the standard polyster fibre, C: cotton 80/20 promptly contains washs 80% to contain cotton 20% big chemical fibre is that oil is a raw material, is regardless of lot number, with the terylene chemical fibre of appearance Zheng chemical fibre factory production big chemical fibre.Utilize the prepared big chemical fibre polyester-cotton blend RING SPINNING of this production method abrasive band base cloth to have the incomparable advantage of other types base cloth: impurity is few, filoplume is few, brute force is even, cloth cover is smooth, cohesive is good, and it adopts the compound drafting in three roads to make yarn, cloth reasonable mixture ratio, evenly powerful.This invention is applied widely, is metal material, alloy material, hard alloy material, the grinding of high-grade stone product, cutting, the desirable selection of polishing.The present invention has filled up domestic and international blank, has solved the U.S. and European Union's high-tech product and such base cloth product restricted problem to China's outlet, has effectively improved high-end product occupation rate of market and international competitiveness at home.
What should explain is; Above embodiment is only unrestricted in order to technical scheme of the present invention to be described; Although with reference to preferred embodiment the present invention is specified, those of ordinary skill in the art should be appreciated that and can make amendment or be equal to replacement technical scheme of the present invention; And not breaking away from the spirit and the scope of technical scheme of the present invention, it all should be encompassed in the middle of the claim scope of the present invention.
Claims (4)
1. one kind big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth; It is characterized in that: said big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth comprises: a plurality of big chemical fibre polyester fiber warp thread; Said a plurality of big chemical fibre polyester fiber warp thread and a plurality of big chemical fibre polyester fiber weft yarns interweave; Said big chemical fibre polyester fiber warp thread and said big chemical fibre polyester fiber weft yarn are woven into twill-weave, and said twill-weave is twill once on two; Its warp-wise density is 83-108/10cm, 45-58/10cm of latitudinal density.
2. big chemical fibre polyester-cotton blend RING SPINNING as claimed in claim 1 abrasive band base cloth is characterized in that: said big chemical fibre polyester fiber warp thread and said big chemical fibre polyester fiber weft yarn are woven into the angle that interweaves of certain angle.
3. big chemical fibre polyester-cotton blend RING SPINNING as claimed in claim 2 abrasive band base cloth, it is characterized in that: the angle that interweaves of said certain angle is 30 °～60 °.
4. big chemical fibre polyester-cotton blend RING SPINNING as claimed in claim 1 abrasive band base cloth; It is characterized in that: said big chemical fibre polyester-cotton blend RING SPINNING abrasive band base cloth; Said big chemical fibre polyester fiber warp thread and said big chemical fibre polyester fiber weft yarn are woven into twill-weave, and said twill-weave is florentine drill.