CN102675994A - Thermal insulation waterproof building coating for wear resistant cement roof - Google Patents
Thermal insulation waterproof building coating for wear resistant cement roof Download PDFInfo
- Publication number
- CN102675994A CN102675994A CN2012101638735A CN201210163873A CN102675994A CN 102675994 A CN102675994 A CN 102675994A CN 2012101638735 A CN2012101638735 A CN 2012101638735A CN 201210163873 A CN201210163873 A CN 201210163873A CN 102675994 A CN102675994 A CN 102675994A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- mass
- wear
- cement roof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a thermal insulation waterproof building coating for a wear resistant cement roof. The thermal insulation waterproof building coating comprises 20-30 parts by mass of styrene-acrylic emulsion, 20-30 parts by mass of EVA (ethylene vinyl acetate) resin, 3-10 parts by mass of coating dispersing agent, 5-10 parts by mass of glycol, 0.5-1 part by mass of defoaming agent, 10-20 parts by mass of pigment, 20-30 parts by mass of low-conducting-coefficient filling, 20-30 parts by mass of wear resistant filling, 4-8 parts by mass of white carbon black and 10-15 parts by mass of water. The thermal insulation waterproof building coating for the wear resistant cement roof has excellent wear resistance and can meet using requirements of the thermal insulation waterproof coating for the cement roof, and the problem that the service life of the coating is influenced due to poor wear resistance of the common thermal insulation waterproof coating for the cement roof is solved, the coating has no heavy metals and formaldehyde, and is beneficial to body health. The coating has strong adhesion, and after the cotating is applied, phenomenon such as crack, stripping, sheet falling or efflorescence does not exist, and the coating is suitable for a concrete surface, an asphalt surface, a plastic surface, a glass steel surface and a metal surface, and has wide application range.
Description
Technical field
The invention belongs to the trade sales coating field, be specifically related to a kind of wear-resistant type cement roof insulating water-proof trade sales coating.
Background technology
Solar radiation can cause the rising of buildings room temp, when weather is hot, for keeping indoor feeling nice and cool, needs to consume a large amount of energy.At present, it is relatively poor that cement roof is used more its wear resistance of reflective heat-insulation paint, and it is not strong because of the wear resistance index often to utilize cement roof to carry out the ground finishing coat of activity (like airing clothes, airing grain) at needs, and causes the coating life-span to shorten greatly.
Summary of the invention
The purpose of this invention is to provide a kind of novel wear-resistant type cement roof insulating water-proof trade sales coating.
The technical scheme that the present invention adopted is:
A kind of wear-resistant type cement roof insulating water-proof trade sales coating comprises benzene emulsion 20～30 weight parts, EVA resin 20～30 weight parts, coating dispersant 3～10 weight parts, terepthaloyl moietie 5～10 weight parts, skimmer 0.5～1 weight part, pigment 10～20 weight parts, low thermal conductivity filler 20～30 weight parts, 20～30 parts of wear resistant fillers, WHITE CARBON BLACK 4～8 weight parts, water 10～15 weight parts.
Said coating dispersant is water-borne coatings dispersion agent
.
Said skimmer is silicone antifoam agent
.
Said pigment is at least a in rutile titanium white powder, the ceramics powder.
Said low thermal conductivity filler is at least a in zeyssatite, clay, process white, the calcium silicate powder.
Said wear resistant filler is at least a in carborundum powder, wollastonite powder, the marble dust.
Said WHITE CARBON BLACK is a gas-phase silica.
Beneficial effect of the present invention is:
(1) wear-resistant type cement roof insulating water-proof trade sales coating of the present invention; Good heat-insulation effect can completely cut off nearly 95% heat from sunlight, can make the roof surface temperature reduce by 15～25 ℃; The room temp reduction reaches 5～10 ℃; In the summer of sweltering heat, can significantly reduce the cooling energy consumption of building, energy-conserving and environment-protective;
(2) wear-resistant type cement roof insulating water-proof trade sales coating of the present invention; Strong adhesion, after the construction, coating does not have crackle, peels off, falls sheet or powder phenomenon-tion appearance; Be applicable to concrete surface, bituminous sheaths, plastic cover, glass steel surface, metal covering, widely applicable.Can adopt spraying, brushing, the multiple mode of roller coating to construct easy construction;
(3) durability of coating is extremely strong, the Ginkgo Biloba Leaf Extract effect is good, and surperficial oleophobic is hydrophobic, can effectively prevent the water droplet seepage; Resistance of rainwater washing against, good water-proof effect, coating life reaches 10 years; Significantly reduced maintenance cost, can also play the certain protection effect, prolonged the work-ing life of building building;
(4) much more more wear-resistant type cement roof heat-insulating waterproof coating high abrasion resistance of the present invention can satisfy the request for utilizations of cement roof heat-insulating waterproof coating, has solved general cement roof thermal insulating coating influences its coating because of wear resistance is bad work-ing life.And do not contain heavy metal in the coating, do not contain formaldehyde yet, more help HUMAN HEALTH.
Embodiment
Below in conjunction with embodiment the present invention is further described, but is not limited thereto.
Used coating dispersant is the water-borne coatings dispersant with high efficiency 5040 of Beijing Mayor Chemical Technology Co., Ltd. in following examples; Used skimmer is the high-efficient and lasting type skimmer GRS HY-1040 of Beijing Mayor Chemical Technology Co., Ltd..
Embodiment 1
A kind of wear-resistant type cement roof insulating water-proof trade sales coating, in weight part, it is filled a prescription as follows:
20 parts of benzene emulsions, 20 parts of EVA resins, 3 parts of coating dispersants, 5 parts of terepthaloyl moietie, 0.5 part of skimmer, 10 parts in rutile titanium white powder, 20 parts of wollastonite powder, carborundum powder 2,10 parts in zeyssatite, 5 parts of clays, 5 parts of process whites, 4 parts of gas-phase silicas, 10 parts in water.
Embodiment 2
A kind of wear-resistant type cement roof insulating water-proof trade sales coating, in weight part, it is filled a prescription as follows:
25 parts of benzene emulsions, 20 parts of EVA resins, 4 parts of coating dispersants, 6 parts of terepthaloyl moietie, 0.6 part of skimmer, 12 parts in rutile titanium white powder, 20 parts of marble dusts, 20 parts in zeyssatite, 3 parts of clays, 3 parts of carborundum powders, 7 parts of gas-phase silicas, water 15 weight parts.
Embodiment 3
A kind of wear-resistant type cement roof insulating water-proof trade sales coating, in weight part, it is filled a prescription as follows:
20 parts of benzene emulsions, 25 parts of EVA resins, 3.5 parts of coating dispersants, 7 parts of terepthaloyl moietie, 0.7 part of skimmer, 15 parts of ceramics powders, 20 parts of wollastonite powder, 25 parts in zeyssatite, 2 parts of clays, 1.5 parts of carborundum powders, 5 parts of gas-phase silicas, 15 parts in water.
Embodiment 4
A kind of wear-resistant type cement roof insulating water-proof trade sales coating, in weight part, it is filled a prescription as follows:
30 parts of benzene emulsions, 20 parts of EVA resins, 5 parts of coating dispersants, 5 parts of terepthaloyl moietie, 0.9 part of skimmer, 14 parts in rutile titanium white powder, 25 parts of marble dusts, 5 parts of clays, 1 part of carborundum powder, 20 parts of calcium silicate powders, 8 parts of gas-phase silicas, 15 parts in water.
Embodiment 5
A kind of wear-resistant type cement roof insulating water-proof trade sales coating, in weight part, it is filled a prescription as follows:
25 parts of benzene emulsions, 30 parts of EVA resins, 6 parts of coating dispersants, 10 parts of terepthaloyl moietie, 1 part of skimmer, 15 parts in rutile titanium white powder, 18 parts of wollastonite powder, 2 parts of carborundum powders, 10 parts in zeyssatite, 10 parts of clays, 5 parts of process whites, 5 parts of calcium silicate powders, 6 parts of gas-phase silicas, 15 parts in water.
Embodiment 6
A kind of wear-resistant type cement roof insulating water-proof trade sales coating, in weight part, it is filled a prescription as follows:
30 parts of benzene emulsions, 25 parts of EVA resins, 10 parts of coating dispersants, 8 parts of terepthaloyl moietie, 1 part of skimmer, 10 parts in rutile titanium white powder, 10 parts of ceramics powders, 15 parts of wollastonite powder, 15 parts of marble dusts, 10 parts of process whites, 15 parts of calcium silicate powders, 4 parts of gas-phase silicas, 15 parts in water.
The preparation method of embodiment 1～6 said coating:
1) water (preferably using deionized water) and dispersion agent, skimmer, WHITE CARBON BLACK are mixed, and carries out stirring at low speed;
2) carry out high speed dispersion behind the adding color stuffing, grind in case of necessity and process mill base;
3) join mill base in the mixed emulsion of benzene emulsion, EVA resin and terepthaloyl moietie at a slow speed in batches; Batch mill base that adds continues to add after stirring at low speed is even again before treating; Stirring at low speed evenly obtains coating; Be that wear-resistant type cement roof insulating water-proof trade sales coating is painted article, through filtration, weighing, packing, just can put in storage or list marketing after the assay was approved.
The wear-resistant type cement roof insulating water-proof trade sales coating that embodiment 1～6 is made carries out performance test, and the result is as shown in the table.The assay of institute's Interventions Requested (1-15 item) meets the technical requirement of exterior wall class in the JG/T172-2005 standard; The assay of sunshine reflectivity, hemispherical emissivity meets the technical requirement of JG/T235-2008.
The present invention comprises the rutile titanium white powder of zeyssatite, clay, process white, calcium silicate powder and high reflection good weatherability with the low thermal conductivity filler and wear resistance is heat insulation, the carborundum powder of fine heat radiation property, wollastonite powder, marble dust, develops a kind of wear-resistant type cement roof heat-insulating waterproof coating.Wear-resistant type cement roof heat-insulating waterproof coating high abrasion resistance of the present invention; Can much more more to satisfy the request for utilizations of cement roof heat-insulating waterproof coating; Solve general cement roof thermal insulating coating and influenced its coating problem in work-ing life because of wear resistance is bad; And do not contain heavy metal in the coating, do not contain formaldehyde yet, more help HUMAN HEALTH.In addition, this ADHESION OF PAINTS power is strong, and after the construction, coating does not have crackle, peels off, falls sheet or powder phenomenon-tion appearance, is applicable to concrete surface, bituminous sheaths, plastic cover, glass steel surface, metal covering, and is widely applicable.Can adopt spraying, brushing, the multiple mode of roller coating to construct easy construction.
Claims (7)
1. a wear-resistant type cement roof insulating water-proof trade sales coating comprises benzene emulsion 20～30 weight parts, EVA resin 20～30 weight parts, coating dispersant 3～10 weight parts, terepthaloyl moietie 5～10 weight parts, skimmer 0.5～1 weight part, pigment 10～20 weight parts, low thermal conductivity filler 20～30 weight parts, 20～30 parts of wear resistant fillers, WHITE CARBON BLACK 4～8 weight parts, water 10～15 weight parts.
2. wear-resistant type cement roof insulating water-proof trade sales coating according to claim 1 is characterized in that, said coating dispersant is water-borne coatings dispersion agent
.
3. wear-resistant type cement roof insulating water-proof trade sales coating according to claim 1 is characterized in that, said skimmer is silicone antifoam agent
.
4. colorful insulating water-proof trade sales coating according to claim 1 is characterized in that, said pigment is at least a in rutile titanium white powder, the ceramics powder.
5. wear-resistant type cement roof insulating water-proof trade sales coating according to claim 1 is characterized in that, said low thermal conductivity filler is at least a in zeyssatite, clay, process white, the calcium silicate powder.
6. wear-resistant type cement roof insulating water-proof trade sales coating according to claim 1 is characterized in that, said wear resistant filler is at least a in carborundum powder, wollastonite powder, the marble dust.
7. wear-resistant type cement roof insulating water-proof trade sales coating according to claim 1 is characterized in that said WHITE CARBON BLACK is a gas-phase silica.