CN102618163A - A kind of UV wear-resistant primer and preparation method thereof - Google Patents
A kind of UV wear-resistant primer and preparation method thereof Download PDFInfo
- Publication number
- CN102618163A CN102618163A CN2012101000796A CN201210100079A CN102618163A CN 102618163 A CN102618163 A CN 102618163A CN 2012101000796 A CN2012101000796 A CN 2012101000796A CN 201210100079 A CN201210100079 A CN 201210100079A CN 102618163 A CN102618163 A CN 102618163A
- Authority
- CN
- China
- Prior art keywords
- wear
- resistant primer
- stirring
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
技术领域 technical field
本发明涉及一种UV耐磨底漆，本发明还涉及一种制备该UV耐磨底漆的方法。The invention relates to a UV wear-resistant primer, and also relates to a method for preparing the UV wear-resistant primer.
背景技术 Background technique
现有用于木地板表面上的油漆很多不够耐磨以及硬度不够，导致木地板在铺装之后，踩在上面很容易把涂料磨穿，影响了整体的美感；为了可克服这个问题，有的把油漆的涂布量放大来增加耐磨和硬度，这样会导致整体成本增加。还有的是向油漆中添加一些硬质的粉体，但这种做法往往会导致涂装后板面模糊不清晰。Many of the existing paints used on the surface of wooden floors are not wear-resistant and hard enough, which leads to the fact that after the wooden floor is paved, it is easy to wear the paint when stepping on it, which affects the overall aesthetic feeling; in order to overcome this problem, some The amount of paint applied is enlarged to increase wear resistance and hardness, which will lead to an increase in overall cost. There is also adding some hard powder to the paint, but this approach often leads to blurred board surface after painting.
本发明的耐磨底漆涂装之后增加了耐磨度同时不影响涂装后的整体清晰度。The wear-resistant primer of the present invention increases the wear resistance after painting and does not affect the overall clarity after painting.
发明内容 Contents of the invention
本发明的目的是为了克服现有技术中的不足之处，提供一种用于木地板的耐磨、硬度高，涂装后清晰度好的UV耐磨底漆。The purpose of the present invention is to overcome the deficiencies in the prior art, and provide a UV wear-resistant primer for wooden floors with high hardness and good clarity after painting.
本发明的另一个目的是提供一种制备上述UV耐磨底漆的方法。Another object of the present invention is to provide a method for preparing the above UV wear-resistant primer.
为了达到上述目的，本发明采用以下方案：In order to achieve the above object, the present invention adopts the following scheme:
一种UV耐磨底漆，其特征在于按重量份由以下组分组成：A UV wear-resistant primer is characterized in that it is made up of the following components by weight:
如上所述的一种UV耐磨底漆，其特征在于按重量份由以下组分组成：A kind of UV wear-resistant primer as above is characterized in that it is made up of the following components by weight:
如上所述的一种UV耐磨底漆，其特征在于按重量份由以下组分组成：A kind of UV wear-resistant primer as above is characterized in that it is made up of the following components by weight:
如上所述的一种UV耐磨底漆，其特征在于所述的聚氨酯丙烯酸酯为脂肪族聚氨酯六丙烯酸酯。A kind of UV wear-resistant primer as described above, is characterized in that described urethane acrylate is aliphatic urethane hexaacrylate.
如上所述的一种UV耐磨底漆，其特征在于所述的光引发剂为光引发剂1173。A UV wear-resistant primer as described above is characterized in that the photoinitiator is photoinitiator 1173.
本发明一种制备如上所述的任一种UV耐磨底漆的方法，其特征在于包括以下步骤：The present invention prepares a kind of method for above-mentioned any kind of UV abrasion-resistant primer, it is characterized in that comprising the following steps:
将三丙二醇二丙烯酸酯和三羟甲基丙烷三丙烯酸酯先混合溶解搅拌，再加入光引发剂再搅拌，然后加入聚氨酯丙烯酸酯混合搅拌，再边搅拌边加入气相二氧化硅和三氧化二铝，加入完后搅拌10-20分钟后静止1-2小时用过滤网过滤即得。Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate and stir first, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add fumed silica and aluminum oxide while stirring , Stir for 10-20 minutes after adding, then stand still for 1-2 hours and filter with a filter.
如上所述的制备方法，其特征在于所述过滤网为150目的过滤网。The above-mentioned preparation method is characterized in that the filter screen is a 150-mesh filter screen.
综上所述，本发明的有益效果：In summary, the beneficial effects of the present invention:
本发明产品耐磨性能好，硬度高，涂装在木地板后，木地板的整体清晰度好，配方简单合理。本发明方法工艺简单，加工方便。The product of the invention has good wear resistance and high hardness, and after being coated on the wooden floor, the overall definition of the wooden floor is good, and the formula is simple and reasonable. The method of the invention has simple process and convenient processing.
具体实施方式 Detailed ways
下面结合具体实施方式对本发明做进一步描述：The present invention will be further described below in conjunction with specific embodiment:
实施例1Example 1
本发明UV耐磨底漆，按重量份由以下组分组成：The UV wear-resistant primer of the present invention consists of the following components in parts by weight:
制备方法：按上述配比将三丙二醇二丙烯酸酯和三羟甲基丙烷三丙烯酸酯先混合溶解搅拌，再加入光引发剂再搅拌，然后加入聚氨酯丙烯酸酯混合搅拌，再边搅拌边加入气相二氧化硅和三氧化二铝，加入完后搅拌10分钟后静止1-2小时用150目的过滤网过滤即得。Preparation method: Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate according to the above ratio, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add gas phase two while stirring Silicon oxide and aluminum oxide, after adding, stir for 10 minutes, then stand still for 1-2 hours and filter through a 150-mesh filter.
实施例2Example 2
本发明UV耐磨底漆，按重量份由以下组分组成：The UV wear-resistant primer of the present invention consists of the following components in parts by weight:
制备方法：按上述配比将三丙二醇二丙烯酸酯和三羟甲基丙烷三丙烯酸酯先混合溶解搅拌，再加入光引发剂再搅拌，然后加入聚氨酯丙烯酸酯混合搅拌，再边搅拌边加入气相二氧化硅和三氧化二铝，加入完后搅拌15分钟后静止1-2小时用150目的过滤网过滤即得。Preparation method: Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate according to the above ratio, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add gas phase two while stirring Silicon oxide and aluminum oxide, after adding, stir for 15 minutes, then stand still for 1-2 hours and filter through a 150-mesh filter.
实施例3Example 3
本发明UV耐磨底漆，按重量份由以下组分组成：The UV wear-resistant primer of the present invention consists of the following components in parts by weight:
制备方法：按上述配比将三丙二醇二丙烯酸酯和三羟甲基丙烷三丙烯酸酯先混合溶解搅拌，再加入光引发剂再搅拌，然后加入聚氨酯丙烯酸酯混合搅拌，再边搅拌边加入气相二氧化硅和三氧化二铝，加入完后搅拌10-20分钟后静止1-2小时用150目的过滤网过滤即得。Preparation method: Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate according to the above ratio, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add gas phase two while stirring Silica and Al2O3, after adding, stir for 10-20 minutes, then stand still for 1-2 hours and filter through a 150-mesh filter.
实施例4Example 4
本发明UV耐磨底漆，按重量份由以下组分组成：The UV wear-resistant primer of the present invention consists of the following components in parts by weight:
制备方法：按上述配比将三丙二醇二丙烯酸酯和三羟甲基丙烷三丙烯酸酯先混合溶解搅拌，再加入光引发剂再搅拌，然后加入聚氨酯丙烯酸酯混合搅拌，再边搅拌边加入气相二氧化硅和三氧化二铝，加入完后搅拌10-20分钟后静止1-2小时用150目的过滤网过滤即得。Preparation method: Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate according to the above ratio, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add gas phase two while stirring Silica and Al2O3, after adding, stir for 10-20 minutes, then stand still for 1-2 hours and filter through a 150-mesh filter.
实施例5Example 5
本发明UV耐磨底漆，按重量份由以下组分组成：The UV wear-resistant primer of the present invention consists of the following components in parts by weight:
制备方法：按上述配比将三丙二醇二丙烯酸酯和三羟甲基丙烷三丙烯酸酯先混合溶解搅拌，再加入光引发剂再搅拌，然后加入聚氨酯丙烯酸酯混合搅拌，再边搅拌边加入气相二氧化硅和三氧化二铝，加入完后搅拌20分钟后静止1-2小时用150目的过滤网过滤即得。Preparation method: Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate according to the above ratio, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add gas phase two while stirring Silicon oxide and aluminum oxide, after adding, stir for 20 minutes, then stand still for 1-2 hours and filter with a 150-mesh filter.
本发明实施例1-5中各产品的一些性质见表1：Some properties of each product in the embodiment of the present invention 1-5 are shown in Table 1:
Claims (7)