CN102504653A - 一种贝壳制工艺品涂饰剂的制备方法 - Google Patents
一种贝壳制工艺品涂饰剂的制备方法 Download PDFInfo
- Publication number
- CN102504653A CN102504653A CN2011103111765A CN201110311176A CN102504653A CN 102504653 A CN102504653 A CN 102504653A CN 2011103111765 A CN2011103111765 A CN 2011103111765A CN 201110311176 A CN201110311176 A CN 201110311176A CN 102504653 A CN102504653 A CN 102504653A
- Authority
- CN
- China
- Prior art keywords
- weight parts
- mass parts
- shell
- art products
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种贝壳制工艺品涂饰剂的制备方法，该方法的制备步骤如下：在反应釜中加入30-34质量份聚乙烯蜡、5-7质量份松香、3质量份白蜡和30-40质量份软脂酸，混合搅拌，加热至160℃，加入50-56质量份硬脂酸和1-2质量份油水混合促进剂，继续升温到180℃，在加入140-160质量份90-100℃热水，继续搅拌1h，冷却至室温。本发明方法制备出的产品经工业试验证明，能有效的保护贝壳不因外界的接触而腐蚀褪色或失去光泽。
Description
技术领域
本发明涉及一种贝壳制工艺品涂饰剂的制备方法，属于化工涂料技术领域。
技术背景
贝壳是蛤蚌等有壳动物的外壳。其中有的具有珍珠般的虹彩光泽，因而被用于珠宝业，制作项链、服装珠宝(钮扣等)，甚至安装在首饰上，更多用于制作贝雕、拼贴画、镶嵌刀柄等。在各类贝壳中，以澳大利亚北部托雷斯海峡一带所产的真珠牡蛎(pinctada maxina)、菲律宾的马尼拉贝、缅甸的缅甸贝以及西印度群岛的巨蚌、皇后大蛤等为优。尤其是近两年，珠宝级的贝壳类首饰也开始越来越被我们都市中喜欢帅性自然的人们所特别钟爱。珍珠母贝是天然材料，因此每件的颜色及纹路都十分独特，满足了越来越多消费者对个性化首饰的需求，珍珠母贝饰品的加工非常复杂，原始的珍珠母贝要进行非常细致的打磨、精确的切割，根据设计要求镶嵌。历经多道工艺处理，才能制成令人赏心悦目的贝壳饰品。但是贝壳的主要成分为95%的碳酸钙和少量的壳质素。长时间与外界接触的话，会被腐蚀而褪色或失去光泽，这样贝壳的本身的价值就会丧失，因此贝壳的表层需要涂抹一层防护层。
发明内容
本发明目的是提供一种贝壳制工艺品涂饰剂的制备方法，该方法制备出的涂饰剂能有效的保护贝壳不因外界的接触而腐蚀褪色。
为了达到上述目的，本发明采用一个技术方案是：一种贝壳制工艺品涂饰剂的制备方法，该方法的制备步骤如下：在反应釜中加入30-34质量份聚乙烯蜡、5-7质量份松香、3质量份白蜡和30-40质量份软脂酸，混合搅拌，加热至160℃，加入50-56质量份硬脂酸和1-2质量份油水混合促进剂，继续升温到180℃，在加入140-160质量份90-100℃热水，继续搅拌1h，冷却至室温。
本发明方法制备出的产品经工业试验证明，能有效的保护贝壳不因外界的接触而腐蚀褪色或失去光泽。
具体实施方式
实施例1
一种贝壳制工艺品涂饰剂的制备方法，该方法的制备步骤如下：在反应釜中加入30-34质量份聚乙烯蜡、5-7质量份松香、3质量份白蜡和30-40质量份软脂酸，混合搅拌，加热至160℃，加入50-56质量份硬脂酸和1-2质量份油水混合促进剂，继续升温到180℃，在加入140-160质量份90-100℃热水，继续搅拌1h，冷却至室温。
Claims (1)
1.一种贝壳制工艺品涂饰剂的制备方法，其特征在于该方法的制备步骤如下：在反应釜中加入30-34质量份聚乙烯蜡、5-7质量份松香、3质量份白蜡和30-40质量份软脂酸，混合搅拌，加热至160℃，加入50-56质量份硬脂酸和1-2质量份油水混合促进剂，继续升温到180℃，在加入140-160质量份90-100℃热水，继续搅拌1h，冷却至室温。