CN102399493A - 蠕变型热熔橡胶沥青防水涂料 - Google Patents
蠕变型热熔橡胶沥青防水涂料 Download PDFInfo
- Publication number
- CN102399493A CN102399493A CN2011103312054A CN201110331205A CN102399493A CN 102399493 A CN102399493 A CN 102399493A CN 2011103312054 A CN2011103312054 A CN 2011103312054A CN 201110331205 A CN201110331205 A CN 201110331205A CN 102399493 A CN102399493 A CN 102399493A
- Authority
- CN
- China
- Prior art keywords
- waterproof coating
- rubber asphalt
- asphalt waterproof
- pitch
- hot melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明请求保护一种蠕变型热熔橡胶沥青防水涂料，该涂料固含量高(99％以上)，耐高温性好，低温柔性优异，并具有更好的蠕变性。可单独作为涂膜防水层用，也可与高聚物(SBS或APP)改性沥青防水卷材复合使用，构成二道防水层设防，相类似的产品都采用热塑性弹性体(如星形SBS)及胶粉改性剂对沥青进行改性。本发明采用全新的聚烯烃弹性体改性剂和塑料改性剂复合体系，该产品比现有的非固化沥青涂料，具有更好的蠕变性、粘结强度更高，更好适应立面施工要求。
Description
技术领域
本发明涉及一种沥青基防水涂料，主要用于各种防水工程，可单独防水施工，也可与防水卷材的复合施工。
技术背景
国内改性沥青涂料主要是溶剂型和水乳型改性沥青防水涂料，在使用过程中，存在着不同程度的缺陷，特别是在通风不良的厨卫间和建筑物内使用，一是延长施工作业的周期，二是对作业人员造成健康影响。为了改变这一状况，研发出蠕变型热熔橡胶沥青防水涂料，该涂料固含量高(99％以上)，耐高温性好，低温柔性优异，并具有更好的蠕变性。
蠕变型热熔橡胶沥青防水涂料可单独作为涂膜防水层用，也可与高聚物(SBS或APP)改性沥青防水卷材复合使用，构成二道防水层设防，即一道涂膜层和一道卷材层，在此涂料层兼作卷材的胶粘剂(相当热粘玛碲脂)用。
目前市场是的非固化沥青涂料，固含量高(99％以上)，蠕变性强，可大面积涂覆，可以作为填充密封材料，使用方便等优点，但是它存在缺点是强度太低、在立面施工时容易流淌。
蠕变型热熔橡胶沥青防水涂料与一般改性沥青防水涂料的主要区别在于其良好的蠕变性赋予复合体系自愈合能力和应对基层开裂能力，大大减少了工程维护成本。蠕变型热熔橡胶沥青防水涂料既可用于新建防水层，也可用于修复受损防水层；既可用于常规区域的防水，也可用于变形缝等特殊区域的防水，相对于其它防水材料，它对特殊区域的防水具有独特优势。防水主体产生渗透的要素是水、缝隙和通过缝隙的水的迁移力，防水工程就是采取致密的材料堵塞防水主体的孔和缝，阻止水的通过。因此从工程的角度出发，应该首先封闭基层的裂缝和毛细孔道，使基层具有一定的防水能力；然后再设置具有蠕变功能的粘结层，能将主防水层与基层牢固粘结，并具有很好的蠕变能力来消除或减少各种不利因素对防水层产生的拉伸应力，避免防水层受拉破坏；再在其上设置具有不透水性和耐久性的主防水层；最后加上有效的保护，即形成完整的防水构造层次。这样的设置可以最大程度地减少不利因素对防水层的影响，大大提高防水层的可靠性和使用年限。而且蠕变性的粘结层具有较强的自愈功能，即一旦防水层的某个部位被穿刺破坏，其防水失效区域仅局限于破损部位而不会扩散；同时，蠕变性材料的流变性会促使周边的部分蠕变性材料逐渐向该部位迁移，填补破损部位，使其重新具有防水功能。
发明内容
本发明的目的就是要提供一种蠕变型热熔橡胶沥青防水涂料，该涂料固含量高(99％以上)，耐高温性好，低温柔性优异，并具有更好的蠕变性。可单独作为涂膜防水层用，也可与高聚物(SBS或APP)改性沥青防水卷材复合使用，构成二道防水层设防，相类似的产品都采用热塑性弹性体(如星形SBS)及胶粉改性剂对沥青进行改性。本发明采用全新的聚烯烃弹性体改性剂和塑料改性剂复合体系，该产品比现有的非固化沥青涂料，具有更好的蠕变性、粘结强度更高，更好适应立面施工要求，比CN201010293450.6专利产品有更好的蠕变性。
本发明所涉及的技术方案：
本发明的蠕变型热熔橡胶沥青防水涂料组成为：(按重量计，以下同)
沥青40％-60％，最好50％-55％；
增塑剂15％-25％，最好16％-20％；
聚烯烃弹性体5％-15％，最好8％-12％；
塑料改性剂2％-15％，最好5％-10％；
增粘树脂：1％-10％，最好1％-3％；
填料：10％-30％，最好10％-20％。
其中的沥青可以是天然沥青、石油沥青、煤沥青及其混合物，最好是石油重交通沥青，其针入度为60-100(1/10mm)。
增塑剂是减三线油、芳烃油、环烷油及其混合物，聚烯烃弹性体改性剂是POE，塑料改性剂是乙烯-醋酸乙烯共聚物，增粘树脂是古马隆树脂、萜烯树脂、松香树脂、加氢石油树脂及其混合物。填料是重钙、轻钙、滑石粉及其混合物。
蠕变型热熔橡胶沥青防水涂料生产工艺如下：
a、将沥青加热升温至130-160℃备用；
b、将增塑剂和增粘树脂加入到130-160℃沥青中，低速搅拌20分钟-1小时；
c、温度升高到180-200℃，加入POE和乙烯-醋酸乙烯共聚物，并开启胶体磨，约需搅拌1-2小时，改性剂全部融熔为止；
d、保持温度在160-180℃，加入填料搅拌30-50分钟，至颗粒均匀分散；
e、降温到140-160℃，出料。
本发明的技术效果
本发明提出的蠕变型热熔橡胶沥青防水涂料，该涂料固含量高(99％以上)，耐高温性好，低温柔性优异，并具有更好的蠕变性。
具体实施方式
实施例1给出实施例中原料的生产商
将蠕变型热熔橡胶沥青防水涂料原材料按下述(表1)进行配比(重量比，下同)：
表1蠕变型热熔橡胶沥青防水涂料配方表
蠕变型热熔橡胶沥青防水涂料制造工艺如下：
a、将沥青加热升温至130-160℃备用；
b、将增塑剂和增粘树脂加入到130-160℃沥青中，低速搅拌半小时；
c、温度升高到180-200℃，加入POE和乙烯-醋酸乙烯共聚物，并开启胶体磨，约需搅拌1-2小时，改性剂全部融熔为止；
d、保持温度在160-180℃，加入填料搅拌30-50分钟，至颗粒均匀分散；
e、降温到140-160℃，出料。
实施例2
将蠕变型热熔橡胶沥青防水涂料原材料按下述(表2)进行配比(重量比，下同)：
表2蠕变型热熔橡胶沥青防水涂料配方表
实施例2的蠕变型热熔橡胶沥青防水涂料制造工艺如实施例1。
实施例3
将蠕变型热熔橡胶沥青防水涂料原材料按下述(表3)进行配比(重量比，下同)：
表3蠕变型热熔橡胶沥青防水涂料配方表
实施例3的蠕变型热熔橡胶沥青防水涂料制造工艺如实施例1。
实施例4
将蠕变型热熔橡胶沥青防水涂料原材料按下述(表4)进行配比(重量比，下同)：
表4蠕变型热熔橡胶沥青防水涂料配方表
实施例4的蠕变型热熔橡胶沥青防水涂料制造工艺如实施例1。
表5蠕变型热熔橡胶沥青防水涂料部分性能表
表6蠕变型热熔橡胶沥青防水涂料检测标准及方法
Claims (6)
1.一种蠕变型热熔橡胶沥青防水涂料，以重量百分比计包括如下组分：
沥青 40％-60％；
增塑剂15％-25％；
聚烯烃弹性体5％-15％；
塑料改性剂2％-15％；
增粘树脂：1％-10％；
填料：10％-30％。
2.如权利要求1所述的蠕变型热熔橡胶沥青防水涂料，以重量百分比计包括如下组分：
沥青50％-55％；
增塑剂16％-20％；
聚烯烃弹性体8％-12％；
塑料改性剂5％-10％；
增粘树脂1％-3％；
填料10％-20％。
3.根据权利要求1或2所述的蠕变型热熔橡胶沥青防水涂料，其特征在于：所述的沥青选自天然沥青、石油沥青、煤沥青及其混合物。
4.根据权利要求3所述的蠕变型热熔橡胶沥青防水涂料，其特征在于所述沥青为石油重交通沥青，其针入度为60-100(1/10mm)。
5.根据权利要求1或2所述的蠕变型热熔橡胶沥青防水涂料，其特征在于：增塑剂是减三线油、芳烃油、环烷油及其混合物，聚烯烃弹性体改性剂是POE，塑料改性剂是乙烯-醋酸乙烯共聚物，增粘树脂是古马隆树脂、萜烯树脂、松香树脂、加氢石油树脂及其混合物。填料是重钙、轻钙、滑石粉及其混合物。
6.一种如权利要求1-5所述蠕变型热熔橡胶沥青防水涂料生产工艺，其包括如下步骤如下：
a、将沥青加热升温至130-160℃备用；
b、将增塑剂和增粘树脂加入到130-160℃沥青中，低速搅拌20分钟-1小时；
c、温度升高到180-200℃，加入POE和乙烯-醋酸乙烯共聚物，并开启胶体磨，搅拌1-2小时，改性剂全部融熔为止；
d、保持温度在160-180℃，加入填料搅拌30-50分钟，至颗粒均匀分散；
e、降温到140-160℃，出料。