CN102304298A - 颜料红254的后处理工艺 - Google Patents
颜料红254的后处理工艺 Download PDFInfo
- Publication number
- CN102304298A CN102304298A CN201110167976A CN201110167976A CN102304298A CN 102304298 A CN102304298 A CN 102304298A CN 201110167976 A CN201110167976 A CN 201110167976A CN 201110167976 A CN201110167976 A CN 201110167976A CN 102304298 A CN102304298 A CN 102304298A
- Authority
- CN
- China
- Prior art keywords
- pigment red
- weight
- crude product
- solution
- paratonere
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了颜料红254的后处理工艺，其特征是：包括如下步骤，将颜料红254的粗品加入反应釜中，同时加入质量浓度为95%的有机溶液和质量浓度为30%的NaOH溶液，加入的有机溶液的重量为颜料红254粗品重量的9—11倍，加入的NaOH溶液的重量为颜料红254粗品重量的0.05—0.1倍，升高温度至60—80℃，并搅拌4.5—5.5小时，然后将物料压入压滤机中，用质量浓度大于95%的有机溶剂对物料进行洗涤，加入的有机溶剂的重量为颜料红254重量的1.5—3倍，再用水洗涤，直至滤液的pH值为8，将所得的含固量为40%—45%的滤饼放入普通烘箱进行干燥，即得成品。本发明的优点是：本操作方便，简单易行，工作效率高，做出的产品稳定性更好。
Description
技术领域
本发明涉及颜料红254的后处理工艺，属于化工领域。
背景技术
目前对颜料红254的后处理工艺一般是采用研磨工艺，该工艺能耗较高，而且产能很低，损耗比较大。
发明内容
本发明的目的是：针对上述不足，提供一种操作容易、简单易行、能耗低、效率高的颜料红254的后处理工艺。
为实现上述目的，本发明采用的技术方案是：
颜料红254的后处理工艺，其特征是：包括如下步骤，在常温下将颜料红254的粗品加入反应釜中，同时加入质量浓度为95%的有机溶液和质量浓度为30%的NaOH溶液，加入的有机溶液的重量为颜料红254粗品重量的9—11倍，加入的NaOH溶液的重量为颜料红254粗品重量的0.05—0.1倍，升高温度至60—80℃，并搅拌4.5—5.5小时，然后将物料压入压滤机中，用质量浓度大于95%的有机溶剂对物料进行洗涤，加入的有机溶剂的重量为颜料红254重量的1.5—3倍，有机溶剂使用完后，接着再用水洗涤，直至滤液的PH值为8，将所得的含固量为40%—45%的滤饼放入普通烘箱进行干燥，即得成品。
进一步的，所述的NaOH溶液可以用去离子水代替，去离子水的重量为颜料红254粗品重量的1.5—2.5倍。
进一步的，所述有机溶液为甲醇溶液、乙醇溶液或DMF溶液中的任意一种。
更进一步的，所述有机溶剂为甲醇、乙醇或DMF中的任意一种。
本发明的优点是：本发明颜料红254的后处理工艺，相比于采用研磨工艺对颜料红进行后处理，其操作更为方便，简单易行，工作效率更高，做出的产品稳定性更好。
具体实施方式
以下所有实施例仅是对本发明的进一步说明，但不限定本发明的保护范围。
实施例1
将300重量份的颜料红254的粗品加入反应釜中，同时加入2900重量份浓度为95%的甲醇溶液和20重量份浓度为30%的NaOH溶液，升高温度至65℃，并搅拌4.5小时，然后将物料压入压滤机中，用500重量份的质量浓度大于95%的甲醇洗涤，有机溶剂使用完后，再用水洗涤，直到滤液的PH值为8，然后将700重量份含固量为40%的滤饼放进普通烘箱进行干燥，即得成品。
实施例2
将300重量份的颜料红254的粗品加入反应釜中，同时加入3200重量份浓度为95%的乙醇溶液和20重量份浓度为30%的NaOH溶液，升高温度至75℃，并搅拌5小时，然后将物料压入压滤机中，用500重量份的质量浓度大于95%的甲醇洗涤，有机溶剂使用完后，再用水洗涤，直到滤液的PH值为8，然后将700重量份含固量为42%的滤饼放进普通烘箱进行干燥，即得成品。
实施例3
将300重量份的颜料红254的粗品加入反应釜中，然后，同时加入2950重量份浓度为DMF溶液和500重量份的去离子水，升高温度至回流温度，并搅拌4小时，然后将物料压入压滤机中，用800重量份质量浓度大于95%的DMF洗涤，有机溶剂使用完后，再用水洗涤，直到滤液的PH值为8，然后将700重量份含固量为45%的滤饼放进普通烘箱进行干燥，即得成品。
本发明颜料红254的后处理工艺，相比于采用研磨工艺对颜料红进行后处理，其操作更为方便，简单易行，工作效率更高，做出的产品稳定性更好。
Claims (4)
1.颜料红254的后处理工艺，其特征是：包括如下步骤，在常温下将颜料红254的粗品加入反应釜中，同时加入质量浓度为95%的有机溶液和质量浓度为30%的NaOH溶液，加入的有机溶液的重量为颜料红254粗品重量的9—11倍，加入的NaOH溶液的重量为颜料红254粗品重量的0.05—0.1倍，升高温度至60—80℃，并搅拌4.5—5.5小时，然后将物料压入压滤机中，用质量浓度大于95%的有机溶剂对物料进行洗涤，加入的有机溶剂的重量为颜料红254重量的1.5—3倍，有机溶剂使用完后，接着再用水洗涤，直至滤液的PH值为8，将所得的含固量为40%—45%的滤饼放入普通烘箱进行干燥，即得成品。
2.根据权利要求1所述的颜料红254的后处理工艺，其特征是：所述的NaOH溶液可以用去离子水代替，去离子水的重量为颜料红254粗品重量的1.5—2.5倍。
3.根据权利要求1所述的颜料红254的后处理工艺，其特征是：所述有机溶液为甲醇溶液、乙醇溶液或DMF溶液中的任意一种。
4.根据权利要求1所述的颜料红254的后处理工艺，其特征是：所述有机溶剂为甲醇、乙醇或DMF中的任意一种。