CN102039686A - 聚苯硫醚(pps)塑料制成品后序热处理工艺 - Google Patents
聚苯硫醚(pps)塑料制成品后序热处理工艺 Download PDFInfo
- Publication number
- CN102039686A CN102039686A CN2009101532052A CN200910153205A CN102039686A CN 102039686 A CN102039686 A CN 102039686A CN 2009101532052 A CN2009101532052 A CN 2009101532052A CN 200910153205 A CN200910153205 A CN 200910153205A CN 102039686 A CN102039686 A CN 102039686A
- Authority
- CN
- China
- Prior art keywords
- pps
- drying oven
- oven
- heat treatment
- treatment process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚苯硫醚(PPS)塑料制成品后序热处理工艺。其工艺过程为：a.将聚苯硫醚(PPS)塑料颗粒加入注塑料机，经注塑机注塑成制成品，自然冷却，b.将制成品放入恒温烘箱，启动烘箱将烘箱温度设定在200℃±30℃，c.当温度达到设定要求后，保温0.5～24小时，再关闭恒温烘箱，d.制成品在烘箱中自然冷却0.5～12小时后，打开恒温烘箱取出制成品，即完成所述后序热处理工艺。本发明具有能满足高强度环境使用，提高螺纹连接扭力强度，代替金属部件，保证产品成型速度快，有效降低生产加工成本等优点。
Description
技术领域
本发明涉及一种高强度工程塑料聚苯硫醚(PPS)塑料制成品后序的热处理工艺。
背景技术
目前聚苯硫醚(PPS)塑料制成品，在实际使用中连接螺纹扭力和强度不是很稳定，导致产品机械性能不能够满足高强度环境使用要求。
发明内容
本发明的目的是提供一种能满足高强度环境使用，提高螺纹连接扭力强度，代替金属部件，保证产品成型速度快，有效降低生产加工成本的聚苯硫醚(PPS)塑料制成品后序热处理工艺。
为达到上述目的，本发明是通过以下技术方案实现的。聚苯硫醚(PPS)塑料制成品后序热处理工艺过程为：a.将聚苯流醚(PPS)塑料颗粒加入注塑料机，经注塑机注塑成制成品，自然冷却，b.将制成品放入恒温烘箱，启动烘箱将烘箱温度设定在200℃±30℃，c.当温度达到设定要求后，保温0.5～24小时，再关闭恒温烘箱，d.制成品在烘箱中自然冷却0.5～12小时后，打开恒温烘箱取出制成品，即完成所述后序热处理工艺。
本发明具有如下有益效果：(一)是工艺简单、合理、方便、生产成本低；(二)是经过后序热处理工艺，可使聚苯硫醚(PPS)塑料制成品的机械强度、螺纹连接扭力比没经过处理的高一倍左右，能有效提高机械强度，代替金属部件；(三)是产品成型速度快。
具体实施方式
下面对本发明的实施例作进一步详细的描述。
实施例1：聚苯硫醚(PPS)塑料制成品后序热处理工艺过程为：a.将聚苯流醚(PPS)塑料颗粒加入注塑料机，经注塑机注塑成制成品，自然冷却，b.将制成品放入恒温烘箱，启动烘箱将烘箱温度设定在180℃，c.当温度达到设定要求后，保温2小时，再关闭恒温烘箱，d.制成品在烘箱中自然冷却3小时后，打开恒温烘箱取出制成品，即完成所述后序热处理工艺。
实施例2：启动烘箱将烘箱温度设定在200℃，当温度达到设定要求后，保温6小时，再关闭恒温烘箱，制成品在烘箱中自然冷却6小时后，打开恒温烘箱取出制成品，其余同实施例1。
实施例3：启动烘箱将烘箱温度设定在220℃，当温度达到设定要求后，保温16小时，再关闭恒温烘箱，制成品在烘箱中自然冷却10小时后，打开恒温烘箱取出制成品，其余同实施例1。
Claims (1)
1.一种聚苯硫醚(PPS)塑料制成品后序热处理工艺，其特征在于其工艺过程为：
a.将聚苯流醚(PPS)塑料颗粒加入注塑料机，经注塑机注塑成制成品，自然冷却，
b.将制成品放入恒温烘箱，启动烘箱将烘箱温度设定在200℃±30℃，
c.当温度达到设定要求后，保温0.5～24小时，再关闭恒温烘箱，
d.制成品在烘箱中自然冷却0.5～12小时后，打开恒温烘箱取出制成品，即完成所述后序热处理工艺。