CN101928496A - 高性能可见光催化内墙抗菌涂料 - Google Patents
高性能可见光催化内墙抗菌涂料 Download PDFInfo
- Publication number
- CN101928496A CN101928496A CN2010102564693A CN201010256469A CN101928496A CN 101928496 A CN101928496 A CN 101928496A CN 2010102564693 A CN2010102564693 A CN 2010102564693A CN 201010256469 A CN201010256469 A CN 201010256469A CN 101928496 A CN101928496 A CN 101928496A
- Authority
- CN
- China
- Prior art keywords
- coating
- parts
- tio
- defoamer
- visible light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种含有可见光光响应的氮掺杂纳米二氧化钛作为改性剂的内墙抗菌涂料。制备方法为：采用SFJ-400型高速分散机分散纳米TiO2于含有一定量分散剂或分散剂组合、消泡剂，成膜助剂的水体系中，高速搅拌20min，用氨水调节PH值至9-10，超声分散15min，依次加入水、各种填料、消泡剂，再搅拌10min，超声分散30min，得到预分散体即半成品，再往上述半成品中加入适量消泡剂和硅丙乳液，搅拌均匀后加入适量增稠剂，调节pH值9-10，将涂料调至合适粘度，再充分搅拌30min，再超声分散1h，均匀后过滤即成涂料产品。该涂料可以运用在室内装修装饰、防霉抗菌等场所，具有明显的抗菌能力及防沉降能力。
Description
技术领域
本发明涉及一种内墙抗菌涂料领域，特别是一种氮掺杂纳米光催化涂料及其制备方法，利用具有可见光光响应的氮掺杂纳米二氧化钛作为改性剂的内墙抗菌涂料，该涂料可以运用在室内装修装饰、防霉抗菌等场所，具有明显的抗菌能力及防沉降能力。
背景技术
随着人类对自身健康状况的重视，与之朝夕相处的居住环境也越来越受到人们的关注。居室环境微生物污染和室内空气污染已经对人类的健康状况产生了很大的影响。根据相关报道，室内环境污染已经引起35.7％的呼吸道疾病，22％的慢性肺病和15％的气管炎、支气管炎和肺癌。要阻止细菌、病毒对人类感染，减少室内有害气体的含量，一个切实可行的办法就是使用绿色、环保性建材。体现在涂装材料方面就要求开发低TVOC(有机挥发物)的含量，具有抗菌、降解有害气体的新型水性抗菌涂料。
氮掺杂TiO2可以在可见光催化下具有一定的抗菌能力已经被行业内人士所逐步认识。
氮掺杂纳米TiO2作为一种新型的抗菌材料，由于其独特的光催化效应，已被广泛用于抗菌抑菌，已成为光催化研究领域中最具潜力的方向之一。但带TiO2带隙较宽(3.2eV)，只能影响波长小于400nm的紫外光(大约占太阳光的4％)，对可见光(大约占太阳光的43％)几乎无响应，加之光生电子和光生空穴易于复合，光量子效率低，严重制约了TiO2光催化效应的实际应用效率。
同时，在液相介质中，由于纳米TiO2粒子表面的活性，使它们很容易团聚在一起，形成带有若干弱连接界面的较大的团聚体。要阻止TiO2形成高密度、硬块状沉淀的方法之一，就是减小粒子间的范德华引力，使初级粒子不易团聚成二级粒子，从而避免进一步发生原子间的键合而导致生成高密度、硬块状沉淀。
团聚体的存在大大阻碍纳米粉体特性的充分发挥，因此研究纳米粉体的分散性能将是进一步提高材料稳定性能的前提和基础，研究纳米TiO2分散技术及其稳定性已经成为纳米TiO2应用中不可或缺的一部分。氮掺杂纳米TiO2用于涂料是涂料发展的一个重大成就，它是涂料向高层次、高性能、高档次发展的一个新动力，尤其是纳米TiO2涂料的抗菌杀毒作用，使其已成为国内外关注的焦点，具有广泛的应用。
但纳米TiO2和氮掺杂TiO2如果在内墙抗菌涂料体系中添加量太大，非常容易产生团聚现象而影响涂料的稳定性，进而影响涂料的整体性能。因而筛选合适的分散剂保持涂料的稳定性成为关键。
纳米TiO2和氮掺杂TiO2产生团聚现象体现在静置数个小时后倒掉上层清液，依然会有不同程度的沉降分层现象。如果沉降程度越小，表明分散剂选择恰当，涂料的稳定性越好。
发明内容
本发明的目的是提供一种具有明显抗菌及防沉降能力的的内墙涂料，特别是一种含有可见光光响应的氮掺杂纳米二氧化钛作为改性剂的内墙抗菌涂料。该高性能可见光催化内墙抗菌涂料中添加了聚丙烯酸钠、六偏磷酸钠、三聚磷酸钠三个组分的复合分散剂，因而具有较强的防沉降能力。同时氮掺杂纳米TiO2还具有明显的抑菌抗菌效果。
本发明涉及的纳米TiO2的制备方法可以参考见文献《表面活性剂对TiOSO4常温水解法制备纳米TiO2粉末的影响》唐小红，周大利，尹光福，张云，杨为中，郑昌琼，中图分类号：0643文献标识码：A文章编号：1000-6532(2004)06-0011-05。
本发明涉及的氮掺杂TiO2可以参考见文献《水解沉淀法制备氮掺杂TiO2光催化剂的活性研究》唐玉朝，刘绍根，薛莉娉，况敬静，黄雪峰，中图分类号：0643文献标识码：A文章编号：1006-4540(2005 J 03-056-03。
实际上纳米TiO2和氮掺杂TiO2是常规的可以获得的物质，市场上已有多家供应商可以提供，本发明也可以在市场上购买到纳米TiO2和氮掺杂TiO2。
以下为高性能可见光催化内墙抗菌涂料的抗菌效果实验：
1、实验方法
1.1实验方案
按国家标准ASTM D 3274-95《在微生物和泥土中漆膜表面破坏程度的评价方法》和GB1741-79(89)《漆膜耐霉菌测定法-甲法》，采用平板记数法对改性涂料的抗菌性能进行了检测。
一、材料：
1、试验菌：大肠杆菌(8099)第6代由军事医学科学院提供
金黄色葡萄球菌(ATCC6538)第6代由军事医学科学院提供
白色念珠菌(ATCC10231)第6代由军事医学科学院提供
2、试验样品：高性能可见光催化内墙抗菌涂料(批号：20100202)试样A
普通纳米TiO2分散体系涂料。试样B其中普通纳米TiO2由法国美礼联公司提供
二、方法
1、检验依据：GB 15979-2002
2、抑菌试验：作用时间：2h，4h，试验温度：20℃±1℃。试验重复3次
1.2涂料涂膜样品的制备
将载玻片表面进行酸蚀，用去离子水洗净、凉干，分别取一定量两种实验用水性涂料各加10％水调漆搅拌均匀，采用XB-50涂布器将改性涂料均匀涂于载玻片上，膜厚0.1～0.2mm。
1.3抗菌实验流程
(1)采用平板记数法进行抗菌性能的测定。取样丝经高温灭菌后，放入灭菌生理盐水中冷却，迅速冷却后取大肠杆菌少许(整个操作过程中，所有试管及容器口都应朝向高温灯或在其附近以防其他菌种感染)。
(2)将取出的细菌置入10ml生理盐水中，配制成0.1mol/ml的菌液。
(3)取2步中的菌液1ml放入装有10ml生理盐水的试管中，配制成0.01mol/ml的菌液。
(4)用移液枪取0.01mol/ml的菌液0.2ml，轻涂于附着有纳米TiO2改性涂料涂膜的载玻片上。
(5)根据样品反应要求不同，进行反应一段时间(0-8h)，用棉棒(灭菌后)轻轻滚擦洗涂膜膜表面。
(6)将擦洗后的棉棒头放入10ml生理盐水中(每个样品均采用相同数目棉棒擦洗)，在80转速的漩涡混合器上振摇，以保证反应物全部被洗入生理盐水。
(7)用移液枪取(6)中的溶液0.3ml置入表面皿(灭菌后)，立即向表面皿中倒入牛肉膏培养液少许(以恰好覆盖皿底为宜)。
(8)将表面皿放入37℃培养箱中培养48小时。
实验结果与讨论
表一、表二分别给出了采用高性能可见光催化内墙抗菌涂料和对普通纳米TiO2分散体系涂料对大肠杆菌、白色念珠菌、金黄色葡萄球菌的抗菌结果。
表一：高性能可见光催化内墙抗菌涂料(批号：20100202)。试样A
表二：普通纳米TiO2分散体系涂料。试样B
实验结果：在20℃±1℃的及其它同等环境条件下，从高性能可见光催化内墙抗菌涂料试验效果可以看出，高性能可见光催化内墙抗菌涂料的抗菌抑菌效果明显高于普通纳米TiO2分散体系涂料的抑菌效果，由此可见氮掺杂纳米TiO2由于其独特的光催化效应，抗菌抑菌效果非常明显。
本发明的技术方案如下：
高性能可见光催化内墙抗菌涂料，其中：它是由含有下述重量配比的原料制备而成：硅丙乳液30-45份、纳米TiO2 25-37份、掺氮纳米TiO2 15-23份、钛白粉20-36份、高岭土12-20份、重质碳酸钙10-24份、轻质碳酸钙15-27份、硅石灰粉18-27份、水28-35份、消泡剂1.3-3.5份、氯乙酰胺0.09-0.34份、烷基酚聚氧乙烯醚(APE或OP)1.2-7份、聚丙烯酸钠1.2-3.5份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.12-1.5份、木质纤维增稠剂6-10份，
其中：该涂料的制备方法为：采用SFJ-400型高速分散机分散纳米TiO2于含有一定量聚丙烯酸钠、三分之一重量的三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品。
高性能可见光催化内墙抗菌涂料，包含以下重量百分比的组份：硅丙乳液30-45份、纳米TiO2 25-37份、掺氮纳米TiO2 15-23份、钛白粉20-36份、高岭土12-20份、重质碳酸钙10-24份、轻质碳酸钙15-27份、硅石灰粉18-27份、水28-35份、消泡剂1.3-3.5份、氯乙酰胺0.09-0.34份、烷基酚聚氧乙烯醚(APE或OP)1.2-7份、聚丙烯酸钠0.7-2.8份、六偏磷酸钠0.3-1.2份、三聚磷酸钠0.5-1.3份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.12-1.5份、木质纤维增稠剂6-10份，
其中：该涂料的制备方法为采用SFJ-400型高速分散机分散纳米TiO2于含有一定量聚丙烯酸钠、六偏磷酸钠、三聚磷酸钠、三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品，
其中：分散剂组合是由含有下述重量配比的原料制备而成：聚丙烯酸钠0.7-2.8份、六偏磷酸钠0.3-1.2份、三聚磷酸钠0.5-1.3份。
较优的技术方案为：
高性能可见光催化内墙抗菌涂料，其中：它是由含有下述重量配比的原料制备而成：硅丙乳液45份、纳米TiO2 37份、掺氮纳米TiO2 23份、钛白粉25份、高岭土20份、重质碳酸钙24份、轻质碳酸钙27份、硅石灰粉27份、水35份、消泡剂2.7份、氯乙酰胺0.21份、烷基酚聚氧乙烯醚(APE或OP)4.2份、聚丙烯酸钠1.3份、六偏磷酸钠0.9份、三聚磷酸钠0.9份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.98份、木质纤维增稠剂7份。其中：该涂料的制备方法为采用SFJ-400型高速分散机分散纳米TiO2于含有一定量聚丙烯酸钠、六偏磷酸钠、三聚磷酸钠、三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品，
其中：分散剂组合包括重量百分比的组份聚丙烯酸钠1.3份、六偏磷酸钠0.9份、三聚磷酸钠0.9份。
高性能可见光催化内墙抗菌涂料，其中：该涂料具有较强的抗菌抑菌能力可以运用在室内装修装饰、防霉抗菌等场所。
目前的大多数纳米TiO2改性抗菌涂料都是以紫外线作为激发光源，而具有可见光响应的光催化涂料少，光催化效率不高，这主要是因为二氧化钛在水溶剂中分散稳定性不高造成的。以可见光活性的氮掺杂改性纳米二氧化钛粉末为功能填料、水作为溶剂，采用新的超声-分散剂复合分散技术，制备一种常规性能优越、在可见光范围响应的具有良好光催化效率的抗菌抑菌环保内墙涂料。
具体实施例：
实施例1、高性能可见光催化内墙抗菌涂料，其中：它是由含有下述重量配比的原料制备而成：硅丙乳液45份、纳米TiO2 37份、掺氮纳米TiO2 23份、钛白粉25份、高岭土20份、重质碳酸钙24份、轻质碳酸钙27份、硅石灰粉27份、水35份、消泡剂2.7份、氯乙酰胺0.21份、烷基酚聚氧乙烯醚(APE或OP)4.2份、分散剂0.9份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.98份、木质纤维增稠剂7份。
其中：该涂料的制备方法为采用SFJ-400型高速分散机分散纳米TiO2于含有分散剂、三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯、二分之一重量的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入二分之一重量的水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品。
分散剂是聚乙烯醇。
其中：纳米TiO2的制备方法参考见文献《表面活性剂对TiOSO4常温水解法制备纳米TiO2粉末的影响》唐小红，周大利，尹光福，张云，杨为中，郑昌琼，中图分类号：0643文献标识码：A文章编1000-6532(2004)06-0011-05；氮掺杂TiO2的制备方法参考见文献《水解沉淀法制备氮掺杂TiO2光催化剂的活性研究》唐玉朝，刘绍根，薛莉娉，况敬静，黄雪峰，中图分类号：0643文献标识码：A文章编号：1006-4540(2005 J 03-056-03。
例如市场上可以购买到的硅丙乳液如下：
硅丙乳液是丙烯酸酯类和有机硅单体接枝共聚合而成的水性乳液，成膜有较高的光泽，较佳的耐盐雾性，耐碱性、防腐性、极强的附着力，耐水性好，耐候优异等特点。硅丙乳液可直接用于金属材料的防腐材料，金属漆、富锌漆、防水涂料、木器漆和各种涂料的面漆，高档外墙漆。其技术指标如下：
| 项目 | 指标 | 项目 | 指标 |
| 外观 | 乳白色泛兰液体 | 固含量(wt％) | 45±2 |
| 最低成膜温度(Tg) | 15-20℃ | 粘度(mpa.a) | 500-1000 |
| PH值(酸碱度) | 8.0-9.5 | 残余单体(溴值％) | ≤1.0 |
| 稀释稳定性 | 20％水溶液通过 | 化学稳定性(5％的氯化钙乳液) | 1∶1通过 |
| 机械稳定性 | 4000r/min半小时通过 | 冻融稳定性 | 5个循环通过 |
实施例2、高性能可见光催化内墙抗菌涂料，其中：分散剂是聚丙烯酸钠0.9份。其余同实施例1。
实施例3、高性能可见光催化内墙抗菌涂料，其中：分散剂是六偏磷酸钠0.9份。其余同实施例1。
实施例4、高性能可见光催化内墙抗菌涂料，其中：分散剂是三聚磷酸钠0.9份。其余同实施例1。
实施例5、高性能可见光催化内墙抗菌涂料，其中：硅丙乳液45份、纳米TiO2 37份、掺氮纳米TiO2 23份、钛白粉25份、高岭土20份、重质碳酸钙24份、轻质碳酸钙27份、硅石灰粉27份、水35份、消泡剂2.7份、氯乙酰胺0.21份、烷基酚聚氧乙烯醚(APE或OP)4.2份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.98份、木质纤维增稠剂7份。其余同实施例1。
其中：该涂料的制备方法为采用SFJ-400型高速分散机分散纳米TiO2于含有三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯、二分之一重量的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入二分之一重量的水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品。
实施例6、高性能可见光催化内墙抗菌涂料，其中：它是由含有下述重量配比的原料制备而成：硅丙乳液45份、纳米TiO2 37份、掺氮纳米TiO2 23份、钛白粉25份、高岭土20份、重质碳酸钙24份、轻质碳酸钙27份、硅石灰粉27份、水35份、消泡剂2.7份、氯乙酰胺0.21份、烷基酚聚氧乙烯醚(APE或OP)4.2份、聚丙烯酸钠1.3份、六偏磷酸钠0.9份、三聚磷酸钠0.9份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.98份、木质纤维增稠剂7份，
其特征在于：该涂料的制备方法为：采用SFJ-400型高速分散机分散纳米TiO2于含有一定量的聚丙烯酸钠、六偏磷酸钠、三聚磷酸钠、三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品，
其中：分散剂是重量比的聚丙烯酸钠1.3份、六偏磷酸钠0.9份、三聚磷酸钠0.9份。
对比试验如下：
将由实施例1、实施例2、实施例3、实施例4、实施例5、实施例6经不同的分散剂制得的不同水分散体系的氮掺杂纳米TiO2分散体系分置于五个相同的烧杯中并编号A，B，C，D，E，F同时静置5个小时后倒掉上层清液，将沉淀放入真空干燥箱干燥，将制得的分散体系后分别采用FA1004电子天平称量沉淀重量。(其中，样品A，B，C，D，E，F采用的分散剂分别是A聚乙烯醇，B聚丙烯酸钠，C六偏磷酸钠，D三聚磷酸钠，E不采用分散剂，F聚丙烯酸钠，六偏磷酸钠，三聚磷酸钠三个成分的组合。)
实验结果如下：
五个小时的静置后，A的沉淀量高达93.23％、B的沉淀量有43.65％、C的沉淀量有74.34％、D的沉淀量有62.33％、E的沉淀量有91.25％、F的沉淀量最低达30.56％。
根据实验结果的数据可以得到：即采用分散剂聚丙烯酸钠(PAANa)的TiO2
水分散体系所产生的沉淀量较少，分散效果也较好，但是采用聚丙烯酸钠、六偏磷酸钠、三聚磷酸钠三中成分的分散剂组合制得的TiO2水分散体系所产生的沉淀量最少，分散效果明显最好。采用六偏磷酸钠的样品C和采用三聚磷酸钠的样品D较未加分散剂方案E分散效果有较大改善，而采用聚乙烯醇的样品A，对TiO2水分散体系的作用效果并不理想。
Claims (7)
1.高性能可见光催化内墙抗菌涂料，其中：它是由含有下述重量配比的原料制备而成：硅丙乳液30-45份、纳米TiO2 25-37份、掺氮纳米TiO2 15-23份、钛白粉20-36份、高岭土12-20份、重质碳酸钙10-24份、轻质碳酸钙15-27份、硅石灰粉18-27份、水28-35份、消泡剂1.3-3.5份、氯乙酰胺0.09-0.34份、烷基酚聚氧乙烯醚(APE或OP)1.2-7份、聚丙烯酸钠0.7-2.8份、六偏磷酸钠0.3-1.2份、三聚磷酸钠0.5-1.3份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.12-1.5份、木质纤维增稠剂6-10份，
其特征在于：该涂料的制备方法为：采用SFJ-400型高速分散机分散纳米TiO2于含有一定量聚丙烯酸钠、六偏磷酸钠、三聚磷酸钠、三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品，
其中：分散剂组合是由含有下述重量配比的原料制备而成：聚丙烯酸钠0.7-2.8份、六偏磷酸钠0.3-1.2份、三聚磷酸钠0.5-1.3份。
2.高性能可见光催化内墙抗菌涂料，其中：它是由含有下述重量配比的原料制备而成：硅丙乳液30-45份、纳米TiO2 25-37份、掺氮纳米TiO2 15-23份、钛白粉20-36份、高岭土12-20份、重质碳酸钙10-24份、轻质碳酸钙15-27份、硅石灰粉18-27份、水28-35份、消泡剂1.3-3.5份、氯乙酰胺0.09-0.34份、烷基酚聚氧乙烯醚(APE或OP)1.2-7份、聚丙烯酸钠1.2-3.5份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.12-1.5份、木质纤维增稠剂6-10份，
其特征在于：该涂料的制备方法为：采用SFJ-400型高速分散机分散纳米TiO2于含有一定量的聚丙烯酸钠、三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品。
3.高性能可见光催化内墙抗菌涂料，其中：它是由含有下述重量配比的原料制备而成：硅丙乳液45份、纳米TiO2 37份、掺氮纳米TiO2 23份、钛白粉25份、高岭土20份、重质碳酸钙24份、轻质碳酸钙27份、硅石灰粉27份、水35份、消泡剂2.7份、氯乙酰胺0.21份、烷基酚聚氧乙烯醚(APE或OP)4.2份、聚丙烯酸钠1.3份、六偏磷酸钠0.9份、三聚磷酸钠0.9份、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯0.98份、木质纤维增稠剂7份，
其特征在于：该涂料的制备方法为：采用SFJ-400型高速分散机分散纳米TiO2于含有一定量的聚丙烯酸钠、六偏磷酸钠、三聚磷酸钠、三分之一重量的消泡剂、成膜助剂2，2，4-三甲基-1，3-戊二醇单异丁酸酯的水体系中，并且高速搅拌20min，氨水调节PH值至9-10，超声分散15min；然后依次加入水、掺氮纳米TiO2、纳米TiO2、钛白粉、高岭土、重质碳酸钙、轻质碳酸钙、硅石灰粉、三分之一重量的消泡剂、氯乙酰胺、烷基酚聚氧乙烯醚(APE或OP)，再以1500r/min转速搅拌10min，超声分散30min，得到预分散体即半成品；再往上述半成品中加入三分之一重量的消泡剂和硅丙乳液，搅拌均匀后加入适量木质纤维增稠剂，氨水调节PH值至9-10，再充分搅拌、超声分散，均匀后经过滤即成涂料产品，
其中：分散剂是重量比的聚丙烯酸钠1.3份、六偏磷酸钠0.9份、三聚磷酸钠0.9份。
4.如权利要求3所述的高性能可见光催化内墙抗菌涂料，其特征在于：该涂料的分散剂组合中包括聚丙烯酸钠、六偏磷酸钠、三聚磷酸钠三种成分。
5.如权利要求3所述的高性能可见光催化内墙抗菌涂料，其特征在于：该涂料的防沉降作用较强，水分散体系所产生的沉淀量少，分散效果最好。
6.如权利要求1或2或3所述的高性能可见光催化内墙抗菌涂料，其特征在于：助剂组分中的烷基酚聚氧乙烯醚(APE或OP)属于醚类活性物质，属于一种表面活性剂。
7.高性能可见光催化内墙抗菌涂料，其特征在于：该涂料具有较强的抗菌抑菌能力可以运用在室内装修装饰、防霉抗菌等场所。