CN101864716A - Pavior brick produced by utilizing building wastes and preparation method thereof - Google Patents
Pavior brick produced by utilizing building wastes and preparation method thereof Download PDFInfo
- Publication number
- CN101864716A CN101864716A CN 201010225076 CN201010225076A CN101864716A CN 101864716 A CN101864716 A CN 101864716A CN 201010225076 CN201010225076 CN 201010225076 CN 201010225076 A CN201010225076 A CN 201010225076A CN 101864716 A CN101864716 A CN 101864716A
- Authority
- CN
- China
- Prior art keywords
- building castoff
- pavior brick
- utilizes
- brick
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of building materials, in particular to a pavior brick produced by utilizing building wastes and a preparation method thereof. The pavior brick produced by utilizing the building wastes comprises the following raw materials in percentage by weight: 5-15% of coarse aggregate, 30-40% of middle aggregate, 30-40% of fine aggregate and 10-20% of cement. The invention utilizes the building wastes to produce the pavior brick, thereby saving resources, lowering cost and reducing environment pollution; and meanwhile, because the weight percentages of the coarse aggregate, the middle aggregate and the fine aggregate are confined within certain ranges, the compression strength of the produced pavior brick totally conforms to the standard.
Description
Technical field
The invention belongs to building material technical field, be specifically related to a kind of pavior brick that utilizes building castoff production and preparation method thereof.
Background technology
Along with the continuous quickening of urbanization process, the building castoff in the city is also more and more, bring for the normal live and work of people and have a strong impact on, so the processing of building castoff and utilization becomes one of urgent problem in the urbanization process.
At present the processing of building castoff is mainly adopted the mode of burning or landfill, but can not thoroughly be solved environment pollution like this.Meanwhile, the construction in city needs a large amount of pavior bricks, and the pavior brick of Xiao Shouing mainly is with raw material such as cement, yellow ground, clays in the market, generally adopts sintering, pressurization, technology such as steam-cured, investment greatly, it is many to expend land resources.Make pavior brick if building castoff can be used, both can save resource, reduce cost, can reduce environment pollution again.
Summary of the invention
One of purpose of the present invention provides a kind of pavior brick that utilizes building castoff to produce that not only can save resource, reduce cost but also can reduce environment pollution.
The object of the present invention is achieved like this.
A kind of pavior brick that utilizes building castoff to produce comprises following raw materials by weight percent composition:
Coarse aggregate 5%-15%
In the 30%-40% that gathers materials
Fine aggregate 30%-40%
Cement 10%-20%.
Wherein, described coarse aggregate is for being the coarse aggregate of 10-30mm with the diameter that filters out after the building castoff fragmentation.
Wherein, gather materials in described for the diameter that will filter out after the building castoff fragmentation be 5-10mm, 4-6mm in gather materials.
Wherein, described fine aggregate is for being the fine aggregate of 0-2.5mm, 2.5-4mm with the diameter that filters out after the building castoff fragmentation.
Described building castoff comprise brick, watt, dust and sand and concrete block.
Described cement is portland cement.
Also can add a kind of or several arbitrarily in pigment, river sand or the Concrete admixtures.
Described Concrete admixtures is an early strength admixture.
Two of purpose of the present invention provides a kind of preparation method who utilizes the pavior brick of building castoff production, and it comprises following preparation process:
A, take by weighing above-mentioned percentage by weight coarse aggregate, in gather materials and fine aggregate stirs in mixer;
Continue to be stirred to evenly in b, the cement adding mixer with above-mentioned percentage by weight;
The water of c, the above-mentioned total raw material 5%-15% percentage by weight of adding continues to be stirred to evenly;
D, the material that stirs is added extrusion modling, the demoulding then in the model;
E, the pavior brick after the demoulding is sent into curing kilns carry out maintenance, curing time is 2-8 hour;
F, send into the stockyard and carry out natural maintenance more than 28 days, get product.
Wherein, also can add a kind of or several arbitrarily in pigment, river sand or the Concrete admixtures among the step b.
Wherein, in the steps d, add the material of one deck prevailing roadway brick prescription above the described material that stirs, extrusion modling then obtains having double-deck pavior brick.
Beneficial effect of the present invention is: the present invention utilizes building castoff to produce pavior brick and not only can save resource, reduces cost but also can reduce environment pollution, simultaneously since the present invention with coarse aggregate, in gather materials and fine aggregate three's percentage by weight restriction within the specific limits, make the compressive strength of the pavior brick of producing meet standard fully.
The specific embodiment
The invention will be further described below by embodiment, but practical range of the present invention is not limited to this.
Embodiment 1.
A kind of pavior brick that utilizes building castoff to produce comprises that the raw material of following weight is formed:
Coarse aggregate 5kg
In the 40kg that gathers materials
Fine aggregate 35kg
Cement 20kg.
Wherein, described coarse aggregate is for being the coarse aggregate of 10-30mm with the diameter that filters out after the building castoff fragmentation.
Wherein, gather materials in described for the diameter that the building castoff fragmentation is filtered out be 5-10mm, 4-6mm in gather materials.
Wherein, described fine aggregate is the fine aggregate of 0-2.5mm, 2.5-4mm for the diameter that the building castoff fragmentation is filtered out.
Described building castoff comprise brick, watt, dust and sand and concrete block, comprise that also other is fit to do the building castoff that pavior brick is used certainly.
Described cement is portland cement, can certainly be the cement of other type.
A kind of preparation method who utilizes the pavior brick of building castoff production, it comprises following preparation process:
A, take by weighing above-mentioned weight coarse aggregate, in gather materials and fine aggregate stirs in mixer;
Continue to be stirred to evenly in b, the cement adding mixer with above-mentioned weight;
The water of c, adding 12kg continues to be stirred to evenly;
D, the material that stirs is added extrusion modling, the demoulding then in the model;
E, the pavior brick after the demoulding is sent into curing kilns carry out maintenance, curing time is 2 hours;
F, send into the stockyard and carry out natural maintenance 28 days, get product.
Embodiment 2.
A kind of pavior brick that utilizes building castoff to produce comprises that the raw material of following weight is formed:
Coarse aggregate 10kg
In the 30kg that gathers materials
Fine aggregate 40kg
Cement 20kg.
Wherein, described coarse aggregate is the coarse aggregate of 10-30mm for the diameter that the building castoff fragmentation is filtered out.
Wherein, gather materials in described for the diameter that the building castoff fragmentation is filtered out be 5-10mm, 4-6mm in gather materials.
Wherein, described fine aggregate is the fine aggregate of 0-2.5mm, 2.5-4mm for the diameter that the building castoff fragmentation is filtered out.
Described building castoff comprise brick, watt, dust and sand and concrete block, comprise that also other is fit to do the building castoff that pavior brick is used certainly.
Described cement is portland cement, can certainly be the cement of other type.
A kind of preparation method who utilizes the pavior brick of building castoff production, it comprises following preparation process:
A, take by weighing above-mentioned weight coarse aggregate, in gather materials and fine aggregate stirs in mixer;
Continue to be stirred to evenly in b, the cement adding mixer with above-mentioned weight;
The water of c, adding 15kg continues to be stirred to evenly;
D, the material that stirs is added extrusion modling, the demoulding then in the model;
E, the pavior brick after the demoulding is sent into curing kilns carry out maintenance, curing time is 6 hours;
F, send into the stockyard and carried out natural maintenance sky 29 days, get product.
Embodiment 3.
A kind of pavior brick that utilizes building castoff to produce comprises that the raw material of following weight is formed:
Coarse aggregate 15kg
In the 35kg that gathers materials
Fine aggregate 40kg
Cement 10kg.
Wherein, described coarse aggregate is the coarse aggregate of 10-30mm for the diameter that the building castoff fragmentation is filtered out.
Wherein, gather materials in described for the diameter that the building castoff fragmentation is filtered out be 5-10mm, 4-6mm in gather materials.
Wherein, described fine aggregate is the fine aggregate of 0-2.5mm, 2.5-4mm for the diameter that the building castoff fragmentation is filtered out.
Described building castoff comprise brick, watt, dust and sand and concrete block, comprise that also other is fit to do the building castoff that pavior brick is used certainly.
Described cement is portland cement, can certainly be the cement of other type.
Also can add a kind of or several arbitrarily in pigment, river sand or the Concrete admixtures.
Described Concrete admixtures is an early strength admixture.
A kind of preparation method who utilizes the pavior brick of building castoff production, it comprises following preparation process:
A, take by weighing above-mentioned weight coarse aggregate, in gather materials and fine aggregate stirs in mixer;
Continue to be stirred to evenly in b, the cement adding mixer with above-mentioned weight;
The water of c, adding 5kg continues to be stirred to evenly;
D, the material that stirs is added extrusion modling, the demoulding then in the model;
E, the pavior brick after the demoulding is sent into curing kilns carry out maintenance, curing time is 8 hours;
F, send into the stockyard and carry out natural maintenance 29 days, get product.
Embodiment 4.
A kind of pavior brick that utilizes building castoff to produce comprises that the raw material of following weight is formed:
Coarse aggregate 8kg
In the 32kg that gathers materials
Fine aggregate 40kg
Cement 20kg.
Wherein, described coarse aggregate is the coarse aggregate of 10-30mm for the diameter that the building castoff fragmentation is filtered out.
Wherein, gather materials in described for the diameter that the building castoff fragmentation is filtered out be 5-10mm, 4-6mm in gather materials.
Wherein, described fine aggregate is the fine aggregate of 0-2.5mm, 2.5-4mm for the diameter that the building castoff fragmentation is filtered out.
Described building castoff comprise brick, watt, dust and sand and concrete block, comprise that also other is fit to do the building castoff that pavior brick is used certainly.
Described cement is portland cement, can certainly be the cement of other type.
Also can add pigment, can select different colors according to user's request, consumption can be 0.01-0.1kg in the present embodiment, specifically can regulate according to shade.
A kind of preparation method who utilizes the pavior brick of building castoff production, it comprises following preparation process:
A, take by weighing above-mentioned weight coarse aggregate, in gather materials and fine aggregate stirs in mixer;
B, the pigment of the cement of above-mentioned weight and 0.01-0.1kg added continue to be stirred in the mixer evenly;
The water of c, adding 12kg continues to be stirred to evenly;
D, the material that stirs is added extrusion modling, the demoulding then in the model;
E, the pavior brick after the demoulding is sent into curing kilns carry out maintenance, curing time is 4 hours;
F, send into the stockyard and carry out natural maintenance 30 days, get product.
Embodiment 5.
A kind of pavior brick that utilizes building castoff to produce comprises that the raw material of following weight is formed:
Coarse aggregate 12kg
In the 38kg that gathers materials
Fine aggregate 40kg
Cement 10kg.
Wherein, described coarse aggregate is the coarse aggregate of 10-30mm for the diameter that the building castoff fragmentation is filtered out.
Wherein, gather materials in described for the diameter that the building castoff fragmentation is filtered out be 5-10mm, 4-6mm in gather materials.
Wherein, described fine aggregate is the fine aggregate of 0-2.5mm, 2.5-4mm for the diameter that the building castoff fragmentation is filtered out.
Described building castoff comprise brick, watt, dust and sand and concrete block, comprise that also other is fit to do the building castoff that pavior brick is used certainly.
Described cement is portland cement, can certainly be the cement of other type.
Also can add river sand and Concrete admixtures, Concrete admixtures described in the present embodiment is an early strength admixture, certainly also can select the Concrete admixtures of other types as required, the consumption of river sand is 2-6kg, early strength admixture is selected triethanolamine early strength admixture for use, addition is 0.2kg, also can select the early strength admixture of other type certainly as required for use, and can regulate consumption as required.
A kind of preparation method who utilizes the pavior brick of building castoff production, it comprises following preparation process:
A, take by weighing above-mentioned weight coarse aggregate, in gather materials and fine aggregate stirs in mixer;
B, the cement of above-mentioned weight, an amount of river sand and early strength admixture added continue to be stirred in the mixer evenly;
The water of c, adding 8kg continues to be stirred to evenly;
D, the material that stirs is added extrusion modling, the demoulding then in the model;
E, the pavior brick after the demoulding is sent into curing kilns carry out maintenance, curing time is 2 hours;
F, send into the stockyard and carry out natural maintenance 28 days, get product.
Embodiment 6.
A kind of pavior brick that utilizes building castoff to produce comprises that the raw material of following weight is formed:
Coarse aggregate 10kg
In the 30kg that gathers materials
Fine aggregate 40kg
Cement 20kg.
Wherein, described coarse aggregate is the coarse aggregate of 10-30mm for the diameter that the building castoff fragmentation is filtered out.
Wherein, gather materials in described for the diameter that the building castoff fragmentation is filtered out be 5-10mm, 4-6mm in gather materials.
Wherein, described fine aggregate is the fine aggregate of 0-2.5mm, 2.5-4mm for the diameter that the building castoff fragmentation is filtered out.
Described building castoff comprise brick, watt, dust and sand and concrete block, comprise that also other is fit to do the building castoff that pavior brick is used certainly.
Described cement is portland cement, can certainly be the cement of other type.
A kind of preparation method who utilizes the pavior brick of building castoff production, it comprises following preparation process:
A, take by weighing above-mentioned weight coarse aggregate, in gather materials and fine aggregate stirs in mixer;
Continue to be stirred to evenly in b, the cement adding mixer with above-mentioned weight;
The water of c, adding 15kg continues to be stirred to evenly;
D, the material that stirs is added extrusion modling, the demoulding then in the model;
E, the pavior brick after the demoulding is sent into curing kilns carry out maintenance, curing time is 8 hours;
F, send into the stockyard and carry out natural maintenance 30 days, get product.
Wherein, in the steps d, add the material of one deck prevailing roadway brick prescription above the described material that stirs, extrusion modling then obtains having double-deck pavior brick.
The pavior brick of embodiment 1 to 6 has been carried out the test of compressive strength at the universal testing machine LX-06 of 1000kN, table specific as follows:
After testing, the testing result of embodiment 1 to embodiment 6 meets the standard-required of Cc35 level in " concrete road pavement brick " JC/T446-2000 standard.
The above only is a better embodiment of the present invention, so all equivalences of doing according to the described structure of patent claim of the present invention, feature and principle change or modify, is included in the patent claim of the present invention.
Claims (8)
1. pavior brick that utilizes building castoff to produce is characterized in that: comprise that following raw materials by weight percent forms:
Coarse aggregate 5%-15%
In the 30%-40% that gathers materials
Fine aggregate 30%-40%
Cement 10%-20%,
Wherein, described coarse aggregate is the coarse aggregate of 10-30mm for the diameter that the building castoff fragmentation is filtered out;
Wherein, gather materials in described for the diameter that the building castoff fragmentation is filtered out be 5-10mm, 4-6mm in gather materials;
Wherein, described fine aggregate is the fine aggregate of 0-2.5mm, 2.5-4mm for the diameter that the building castoff fragmentation is filtered out.
2. the pavior brick that utilizes building castoff to produce according to claim 1 is characterized in that: described building castoff comprise brick, watt, dust and sand and concrete block.
3. the pavior brick that utilizes building castoff to produce according to claim 1, it is characterized in that: described cement is portland cement.
4. the pavior brick that utilizes building castoff to produce according to claim 1 is characterized in that: also can add a kind of or several arbitrarily in pigment, river sand or the Concrete admixtures.
5. the pavior brick that utilizes building castoff to produce according to claim 4, it is characterized in that: described Concrete admixtures is an early strength admixture.
6. each described preparation method who utilizes the pavior brick that building castoff produces of claim 1-3, it is characterized in that: it comprises following preparation process:
A, take by weighing above-mentioned percentage by weight coarse aggregate, in gather materials and fine aggregate stirs in mixer;
Continue to be stirred to evenly in b, the cement adding mixer with above-mentioned percentage by weight;
The water of c, the above-mentioned total raw material 5%-15% percentage by weight of adding continues to be stirred to evenly;
D, the material that stirs is added extrusion modling, the demoulding then in the model;
E, the pavior brick after the demoulding is sent into curing kilns carry out maintenance, curing time is 2-8 hour;
F, send into the stockyard and carry out natural maintenance more than 28 days, get product.
7. the preparation method who utilizes the pavior brick that building castoff produces according to claim 6 is characterized in that: also can add a kind of or several arbitrarily in pigment, river sand or the Concrete admixtures among the described step b.
8. the preparation method who utilizes the pavior brick of building castoff production according to claim 6, it is characterized in that: in the steps d, add the material of one deck prevailing roadway brick prescription above the described material that stirs, extrusion modling then obtains having double-deck pavior brick.