CN101782111B - High-hardness abrasion-resistant bush - Google Patents
High-hardness abrasion-resistant bush Download PDFInfo
- Publication number
- CN101782111B CN101782111B CN2010101246015A CN201010124601A CN101782111B CN 101782111 B CN101782111 B CN 101782111B CN 2010101246015 A CN2010101246015 A CN 2010101246015A CN 201010124601 A CN201010124601 A CN 201010124601A CN 101782111 B CN101782111 B CN 101782111B
- Authority
- CN
- China
- Prior art keywords
- percent
- copper
- abrasion
- bush
- hardness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a high-hardness abrasion-resistant bush which comprises a substrate made of a copper-based alloy. The copper-based alloy comprises the following components in percentage by weight: 67-81 percent of copper, 15-25 percent of nickel, 3-7 percent of tin, 0.5-1.2 percent of zinc, 0.05-0.20 percent of lead, 0.05-0.25 percent of manganese and the balance of inevitable impurities. By adopting the materials, the bush has lessened abrasion in adverse production environment, prolonged service life, reduced replacement number of a bearing, improved production efficiency and decreased cost. The invention has the advantages of less abrasion and long service life.
Description
Technical field
The present invention relates to a kind of bearing shell.
Background technique
The fin tube milling train is because the defective of work under bad environment and lubricated cooling aspect is used for the performance requirement that the bearing between cutter hub and the cutter shaft need have high abrasion, high hardness.It is main raw material(s) that plain bushing adopts tin bronze (Qsn10-1), is difficult to satisfy wear-resisting and requirement hardness; The external normal Babbitt (Zchsnsb11-6) that adopts, its abrasion resistance is better than tin bronze, but costs an arm and a leg; These material common drawback are that hardness is not high, are not suitable as the bush material of bearing between fin tube milling train cutter hub and the cutter shaft.
Summary of the invention
Technical problem to be solved by this invention provide a kind of wearing and tearing in abominable production environment less, long high-hardness abrasion-resistant bush of life-span.
For solving the problems of the technologies described above, technological scheme of the present invention is: high-hardness abrasion-resistant bush, comprise matrix, the material of described matrix is a copper base alloy, described copper base alloy comprises following component by weight percentage: 67%～81% copper, 15%～25% nickel, 3%～7% tin, 0.5%～1.2% zinc, 0.05%～0.20% lead, 0.05%～0.25% manganese, all the other are unavoidable impurities.
As optimized technical scheme, described copper base alloy comprises following component by weight percentage: 72.60% copper, 20.98% nickel, 5.24% tin, 0.80% zinc, 0.13% lead, 0.15% manganese, all the other are unavoidable impurities.
Owing to adopted technique scheme, high-hardness abrasion-resistant bush, comprise matrix, the material of described matrix is a copper base alloy, described copper base alloy comprises following component by weight percentage: 67%～81% copper, 15%～25% nickel, 3%～7% tin, 0.5%～1.2% zinc, 0.05%～0.20% lead, 0.05%～0.25% manganese, all the other are unavoidable impurities.Owing to adopted above-mentioned material, the wearing and tearing of bearing shell in abominable production environment reduce, and have prolonged the working life of bearing shell, have reduced the replacing number of times of bearing, have improved manufacturing efficiency, have reduced cost.The present invention have wearing and tearing less, long advantage of life-span.
Description of drawings
Accompanying drawing is the structural representation of the embodiment of the invention.
Among the figure: the 1-matrix; The 2-oil groove.
Embodiment
As shown in drawings, high-hardness abrasion-resistant bush, comprise matrix 1, the material of described matrix 1 is a copper base alloy, described copper base alloy comprises following component by weight percentage: 67%～81% copper, 15%～25% nickel, 3%～7% tin, 0.5%～1.2% zinc, 0.05%～0.20% lead, 0.05%～0.25% manganese, all the other are unavoidable impurities.
In the present embodiment, described copper base alloy comprises following component by weight percentage: 72.60% copper, 20.98% nickel, 5.24% tin, 0.80% zinc, 0.13% lead, 0.15% manganese, all the other are unavoidable impurities.
In the present embodiment, the working surface of described body is provided with oil groove 2, and the two ends of working surface are respectively equipped with annular oil groove, and the working surface between the two described annular oil grooves is provided with the X type oil groove of intersection, and above-mentioned annular oil groove and X type oil groove are communicated with in the intersection.
More than be the application's a embodiment, should be understood that these embodiments only be used to the invention is described and be not used in the restriction the invention scope.Should be understood that in addition those skilled in the art can make various changes or modifications the invention after the content of having read the invention instruction, these equivalent form of values fall within the application's appended claims institute restricted portion equally.
Claims (2)
1. high-hardness abrasion-resistant bush, comprise matrix, the material of described matrix is a copper base alloy, it is characterized in that, described copper base alloy comprises following component by weight percentage: 67%～81% copper, 15%～25% nickel, 3%～7% tin, 0.5%～1.2% zinc, 0.05%～0.20% lead, 0.05%～0.25% manganese, all the other are unavoidable impurities.
2. high-hardness abrasion-resistant bush as claimed in claim 1, it is characterized in that: described copper base alloy comprises following component by weight percentage: 72.60% copper, 20.98% nickel, 5.24% tin, 0.80% zinc, 0.13% lead, 0.15% manganese, all the other are unavoidable impurities.