CN101638542A - 纳米水性弹性金属光泽漆 - Google Patents
纳米水性弹性金属光泽漆 Download PDFInfo
- Publication number
- CN101638542A CN101638542A CN200810041308A CN200810041308A CN101638542A CN 101638542 A CN101638542 A CN 101638542A CN 200810041308 A CN200810041308 A CN 200810041308A CN 200810041308 A CN200810041308 A CN 200810041308A CN 101638542 A CN101638542 A CN 101638542A
- Authority
- CN
- China
- Prior art keywords
- nano
- agent
- percent
- class
- metal luster
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种纳米水性弹性金属光泽漆，主要组分及其重量配比包括：固体含量为50％的纳米水性树脂40％～80％，纳米消泡剂0.05％～1.5％，分散剂0.05％～3％，纳米消光剂0～15％，颜料5％～35％，纳米增稠剂0.1％～1％，防缩边剂0.1％～1％，流平剂0.1％～1％，防冻剂1％～10％，纳米抗菌剂0.5％～10％，纳米抗污剂1％～8％，水0～40％。本发明能够广泛用于砖石、混凝土结构的内外墙上，且成本低、金属光泽强烈、装饰效果极佳、施工简便的新型涂料，本发明的水性弹性金属光泽漆涂装系统，有效的将装饰性、抗开裂性、环保三大主题完美融合。
Description
技术领域
本发明涉及一种纳米水性弹性金属光泽漆，尤其涉及一种纳米水性弹性丙烯酸树脂金属光泽漆。
背景技术
普通涂料用于外墙不能有效遮盖墙体裂纹，尤其在北方冬夏温差大，易导致涂膜开裂，普通涂料颜色单调，没有生机，如仿高级装饰材料的外墙涂料及施工方法(CN01125008.9)专利公开的技术。
发明内容
本发明要解决的技术问题在于提供一种纳米水性弹性金属光泽漆，以克服现有技术存在的上述缺陷。
本发明所说的纳米水性弹性金属光泽漆，主要组分及其重量配比包括：
固体含量为50％的纳米水性树脂 40％～80％
纳米消泡剂 0.05％～1.5％
分散剂 0.05％～3％
纳米消光剂 0～15％
颜料 5％～35％
纳米增稠剂 0.1％～1％
防缩边剂 0.1％～1％
流平剂 0.1％～1％
防冻剂 1％～10％
纳米抗菌剂 0.5％～10％
纳米抗污剂 1％～8％
水 0～40％。
当需配制有色金属闪光漆时，可需加入重量比为0～10％的纳米高透明、高耐候水性色浆，如BASF公司牌号为XFAST系列的产品；
优选的组分及重量配比为：
固体含量为50％的纳米水性丙烯酸弹性乳液52.5％，消泡剂0.15％，分散剂0.15％，金属效果颜料12.5％，增稠剂0.5％，防缩边剂0.8％，流平剂0.3％，抗污剂4.5％，防冻剂4％，抗菌剂1％，水23.6％。
所述纳米水性树脂为水性纳米乳液，上海居宁高分子材料有限公司GP-400“微纳米相分离”乳液，江苏南通生达化工有限公司SD-508纳米高弹乳液，塞拉尼斯Mowilth Nano 9420纳米乳液，台湾长兴化学4315纳米水性弹性氟碳乳液。各材料特性如下：
SD-508水性纳米高弹性乳液：
| 聚合物类型 | 固含量 | 玻璃化温度 | 最低成膜温度 | PH值 | 比重 |
| 改性聚丙烯酸乳液 | 50±1％ | 5℃ | 0℃ | 7～9 | 1.06g/ml |
GP-400“微纳米相分离”乳液水性弹性乳液：
| 聚合物类型 | 固含量 | 玻璃化温度 | 最低成膜温度 | PH值 | 比重 |
| 聚丙烯酸乳液 | 50±0.5％ | -10℃ | 0℃ | 7～8 | 1.03g/ml |
塞拉尼斯Mowilth Nano 9420纳米乳液
| 聚合物类型 | 固含量 | 玻璃化温度 | 最低成膜温度 | PH值 | 比重 |
| 改性聚丙烯酸乳液 | 50±1％ | 5℃ | 0℃ | 7～9 | 1.05g/ml |
台湾长兴化学4315纳米水性弹性氟碳乳液
| 聚合物类型 | 固含量 | 玻璃化温度 | 最低成膜温度 | PH值 | 比重 |
| 聚丙烯酸改性氟碳乳液 | 50±1％ | -5℃ | 0℃ | 7～9 | 1.05g/ml |
所述纳米消泡剂为纳米聚硅氧烷-聚醚共聚物乳液类、聚丙二醇类、聚乙二醇-憎水固体-聚硅氧烷混合物类、矿物油基类或其混合物；
所说的纳米聚硅氧烷-聚醚共聚物乳液类可采用美国科宁公司的A10；所说的聚丙二醇类可采用德国巴斯夫化工有限公司生产的Pluriol P 2000；所说的聚乙二醇-憎水固体-聚硅氧烷混合物类可采用德国毕克化学(亚太)私人有限公司生产的BYK024；矿物油基类可采用深圳市海川化工有限公司生产的Foamster309A；
所说的纳米消光剂为未经表面处理的微粉化二氧化硅，如美国GRACE公司的C803、C805、C807或C809等中的一种；
所述分散剂为聚丙烯酸铵盐类、改性聚丙烯酸溶液类、改性聚羧酸盐类或其混合物；可采用市售产品；所述聚丙烯酸铵盐类可采用深圳市海川化工有限公司生产的Hydropalat 640A；改性聚丙烯酸溶液类可采用德国迪高化工有限公司生产的TEGO Dispers750W；改性聚羧酸盐类可采用德国巴斯夫化工有限公司生产的Sokalan PA30CL；
所述金属效果颜料可采用德国ECKART公司的HYDROLAN系列水性铝浆或德国MERK公司的高耐候系列珠光粉。金属效果颜料是在人工合成的氧化铝基材上进行处理的新型材料，通过高科技的结晶化处理，这种人工合成的氧化铝便能得到更加完美平滑的表面和狭窄的粒径分布，同时在这种基材上还包裹了反射性极强的金属氧化物，使其有闪烁效果，并且在水中可以稳定分散，其粒径为5～30μm。效果颜料还包括由天然云母薄片包裹金属氧化物(如氧化铁、二氧化钛等)薄层制成，通过光的反射、折射和干涉效应的叠加形成独特的颜色和光泽，其粒径为5～60μm，可采用MERK公司生产的牌号为Xirallic以氧化铝为基材的高彩度水晶效应颜料系列和Iriodin100银白系列的产品；
所述纳米增稠剂为纳米气相二氧化硅类或其混合物，可采用深圳纳诺科技发展有限公司生产的纳米气相二氧化硅粉体；也可采用浙江宇达化工有限公司纳米气相二氧化硅粉体。
所述防缩边剂为聚硅氧烷-聚醚共聚物类，可采用德国迪高化工有限公司生产的TEGO245；
所述流平剂为交联型有机硅聚醚丙烯酸酯类共聚物、二甲基聚硅氧烷乳液，聚硅氧烷-聚醚共聚物类可采用德国迪高化工有限公司生产的TEGOGlide450；二甲基聚硅氧烷乳液可采用TEGO Glide482；
所述防冻剂为丙二醇或乙二醇或其混合物；
所述纳米抗菌剂光触媒类纳米抗菌剂纳米TiO2或TiO2作载体的纳米氯化银离子类抗菌剂、银离子类抗菌剂或它们的混合物；抗菌剂可采用日本SR商事株式会社或鞍山市裕原塑胶抗菌剂公司生产的牌号为长福明牌IOR-250无机抗菌剂的产品，银离子类抗菌剂可采用鞍山市裕原塑胶抗菌剂公司生产的牌号为长福明牌IOR-350无机抗菌剂的产品；
所述抗粘污剂为有机物改性纳米二氧化硅类或其混合物，可采用北京首创公司的水性纳米抗污剂NZW-1(化学名称是纳米材料金属氧化物制成均匀稳定、纳米尺寸含量大于95％的纳米胶体)，也可采用深圳国达科技纳米材料中心生产的牌号为居安仕纳米防污剂的产品；
该漆还包括重量比为0～15％的经表面处理过的金属颜料，如水性铝粉浆，水性化处理后的铝浆与常规铝浆差别在于，其一是先对单个金属铝片状颜料粒子表面包覆上一层无色透明的树脂皮膜，这层膜非常薄，仅有100nm左右，因此不影响原有的金属质感，反而使金属颜料的性能得到质的飞跃；其二为增强其在水中的分散性，还要在表面进行亲水化处理，主要采用涂覆硅酸乙酯等，然后水解在其表面生成一层无机SiO2薄膜，使其更易于分散于水中。可采用市售产品，如德国ECKART公司的生产的牌号为HYDROLAN系列水性铝浆产品，其主要技术特征如下：
本发明的水性弹性金属光泽漆的制备方法包括如下步骤：
配制时，将水性树脂和防冻剂、消泡剂、分散剂、流平剂、增稠剂等各种原料分散后，然后加入抗菌剂分散均匀即可。
涂装施工时，可根据具体情况加入适量的水调节粘度，再用喷涂的方法将漆涂建筑物墙面、水泥制品表面使其全面封闭即可。
同现有技术相比较，本发明水性弹性金属光泽漆是采用水性弹性有机硅乳液、水性铝浆和效果颜料等关键材料，能够广泛用于砖石、混凝土结构的内外墙上，且成本低、金属光泽强烈、装饰效果极佳、施工简便的新型涂料，本发明的水性弹性金属光泽漆涂装系统，有效的将装饰性、抗开裂性、环保三大主题完美融合。
具体实施方式
实施例中，如无特别说明，均为重量份，所采用的原料如下：
| 实施例1 | 实施例2 | |
| 水性树脂 | 纳米水性弹性树脂 | 纳米水性弹性树脂 |
| 纳米消泡剂 | A10 | Pluriol P 2000 |
| 分散剂 | Hydropalat 640A | TEGO Dispers750W |
| 纳米氧化铁色浆 | BASF的XFAST | BASF的XFAST |
| 颜料 | HYDROLAN系列水性铝浆 | Xirallic水晶效应颜料 |
| 消光剂 | 无 | 无 |
| 增稠剂 | 纳米气相二氧化硅 | 纳米气相二氧化硅 |
| 防缩边剂 | TEGO245 | TEGO245 |
| 流平剂 | TEGO Glide450 | TEGO Glide450 |
| 防冻剂 | 丙二醇 | 丙二醇 |
| 纳米抗菌剂 | NZW-1 | |
| 纳米抗菌剂 | 纳米二氧化钛 | 纳米银离子类抗菌剂 |
| 实施例3 | 实施例4 | |
| 水性树脂 | 纳米水性弹性树脂 | 纳米水性弹性氟碳树脂 |
| 纳米消泡剂 | TEGO805 | Foamster309A |
| 分散剂 | Sokalan PA30CL | Sokalan PA30CL |
| 纳米氧化铁色浆 | BASF的XFAST | BASF的XFAST |
| 颜料 | 族兴铝业的水性铝浆 | Iriodin100珠光粉 |
| 消光剂 | C-807 | C-809 |
| 增稠剂 | 纳米气相二氧化硅 | 纳米气相二氧化硅 |
| 防缩边剂 | TEGO245 | TEGO245 |
| 流平剂 | TEGO Glide482 | TEGO Glide482 |
| 防冻剂 | 乙二醇 | 乙二醇 |
| 纳米抗菌剂 | “居安仕”纳米防污剂 | |
| 纳米抗菌剂 | 纳米氯化银离子类 | 银离子类 |
所述纳米色浆为BASF的XFAST系列中的高透明、高耐候的纳米氧化铁颜料，又有帮助涂膜吸收紫外线功能，增强耐候性。
实施例1
纳米水性弹性乳液(固体含量：50％)为52.5％、纳米消泡剂A10为0.15％、分散剂为0.15％、金属效果颜料为12.5％、纳米增稠剂为0.5％，防缩边剂为0.8％、流平剂为0.3％、纳米抗粘污剂NZW-1为4.5％、防冻剂为4％、纳米抗菌剂为1％以及水23.6％。
配制时，将纳米水性树脂和防冻剂、消泡剂、分散剂、流平剂、增稠剂等各种原料分散后，然后加入抗菌剂分散均匀即可。涂装施工时，可根据具体情况加入适量的水调节粘度，再用喷涂的方法将漆涂建筑物墙面、水泥制品表面使其全面封闭即可。
实施例2
纳米水性弹性乳液(固体含量：50％)为55％、消泡剂为0.2％、分散剂为0.4％、金属效果颜料为20％、纳米增稠剂为0.3％、防缩边剂为0.3％、流平剂为0.5％、纳米抗粘污剂0％、防冻剂为6％、纳米抗菌剂为2.3％、以及水15％。
涂装施工时，可根据具体情况加入适量的水调节粘度，再用喷涂的方法将漆涂建筑物墙面、水泥制品表面使其全面封闭即可。
实施例3
纳米水性弹性乳液(固体含量：50％)为67％、消泡剂为0.3％、分散剂为0.5％、金属效果颜料为18％、纳米增稠剂为0.2％、防缩边剂为0.4％、流平剂为0.6％、“居安仕”纳米防污剂5％、防冻剂为3％、纳米抗菌剂为2％、纳米消光剂3％以及水0％。
涂装施工时，可根据具体情况加入适量的水调节粘度，再用喷涂的方法将漆涂建筑物墙面、水泥制品表面使其全面封闭即可。
实施例4
水性丙烯酸弹性乳液(固体含量：50％)为60％、消泡剂为0.3％、分散剂为0.5％、金属效果颜料为20％、增稠剂为0.2％、防缩边剂为0.4％、流平剂为0.6％、纳米抗粘污剂NZW-1为3％、防冻剂为4％、纳米银抗菌剂为3％以及水8％。
涂装施工时，可根据具体情况加入适量的水调节粘度，再用喷涂的方法将漆涂建筑物墙面、水泥制品表面使其全面封闭即可。如需调色，则可添加0～15％BASF公司的XFAST系列中的高透明、高耐候的纳米氧化铁颜料色浆。
经检测，实施例1的水性弹性金属光泽漆的主要质量技术指标如下：
实施例2的水性弹性金属光泽漆的主要质量技术指标如下：
实施例3的水性弹性金属光泽漆的主要质量技术指标如下：
实施例4的水性弹性金属光泽漆的主要质量技术指标如下：
Claims (6)
1.纳米水性弹性金属光泽漆，其特征在于，主要组分及其重量配比包括：固体含量为50％的纳米水性树脂40％～80％，纳米消泡剂0.05％～1.5％，分散剂0.05％～3％，纳米消光剂0～15％，颜料5％～35％，纳米增稠剂0.1％～1％，防缩边剂0.1％～1％，流平剂0.1％～1％，防冻剂1％～10％，纳米抗菌剂0.5％～10％，纳米抗污剂1％～8％，水0～40％。
2.根据权利要求1所述的纳米水性弹性金属光泽漆，其特征在于，主要组分及其重量配比包括：固体含量为50％的纳米水性丙烯酸弹性乳液52.5％，消泡剂0.15％，分散剂0.15％，金属效果颜料12.5％，增稠剂0.5％，防缩边剂0.8％，流平剂0.3％，抗污剂4.5％，防冻剂4％，抗菌剂1％，水23.6％。
3.根据权利要求1或2所述的纳米水性弹性金属光泽漆，其特征在于，还包括重量比为0～10％的纳米高透明、高耐候水性色浆。
4.根据权利要求1或2所述的纳米水性弹性金属光泽漆，其特征在于，所述纳米水性树脂为改性聚丙烯酸乳液、聚丙烯酸乳液或聚丙烯酸改性氟碳乳液。
5.根据权利要求1或2所述的纳米水性弹性金属光泽漆，其特征在于，所述纳米消泡剂为纳米聚硅氧烷-聚醚共聚物乳液类、聚丙二醇类、聚乙二醇-憎水固体-聚硅氧烷混合物类、矿物油基类或其混合物，所说的纳米消光剂为未经表面处理的微粉化二氧化硅，所述分散剂为聚丙烯酸铵盐类、改性聚丙烯酸溶液类、改性聚羧酸盐类或其混合物，所述纳米增稠剂为纳米气相二氧化硅类或其混合物，所述防缩边剂为聚硅氧烷-聚醚共聚物类，所述流平剂为交联型有机硅聚醚丙烯酸酯类共聚物、二甲基聚硅氧烷乳液，聚硅氧烷-聚醚共聚物类，所述防冻剂为丙二醇或乙二醇或其混合物，所述纳米抗菌剂光触媒类纳米抗菌剂纳米TiO2或TiO2作载体的纳米氯化银离子类抗菌剂、银离子类抗菌剂或它们的混合物，所述抗粘污剂为有机物改性纳米二氧化硅类或其混合物。
6.根据权利要求1或2所述的纳米水性弹性金属光泽漆，其特征在于，该漆还包括重量比为0～15％的经表面处理过的金属颜料。