CN101549973A - 复合型混凝土高效减水剂 - Google Patents

复合型混凝土高效减水剂 Download PDF

Info

Publication number
CN101549973A
CN101549973A CNA2009100265232A CN200910026523A CN101549973A CN 101549973 A CN101549973 A CN 101549973A CN A2009100265232 A CNA2009100265232 A CN A2009100265232A CN 200910026523 A CN200910026523 A CN 200910026523A CN 101549973 A CN101549973 A CN 101549973A
Authority
CN
China
Prior art keywords
high efficiency
water reducing
reducing agent
efficiency water
concrete high
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2009100265232A
Other languages
English (en)
Other versions
CN101549973B (zh
Inventor
金卫民
陈红根
付强善
熊飞
张腊琴
高进军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changzhou Institute of building science group Limited by Share Ltd
Original Assignee
JIANGSU DINGDA MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU DINGDA MATERIALS CO Ltd filed Critical JIANGSU DINGDA MATERIALS CO Ltd
Priority to CN2009100265232A priority Critical patent/CN101549973B/zh
Publication of CN101549973A publication Critical patent/CN101549973A/zh
Application granted granted Critical
Publication of CN101549973B publication Critical patent/CN101549973B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种复合型混凝土高效减水剂，本发明是由减水母液、缓凝保塑剂、粘度调节剂、引气剂等物质组成的。本发明大幅度提高混凝土外加剂的适应性，改善混凝土的可操作性，对控制混凝土坍落度损失具有良好的效果，提高混凝土抗冻融性能。

Description

复合型混凝土高效减水剂
技术领域
本发明涉及混凝土外加剂，属于建筑材料领域，尤其涉及一种复合型混凝土高效减水剂。
背景技术
近年，混凝土技术突飞猛进，其中，最重要的技术突破是混凝土外加剂的使用。混凝土外加剂可以用于提高新拌混凝土工作性、改善硬化混凝土物理力学性能和耐久性。目前，混凝土外加剂发展的方向是高性能、多功能复合外加剂，只有复合化才能应对日益复杂的水泥组份，促进新型混凝土和新的施工工艺的发展。高效减水剂是其中最重要的一类材料。
减水作用机理研究表明，通过三种作用可以减少水泥混凝土用水量(相同工作性下)，即：分散作用、初期水化抑制作用、引气作用。
混凝土加水搅拌后，体系是不稳定的，其中水泥粒子容易絮凝成团，这样一部分游离水被包裹在絮凝的水泥粒子中间。
随着水泥行业节能减排的深入以及环保要求，混凝土中的各种废弃物掺合料日渐复杂，当前的外加剂产品，经常遇到一些适应性问题，迫切需要解决。
发明内容
为了克服上述缺陷，本发明要解决的技术问题是：提供一种高性能的复合型混凝土高效减水剂。
为了克服背景技术中存在的缺陷，本发明解决其技术问题所采用的技术方案是：一种复合型混凝土高效减水剂，所述混凝土高效减水剂包含：70～90重量％减水母液，1～6重量％缓凝保塑剂、0.1～1重量％粘度调节剂、0.1～2重量％引气剂，余量为水。
根据本发明的另一个技术方案，混凝土高效减水剂包括的减水剂为萘磺酸甲醛缩合物、醛酮磺化缩合物、氨基磺酸盐甲醛缩合物的一种或两种以上的混合物。
根据本发明的另一个技术方案，混凝土高效减水剂包括的缓凝保塑剂为柠檬酸或葡萄糖酸钠、三聚磷酸钠或六偏磷酸钠的一种或两种以上的混合物。
根据本发明的另一个技术方案，混凝土高效减水剂包括的粘度调节剂为纤维素醚、黄原胶、温轮胶的一种或两种以上的混合物。
根据本发明的另一个技术方案，混凝土高效减水剂包括的引气剂为动物废弃毛发水解物、十二烷基苯磺酸钠的一种或两种的混合物。
本发明还提供了制备混凝土高效减水剂的方法，首先，在反应釜内加入减水母液，加热搅拌升温至20℃～50℃；接着向溶液中加入缓凝保塑剂，继续搅拌；然后，向溶液中加入粘度调节剂和引气剂搅拌；最后，向溶液中加入水，搅拌调整溶液浓度，出料。
本发明相对于现有技术具有如下效果：当加入高效减水剂后，减水剂分子在水中离解成的阴离子吸附在混凝土的水泥粒子上降低了其表面能，并且在水泥粒子上形成强电场的吸附层，破坏了水泥凝聚体，释放出这部分包裹着的水而产生分散作用，进而提高了混凝土的流动性；而不同的减水剂由于具有不同分子结构而具有不同的分散作用机理，使用不同结构的减水剂复合能产生叠加效应，进一步提高减水效果。本发明大幅度提高混凝土外加剂的适应性，改善混凝土的可操作性，对控制混凝土坍落度损失具有良好的效果，提高混凝土抗冻融性能。
具体实施方式
实施例1
按下列重量比例备料
Figure A20091002652300061
首先加入萘磺酸甲醛缩合物、醛酮磺化缩合物、氨基磺酸盐甲醛缩合物，调节温度到20-50℃，搅拌十分钟，加入柠檬酸、三聚磷酸钠，继续搅拌15分钟，最后加入动物废弃毛发水解物水溶液、十二烷基苯磺酸钠和黄原胶，搅拌30分钟，静置1小时后，加水调整好浓度，再搅拌15分钟，出料。
实施例2
按下列质量比例备料
Figure A20091002652300062
Figure A20091002652300071
首先加入萘磺酸甲醛缩合物、醛酮磺化缩合物、氨基磺酸盐甲醛缩合物，调节温度到20-50℃，搅拌十分钟，加入葡萄糖酸钠、六偏磷酸钠，继续搅拌15分钟，最后加入动物废弃毛发水解物水溶液、十二烷基苯磺酸钠和黄原胶，搅拌30分钟，静置1小时后，加水调整好浓度，再搅拌15分钟，出料。
实施例3
按下列质量比例备料
Figure A20091002652300072
首先加入萘磺酸甲醛缩合物、醛酮磺化缩合物、氨基磺酸盐甲醛缩合物，调节温度到20-50℃，搅拌十分钟，加入柠檬酸、三聚磷酸钠，继续搅拌15分钟，最后加入动物废弃毛发水解物水溶液、十二烷基苯磺酸钠和黄原胶，搅拌30分钟，静置1小时后，加水调整好浓度，再搅拌15分钟，出料。
经过检测，本发明实施例1中产品的性能如下：
表一：混凝土拌合物及硬化混凝土性能
Figure A20091002652300081
注：掺量0.6％(折固量)    水泥：基准水泥。
表二：氨含量测定
  编号   项目   标准值   实测值   结论
  1   氨含量％   ≤0.1   0.00903   合格
由以上数据显示，采用本发明大幅度提高混凝土外加剂的适应性，改善混凝土的可操作性，对控制混凝土坍落度损失具有良好的效果，另外在一定程度上可以提高混凝土抗冻融性能。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。

Claims (6)

1、一种复合型混凝土高效减水剂，其特征在于：所述混凝土高效减水剂包含：70～90重量％减水母液，1～6重量％缓凝保塑剂、0.1～1重量％粘度调节剂、0.1～2重量％引气剂，余量为水。
2、如权利要求1所述的复合型混凝土高效减水剂，其特征在于：所述的减水母液为萘磺酸甲醛缩合物、醛酮磺化缩合物、氨基磺酸盐甲醛缩合物的一种或两种以上的混合物。
3、如权利要求1所述的复合型混凝土高效减水剂，其特征在于：所述的缓凝保塑剂为柠檬酸或葡萄糖酸钠、三聚磷酸钠或六偏磷酸钠的一种或两种以上的混合物。
4、如权利要求1所述的复合型混凝土高效减水剂，其特征在于：所述的粘度调节剂为纤维素醚、黄原胶、温轮胶的一种或两种以上的混合物。
5、如权利要求1所述的复合型混凝土高效减水剂，其特征在于：所述的引气剂为动物废弃毛发水解物、十二烷基苯磺酸钠的一种或两种的混合物。
6、一种制备如权利要求1所示的混凝土高效减水剂的方法，其特征在于：首先，在反应釜内加入减水母液，加热搅拌升温至20℃～50℃；接着向溶液中加入缓凝保塑剂，继续搅拌；然后，向溶液中加入粘度调节剂和引气剂搅拌；最后，向溶液中加入水，搅拌调整溶液浓度，出料。
CN2009100265232A 2009-05-11 2009-05-11 复合型混凝土高效减水剂 Expired - Fee Related CN101549973B (zh)