CN101220525A - 一步法生产超高强丙纶工业长丝的工艺 - Google Patents
一步法生产超高强丙纶工业长丝的工艺 Download PDFInfo
- Publication number
- CN101220525A CN101220525A CNA2008100187563A CN200810018756A CN101220525A CN 101220525 A CN101220525 A CN 101220525A CN A2008100187563 A CNA2008100187563 A CN A2008100187563A CN 200810018756 A CN200810018756 A CN 200810018756A CN 101220525 A CN101220525 A CN 101220525A
- Authority
- CN
- China
- Prior art keywords
- fibers
- filament yarn
- heat
- heat setting
- lax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种超高强丙纶工业长丝的生产工艺,采用纺丝和拉伸一步法,包括:切片干燥增粘、熔融纺丝、高温拉伸、热定型、卷绕成型。本发明采用创新的5对热辊拉伸热定型工艺,有效降低了纤维的拉伸速度,延长了纤维的热定型时间,使得纤维具有均匀稳定的取向结构,在保证产品物理性能的同时,优化了纺丝的状况,利用本发明方法制备的超高强丙纶工业长丝具备强度高、伸长与干热收缩合理、耐热性能好、耐冲击耐疲劳性能好的优点。
Description
技术领域
本发明公开了一种超高强丙纶工业长丝的生产工艺,属于纺织工艺技术领域。
背景技术
丙纶自问世以来,一直是作为一种性能优异的民用化纤产品在使用,广泛应用于服装、箱包、鞋帽等各个民用领域。其在工业用途上的开发只是近三十年的事情,但也取得了很大的进展。作为工业丝的一个重要的品种,丙纶强力丝也得到了较为良好的应用,因其具有强度高、收缩率低等优点,丙纶强力丝也补充广泛用于织造吊装带、线绳、拉索等方面。
目前,国内生产的一般为普通高强丙纶工业长丝,其质量如下:断裂强度为6.9~7.4cN/dtex,干热收缩率为8~13%,5%定伸长负荷<3cN/dtex。这种普通高强丝只能用来制成一般的工业产品,而且与高性能的产品相比,制造可以吊装相同负荷的产品,需要使用更多根数的原丝,对下游用户来说在经济上也是不合算的。近年来,由于高强丙纶工业长丝在军事装备等领域的广泛应用,对于其强度又提出了更高的要求,因此研制一种更高强度的丙纶工业长丝显得极为迫切。
我们分析认为,国内工业丝厂家只所以没有生产出强度≥7.2cN/dtex且伸度及干热收缩率均合乎要求的丙纶工业丝产品,究其原因有以下几点:
1、对丙纶前纺工艺的研究不够,对其相关参数的重要性未引起足够的重视
2、如果采用一步法进行生产,其牵伸倍率及相关的热盘温度的设定不合理
3、采用二步法进行生产时,对原丝UDY的平衡没有引起足够的重视。后纺牵伸工艺也不合理,尤其是未选择合理的松驰比。
发明内容
本发明的目的在于提供一种采用纺丝、拉伸一步法的超高强丙纶工业长丝的制备工艺,用该工艺制备的丙纶工业长丝具有断裂强度高、断裂伸长与干热收缩率指标合理的特点。
为实现上述目的,本发明采用的技术方案为:一种超高强丙纶工业长丝的制备工艺,采用纺丝和拉伸一步法工艺,包括:
1、PP切片干燥、增粘:PP切片投料进入干燥系统以后,本发明将切片置于一种高温、高真空度、高回流性的环境中进行除湿及增粘。由于切片实际上重新参与了一种聚合反应,因此会伴有许多副产物出现。本系统加装有一套小分子物质回收装置,可以很好地去除这些可能影响主反应的东西,以确保正常反应的实现。在整个干燥、增粘过程中,切片完全以平推流的形式在加热器内流动,所以能够保证所有的切片在加热器内停留时间的一致性,整个工艺流程中没有机械搅拌,切片在一个温和的环境下进行固相增粘,这样在增粘过程中不会产生额外的粉尘,保证了高粘切片的纯净度和粘度均匀性,整个输送系统都使用纯净的氮气作为工作介质,避免产生粉尘,螺杆入口由于氮气保护也不会发生降解。
2、熔融纺丝:高粘切片经螺杆挤出机熔融挤压,从喷丝孔喷出后,经缓冷,侧吹风冷却成型后上油。
3、高温拉伸、热定型:采用5辊牵伸工艺,两级拉伸、两级热松弛,第一步拉伸温度70~95℃,拉伸比为3.8~4.2,第二步拉伸温度125~145℃,拉伸比为1.42~1.45,总拉伸比为5.7~6.0,第一步热定型温度100~110℃,松弛比4.4%~4.6%,第二步热定型温度135~150℃,松弛比7.4~7.6%,总松弛比为11%~12%。我们通过大量试验后发现:松弛比越大,卷绕张力越小,产品的断裂强度越高,但是在两级松弛的对应关系上,如果一级松弛过大,纺况总是不理想,丝条在最后一对热辊上跳动比较明显,容易产生断头。因为在松弛过程中,由于丝条张力在后三对辊之间,逐渐减小,在几对热辊上张力传递现象比较明显,一级松弛过大,导致二级松弛过程中,丝条中张力差异变大,热辊上不同的丝束之间相对滑移,容易产生跳丝,引起断头。采用两级松弛的优点是可以延长松弛热定型的时间,使纤维中的不稳定取向结构解取向形成较大尺寸的结晶结构,但是两级松弛的配比必须合理,要尽量减少丝束张力在热辊上的传递,控制丝束在热辊上的相对滑移,因此卷绕张力与1、2级松弛比要合理搭配,才能保证稳定的纺丝状况。
4、卷绕成型:将上述纤维以800~1500米/分的的速度卷绕成型后得到成品。
本发明的有益效果为:
1、本发明的干燥、增粘一体化系统及配套工艺,可使PP切片的粘度增加到一个合适的水平,同时又可保证原料高粘切片的粘度均匀性,粘度波动控制在士0.015以内,粉尘含量可以控制在50PPM以下。而传统工艺PP切片的粘度波动一般只能控制到士0.025,粉尘含量达到100PPM以上。原料切片精确的粘度控制,极低的粉尘含量,保证了在纺丝卷绕比较苛刻的工艺条件下,仍能够保持稳定,为后道的工艺调整提供了更大的空间。
2、本发明所采用创新的5对热辊拉伸热定型工艺,与传统的2对热辊拉伸热定型相比,采用2级热拉伸,2级热定型的处理方法,有效降低了纤维的拉伸速度,延长了纤维的热定型时间,使得纤维具有均匀稳定的取向结构,在保证产品物理性能的同时,优化了纺丝的状况。而且由于热辊采用多区高频电加热方式加热,热辊表面温度均一稳定,使得工艺过程控制稳定,纤维的干热收缩率波动范围比传统工艺缩小了一倍。
3、利用本发明方法制备的超高强丙纶工业长丝具有断裂强度高、断裂伸长与干热收缩率合理、耐冲击耐疲劳性能好的优点,可以很好地满足下游用户的需要。
具体实施方式
下面通过一个具体的实施例子对本发明进行说明:
①普通聚丙烯(PP)切片经干燥、增粘后成为可以生产工业丝的工业级高粘切片;②合格的切片由中间料仓投入至螺杆,由其熔融挤压,从喷丝孔喷出后,经缓冷,侧吹风冷却成型。熔融挤出过程中,控制螺杆出口的熔体温度150℃,经过高300mm、温度330℃的缓冷装置,再通过温度20℃、相对湿度80%的侧吹风系统延迟冷却。该过程中,控制挤出速10m/min、喷丝头拉伸比65左右。③经上油、拉伸、热定型、卷绕工序,得到具有超高强度、低收缩率的成品丙纶工业丝。丝束上油后经过二步拉伸、二步热定型:第一步拉伸温度85℃,拉伸比4.0,第二步拉伸温度140℃,拉伸比1.45;第一步热定型温度100℃,松弛比4.5%,第二步热定型温度150℃,松弛比7.5%;总拉伸倍率5.8,总松弛比12%。最后制得规格555dtex/96f、强度7.8cN/dtex、伸长16%、干热收缩率5.4%的丙纶超高强丝。(一般丙纶高强丝的断裂强度≤7.4cN/dtex)
Claims (3)
1.一种超高强丙纶工业长丝的生产工艺,其特征在于:采用纺丝和拉伸一步法,包括:切片干燥增粘、熔融纺丝、高温拉伸、热定型、卷绕成型。
2.根据权利要求1所述的一种超高强丙纶工业长丝的生产工艺,其特征在于:采用5辊牵伸工艺,两级拉伸、两级热松弛,第一步拉伸温度70~95℃,拉伸比为3.8~4.2,第二步拉伸温度125~145℃,拉伸比为1.42~1.45,总拉伸比为5.7~6.0,第一步热定型温度100~110℃,松弛比4.4%~4.6%,第二步热定型温度135~150℃,松弛比7.4~7.6%,总松弛比为11%~12%。
3.根据权利要求1所述的一种超高强丙纶工业长丝的生产工艺,其特征在于:最终产品强度≥7.4cN/dtex。