Abstract

The invention discloses a luminescent resin artware, compositions of which are: 30-40 percent of unsaturated polyester resin, 15-25 percent of energy accumulation and luminescent materials, 1.0-1.5 percent of curing agent cyclohexanone peroxide, 30-40 percent of transparent glass cinnabar, 0-1.0 percent of transparent oil soluble pigment, 0.5-1.0 percent of accelerator cobalt naphthenate and appropriate amount of antioxidant. A producing method of the invention comprises the steps: 1. model producing; 2. mould producing; 3. die producing; 4, a secondary mould producing; 5. pulp producing of the luminescent resin artware; 6. casting technique; 7. demolding, repairing and color drawing; 8. obtaining finish products. The environment-friendly luminescent resin artware can be automatically luminescent with quite beautiful color and has simple producing method, low production cost, energy saving, stable product quality and reliability.

Description

Luminous resin art ware and preparation method thereof

Affiliated technical field

The present invention relates to the improvement of a kind of artwork and preparation method thereof.It is an artwork, also is the collection souvenir.Still show bright article a kind of night.

Technical background

Resin craft is a kind of common artwork, and natural legendary luminous pearl is quite rare, therefore constantly the someone proposes the technical scheme of relevant artificial legendary luminous pearl, for example mention that about " self-luminescent art wares and manufacture method thereof " self-luminescent art wares comprises the artwork body Chinese patent CN200610034865.5 number, the quality percentage composition of the component of artwork body and component is: alkaline earth aluminate luminescent powder 9～30%, glass powder 64～90%, glass fusing assistant 0-10%, the self-luminescent art wares manufacture method comprises the steps: the silica powder with selected mass fraction, feldspar, boric acid, yellow soda ash, strontium oxide, zirconium white, aluminum oxide, barium carbonate, salt of wormwood and zinc oxide, burn till at 1100～1125 ℃ and to be glass, be ground into 80～150 purpose glass powder after cooling, get luminescent powder, behind glass powder and the glass fusing assistant thorough mixing, put into the cream mould, 880～1050 ℃ of insulations 50～80 minutes, annealing, artwork of the present invention can be luminous voluntarily a little less than light the time, but its complex manufacturing technology, the cost height, the quality instability, power consumption, consumption fuel.

Summary of the invention

Task of the present invention is that a kind of luminous resin art ware and preparation method thereof will be provided, this luminous resin art ware can be luminous automatically in dark after absorbing visible light, certain illuminating effect is arranged, make the artwork color and luster more beautiful, and its making method is simple, processing ease, save energy, production cost is low, and quality product is also more stable.

Task of the present invention is to finish in such a way, it is to select unsaturated polyester resin for use, energy-saving luminous material, the solidifying agent cyclohexanone peroxide, transparent glass pearl sand, transparent oil color, and the promotor and the additive that are suitable for, they are made starchiness by certain proportioning, be cast in the hollow mould, treating promptly becomes a kind of breaking fresh ground behind the dry forming, beautiful luminous resin art ware, the constituent mass per-cent of this luminous resin art ware is: unsaturated polyester resin is 30～40%, energy-saving luminous material is 15～25%, the solidifying agent cyclohexanone peroxide is 1.0～1.5%, transparent glass pearl sand is 30～40%, transparent oil color is 0～1.0%, the promotor cobalt naphthenate is 0.5～1.0% and an amount of anti-aging agent, its making method is: analogue formation at first, model can be by the manual carving of moulding, also can utilize existing material object, make mould again, by silicon rubber and catalyzer, silicone oil, gauze and gypsum cooperate to be made, then make the mould kind, silicon rubber mould and gypsum skin are proofreaied and correct and fixed, unsaturated polyester resin is joined after the slurry of mixing silica powder pours mould into, wait to do the back demoulding, and utilize the mould kind to carry out the secondary Mold Making, make the slurry of luminous resin art ware subsequently, linking agent and solidifying agent mix according to a certain percentage, add a certain amount of 180 purpose energy-saving luminous materials and transparent granulated glass sphere sand, add promotor and anti-aging agent and form slurry, pouring technology is to pour the slurry of this luminous resin art ware into secondary to make in the mould, require constantly to shake, treat that slurry stops action when parallel with opening for feed, stand upside down to place and wait to do, to repair and colored drawing after the demoulding, select transparent oil soluble colorant during colored drawing for use.This luminous resin art ware is an environment-friendly type, and is nonpoisonous and tasteless, energy-conservation luminous, because it is handled through anti-aging, can be used as permanent collectibles, the form of this artwork is diversified, personage, animal-shaped is arranged, bonsai flower, utensil jewellery, board extension or ornament or the like are also arranged.

Description of drawings

The present invention is further illustrated below in conjunction with accompanying drawing.

Fig. 1 is a luminous resin art ware manufacture craft schema of the present invention.

Specific implementation method:

From the luminous resin art ware manufacture craft schema of Fig. 1, can know that its making method can be divided into following step:

1, Modelling: it is to be plastic with the handicraft model sculpture, and model can be moulded carving by manual, also can utilize material objects such as woodcarving, metal or ceramic.

2, Mold Making: different artworks will select for use different materials as mould, and the most frequently used is silicon rubber, and it cooperates with catalyzer, silicone oil, gauze and gypsum etc. makes mould.

3, the mould kind is made: proofread and correct and fix silicon rubber mould and gypsum are outer, immediately solidifying agent is added into unsaturated polyester resin and join in the slurry of mixing silica powder, the back one-tenth starchiness that stirs is cast in the opening for feed of mold bottom.Marginal not is gone into the limit vibrations, treats that slurry stops to shake when parallel with opening for feed, stand upside down and wait to do, and just obtains a resin craft similar to model after the demoulding, and it is polished, repairs, polishes, and just becomes a mould kind.

4, secondary Mold Making: different artworks selects for use different materials to make mould, usually make the secondary mould with material-mix mould kinds such as silicon rubber and catalyzer, silicone oil, gauze and gypsum, at this moment should suitably adjust the proportioning of silicone rubber component, make thickness, elasticity, intensity and the hardness of mould moderate.

5, the slurry of luminous resin art ware is made: select linking agent unsaturated polyester resin 30～40% for use, solidifying agent cyclohexanone peroxide 1.0～1.5%, both mix earlier, add 180 purpose energy-saving luminous materials 15～25% then, stir, the transparent granulated glass sphere sand 30～40% of same adding, granulated glass sphere sand must be transparent, and require each particle all not have corner angle, its fine granularity should be suitable with energy-accumulating luminous powder, the luminosity that so just helps product adds promotor cobalt naphthenate 0.5～1.0% and an amount of anti-aging agent subsequently, so just makes the slurry of cast light-emitting workmanship.

6, pouring technology: the slurry of luminous resin art ware is stirred into pours into behind the starchiness in the mold bottom opening for feed that secondary makes, will shake during injection, when treating that slurry rises to the opening for feed place, stop cast and shake, stand upside down to place and wait to do.

7, the demoulding, repairing and colored drawing: crude phenomenon appears in luminous resin art ware after the demoulding sometimes; incomplete position also can appear sometimes; after artwork thoroughly condenses; polish, repair, polishing or colored drawing; spray the paint vehicle of layer of transparent at last, to play the certain protection effect.Sometimes because of the needs of technology kind, certain color of palpus colored drawing must be selected transparent oil soluble colorant for use, avoids too high opacifying power, reduces the due effect of luminescent material, and generally selecting transparent oil color for use is 0～1.0%.Because environment protection luminous material itself just has multiple color, multiple coloured light, large-area substrate will be selected the light color material of high brightness for use when making multicolor luminous artwork.

8, finished product: this environment protection luminous resin craft is as long as absorb after visible light reaches capacity, night secretly can be luminous automatically more than 12 hours, it is beautiful bright-coloured, melt art and be useful for one, illuminating effect with certain limit, be convenient to people's nocturnalism, it can be used as nonvolatil collectibles after handling through anti-aging.

The moiety of this luminous resin art ware is: unsaturated polyester resin accounts for 30～40%, energy-saving luminous material accounts for 15～25%, the solidifying agent cyclohexanone peroxide accounts for 1.0～1.5%, transparent glass pearl sand accounts for 30～40%, transparent oil color accounts for 0～1.0%, and the promotor cobalt naphthenate accounts for 0.5～1.0% and an amount of anti-aging agent.This luminous resin art ware is an environment-friendly type, and its form is varied, can be personage, animal, also can be bonsai flower, can also be utensil jewellery, board extension and ornament or the like.

Claims

1. luminous resin art ware, it is characterized in that: the moiety of this artwork is that unsaturated polyester resin accounts for 30～40%, energy-saving luminous material accounts for 15～25%, the solidifying agent cyclohexanone peroxide accounts for 1.0～1.5%, transparent glass pearl sand accounts for 30～40%, transparent oil color accounts for 0～1.0%, and the promotor cobalt naphthenate accounts for 0.5～1.0% and an amount of anti-aging agent.

2. press the luminous resin art ware of claim 1 defined, the feature of its making method is: analogue formation at first, model can be by the manual carving of moulding, also can utilize existing material object, make mould again, by silicon rubber and catalyzer, silicone oil, gauze and gypsum cooperate to be made, then make the mould kind, silicon rubber mould and gypsum skin are proofreaied and correct and fixed, unsaturated polyester resin is joined after the slurry of mixing silica powder pours mould into, wait to do the back demoulding, and utilize the mould kind to carry out the secondary Mold Making, make the slurry of luminous resin art ware subsequently, linking agent and solidifying agent mix according to a certain percentage, add a certain amount of 180 purpose energy-saving luminous materials and transparent granulated glass sphere sand, add promotor and anti-aging agent and form slurry, pouring technology is that this luminous resin slurry is poured in the mould of secondary making, require constantly to shake, treat that slurry stops action when parallel with opening for feed, stand upside down to place and wait to do, to repair and colored drawing after the demoulding, select transparent oil soluble colorant during colored drawing for use.