CA2503947C - Fuel system component and method of manufacture - Google Patents

Abstract

A fuel tank that is substantially impermeable to fuel vapor has a shell with an interior for holding fuel, an opening for receiving fuel into the interior, and a fill nipple with a barrier layer. The fill nipple has an outer surface and an inner surface defining a passage extending between a pair of generally opposed ends of the fill nipple. One of the ends is attached to the shell such that the passage is aligned with the opening to allow fuel to flow through the passage and into the interior of the fuel tank. The fill nipple has an inner layer of material forming the inner surface, and an outer layer of material forming the outer surface, and has at least one intermediate layer of material forming the barrier layer. The intermediate layer is formed from a material that is different in composition from the inner and outer layers.

Description

FUEL SYSTEM COMPONENT AND
METHOD OF MANUFACTURE

Field of the Invention [0001] [0002] This invention relates generally to fuel systems, and more particularly to a fuel system component and a method of making it.

Background of the Invention [0003] It is known to blow mold fuel tanks from co-extruded six layer parisons that include inner and outer layers of HDPE, a vapor bather layer sandwiched between a pair of adhesive layers, and a layer of regrind material between one of the adhesive layers and the outer layer. Wherever the vapor barrier layer is interrupted there is a potential path through which hydrocarbons can more easily escape to the atmosphere from the fuel tank.

The vapor bather layer may be interrupted in, for example, the area of openings through the fuel tank wall and in the area of the pinch or seam formed when the parison is closed for molding.

[0004] One opening in the fuel tank is provided to receive fuel into the fuel tank through a fill pipe that is attached to the tank via a fill nipple at one end, and receives a refueling nozzle of a refueling or gas station pump at its other end. Conventional fill nipples where made of monolayer HDPE that = easily bonded to the fuel tank, but were not highly effective at reducing or inhibiting hydrocarbon permeation to the atmosphere.
[0005] In order to meet increasingly strict emission standards, largely promulgated by governmental agencies, it is desirable to form fuel tank and system components that contact liquid fuel or fuel vapor to limit fuel vapor emissions to the atmosphere.

Summary of the Invention [0006] A fuel tank that is substantially impermeable to fuel vapor has a shell with an interior for holding fuel, an opening for receiving fuel into the interior, and a fill nipple in communication with the opening and having a fuel vapor barrier layer. The fill nipple defines a passage and is attached to the shell so that the passage is aligned with the opening to allow fuel to flow through the fill nipple and into the interior of the fuel tank. The fill nipple has an inner layer of material forming the inner surface, and an outer layer of material forming the outer surface, and has at least one intermediate layer of material forming the barrier layer. The intermediate layer is formed from a material that is different in composition from the inner and outer layers and preferably resists permeation of hydrocarbons therethrough.
[0007] In one presently preferred embodiment, the fill nipple has six layers including the inner and outer layers, a vapor barrier layer disposed between two adhesive layers, and a layer of regrind material between the outer layer and one of the adhesive layers. The fill nipple is preferably thermoformed by various methods, including at least vacuum, blow or compression molding or extruded multi-layer sheets or parisons.

[00081 Some objects, features and advantages of the present invention include providing a construction for fuel tanks having a fill nipple with a substantially vapor impermeable passage between the fuel tank and a fill pipe, providing a fill nipple that can be readily attached to the shell of the fuel tank, providing a fill nipple that resists delamination, providing a high strength joint between the fill nipple and the shell of the fuel tank, providing a relatively easy and economical manufacture for the construction of the fill nipple, and providing a construction that is adaptable for various sizes and shapes of fill nipples for different fuel tanks.
100091 It should be recognized that the above list represents only some of the objects, features and advantages of the present invention, and that those skilled in the art will recognize other objects, features and advantages upon review of this disclosure in its entirety. Also, a fill nipple falling within the spirit and scope of the appended claims may achieve none, some or all of the listed advantages.
According to an aspect of the present invention, there is provided a method of manufacturing a fill nipple for a polymeric fuel tank, comprising the steps of:
providing a multi-layer preform of material including an inner layer of material, an intermediate layer of material, and an outer layer of material with the intermediate layer of material having a different composition than the inner and outer layers of material and adapted to resist permeation of hydrocarbon fuel vapors theretluough:
providing a male mold half having a cylindrical plug and an annular wall surrounding and spaced from the plug;3 providing a female mold half having a cylindrical cavity adapted to receive the plug with the preform form between them and an annular cavity complimentary with the annular wall of the male mold half;
heating the preform;
disposing the preform on the male mold half and providing a vacuum between the male mold half and the preform to form the preform on the male mold half;
closing the mold halves together to mold the preform to form a fill nipple with an annular body, an integral outwardly extending flange and the fill nipple having an outer surface and an inner surface that defines a passage extending between a pair of generally opposed ends of the annular body with the inner layer of material defining the inner surface of the annular body and a surface of the flange and the outer layer of material defining the outer surface of the annular body and a surface of the flange and the intermediate layer of material forming a barrier layer to fuel vapor in both the annular body and the flange.
According to another aspect of the present invention, there is provided a method of forming a fill nipple for a polymeric fuel tank, comprising the steps of:
providing a blow mold having at least two axially aligned adjacent mold cavities each with a shape configured to define the desired shape of a fill nipple including an outwardly extending section to define an outwardly extending flange of the fill nipple;
at least one slide associated with the outwardly extending section of each mold cavity and movable relative to its associated mold cavity;

3a disposing in the blow mold a single continuous cylindrical parison having a wall having an inner layer of a polymeric material, an outer layer of a polymeric material and a substantially continuous vapor barrier layer of a polymeric material substantially impermeable to hydrocarbon fuel vapors between and adhered to the inner and outer layers of material with the polymeric material of the vapor barrier layer having a different composition than the polymeric material of the inner and outer layers and with a portion of the parison in each of the mold cavities;
expanding the parison in each mold cavity by blow molding so that the parison wall conforms at least in part to the contour of each of the mold cavities including the outwardly extending section; and moving each slide relative to its respective mold cavity to compress together two portions of the wall of the parison in the outwardly extending section to form a flange section of the fill nipple in each mold cavity wherein each flange section includes two vapor barrier layers within such flange section and continuous with the vapor barrier layer in the wall portion of the fill nipple in the mold cavity.
Brief Description of the Drawin2s [00101 These and other objects, features and advantages of this invention will be apparent from the following detailed description of the preferred embodiments and best mode, appended claims and accompanying drawings in which:
[00111 FIG. 1 is a perspective view of a fuel innk having a fill nipple of one presently preferred embodiment of the invention;
[00121 FIG. 2 is a cross-sectional view taken generally along line 2-2 of FIG. 1; 3b = [0013] FIG. 3 is an enlarged view of the encircled area number 3 of FIG. 2;
[0014] FIG. 4 is an enlarged view of the encircled area number 4 of FIG. 2;
[0015] FIG. 5 is a perspective view illustrating mold halves used to vacuum form a multi-layer parison to form a fill nipple;
[0016] FIG. 6 is a sectional view illustrating a parison received in a mold to form a fill nipple according to another presently preferred embodiment of the invention;
[0017] FIG. 7 is a sectional view as in FIG. 6 illustrating the parison partially expanded within the mold;
[0018] FIG. 8 is a sectional view as in FIG. 6 illustrating the parison more fully expanded within the mold;
[0019] FIG. 9 is a sectional view of the parison and mold illustrating formation of a flange on the fill nipple;
[0020] FIG. 10 is a perspective view of a fill nipple formed according to presently preferred aspects of the present invention and having a check valve assembly connected thereto; and [0021] FIG. 11 is a perspective view of one half of a mold used to form a plurality of fill nipples according to further presently preferred aspects of the present invention.

Detailed Description of the Preferred Embodiments 100221 Referring in more detail to the drawings, FIG. 1 shows one presently preferred embodiment of a fuel tank 10 that has a shell 12 with an outer surface 14 and an inner surface 16 defining a cavity 18 for holding fuel.
The shell 12 has a plurality of openings like opening 15 for receiving or providing access to components, for example and without limitation a fuel pump, pressure sensor, fuel level sensor, electrical connectors (all not shown), and an opening 20 for receiving fuel into the cavity 18. A fill nipple 22 is preferably attached to the outer surface 14 of the fuel tank 10 at a joint 25 and has a passage 24 aligned with the opening 20 so that fuel can pass through the passage 24 and into the cavity 18. The construction of the fill nipple 22 resists and preferably substantially prevents fuel vapor permeation therethrough to control and reduce evaporative emissions from the fuel tank 10. In addition, the joint 25 provides a secure attachment of the fill nipple 22 to the shell and resists crack propagation or separation between the fill nipple 22 and the shell 12.
100231 As shown in FIG. 3, the shell 12 of the fuel tank 10 has inner and outer layers of material 26, 28, respectively, separated by an intermediate layer of material 30. The intermediate layer 30 is preferably bonded to the inner and outer layers 26, 28 by a pair of adhesive layers 32 each disposed on an opposed side of the intermediate layer. The adhesive layers 32 provide a resilient bond between the intermediate layer 30 and the inner and outer layers 26, 28 to resist separation of the inner and outer layers 26, 28 from the intermediate layer 30. Preferably, the inner and outer layers 26, 28 are formed from a high-density polyethylene (HDPE), while the intermediate layer or barrier layer 30 is commonly formed from a material substantially impermeable to hydrocarbons, for example and without limitation, ethylene vinyl alcohol (EVOH). In the presently preferred embodiment, a layer of regrind material 33 is provided between the outer layer 28 and the adjacent adhesive layer 32.
[0024] As sown in FIG. 2, the fill nipple 22 has a body 34 with an outer surface 36 and an inner surface 38. The inner surface 38 defines the passage 24 extending between a pair of generally opposed ends 42, 44, with one end 44 constructed for attachment to the shell 12. Preferably, the end 44 includes in part a radially outwardly extending flange 46. The flange 46 presents at least a portion of the inner surface 38 for attachment to the shell 12.
100251 As best shown in FIG. 4, the body 34 of the fill nipple 22 has an inner layer 48 of polymeric material and an outer layer 50 of polymeric material separated by an intermediate layer or barrier layer 52. Preferably, adhesive layers 54 bond the barrier layer 52 to both the inner and outer layers 48, 50. The inner and outer layers 48, 50 are preferably constructed from HDPE, while the intermediate layer 52 is preferably constructed from EVOH, and thus preferably has a similar laminate construction to that of the shell of the fuel tank 10. The barrier layer 52 is substantially continuous throughout the body 34, and can be configured adjacent the ends 42, 44 to provide optimal sealing to limit the permeation of fuel vapors into the atmosphere. In the presently preferred embodiment, a layer of regrind material 55 is disposed between the outer layer 50 and adjacent adhesive layer 54.
[0026] The end 42 of the fill nipple 22 is preferably constructed to abut a fill pipe 56, and is commonly joined to the fill pipe 56 by a coupler, for example and without limitation, a low permeability rubber hose 58.
Depending on the design requirements or necessities, the end 42 of the fill nipple 22 can have a variety of configurations. AS such, it should be recognized that the orientation of the barrier layer 52 may take on differing configurations to best suit the individual design requirements. In the embodiment shown in FIG. 2, in addition to being configured to abut the fill pipe 56, the end 42 is configured to receive a snap-in inlet check valve assembly 60 that prevents fuel in the fuel tank 10 from escaping through the file nipple 22.
[0027] To form the fill nipple 22, a thermoform process is preferably used, and could be vacuum, blow or compression or hot forming molded, using the multi-layer wall construction preferably of HDPE, EVOH, adhesive and regrind layers discussed above. Forming the fill nipple 22 in this manner provides adhesion of the HDPE inner and outer layers 48, 50 to the EVOH
barrier layer 52 through the adhesive layers 54. Therefore, the potential for permeation of fuel or fuel vapors through the multi-layer wall is greatly reduced.
[0028] In one forming process, an extruded multi-layer preform which may be any suitable shape including a generally flat sheet, preferably comprising the six layers of material previously discussed, is placed between two mold halves. With the parison placed between the two molds, the molds come together and form the parison to form the fill nipple 22. Upon bringing the two molds together, a parting line is formed, with the parting line preferably designed to expose the bather layer 52 for trimming at specified = locations at the ends 42, 44. It should be recognized that the fill nipple 22 can be trimmed while in the mold.
[0029] An alternate manufacturing process can be used that utilizes a vacuum to form the fill nipple 22. As shown in FIG. 5, a multi-layer sheet 70, preferably including the six-layers of material previously discussed, is formed between a male plug mold half 72 and a female mold half 74. The male mold half 72 includes a plug 76 that extends outwardly from a base 78 of the mold half 72 and is generally cylindrical in shape to form a generally cylindrical wall of the fill nipple 22. Preferably, an annular wall 80 extends from the base 78 surrounding and spaced from the plug 76. The annular wall 80 and the space between the annular wall 80 and the plug 76 facilitate taking up some of the sheet material as the sheet 70 is formed over the plug 76 to reduce or eliminate the formation of creases or wrinlcles as the sheet 70 is formed over the plug 76.
10030] The female mold half 74 is complementary shaped to the male mold half 72. The female mold half 74 includes a generally cylindrical cavity 82 adapted to receive the male plug 76 with a sheet 70 of material between them, and an annular cavity 84 which surrounds and is spaced from the cylindrical cavity 82 and is adapted to receive the wall 80 with the sheet 70 of material between them.
100311 To form a fill nipple 22, a heated multi-layer sheet 70 is preformed on the male mold half 72 over the plug 76 by imparting a preforming vacuum between the sheet 70 and the male mold half 72.
Thereafter, the female mold half 74 is disposed over the preformed sheet 70 and male mold half 72. When the female mold half 74 is fully received on the sheet 70 and male mold half 72, the preforming vacuum is turned off, and a finish vacuum is imparted between the female mold half 74 and the preformed sheet 70. For ease of forming, the temperature of the sheet 70 is preferably maintained between about 210 C - 230 C. Preferably, upon forming the fill nipple 22, a suitable minimum wall thickness of, for example, about 2 ¨ 4 mm is maintained so that the fill nipple 22 has adequate strength to resist fracture in use. The fill nipple 22 is then trimmed from the formed sheet 70, and any scrap material is preferably saved for use in a regrind layer of a subsequent sheet 70, fuel tank or other fuel system component.
[0032] After forming the fill nipple 22, the fill nipple 22 can be attached to the outer surface 14 of the fuel tank 10. Preferably, hot plates are used to weld or sand the inner layer 48 of the flange 46 to the outer surface of the shell 12. Generally, both the inner surface 38 of the fill nipple 22 and the outer surface 14 of the shell 12 are heated to about 200 C - 250 C. Upon heating the surfaces, the fill nipple 22, while having the passage 24 aligned with the opening 20 in the fuel tank 10, is pressed against the shell 12 of the fuel tank 10 to attach or bond the fill nipple 22 to the outer surface 14 of the shell 12. The heat applied to the outer surface 14 of the shell 12 and the inner surface 38 of the fill nipple 22 typically creates a melt zone extending into the outer surface 14 and inner surface 38 to a depth of about 1 to 1.5 mm.
[0033] With the fill nipple 22 attached to the shell 12, the check valve 60 and the fill pipe 56 are preferably assembled to the fill nipple 22. The coupler 58 preferably attaches the fill pipe 56 adjacent the end 42 of the fill nipple 22, and preferably a pair of hose clamps 62 are positioned to secure the coupler 58 to both the fill nipple 22 and the fill pipe 56, as is commonly known.
100341 It should be recognized that the fuel tank 10 and fill nipple 22 may be constructed from different materials or compositions of materials, for example and without limitation, as shown in FIG. 2, the outer layer may include carbon black to facilitate welding a cover 66 to the outer surface 36 of the flange portion 46 and to the fuel tank 10. The carbon black facilitates the use of a through-transmission infrared (TTIR) welding process to join the cover 66 to the outer surface 36 of the fill nipple 22 and surface 28 of the fuel tank 10. The cover 66 can further prevent fuel vapor from entering the atmosphere. The cover 66 is preferably formed with a similar multi-layer construction including a vapor barrier layer. The cover 66 preferably overlies the weld zone between the fill nipple 22 and the fuel tank 10.
[0035] As shown in FIGS. 6-9, an alternate embodiment fill nipple 100 preferably is formed by blow molding and includes a vapor barrier layer. The fill nipple 100 preferably is formed from a coextruded multi-layer parison of the same general construction as the fill nipple 22 including inner and outer layers 102, 104 of polymeric material, an intermediate barrier layer 106 and one or more adhesive layers 108, 110 bonding the barrier layer 106 to the inner and outer layers 102, 104. Desirably, the fill nipple 100 can be constructed of the same material of a fuel tank to which the fuel nipple 100 will be bonded, attached or otherwise coupled or connected. Desirably, the fill nipple 100 will then have the same swell and expansion characteristics, and may be readily welded or otherwise connected to the fuel tank. One or more of the layers, such as the inner and outer layers 102, 104 can be formed with a carbon filled polyethylene or similar material so that the fill nipple 100 is conductive to facilitate static discharge from the fuel tank. Additionally, the multi-layer coextruded construction of the fill nipple 100 provides desired bonding between adjacent layers and avoids separation between the layers or of the fill nipple to other assemblies, such as may occur in overmolded multi-layer components with insufficient adhesion or bonding between the layers of the component.
[0036] The fill nipple 100 includes a central, axially extending passage 112 and radially outwardly extending flange 114 to facilitate mounting the fill nipple 100 to the fuel tank. The flange 114 is preferably disposed between opposed ends 116, 118 of the fill nipple 100. One end 118 of the fill nipple is constructed and arranged to be disposed within the fuel tank at least in part, and may receive an inlet check valve assembly 120, as previously described.
The other end 116 of the fill nipple 100 may extend at least partially out of the fuel tank and preferably includes one or more barbs 122, flanges or ribs adapted to receive a fill pipe or flexible hose through which fuel passes when fuel is being added to the fuel tank. The barbs 122 facilitate press fit or friction retention of an end of a hose disposed thereon, or may be threaded or otherwise configured to receive a quick connect fitting that couples a fill pipe to the fill nipple 100.
[0037] To improve the strength of the flange 114 and improve the resistance to hydrocarbon permeation therethrough, the flange 114 may be formed from a double thickness of material so that the flange includes two of each layer 102-110 of the fill nipple material. Desirably, this provides two vapor barrier layers 106 within the flange 14 and overlying the fuel tank when the fill nipple 100 is attached to the fuel tank. Desirably, the vapor barrier layer 106 is at least substantially continuous throughout the fill nipple 100 to improve the resistance to hydrocarbon permeation therethrough.
[0038] To form the fill nipple 100, a coextruded generally cylindrical parison 130 is placed into a cavity 132 of a mold 134 and is thereafter expanded or blow molded to conform to the shape of the cavity 132. In the area of the flange 114 it may be desirable to have additional material or increased thickness of the parison 130 to provide sufficient material for the increased stretching or expanding of the material in that area of the mold cavity 132. Accordingly, it may be necessary to manipulate the parison 130 to provide additional material in the region where the flange 114 will be formed.

In one presently preferred implementation, the parison 130 is inflated or blown into the shape of the mold cavity 132 as generally shown in FIGS. 8 and 9, wherein FIG. 8 shows an initial stage of the blow molding process and FIG. 9 shows the parison 130 generally completely expanded within the mold cavity 132. After the parison 130 is completely expanded within the mold cavity 132, an annular hollow or space is formed in the area where the flange 114 will be formed. In this region, the parison 130 has a pair of radially outwardly extending walls 136 interconnected by an axially extending portion 138 of the parison providing a generally U-shaped flange in cross section. Thereafter, one or more slides 140 carried by the mold 134 are moved to engage at least one of the walls 136 of the flange 114 and to compress the walls 136 of the flange 114 together. Thus, the flange 114 is formed from two wall portions of the parison 130 and has two of each layer of the parison 130 construction as previously described. The flange 114 may take on generally any size and shape as desired to facilitate attaching the fill nipple 100 to a fuel tank.
[0039] As best shown in FIG. 10, according to another presently preferred implementation, a plurality of fill nipples 100 may be formed simultaneously in a mold 134'. And this embodiment, the mold 134' includes a plurality of mold cavities 132 with each mold cavity 132 preferably axially aligned with adjacent mold cavities 132 so that a continuous or single elongated parison 130' can be disposed in the mold 134' with a portion of the parison 130' in each of the mold cavities 132. When the mold 134' is closed to blow mold the parison 130, the parison 130 may be separated generally between each of the mold cavities 132, or parison 130 may be separated into discrete sections prior to closing the mold 134', or formed fill nipples 100 may be initially interconnected and separated after the blow molding process, as desired. Guide rods 142 may be provided in the mold to guide and control the movement of the slides 140 for each mold cavity 132. The slides 40 may be individually actuated, or linked together for simultaneous movement, as desired, to form the flange 114 of each fill nipple 100 as previously described.
The slides 140 may include generally U-shaped heads 144 each coupled to a rod 142 and arranged to selectively engage one-half of the circumference of a flange 114. One U-shaped head 144 may be disposed on one side of the flange 114 in each cavity 132 so that when the slides 140 are moved the heads 144 engage their respective flanges 114 and compress them against an opposed mold section.
[0040] Many modifications and variations of the present invention will be apparent to those of ordinary skill in the art. The invention is defined by the claims that follow.

Claims (3)

1. A method of manufacturing a fill nipple for a polymeric fuel tank, comprising the steps of:
providing a multi-layer preform of material including an inner layer of material, an intermediate layer of material, and an outer layer of material with the intermediate layer of material having a different composition than the inner and outer layers of material and adapted to resist permeation of hydrocarbon fuel vapors therethrough:
providing a male mold half having a cylindrical plug and an annular wall surrounding and spaced from the plug;
providing a female mold half having a cylindrical cavity adapted to receive the plug with the preform between them and an annular cavity complimentary with the annular wall of the male mold half;
heating the preform;
disposing the preform on the male mold half and providing a vacuum between the male mold half and the preform to form the preform on the male mold half;
closing the mold halves together to mold the preform to form a fill nipple with an annular body, an integral outwardly extending flange and the fill nipple having an outer surface and an inner surface that defines a passage extending between a pair of generally opposed ends of the annular body with the inner layer of material defining the inner surface of the annular body and a surface of the flange and the outer layer of material defining the outer surface of the annular body and a surface of the flange and the intermediate layer of material forming a barrier layer to fuel vapor in both the annular body and the flange.14

2. The method of claim 1 wherein said molding step further includes after the step of closing the mold halves together, the steps of discontinuing the vacuum between the male mold half and the preform, and providing a vacuum between the female mold half and the preform to form the fill nipple.

3. A method of forming a fill nipple for a polymeric fuel tank, comprising the steps of:
providing a blow mold having at least two axially aligned adjacent mold cavities each with a shape configured to define the desired shape of a fill nipple including an outwardly extending section to define an outwardly extending flange of the fill nipple;
at least one slide associated with the outwardly extending section of each mold cavity and movable relative to its associated mold cavity;
disposing in the blow mold a single continuous cylindrical parison having a wall having an inner layer of a polymeric material, an outer layer of a polymeric material and a substantially continuous vapor barrier layer of a polymeric material substantially impermeable to hydrocarbon fuel vapors between and adhered to the inner and outer layers of material with the polymeric material of the vapor barrier layer having a different composition than the polymeric material of the inner and outer layers and with a portion of the parison in each of the mold cavities;
expanding the parison in each mold cavity by blow molding so that the parison wall conforms at least in part to the contour of each of the mold cavities including the outwardly extending section; and moving each slide relative to its respective mold cavity to compress together two portions of the wall of the parison in the outwardly extending section to form a flange section of the fill nipple in each mold cavity wherein each flange section includes two vapor barrier layers within such flange section and continuous with the vapor barrier layer in the wall portion of the fill nipple in the mold cavity.