BG108305A

BG108305A - Paint

Info

Publication number: BG108305A
Application number: BG108305A
Authority: BG
Inventors: Roman Magdina; Bohuslav Jacko
Original assignee: Moles Technology,A.S.
Priority date: 2001-04-02
Filing date: 2003-10-30
Publication date: 2004-09-30
Also published as: CZ20032967A3; EA200301085A1; SK13572003A3; EP1401965A2; AU2002250748A1; JP2004532914A; HUP0402272A3; EA006144B1; PL365338A1; CN1274771C; SK285850B6; UA76747C2; PL207152B1; HUP0402272A2; CN1511184A; HK1065059A1; WO2002079329A3; WO2002079329A2; JP4274799B2; CZ305026B6

Abstract

The invention relates to a paint with extended shelf life, finding application in industry, in the house and in other fields. The paint protects to a considerable extent from fire a surface of which the paint is applied, and in many cases increases the corrosion resistance. The paint has a film-binding component, a color-producing component and a fire-retarding component adapted to at least substantially protect from fire a surface of which the paint is applied. The fire-retardant component comprises at last one phosphate or its derivative, such as melamine, polyphosphate, and ammonium polyphosphate. The production method comprises the provision of a film-forming binder component, color-producing component and mixing of the compounds with some of dried powder components and the addition of a fire-retarding component. 11 claims

Description

Област на приложениеField of application

Най-общо настоящото изобретение се отнася до бои и методи за получаването на бои.In general, the present invention relates to paints and methods for producing paints.

Предшестващо състояние на техникатаBACKGROUND OF THE INVENTION

Боите са добре познати и широко използвани в промишлеността, бита и други области на съвременния живот. Известните бои обикновено съдържат филмообразуващо свързващо вещество, осигуряващо образуването на филм и адхезията към субстарта, върху който се нанася боята, като включват още и ю компонент за получаване на цвета, напр. оцветители и други оцветяващи вещества.Paints are well known and widely used in industry, everyday life and other areas of modern life. Known paints typically contain a film-forming binder to provide film formation and adhesion to the substrate on which the paint is applied, and also include a color-forming component, e.g. coloring agents and other coloring matter.

Известните бои осигуряват определена защита от вредното атмосферно въздействие на повърхностите, върху които се нанасят, и им придават определени цветове, но не ги предпазват адекватно от последствията от 15 пожар. Поради това е препоръчително този недостатък да бъде отстранен.Known paints provide some protection against the harmful atmospheric effects of the surfaces they are applied to and give them certain colors, but do not adequately protect them from the effects of 15 fires. It is therefore advisable to remedy this deficiency.

Същност на изобретениетоSUMMARY OF THE INVENTION

В съответствие с това цел на настоящото изобретение е осигуряването на боя, която не притежава недостатъците на тези от предшестващото състояние на техниката, както и метод за получаване на боя.Accordingly, it is an object of the present invention to provide a paint that does not have the disadvantages of those of prior art, as well as a method of producing paint.

За да се изпълнят тези цели и целите, които ще станат очевидни по-долу, един от признаците на настоящото изобретение е най-общо казано боя,In order to accomplish these goals and those which will become apparent below, one of the features of the present invention is generally paint,

CD съдържаща филмообразуващо свързващо вещество, компонент за получаване на цвят и забавящо горенето вещество, адаптирано поне значително да предпазва от пожар повърхността, върху която се нанася боята.A CD comprising a film-forming binder, a color-producing component and a flame retardant adapted at least substantially to protect the paint-applied surface from fire.

Когато боята е направена в съответствие с настоящото изобретение, в допълнение към конвенционалните характеристики за една боя, тя значително предпазва повърхността на субстрата, върху който се нанася, от последствията на пожар, като в много случаи засилва устойчивостта срещу корозия и животът на боята се удължава.When the paint is made in accordance with the present invention, in addition to the conventional characteristics of a paint, it significantly protects the surface of the substrate to be applied from the effects of fire, in many cases enhancing corrosion resistance and prolonging the life of the paint .

Съгласно друг признак на изобретението забавящото горенето вещество включва поне фосфат или негово производно съединение като мел амин полифосфат, амониев полифосфат.According to another feature of the invention, the flame retardant comprises at least phosphate or a derivative thereof such as chalk amine polyphosphate, ammonium polyphosphate.

2-сь2-s

Съгласно друг признак на изобретението забавящото горенето вещество включва меламин или е производно съединение, избрано от групата включваща меламин цианурат, меламин борат, меламин полифосфат, меламин дифосфат, меламин пирофосфат и меламин фосфат.According to another feature of the invention, the flame retardant comprises melamine or is a derivative selected from the group comprising melamine cyanurate, melamine borate, melamine polyphosphate, melamine diphosphate, melamine pyrophosphate and melamine phosphate.

Според първи аспект на изобретението, в боята или други състави за покритие, като забавяща горенето добавка се използва меламин полифосфат или негов подходящ химичен еквивалент, за предпочитане в комбинация с други познати забавящи горенето химикали. Ако се използва в комбинация с други забавители на горенето, меламин полифосфатът 10 молсе да присъства в количества от 5% до 75% от цялото забавящоAccording to a first aspect of the invention, melamine polyphosphate or a suitable chemical equivalent thereof, preferably in combination with other known flame retardant chemicals, is used in paint or other coating compositions. When used in combination with other flame retardants, melamine polyphosphate 10 moles should be present in amounts of 5% to 75% of the total retardant

горенето вещество. В общия повърхностен състав забавящото горенето вещество може да замести определена част от компонентите във вид на сух прах, които иначе биха присъствали в повърхностния състав в количества от около 5 до 40 т. процента от компонентите във вид на сух прах, както са били в оригиналната боя или в други състави за покритие.burning substance. In the total surface composition, the flame retardant may replace a certain portion of the dry powder components that would otherwise be present in the surface composition in amounts of about 5 to 40 percent by weight of the dry powder components as they were in the original surface composition. paint or other coating compositions.

Според друг аспект на изобретението, забавящото горенето вещество както е описани тук, може да се използва като съставна добавка, която предпазва бои и покрития, включително продукти, спиращи горенето, забавители на горенето, като в същото време по 20 същество поддържа физическите свойства на покритието.According to another aspect of the invention, the flame retardant substance as described herein can be used as a compound additive that protects paints and coatings, including flame retardants, flame retardants, while maintaining the physical properties of the coating at 20 .

Добавката има три основни компонента: (1) 10 до 65 т. % подходящ карбонизиращ агент като пентаеритритол; (2) 10 до 65 т. % подходящ разбухвател като меламин; и (3) 5 до 75 т. % меламин полифосфат или негов подходящ химичен еквивалент.The additive has three main components: (1) 10 to 65% by weight of a suitable carbonizing agent such as pentaerythritol; (2) 10 to 65% by weight of a suitable melamine enhancer; and (3) 5 to 75% by weight of melamine polyphosphate or a suitable chemical equivalent thereof.

В съответствие с горните насоки, забавящото горенето вещество в целия състав на повърхността може да замести компонентите във вид на сух прах в количества от около 5 до 40 т. % от компонетните във вид на сух прах, както е било в оригиналната боя или други състави за покритие. Прибавя се подходящо количество от тиксотропни химикали, зо за да се осигури забавянето на горенето на боята или друго покритие с подходящ вискозитет.In accordance with the above guidelines, the flame retardant throughout the surface composition can replace the dry powder components in amounts of about 5 to 40% by weight of the dry powder components as in the original paint or other compositions to cover. An appropriate amount of thixotropic chemicals is added to ensure the retardation of the paint combustion or other coating of suitable viscosity.

Настоящото изобретение предлага и метод за получаване на боя, включващ етапите на осигуряване на филмообразуващо свързващо вещество и компонент за получаване на цвят, смесване на компонентите с някои допълнителни компоненти във вид на сух прах и прибавяне на забавящо 5 горенето вещество, което замества сухия прахообразен компонент.The present invention also provides a method of producing a paint comprising the steps of providing a film-forming binder and a color-forming component, mixing the components with some additional components in the form of a dry powder, and adding a flame retardant 5 to replace the dry powder component .

Новите признаци, които се смятат за признаци на това изобретение, са представени подробно в приложените патентни претенции. Самото изобретение обаче, както като състав, така и като метод на действие заедно с допълнителните му цели и предимства може да бъде най-добре разбрано от Ю следващото описание на конкретни изпълнения.The new features which are considered to be features of this invention are presented in detail in the appended claims. However, the invention itself, both as a composition and as a method of action, together with its additional aims and advantages, can best be understood by the following description of specific embodiments.

Описание на предпочитаните изпълненияDescription of preferred embodiments

В съответствие с настоящото изобретение се осигурява боя, съдържаща филмообразуващо свързващо вещество, компонент за получаване на цвят и забавящо горенето вещество, адаптирано да предпазва поне значително от 15 пожар повърхността, върху която се нанася боята.In accordance with the present invention, a paint is provided comprising a film-forming binder, a color-producing component and a flame retardant adapted to protect at least substantially 15 fires the surface on which the paint is applied.

Композицията има три основни компонента: (1) подходящ карбонизиращ агент, например пентаеритритол, моно-пентаеритритол или ди-пентаеритритол, като пентаеритритол; (2) подходящ разбухвател като меламин или негови производни съединения като 20 меламин цианурат, меламин борат, меламин полифосфат, меламин дифосфат, меламин пирофосфат и меламин фосфат; и (3) фосфат или негови производни съединения като меламин полифосфат, амониев полифосфат, меламин полифосфат или техен подходящ химичен еквивалент. Първият компонент, пентаеритритол, присъства в 25 количества от 10 до 65 т. % от добавката за забавяне на горенето.The composition has three main components: (1) a suitable carbonizing agent, for example pentaerythritol, mono-pentaerythritol or dipentaerythritol, such as pentaerythritol; (2) a suitable excipient such as melamine or its derivatives such as 20 melamine cyanurate, melamine borate, melamine polyphosphate, melamine diphosphate, melamine pyrophosphate and melamine phosphate; and (3) phosphate or derivatives thereof such as melamine polyphosphate, ammonium polyphosphate, melamine polyphosphate, or a suitable chemical equivalent thereof. The first component, pentaerythritol, is present in 25 amounts of from 10 to 65% by weight of the additive for flame retardant.

Вторият компонент, меламин, присъства в количества от 10 до 65 т. % от добавката за забавяне на горенето. Третият компонент, меламин полифосфат или негов еквивалент, присъства в количества от 5 до 75 т. % от добавката за забавяне на горенето.The second component, melamine, is present in amounts of from 10 to 65% by weight of the additive to slow down the burning. The third component, melamine polyphosphate or equivalent, is present in amounts of from 5 to 75% by weight of the additive to slow down the combustion.

Забавящото горенето вещество включва фосфат или негово производно съединение като меламин полифосфат, амониев полифосфат.The flame retardant includes phosphate or a derivative thereof such as melamine polyphosphate, ammonium polyphosphate.

Забавящото горенето вещество може да включва и меламин или негово производно съединение като меламин цианурат, меламин борат, меламин полифосфат, меламин дифосфат, меламин пирофосфат и меламин фосфат.The flame retardant may also include melamine or a derivative thereof such as melamine cyanurate, melamine borate, melamine polyphosphate, melamine diphosphate, melamine pyrophosphate and melamine phosphate.

В боята съгласно настоящото изобретение забавящото горенето вещество 5 може да включва карбонизиращ агент, например пентаеритритол, монопентаеритритол или ди-пентаеритритол, разбухвател, например меламин и допълнителен агент, избран от групата вещества посочени по-горе.In the paint according to the present invention, the flame retardant 5 may include a carbonizing agent, for example pentaerythritol, monopentaerythritol or dipentaerythritol, a blowing agent, for example melamine and an additional agent selected from the group of substances mentioned above.

Както беше споменато по-горе, разбухващата се боя защитава субстрата, към който се прилага чрез оформяне на изолиращ защитен 10 слой върху него при излагането му на високи температури. В химическата реакция на свързване, която се появява при висока температура, меламин полифосфатът действа като разпенващ агент, пентаеритритолът е полихидритен алкохол, който действа като въглероден или карбонизиращ агент, а меламинът действа като 15 разбухвател източник на газ. Очаква се, че други карбонизиращи агенти и разбухватели източници на газ могат да бъдат използвани в замяна на пентаеритритол или меламин, но всяка такава замяна може да бъде емпирично оценена, за да задоволи производителите на състава, така че такава замяна не влияе неблагоприятно върху забавянето на горенето или 20 физическите качества на боята или други покрития.As mentioned above, the swollen paint protects the substrate to which it is applied by forming an insulating protective 10 layer on it when exposed to high temperatures. In the chemical coupling reaction that occurs at high temperature, melamine polyphosphate acts as a blowing agent, pentaerythritol is a polyhydric alcohol that acts as a carbon or carbonizing agent, and melamine acts as a 15 gas source. It is anticipated that other carbonizing agents and gas source enhancers may be used in exchange for pentaerythritol or melamine, but any such replacement may be empirically evaluated to satisfy the manufacturers of the composition so that such a substitution does not adversely affect the delay in the composition. combustion or 20 physical qualities of paint or other coatings.

Ясно е, че освен филмообразуващите вещества (свързващи материали и пластификатори), които са един от основните компоненти на боите, отразяващи се на трайността, блясъка, еластичността, адхезията, гъвкавостта и твърдостта, а също в допълнение на оцветителите, които могат да са цветниIt is clear that, in addition to film-forming substances (binders and plasticizers), which are one of the main components of paints, affecting durability, gloss, elasticity, adhesion, flexibility and hardness, and in addition to colorants that can be colored

Зсь прахове неразтворими в свързващото вещество и разтворими в цветните агенти за създаване на цветови варианти и възможност за оцветяване на повърхността, боята може да включва и летливи вещества, които в комбинация със свързващите компоненти в повечето случаи създават разтвор или т.нар. основен лак (политура). В боята могат да се включат и добавки, които са “помощни” химикали, придаващи й конкретни характеристики.If the powder is insoluble in the binder and soluble in the color agents to create color variants and the ability to color the surface, the paint may also include volatile substances which, in combination with the binder components, in most cases create a solution or so-called. base varnish (polish). Additives may also be included in the paint, which are "auxiliary" chemicals that give it specific characteristics.

Съгласно изобретението боята може да се получи чрез метод, включващ етапи на осигуряване на филмообразуващо свързващо вещество и компонент за получаване на цвят, смесване на тези компоненти с допълнителни сухи ю прахообразни компоненти и прибавяне на забавящо горенето вещество, заместващо сухия прахообразен компонент.According to the invention, paint can be obtained by a method comprising the steps of providing a film-forming binder and a color-forming component, mixing these components with additional dry powder components and adding a flame retardant to replace the dry powder component.

По-специално, пъл нителите като например калциев карбонат и титанов диоксид се заместват със забавящото горенето вещество. Възможно е разбира се, да се заменят и малки количества от филмообразуващото вещество.In particular, fillers such as calcium carbonate and titanium dioxide are replaced by the retardant. Of course, small amounts of the film-forming substance may also be replaced.

Боята съгласно настоящото изобретение е илюстрирана със следните примери:The paint according to the present invention is illustrated by the following examples:

Пример 1аExample 1a

Епоксидна боя - два компонента без забавяне на горенето веществоEpoxy paint - two components without delay of burning substance

Част А Part A Функция Function Материал Material Тегло в % Weight in% Течна епоксидна Liquid epoxy Epotuf 37-127 Epotaph 37-127 32.80 Филмообразуващо 32.80 Film-forming смола resin свързващо вещество binder Разредител Thinner Бензил алкохол Benzyl alcohol 3.75 Филмообразуващо 3.75 Film-forming Дисперсант Dispersant BYKP-104S BYKP-104S свързващо вещество 0.32 Добавки binder 0.32 Additives Противократерна Anticancer BYKA-530 BYKA-530 0.15 Добавки 0.15 Additives добавка Добавка за add - on add - on BYK501 BYK501 0.16 Добавки 0.16 Additives втечняване Основен оцветител liquefaction Main colorant Titanox 2020 Titanox 2020 12.3 Компонент за 12.3 Component for Пълнител Filler Microna 7 Microna 7 получаване на цвят 33.99 Сух прахообразен getting color 33.99 Dry powder

компонентcomponent

ЧастБPartB

Полиамин втвърдител РазредителPolyamine Hardener Thinner

Epotuf37-801Epotuf37-801

Бензил алкохолBenzyl alcohol

13.32 Филмообразуващо свързващо вещество13.32 Film-forming binder

3.21_Филмообразуващо _____свързващо вещество 100.003.21_Film-forming _____ binder 100.00

Пример 16Example 16

Епоксидна боя - два компонента със забавяне на горенетоEpoxy paint - two components with slow burning

Част АPart A

ФункцияFunction

Течна епоксидна смолаLiquid epoxy resin

РазредителThinner

ДисперсантDispersant

Противократерна добавкаAnticancer supplement

Добавка за втечняване Основен оцветителLiquid additive Basic coloring agent

ПълнителFiller

РазбухвателEnhancer

КатализаторCatalyst

МатериалMaterial

Epotuf 37-127Epotaph 37-127

Бензил алкохолBenzyl alcohol

BYKP-104SBYKP-104S

BYKA-53OBYKA-53O

BYK 501BYK 501

Titanox 2020Titanox 2020

Microna 7Microna 7

МеламинMelamine

Меламин полифосфатMelamine polyphosphate

Тегло в %Weight in%

32.80 Филмообразуващо свързващо вещество32.80 Film-forming binder

3.75 Филмообразуващо свързващо вещество3.75 Film-forming binder

0.32 Добавки0.32 Additives

0.15 Добавки0.15 Additives

0.16 Добавки0.16 Additives

12.3 Компонент за получаване на цвят12.3 Color Component

18.99 Сух прахообразен компонент18.99 Dry powder component

5.25 Забавящо горенето вещество5.25 Combustion retardant

4.50 Забавящо горенето вещество4.50 Combustion retardant

КарбонизаторCarbonizer

ПентаеритритолPentaerythritol

ЧастБPartB

Полиамин втвърдител Epotuf 37-801Polyamine hardener Epotuf 37-801

Разредител Бензил алкохолThinner Benzyl alcohol

3.21 Филмообразуващо ______свързващо вещество 100.003.21 Film-forming ______ binder 100.00

Смесване на Част А и Част Б в обемно съотношение 4:1 ©Mixing Part A and Part B in a 4: 1 volume ratio ©

Боята със съдържание на забавящо горенето вещество (FR) от 10 доPaint with FR content from 10 to

т. % от общото тегло на боята и със състав, посочен по-долу в таблицата, беше приготвена по същия начин.% by weight of the total weight of the paint and the composition shown below in the table was prepared in the same way.

Състав на FR [тегло в %] Composition of FR [weight%] Съдържание от FR компонентите от общото тегло на боята [%] Content of FR components of total paint weight [%] Мел амин Mel amine 27 27 2.70 2.70 3.24 3.24 3.78 3.78 4.59 4.59 5.40 5.40 Пентаеритритол Pentaerythritol 30 30 3.00 3.00 3.60 3.60 4.20 4.20 5.10 5.10 6.00 6.00 Меламин Полифосфат Melamine Polyphosphate 43 43 4.30 4.30 5.16 5.16 6.02 6.02 7.31 7.31 8.60 8.60 Общо Total 100 100 10 10 12 12 14 14 17 17 20 20

Пример 2аExample 2a

Алкиден грунд без забавящо горенето веществоAlkyd primer without combustion

ФункцияFunction

Средно маслен алкид 80%Medium oil alkyd 80%

Разтворител Дисперсант Тиксотропи Контрол на огъване Кобалтов изсушителSolvent Dispersant Thixotropes Bending Control Cobalt Dryer

Калциев изсушителCalcium dehydrator

МатериалMaterial

Beckosol АА-203Beckosol AA-203

Неорганичен алкохол Соев лецитин Тиксатрол ST Post 4Inorganic alcohol Soy lecithin Thixatrol ST Post 4

12°/о Кобалтов нафтенат 6% Калциев нафтенат12% Cobalt naphthenate 6% Calcium naphthenate

Тегло в °/оWeight in% / o

31.48 Филмообразуващо свързващо вещество31.48 Film-forming binder

21.94 Летливо вещество21.94 Volatile matter

0.13 Добавки0.13 Additives

0.32 Тиксотроп0.32 Thixotropes

0.44 Тиксотроп0.44 Thixotrop

0.08 Добавки0.08 Additives

0.78 Добавки0.78 Additives

Вещество против образуване на ципа Основен оцветителZipper Substance Main colorant

Метил Етил Кетоксин Tipure 902Methyl Ethyl Ketoxin Tipure 902

Оцветител- Nicron 604 пълнителColoring - Nicron 604 filler

0.33 Добавки0.33 Additives

21.38 Компонент за получаване на цвят21.38 Color Generation Component

23.12 Сух прахообразен компонент23.12 Dry powder component

100.00100.00

Пример 26Example 26

Алкиден грунд със забавяне на горенетоAlkyd primer with combustion retardation

ФункцияFunction

Средно маслен алкид 80%Medium oil alkyd 80%

РазтворителSolvent

ДисперсантDispersant

ТиксотропиThixotropes

Контрол на огъванеBending control

Кобалтов изсушителCobalt dehumidifier

Калциев изсушителCalcium dehydrator

Оцветител-пълнителColoring agent

РазбухвателEnhancer

КатализаторCatalyst

КарбонизаторCarbonizer

МатериалMaterial

Beckosol АА-203Beckosol AA-203

Неорганичен алкохол Соев лецитин Тиксатрол STInorganic alcohol Soy lecithin Thixatrol ST

Post 4Post 4

12% Кобалтов нафтенат12% Cobalt naphthenate

6% Калциев нафтенат Метил Етил Кетоксин6% Calcium Naphthenate Methyl Ethyl Ketoxin

Tipure 902Tipure 902

Nicron 604Nicron 604

МеламинMelamine

Меламин полифосфатMelamine polyphosphate

ПентаеритритолPentaerythritol

Тегло в %Weight in%

21.94 Летливо вещество21.94 Volatile matter

0.13 Добавки0.13 Additives

0.32 Тиксотроп0.32 Thixotropes

0.44 Тиксотроп0.44 Thixotrop

0.08 Добавки0.08 Additives

0.78 Добавки0.78 Additives

0.33 Добавки0.33 Additives

8.12 Сух прахообразен компонент8.12 Dry powder component

5.25 Забавящо горенето _____вещество5.25 Burning _____ substance

100.00100.00

20 т. % от общото тегло на боята и със състав, посочен по-долу в таблицата, беше приготвена по същия начин.20% by weight of the total weight of the paint and the composition shown below in the table was prepared in the same way.

Състав на FR [тегло в %] Composition of FR [weight%] Съдържание от FR компонентите от общото тегло на боята [%] Content of FR components of total paint weight [%] Меламин Melamine 15 15 1.50 1.50 1.80 1.80 2.10 2.10 2.55 2.55 3.00 3.00 Пентаеритритол Pentaerythritol 35 35 3.50 3.50 4.20 4.20 4.90 4.90 5.95 5.95 7.00 7.00

Меламин Полифосфат Melamine Polyphosphate 50 50 5.00 5.00 6.00 6.00 7.00 7.00 8.50 8.50 10.00 10.00 Общо Total 100 100 10 10 12 12 14 14 17 17 20 20

Пример ЗаExample For

Уретанов емайл без забавящо горенето веществоUrethane enamel without combustion

ФункцияFunction

Маслено-модифициран полиуретан ДисперсантOil-modified polyurethane Dispersant

Тиксотроп РазтворителThixotrop Solvent

Основен оцветителPrimary colorant

Кобалтов изсушителCobalt dehumidifier

Калциев изсушителCalcium dehydrator

Циркониев изсушителZirconium dehumidifier

Вещество против образуване на ципаZipper

Пример 36Example 36

МатериалMaterial

Spenkel F47-M-60Spenkel F47-M-60

Nuosperes 657Nuosperes 657

Bentone SD-1Bentone SD-1

Неорганичен алкохолInorganic alcohol

Tronox CR-828Tronox CR-828

12% Кобалтов нафтенат 6% Калциев нафтенат12% Cobalt naphthenate 6% Calcium naphthenate

24% Циркониев нафтенат24% Zirconium naphthenate

Exkin #2Exkin # 2

Тегло в %Weight in%

60.00 Филмообразуващо свързващо вещество60.00 Film-forming binder

0.46 Добавки0.46 Additives

0.95 Тиксотроп0.95 Thixotropes

6.18 Летливо вещество6.18 Volatile substance

29.05 Компонент за получаване на цвят29.05 Color Component

0.38 Добавки0.38 Additives

1.26 Д обавки1.26 E shoes

1.61 Добавки1.61 Additives

0.11 Добавки0.11 Additives

100.00100.00

Уретанов емайл със забавяне на горенетоUrethane flame retardant enamel

Функция МатериалFunction Material

Маслено-модифициран Spenkel F47-M-60 полиуретанOil-modified Spenkel F47-M-60 polyurethane

Дисперсант Nuosperes 657Nuosperes 657 dispersant

Тегло в %Weight in%

50.10 Филмообразуващо свързващо вещество50.10 Film-forming binder

0.46 Добавки0.46 Additives

ТиксотропThixotropes

РазтворителSolvent

Основен оцветителPrimary colorant

Кобалтов изсушител Калциев изсушител Циркониев изсушителCobalt Dryer Calcium Dryer Zirconium Dryer

Вещество против образуване на ципаZipper

РазбухвателEnhancer

КатализаторCatalyst

КарбонизаторCarbonizer

Bentone SD-1 Неорганичен алкохол Тгопох CR-828Bentone SD-1 Inorganic alcohol Tgopoh CR-828

12% Кобалтов нафтена· 6% Калциев нафтенат 24% Циркониев нафтенат12% Cobalt naphtha · 6% Calcium naphthenate 24% Zirconium naphthenate

Exkin #2Exkin # 2

МеламинMelamine

Меламин полифосфатMelamine polyphosphate

ПентаеритритолPentaerythritol

0.95 Тиксотроп0.95 Thixotropes

6.18 Летливо вещество6.18 Volatile substance

23.95 Компонент за получаване на цвят23.95 Color Component

0.38 Добавки0.38 Additives

1.26 Добавки1.26 Additives

1.61 Добавки1.61 Additives

0.11 Добавки0.11 Additives

0.000.00

Боята със съдържание на забавящо горенето вещество (FR) от 10 до 20 т. % от общото тегло на боята и със състав, посочен по-долу в таблицата, беше приготвена по същия начин.Paint with a FR content of 10 to 20% by weight of the total weight of the paint and the composition shown below in the table was prepared in the same way.

Състав на FR [тегло в %] Composition of FR [weight%] Съдържание от FR компонентите от общото тегло на боята [%] Content of FR components of total paint weight [%] Меламин Melamine 30 30 3.00 3.00 3.80 3.80 4.20 4.20 5.10 5.10 6.00 6.00 Пентаеритритол Pentaerythritol 32 32 3.20 3.20 3.84 3.84 4.48 4.48 5.44 5.44 6.40 6.40 Меламин Полифосфат Melamine Polyphosphate 38 38 3.80 3.80 4.56 4.56 5.32 5.32 6.46 6.46 7.60 7.60 Общо Total 100 100 10 10 12 12 14 14 17 17 20 20

Пример 4аExample 4a

Снемаемо винилово покритие без забавяне на горенето веществоRemovable vinyl coating without delay of burning

Функция МатериалFunction Material

Винилова смола с Ucar YVNS голямо молекулно теглVinyl resin with Ucar YVNS high molecular weight

Винилова смола с Ucar VYHD малко молекулно теглоVinyl resin with Ucar VYHD low molecular weight

Пластификатор Диоктил фталатPlasticizer Dioctyl phthalate

Тегло в %Weight in%

15.32 Филмообразуващо свързващо вещество15.32 Film-forming binder

7.66 Филмообразуващо свързващо вещество7.66 Film-forming binder

5.97 Филмообразуващо5.97 Film-forming

Бял оцветителWhite colorant

TiPure 902TiPure 902

РазредителThinner

Толуен свързващо веществоToluene binder

6.50 Компонент за получаван на цвят6.50 Color Receive Component

22.20 Летливо вещество22.20 Volatile matter

Кетонов разтворител Метил изобутил кепи 20.95 Летливо веществоKetone solvent Methyl isobutyl droplets 20.95 Volatile substance

Ацетатен разтворите Бутил ацетатAcetate solutions Butyl acetate

21.40 Летливо вещество21.40 Volatile matter

100.00100.00

Пример 46Example 46

Снемаемо винилово покритие със забавящо горенето веществоRemovable vinyl coating with flame retardant

Функция Function Материал Material Тегло в % Weight in% Винилова смола с Vinyl resin c UcarYVNS UcarYVNS 7.38 Филмообразуващо 7.38 Film-forming голямо молекулно тегло Винилова смола с high molecular weight Vinyl resin c UcarVYHD UcarVYHD свързващо вещество 3.69 Филмообразуващо binder 3.69 Film-forming малко молекулно тегло Пластификатор low molecular weight Plasticizer Диоктил фталат Dioctyl phthalate свързващо вещество 2.88 Филмообразуващо binder 2.88 Film-forming Бял оцветител White colorant TiPure 902 TiPure 902 свързващо вещество 6.50 Компонент за получаваш binder 6.50 Receive Component Разредител Кетонов разтворител Ацетатен разтворител Разбухвател Thinner Ketone solvent Acetate solvent Excipient Толуен Метил изобутил кетон Бутил ацетат Меламин Toluene Methyl isobutyl ketone Butyl acetate Melamine на цвят 22.20 Летливо вещество 20.95 Летливо вещество 21.40 Летливо вещество 5.25 Забавящо горенето in color 22.20 Volatile matter 20.95 Volatile matter 21.40 Volatile matter 5.25 Burning slow Катализатор Catalyst Меламин полифосфат Melamine polyphosphate вещество 4.50 Забавящо горенето substance 4.50 Burning slow Карбонизатор Carbonizer Пентаеритритол Pentaerythritol вещество 5.25 Забавящо горенето substance 5.25 Burning slow

веществоsubstance

100.00100.00

Състав на FR [тегло в %] Composition of FR [weight%] Съдържание от FR компонентите от общото тегло на боята [%[ Content of FR components of total paint weight [% [ Меламин Melamine 38 38 3.80 3.80 4.56 4.56 5.32 5.32 Пентаеритритол Pentaerythritol 37 37 3.70 3.70 4.44 4.44 5.18 5.18 Меламин Полифосфат Melamine Polyphosphate 25 25 2.50 2.50 3.00 3.00 3.50 3.50 Общо Total 100 100 10 10 12 12 14 14

Пример 5аExample 5a

Нитроцелулозен сатенен лак без забавяне на горенето веществоNitrocellulose satin lacquer without burning

Фунцкия Материал Тегло в %Functional Material Weight in%

Нитроцелулоза с ниско Нитроцелулоза 1/4 sec 8.78 Филмообразуващо молекулно тегло Нитроцелулоза сLow-cellulose nitrocellulose 1/4 sec 8.78 Molecular weight film-forming Nitrocellulose with

Нитроцелулоза 1/2 sec високо молекулно теглоNitrocellulose 1/2 sec high molecular weight

Разредител ТолуенThinen Thinner

Вторичен разтворите/ Изопропанол Бърз разтворител Бутил ацетат Бавен разтворител РМ ацетат Кокосов алкид 70% в ВА Букозол 91-470 свързващо веществоSecondary solutions / Isopropanol Quick solvent Butyl acetate Slow solvent PM acetate Coconut alkyd 70% in VA Buccosol 91-470 binder

0.13 Филмообразуващо свързващо вещество0.13 Film-forming binder

13.75 Летливо вещество 2.70 Летливо вещество 27.60Летливо вещество13.75 Volatile substance 2.70 Volatile substance 27.60Volotile substance

2.70 Летливо вещество2.70 Volatile matter

23.52 Филмообразуващо23.52 Film-forming

ПластификаторPlasticizer

Бял оцветителWhite colorant

Агент за напречно свързване Катализатор за напречно свързванеCross-linking agent Catalyst for cross-linking

ДиоктилфталатDioctyl phthalate

TiPure 902TiPure 902

Cymel 303Cymel 303

Фосфат на бутиловата киселина свързващо веществоButyl acid phosphate binder

1.34 Филмообразуващо свързващо вещество1.34 Film-forming binder

12.00 Компонент за получаване на цвят12.00 Color Gain Component

6.95 Филмообразуващо свързващо вещество 0.53 Добавки6.95 Film-forming Binder 0.53 Additives

100.00100.00

Пример 56Example 56

Нитроцелулозен сатенен лак със забавяне на горенетоNitrocellulose, satin lacquer, flame retardant

Фунцкия Funkia Материал Material Тегло в % Weight in% Нитроцелулоза с ниско Low cellulose nitrocellulose Нитроцелулоза 1/4 sec Nitrocellulose 1/4 sec 6.75 Филмообразуващо 6.75 Film-forming молекулно тегло Нитроцелулоза с високо Нитроцелулоза 1/2 sec molecular weight High Cellulose Nitrocellulose 1/2 sec свързващо вещество 0.10 Филмообразуващо binder 0.10 Film-forming молекулно тегло Разредител molecular weight Diluent Толуен Toluene свързващо вещество 13.75 Летливо вещество binder 13.75 Volatile matter Вторичен разтворител Secondary solvent Изопропанол Isopropanol 2.70 Летливо вещество 2.70 Volatile matter Бърз разтворител Fast solvent Бутил ацетат Butyl acetate 27.60 Летливо вещество 27.60 Volatile matter Бавен разтворител Slow solvent РМ ацетат PM acetate 2.70 Летливо вещество 2.70 Volatile matter Кокосов алкид 70% в ВА Букозол 91-470 Coconut alkyd 70% in VA Bukozol 91-470 12.78 Филмообразуващо 12.78 Film-Making Пластификатор Plasticizer Диоктилфталат Dioctyl phthalate свързващо вещество 1.34 Филмообразуващо binder 1.34 Film-forming Бял оцветител White colorant TiPure 902 TiPure 902 свързващо вещество 9.80 Компонент за получаване binder 9.80 Receiving component Агент за напречно Agent for the transverse Cymel 303 Cymel 303 на цвят 6.95 Филмообразуващо in color 6.95 Film-forming свързване Катализатор за connection Catalyst for Фосфат на бутиловата Butyl phosphate свързващо вещество 0.53 Добавки binder 0.53 Additives напречно свързване Разбухвател cross connection Enhancer киселина Меламин acid melamine 5.25 Забавящо горенето 5.25 Burning slow Катализатор Catalyst Меламин полифосфат Melamine polyphosphate вещество 4.50 Забавящо горенето substance 4.50 Burning slow Карбонизатор Carbonizer Пентаеритритол Pentaerythritol вещество 5.25 Забавящо горенето substance 5.25 Burning slow

веществоsubstance

100.00100.00

Състав на FR [тегло в %] Composition of FR [weight%] Съдържание от FR компонентите от общото тегло на боята [%] Content of FR components of total paint weight [%] Меламин Melamine 35 35 3.50 3.50 4.20 4.20 4.90 4.90 Пентаеритритол Pentaerythritol 38 38 3.80 3.80 4.56 4.56 5.32 5.32

Меламин Полифосфат Melamine Polyphosphate 27 27 2.70 2.70 3.24 3.24 3.78 3.78 Общо Total 100 100 10 10 12 12 14 14

Πρ им ep 6αEpρ im ep 6α

Латексна боя цвят “Слонова кост” без забавяне на горенето веществоIvory latex paint without delay of burning substance

Функция Function Материал Material Тегло в % Weight in% Разтворител Solvent Вода Water 25.3 Летливо вещество 25.3 Volatile substance Дисперсант Dispersant Калиев Potassium 0.22 Добавки 0.22 Additives Повърхностно активно Surface active триполифосфат Igepal СО-630 tripolyphosphate Igepal CO-630 0.84 Добавки 0.84 Additives вещество Обезпенител substance Defuse Колоид 643 Colloid 643 0.23 Добавки 0.23 Additives Контрол за повърхностна Пропилен гликол Control of surface Propylene glycol 2.77 Добавки 2.77 Additives увлажняване Биоцид moisturizing Biocide Nuosept 95 Nuosept 95 0.38 Добавки 0.38 Additives Бял оцветител White colorant Tipure 902 Tipure 902 18.11 Компонент за 18.11 Component for Пълнител Filler Microna 7 Microna 7 получаване на цвят 15.00 Сух прахообразен getting color 15.00 Dry powder Целулозен сгъстител Cellulose thickener Bernocol E411 FQ Bernocol E411 FQ компонент 0.32 Тиксотроп component 0.32 Thixotropes Латексен полимер 55% Latex polymer 55% Rovace 9100 Rovace 9100 34.88 Филмообразуващо 34.88 Film-forming Корекция на pH PH adjustment 28% Амониев 28% Ammonium свързващо вещество 0.13 Добавки binder 0.13 Additives Свързан сгъстител Bound thickener хидроокис Акризол RM-5 Acrizol RM-5 hydroxide 1.82 Тиксотроп 1.82 Thixotropes

100.00100.00

Пример 66Example 66

Латексна боя цвят “Слонова кост” със забавяне на горенетоLatex ivory color with flame retardant

ФункцияFunction

РазтворителSolvent

ДисперсантDispersant

Повърхностно активно веществоSurfactant

ОбезпенителDeflector

Контрол за повърхностно увлажняванеSurface Moisture Control

БиоцидBiocide

МатериалMaterial

ВодаWater

Калиев триполифосфатPotassium tripolyphosphate

Igepal СО-630Igepal CO-630

Колоид 643Colloid 643

Пропилея гликолPropyl glycol

Nuosept 95Nuosept 95

Тегло в %Weight in%

25.3 Летливо вещество25.3 Volatile substance

0.22 Добавки0.22 Additives

0.84 Добавки0.84 Additives

0.23 Добавки0.23 Additives

2.77 Добавки2.77 Additives

0.38 Добавки0.38 Additives

1а 1a Бял оцветител White colorant Tipure 902 Tipure 902 18.11 Компонент за получаване на цвят 18.11 Component for getting color Разбухвател Enhancer Меламин Melamine 5.25 Забавящо горенето вещество 5.25 Combustion retardant Катализатор Catalyst Меламин полифосфат Melamine polyphosphate 4.5 Забавящо горенето вещество 4.5 Combustion retardant Карбонизатор Carbonizer Пентаеритритол Pentaerythritol 5.25 Забавящо горенето вещество 5.25 Combustion retardant Целулозен сгъстител Cellulose thickener Bemocol Е411 FQ Bemocol E411 FQ 0.32 Тиксотроп 0.32 Thixotropes Латексен полимер 55% Latex polymer 55% Rovace 9100 Rovace 9100 34.88 Филмообразуващо свързващо вещество 34.88 Film-forming binder Корекция на pH PH adjustment 28% Амониев хидроокис 28% ammonium hydroxide 0.13 Добавки 0.13 Additives Свързан сгъстител Bound thickener Акризол RM-5 Acrisol RM-5 1.82 Тиксотроп 100.00 1.82 Thixotropes 100.00

Метод за получаванеMethod of preparation

Горните примери са приготвени във високоскоростно диспергиращо устройство “Cowles”. Следвайки нормалната технология за получаване на боя, прахообразните материали се диспергират при висока скорост в подходящо 5 количество на носителя, съдържащ дисперсанти и умокрящи агенти.The above examples were prepared in a high-speed Cowles disperser. Following normal paint production technology, the powder materials are dispersed at high speed in an appropriate amount of carrier containing dispersants and wetting agents.

След приключване на диспергирането скоростта се намалява, добавя се балансиращо количество от носителя към останалите ингредиенти на състава.After the dispersion is complete, the rate is reduced, a balancing amount of carrier is added to the other ingredients of the composition.

Боята със съдържание на FR от 10 до 20 процента тегло от общото тегло на боята и със състав, посочен по-долу в таблицата, беше 10 приготвена по същия начин.Paint with a content of FR from 10 to 20 percent by weight of the total weight of the paint and with the composition shown below in the table was 10 prepared in the same way.

Състав на FR [тегло в %>] Composition of FR [weight in%>] Съдържание от FR компонентите от общото тегло на боята [%] Content of FR components of total paint weight [%] Меламин Melamine 36 36 3.60 3.60 4.32 4.32 5.04 5.04 Пентаеритритол Pentaerythritol 35 35 3.50 3.50 4.20 4.20 4.90 4.90 Меламин Полифосфат Melamine Polyphosphate 29 29 2.90 2.90 3.48 3.48 4.06 4.06 Общо Total 100 100 10 10 12 12 14 14

Λ * 1Λ * 1

Пример 7αExample 7α

Акрилно прахово покритие без забавяне на горенетоAcrylic powder coating without delay of combustion

Функция МатериалFunction Material

Глицидил акрилен Fine-Clad A-207-SA полимерGlycidyl acrylic Fine-Clad A-207-SA polymer

Агент за напречно Додеканедиоична свързване киселинаDodecanedioic Acid Crosslinking Agent

Добавка за втечняване Silwet L-7500Liquid additive Silwet L-7500

Бял оцветител Титанокс 2020Titanox 2020 white color

Оцветител-пълнител Nicron 604Nicron 604 coloring agent

Тегло в %Weight in%

56.90 Филмообразуващо свързващо вещество56.90 Film-forming binder

10.83 Филмообразуващо свързващо вещество10.83 Film-forming binder

0.33 Добавки0.33 Additives

16.94 Компонент за получаване на цвят16.94 Component for producing color

15.00 Сух прахообразен _____компонент15.00 Dry powder _____ component

100.00100.00

Ί6Ί6

Акрилно прахово покритие със забавяне на горенетоAcrylic powder coating with flame retardant

ПримерAn example

ФункцияFunction

Глицидил акрилен полимерGlycidyl acrylic polymer

Агент за напречно свързванеCross-linking agent

Добавка за втечняване Бял оцветителLiquid additive White colorant

РазбухвателEnhancer

КатализаторCatalyst

КарбонизаторCarbonizer

МатериалMaterial

Fine-Clad A-207-SAFine-Clad A-207-SA

Додеканедиоична киселинаDodecanedioic acid

Silwet L-7500Silwet L-7500

Титанокс 2020Titanox 2020

МеламинMelamine

Меламин полифосфатMelamine polyphosphate

ПентаеритритолPentaerythritol

Тегло в %Weight in%

0.33 Добавки0.33 Additives

100.00100.00

Температура на изпичане: 20 минути при 150°С.Baking temperature: 20 minutes at 150 ° C.

Метод на получаванеMethod of production

Прахообразните вещества се смесват с помощта на смесител “W & РThe powders are mixed using a W&P mixer

ZSK-30”.ZSK-30 ”.

Температура на цилиндъра 60/80°С.Cylinder temperature 60/80 ° C.

Скорост на въртене: 250 оборота в минута.Speed: 250 rpm.

Класификация: 100% чрез мрежа 200.Classification: 100% through 200 network.

Както се вижда от представените по-горе примери, забавящата горенето част от боята съгласно изобретението е съставена от три забавящи горенето ю вещества, а именно меламин, меламин полифосфат и пентаеритритол. Общото количество на тези забавящи горенето вещества не може да надвишава 15 % от теглото на боята.As can be seen from the examples presented above, the flame retardant part of the invention is composed of three flame retardants, namely melamine, melamine polyphosphate and pentaerythritol. The total amount of these flame retardants may not exceed 15% by weight of the paint.

Ясно е, че всеки от горните елементи или два или повече взети заедно могат да намерят полезно приложение и в други видове субстанции и методи различни от тези, описани по-горе.It is clear that any of the above elements or two or more taken together may find useful applications in other types of substances and methods other than those described above.

Макар че изобретението е илюстрирано и описано като изпълнение на боя и метод за получаването й, то не се ограничава до описаните по-горе подробности, тъй като могат да бъдат направени редица модификации и структурни промени без да има отделяне от духа на изобретението.Although the invention is illustrated and described as an embodiment of a paint and a method for its preparation, it is not limited to the details described above, since a number of modifications and structural changes can be made without departing from the spirit of the invention.

Без по-нататъшни анализи, горното изложение разкрива така пълно същността на това изобретение, че други, прилагайки сегашните знания, могат лесно да го адаптират за различни приложения без да пропускат характеристики, които от позицията на предшестващото състояние на техниката съставляват съществени признаци на това изобретение от общ и специфичен характер.Without further analysis, the foregoing discloses so thoroughly the essence of this invention that others, applying the present knowledge, can easily adapt it for various applications without missing the features which, from the prior art, are essential features of this invention of general and specific character.

Това, за което се претендира, че е ново и се желае да бъде защитено, е изложено в приложените патентни претенции.What is claimed to be new and desired to be protected is set forth in the appended claims.

Claims

Patent Claims

1. Surface paint in a pre-selected color, comprising:

film-forming binder to form a film of paint on the surface;

a color-producing component for imparting a pre-selected surface color;

a flame retardant adapted to protect the surface from the effects of a fire, wherein the flame retardant comprises melanin, pentaerythritol and melamine polyphosphate; and additional components including filler materials and additive.

Paint according to claim 1, characterized in that the retardant comprises 35 wt.% Melamine, 35 wt.% Pentaerythritol and 30 wt.% Melamine polyphosphate.

3. The paint according to claim 1, characterized in that the retardant comprises 5.25 wt.% Melamine, 5.25 wt.% Pentaerythritol and 4.50 wt.% Melamine polyphosphate of the total weight.

Paint according to claim 1, characterized in that the retardant does not exceed 15% by weight of the paint.

C20

5. The paint according to claim 1, the following components:

Epoxy paint - two components

Part A

Function

Liquid epoxy resin

Thinner

Dispersant

Anticancer supplement

Liquid additive

A basic colorant characterized in that it contains

Weight in% from 25 to 39 Film-forming binder 2.9 to 4.5 Film-forming binder 0.29 to 0.35 Additives 0.1 to 0.2 Additives 0.14 to 0.18 Additives 9 to 15 Color-forming component

Filler

Enhancer

Catalyst

Carbonizer

Part B

Polyamine hardener

Thinner

6. Paint according to claim the following components:

Alkyd primer

Function

Medium oil alkyd 80%

Solvent

Dispersant

Thixotropes

Bending control

Cobalt dehumidifier

Calcium dehydrator

Zipper

Primary colorant

Coloring agent

Enhancer

Catalyst

Carbonizer

5

7. The paint according to claim of the following components:

Urethane enamel

Function

Oil-modified polyurethane

Dispersant

Thixotropes

Solvent 16 to 23 Dry Powder Component 3 to 7 Combustion Retardant 2.5 to 6.5 Retardant Combustion 3 to 7 Combustion Retardant 11 to 15 Film Binder 2.6 to 3.9 Film Binder characterized in that contains

Weight in% from 25 to 38 Film-forming binder from 17 to 26 Volatile substance from 0.12 to 0.14 Additives from 0.25 to 0.38 Thixotrop from 0.35 to 0.53 Thixotrop from 0.07 to 0.09 Additives from 0.65 to 0.82 Additives from 0.27 to 0.38 Additives from 17 to 25 6.5 to 9.7 color component Dry powder component 3 to 7 Burning delay 2.5 to 6.5 Burning delay 3 to 7 Burning slower

1, characterized in that it contains

Weight in% from 40 to 60 Film-forming binder from 0.41 to 0.5 Additives from 0.75 to 1.15 Thixotropic from 5 to 7 Volatile substance

Primary colorant

Cobalt dehumidifier

Calcium dehydrator

Zirconium dehumidifier

Zipper

Enhancer

Catalyst

Carbonizer

8. The paint according to claim of the following components:

from 21 to 28 Component for producing a color from 0.34 to 0.42 Additives from 1.13 to 1.38 Additives from 1.45 to 1.77 Additives from 0.10 to 0.12 Additives from 3 to 7 Slow-down substance 2.5 to 6.5 Slow-burn substance 3 to 7 Slow-burn substance

1, characterized in that it contains

Removable vinyl coating

Function

High molecular weight vinyl resin

Low molecular weight vinyl resin

Plasticizer

White colorant

Thinner

Ketone solvent

Acetate solvent

Enhancer

Catalyst

Carbonizer

Weight in% from 6 to 8.5 Film-forming binder 3.3 to 4.0 Film-forming binder 2.6 to 3.2 Film-forming binder 5.2 to 7.8 Color-forming component 17.7 to 26.6 Volatile 16.8 to 25.1 Volatile 17.1 to 25.7 Volatile substance 3 to 7 Combustion retardant 2.5 to 6.5 Retardant 3 to 7 Combustion retardant

9.

Paint according to claim

1, characterized in that it contains

5 the following components:

Nitrocellulose satin lacquer

Function

Low molecular weight nitrocellulose

High molecular weight nitrocellulose

Thinner

Secondary solvent

Fast solvent

Weight in% from 6 to 7.4 Film-forming binder from 0.09 to 0.11 Film-forming binder from 12.3 to 15.1 Volatile substance 2.4 to 3 Volatile substance 22.2 to 33 Volatile substance

Slow solvent Coconut alkyd 70% in VA

Plasticizer

White colorant

Crosslinking Agent

Catalyst for cross-linking

Catalyst

Carbonizer f

10. The paint according to claim 1, the following components:

Ivory latex paint

Function

Solvent

Dispersant

Surfactant

Deflector

Surface wetting control

Biocide

White coloring book with

Enhancer

Catalyst

Carbonizer

Cellulose thickener

Latex polymer 55%

PH correction Bound thickener

11. The paint according to claim 1,

5 the following components:

Acrylic powder coating

Function 2.4 to 3 Volatile matter 10.3 to 15.2 Film-forming binder 1.2 to 1.5 Film-forming binder 7.8 to 11.7 Color-forming component 6.3 to 7.6 Film-forming binder 0.5 to 0.6 Additives 3 to 7 Burning retardant from 2.5 to 6.5 Combustion retardant 3 to 7 Combustion retardant characterized in that it contains

Weight in% from 20 to 30 Volatile substance from 0.2 to 0.24 Additives from 0.7 to 0.9 Additives from 0.2 to 0.25 Additives from 2.5 to 3 Additives from 0.35 to 0.42 Additives from 14.5 to 21.7 Component for producing a color from 3 to 7 Slow-burning substance 2.5 to 6.5 Combustion retardant 3 to 7 Combustion retardant 0.28 to 0.35 Thixotrope 27.9 to 41.8 Film-forming binder 0.11 to 0.0.15 Additives 1.6 to 2 Thixotrope characterized in that it contains

Weight in% s