Effect of Annealing Temperature on Microstructure and Mechanical Properties of Fe50Mn25Co10Cr10Ti5 High Entropy Alloy

  • Original Research Article
  • Published:
Journal of Materials Engineering and Performance Aims and scope Submit manuscript

Abstract

To explore wear-resistant and high-strength materials, Fe50Mn25Co10Cr10Ti5 high entropy alloy with non-equal atomic ratio was designed and prepared. The influence of annealing temperature on wear and mechanical properties was researched. The results show that the as-cast Fe50Mn25Co10Cr10Ti5 alloy presents hypereutectic microstructure which is composed of primary Laves phases and eutectic structure with FCC plus Laves phases. The main wear mechanism is contained fatigue wear, oxidation wear and abrasive wear. The microstructure and wear mechanism of the alloy have not changed significantly after annealing. With the increasing annealing temperature, the hardness and volume wear loss of the alloy present a tendency of going up first and then going down. The friction coefficient has not changed significantly after annealing 900 and 950 °C, while the alloy has increased significantly after annealing 1000 °C. In addition, the mechanical properties of Fe50Mn25Co10Cr10Ti5 alloy have not significantly improved after annealing 900 and 950 °C, while the compression rate and fracture strength have increased from 8.3 to 11.2% and 1493.2 to 1710.2 MPa, respectively, after annealing 1000 °C. The research results could provide experimental references to modify the wear and mechanical performance by using the annealing process.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Subscribe and save

Springer+ Basic
$34.99 /Month
  • Get 10 units per month
  • Download Article/Chapter or eBook
  • 1 Unit = 1 Article or 1 Chapter
  • Cancel anytime
Subscribe now

Buy Now

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Q.F. Wu, Z.J. Wang, T. Zheng, D. Chen, Z.S. Yang, J.J. Li, J.J. Kai, and J.C. Wang, A Casting Eutectic High Entropy Alloy with Superior Strength-Ductility Combination, Mater. Lett., 2019, 253, p 268–271. https://doi.org/10.1016/j.matlet.2019.06.067

    Article  CAS  Google Scholar 

  2. J.W. Yeh, S.K. Chen, S.J. Lin, J.Y. Gan, T.S. Chin, T.T. Shun, C.H. Tsau, and S.Y. Chang, Nanostructured High Entropy Alloys with Multiple Principal Elements: Novel Alloy Design Concepts and Outcomes, Adv. Eng. Mater., 2004, 6(5), p 299–303. https://doi.org/10.1002/adem.200300567

    Article  CAS  Google Scholar 

  3. D.B. Miracle and O.N. Senkov, A Critical Review of High Entropy Alloys and Related Concepts, Acta Mater., 2017, 122, p 448–511. https://doi.org/10.1016/j.actamat.2016.08.081

    Article  CAS  Google Scholar 

  4. X. Yang and Y. Zhang, Prediction of High Entropy Stabilized Solid-Solution in Multi-component Alloys, Mater. Chem. Phys., 2012, 132(2–3), p 233–238. https://doi.org/10.1016/j.matchemphys.2011.11.021

    Article  CAS  Google Scholar 

  5. S. Guo, Q. Hu, C. Ng, and C.T. Liu, More than Entropy in High Entropy Alloys: Forming Solid Solutions or Amorphous Phase, Intermetallics, 2013, 41, p 96–103. https://doi.org/10.1016/j.intermet.2013.05.002

    Article  CAS  Google Scholar 

  6. J.Y. Aguilar-Hurtado, A. Vargas-Uscategui, K. Paredes-Gil, R. Palma-Hillerns, M.J. Tobar, and J.M. Amado, Boron Addition in a Non-Equiatomic Fe50Mn30Co10Cr10 alloy Manufactured by Laser Cladding: Microstructure and Wear Abrasive Resistance, Appl. Surf. Sci., 2020, 515, p 146084. https://doi.org/10.1016/j.apsusc.2020.146084

    Article  CAS  Google Scholar 

  7. Y.Y. Chen, T. Duval, U.D. Hung, J.W. Yeh, and H.C. Shih, Microstructure and Electrochemical Properties of High Entropy Alloys—A Comparison with Type-304 Stainless Steel, Corros. Sci., 2005, 47(9), p 2257–2279. https://doi.org/10.1016/j.corsci.2004.11.008

    Article  CAS  Google Scholar 

  8. C.J. Tong, M.R. Chen, J.W. Yeh, S.J. Lin, S.K. Chen, T.T. Shun, and S.Y. Chang, Mechanical Performance of the AlxCoCrCuFeNi High-Entropy Alloy System with Multiprincipal Elements, Metall. Mater. Trans. A, 2005, 36(5), p 1263–1271. https://doi.org/10.1007/s11661-005-0218-9

    Article  Google Scholar 

  9. Z. Wu, H. Bei, F. Otto, G.M. Pharr, and E.P. George, Recovery, Recrystallization, Grain Growth and Phase Stability of a Family of FCC-Structured Multi-Component Equiatomic Solid Solution Alloys, Intermetallics, 2014, 46, p 131–140. https://doi.org/10.1016/j.intermet.2013.10.024

    Article  CAS  Google Scholar 

  10. R. Tewari, B. Vishwanadh, and V.K. Vasudevan, Formation of the Laves Phase in Nb-Ti-Cr-Si-X-Based Alloys, Trans. Indian Inst. Met., 2022, 75, p 931–939. https://doi.org/10.1007/s12666-022-02530-8

    Article  CAS  Google Scholar 

  11. Y.J. Zhou, Y. Zhang, Y.L. Wang, and G.L. Chen, Solid Solution Alloys of AlCoCrFeNiTix with Excellent Room-Temperature Mechanical Properties, Appl. Phys. Lett., 2007, 90, p 181904. https://doi.org/10.1063/1.2734517

    Article  CAS  Google Scholar 

  12. X.F. Wang, Y. Zhang, Y. Qiao, and G.L. Chen, Novel Microstructure and Properties of Multicomponent CoCrCuFeNiTix Alloys, Intermetallics, 2007, 15, p 357–362. https://doi.org/10.1016/j.intermet.2006.08.005

    Article  CAS  Google Scholar 

  13. P. Cui, Y.M. Ma, L.J. Zhang, M.D. Zhang, J.T. Fan, W.Q. Dong, P.F. Yu, G. Li, and R.P. Liu, Effect of Ti on Microstructures and Mechanical properties of High Entropy Alloys based on CoFeMnNi System, Mater. Sci. Eng. A, 2018, 737, p 198–204. https://doi.org/10.1016/j.msea.2018.09.050

    Article  CAS  Google Scholar 

  14. M.Y. Wu, R.C. Setiawan, and D.Y. Li, Benefits of Passive Element Ti to the Resistance of AlCrFeCoNi High-Entropy Alloy to Corrosion and Corrosive Wear, Wear, 2022, 492, p 204231. https://doi.org/10.1016/j.wear.2021.204231

    Article  CAS  Google Scholar 

  15. S.S. Nene, K. Liu, M. Frank, R.S. Mishra, R.E. Brennan, K.C. Cho, Z. Li, and D. Raabe, Enhanced Strength and Ductility in a Wear Stir Processing Engineered Dual Phase High Entropy Alloy, Sci. Rep., 2017, 7, p 16167. https://doi.org/10.1038/s41598-017-16509-9

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  16. L.A. Chen, Y.S. Lu, Y.T. Lin, and Y.L. Lee, Preparation and Characterization of Cerium-Based Conversion Coating on a Fe50Mn30Co10Cr10 Dual-Phase High-Entropy Alloy, Appl. Surf. Sci., 2004, 2021(562), p 150200. https://doi.org/10.1016/j.apsusc.2021.150200

    Article  CAS  Google Scholar 

  17. Y. Liu, J. Tu, L. Deng, C.H. Wang, and J.R. Luo, Characteristics of Thermal- and Strain-Induced ε-Martensite in Fe50Mn30Co10Cr10 Multi-component Alloy: Effect of Grain Size, Mater. Charact., 2021, 171, p 110817. https://doi.org/10.1016/j.matchar.2020.110817

    Article  CAS  Google Scholar 

  18. D. Kong, J. Guo, R.W. Liu, X.H. Zhang, Y.P. Song, Z.X. Li, F.J. Guo, X.F. Xing, Y. Xu, and W. Wang, Effect of Remelting and Annealing on the Wear Resistance of AlCoCrFeNiTi0.5 High Entropy Alloys, Intermetallics, 2019, 114, p 106560. https://doi.org/10.1016/j.intermet.2019.106560

    Article  CAS  Google Scholar 

  19. Z. Li, K.G. Pradeep, Y. Deng, D. Raabe, and C.C. Tasan, Metastable High-Entropy Dual-Phase Alloys Overcome the Strength-Ductility Trade-off, Nature, 2016, 534(7606), p 227–230. https://doi.org/10.1038/nature17981

    Article  CAS  PubMed  Google Scholar 

  20. J. Wang, J.L. Chai, H.P. Zhang, P.F. Tai, C. Liu, L.J. Niu, W.H. He, W.Y. Huang, R. Shu, L.H. Luo, W.P. Li, Y.B. Zhu, C.F. Yao, and P.F. Gao, Microstructure Investigations of Fe50Mn30Co10Cr10 Dual-Phase High–Entropy Alloy under Fe Ions Irradiation, J. Nucl. Mater., 2021, 552, p 153006. https://doi.org/10.1016/j.jnucmat.2021.153006

    Article  CAS  Google Scholar 

  21. W.N. Jiao, H. Jiang, D.X. Qiao, J.Y. He, H.L. Zhao, Y.P. Lu, and T.J. Li, Effects of Mo on Microstructure and Mechanical Properties of Fe2Ni2CrMox Eutectic High Entropy Alloys, Mater. Chem. Phys., 2021, 260, p 124175. https://doi.org/10.1016/j.matchemphys.2020.124175

    Article  CAS  Google Scholar 

  22. A. Shafiei, Design of Eutectic High Entropy Alloys in Al–Co–Cr–Fe–Ni system, Met. Mater. Int., 2021, 27(1), p 127–138. https://doi.org/10.1007/s12540-020-00655-3

    Article  CAS  Google Scholar 

  23. Y.S. Na, K.R. Lim, H.J. Chang, and J. Kim, Effect of Trace Additions of Ti on the Microstructure of AlCoCrFeNi-Based High Entropy Alloy, Sci. Adv. Mater., 2016, 8(10), p 1984–1988. https://doi.org/10.1166/sam.2016.2793

    Article  CAS  Google Scholar 

  24. W.Y. Huo, H. Zhou, F. Fang, Z.H. Xie, and J.Q. Jiang, Microstructure and Mechanical Properties of CoCrFeNiZrx Eutectic High-Entropy Alloys, Mater. Des., 2017, 134, p 226–233. https://doi.org/10.1016/j.matdes.2017.08.030

    Article  CAS  Google Scholar 

  25. N.D. Stepanov, N.Y. Yurchenko, D.G. Shaysultanov, G.A. Salishchev, and M.A. Tikhonovsky, Effect of Al on Structure and Mechanical Properties of AlxNbTiVZr (x= 0, 05, 1, 15) High Entropy Alloys, Mater. Sci. Technol., 2015, 31(10), p 1184–1193. https://doi.org/10.1179/1743284715Y.0000000032

    Article  CAS  Google Scholar 

  26. N.D. Stepanov, N.Y. Yurchenko, V.S. Sokolovsky, M.A. Tikhonovsky, and G.A. Salishchev, An AlNbTiVZr0.5 High-Entropy Alloy Combining High Specific Strength and Good Ductility, Mater. Lett., 2015, 161, p 136–139. https://doi.org/10.1016/j.matlet.2015.08.099

    Article  CAS  Google Scholar 

  27. V. Rigaud, D. Daloz, and G. Lesoult, Influence of Ti and Zr Additions on Solidification of Fe Base Intermetallics Precipitating Laves Phase, Int. J. Cast Met. Res., 2009, 22(1–4), p 47–50. https://doi.org/10.1179/136404609X367948

    Article  CAS  Google Scholar 

  28. K.B. Zhang and Z.Y. Fu, Effects of Annealing Treatment on Phase Composition and Microstructure of CoCrFeNiTiAlx High-Entropy Alloys, Intermetallics, 2012, 22, p 24–32. https://doi.org/10.1016/j.intermet.2011.10.010

    Article  CAS  Google Scholar 

  29. X.Y. Liu, S.Q. Zhou, and Y. Xu, Microstructure and Tribological Performance of Fe50Mn30Co10Cr10 High-Entropy Alloy Based Self-Lubricating Composites, Mater. Lett., 2018, 233, p 142–145. https://doi.org/10.1016/j.matlet.2018.08.100

    Article  CAS  Google Scholar 

  30. J. Jiang, R. Li, T. Yuan, P. Niu, C. Chen, and K. Zhou, Microstructural Evolution and Wear Performance of the High-Entropy FeMnCoCr Alloy/TiC/CaF2 Self-Lubricating Composite Coatings on Copper Prepared by Laser Cladding for Continuous Casting Mold, J. Mater. Res., 2019, 34(10), p 1714–1725. https://doi.org/10.1557/jmr.2019.57

    Article  CAS  Google Scholar 

  31. P. Shi, R. Li, Y. Li, Y. Wen, Y. Zhong, W. Ren, Z. Shen, T. Zheng, J.C. Peng, and Y.D. Wang, Hierarchical Crack Buffering Triples Ductility in Eutectic Herringbone High-Entropy Alloys, Science, 2021, 373(6557), p 912–918.

    Article  CAS  PubMed  Google Scholar 

  32. C.D. Rabadia, Y.J. Liu, L.Y. Chen, S.F. Jawed, L.Q. Wang, H. Sun, and L.C. Zhang, Deformation and Strength Characteristics of Laves Phases in Titanium Alloys, Mater. Des., 2019, 179, p 107891. https://doi.org/10.1016/j.matdes.2019.107891

    Article  CAS  Google Scholar 

Download references

Acknowledgments

This research was supported by the National Natural Science Foundation of China (No. 51801029), the Natural Science Foundation of Guangdong Province (Nos. 2022A0505050052 and 2022A1515012591).

Author information

Authors and Affiliations

  1. School of Materials and Energy, Guangdong University of Technology, Guangzhou, 510006, China

    Qian Zhang, Ke Yang, Weidong Yuan, Yong Dong, Chuanqiang Li & Zhengrong Zhang

  2. GDUT Analysis and Test Center, Guangdong University of Technology, Guangzhou, 510006, China

    Beibei Jiang

Authors
  1. Qian Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Ke Yang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Weidong Yuan
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Yong Dong
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Beibei Jiang
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Chuanqiang Li
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Zhengrong Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Yong Dong.

Ethics declarations

Conflict of interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Zhang, Q., Yang, K., Yuan, W. et al. Effect of Annealing Temperature on Microstructure and Mechanical Properties of Fe50Mn25Co10Cr10Ti5 High Entropy Alloy. J. of Materi Eng and Perform 33, 9447–9456 (2024). https://doi.org/10.1007/s11665-023-08646-2

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11665-023-08646-2

Keywords