In this study, macroporous graphene aerogels (GAs) were synthesized by chemical reduction of graphene oxide sheets and were used as a support material for in situ synthesis of conductive poly(para-phenylenediamine) (p(p-PDA)). The in situ... more
In this study, macroporous graphene aerogels (GAs) were synthesized by chemical reduction of graphene oxide sheets and were used as a support material for in situ synthesis of conductive poly(para-phenylenediamine) (p(p-PDA)). The in situ synthesis of p(p-PDA) in GA was carried out by using a simple oxidation polymerization technique. Moreover, the prepared conductive p(p-PDA) polymers in the networks of GAs were doped with various types of acids such as hydrochloric acid (HCl), nitric acid (HNO3), sulfuric acid (H2SO4), phosphoric acid (H3PO4), respectively. The prepared GA and different acid-doped forms as GA/p(p-PDA) composites were characterized by FT-IR, TGA, and conductivity measurements. The observed FT-IR peaks at 1574 cm−1, and 1491 cm−1, for stretching deformations of quinone and benzene, respectively, confirmed the in situ synthesis of P(p-PDA) polymers within GAs. The conductivity of GAs with 2.17 × 10−4 ± 3.15 × 10−5 S·cm−1 has experienced an approximately 250-fold incr...