Microstructure and strength of brazed joints of Ti3Al base alloy with AgCuZn filler metal

He et al., 2005

Document ID
1210504561371788047
Author
He P
Feng J
Zhou H
Publication year
Publication venue
Materials science and technology

External Links

Snippet

Brazing Ti3Al alloys with filler metal Ag–Cu34–Zn16 was carried out at 1073–1173 K for 60– 1200 s. The relationship between brazing parameters and shear strength of the joints was investigated, and optimum brazing parameters obtained as follows: brazing temperature …
Continue reading at journals.sagepub.com (other versions)

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/24—Selection of soldering or welding materials proper
    • B23K35/30—Selection of soldering or welding materials proper with the principal constituent melting at less than 1550 degrees C
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C1/00—Making alloys
    • C22C1/04—Making alloys by powder metallurgy
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C14/00—Alloys based on titanium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K2203/00—Materials to be soldered, welded or cut
    • B23K2203/02—Iron or ferrous alloys
    • B23K2203/04—Steel or steel alloys

Similar Documents

Publication Publication Date Title
Chen et al. Microstructural characterization and mechanical properties in friction stir welding of aluminum and titanium dissimilar alloys
Cai et al. Dissimilar joining of TiAl alloy and Ni-based superalloy by laser welding technology using V/Cu composite interlayer
Niu et al. Microstructure and mechanical properties of Al2O3 ceramic and TiAl alloy joints brazed with Ag–Cu–Ti filler metal
Qiu et al. Microstructure and mechanical properties of TiAl alloy joints vacuum brazed with Ti–Zr–Ni–Cu brazing powder without and with Mo additive
Liyanage et al. Joint formation in dissimilar Al alloy/steel and Mg alloy/steel friction stir spot welds
Wang et al. Vacuum brazing of Ti2AlNb and TC4 alloys using Ti—Zr—Cu—Ni and Ti—Zr—Cu—Ni+ Mo filler metals: Microstructural evolution and mechanical properties
Rotundo et al. Mechanical and microstructural characterization of 2124Al/25 vol.% SiCp joints obtained by linear friction welding (LFW)
He et al. Microstructure and strength of brazed joints of Ti3Al-base alloy with NiCrSiB
Çam et al. Progress in joining of advanced materials: Part 1: Solid state joining, fusion joining, and joining of intermetallics
Jiang et al. Microstructure and mechanical properties of brazing bonded WC-15Co/35CrMo joint using AgNi/CuZn/AgNi composite interlayers
Wu et al. Microstructure and phase evolution in γ-TiAl/Ti2AlNb dual alloy fabricated by direct metal deposition
Peng et al. Microstructure and mechanical properties of Al2O3 ceramic and Ti2AlNb alloy joints brazed with Al2O3 particles reinforced Ag–Cu filler metal
He et al. Microstructure and strength of brazed joints of Ti3Al-base alloy with TiZrNiCu filler metal
Cai et al. Influence of intermetallic compounds on the microstructure and strength properties of diffusion bonded W–steel joints using Ti/Ni composite interlayer
Yin et al. Effect of interlayer thickness on the microstructure and strength of WC-Co/Invar/316L steel joints prepared by fibre laser welding
Li et al. Two kinds of α/β phase transformations and enhanced strengths of the bonded interface in laminated Ti alloys
He et al. Mechanical property of induction brazing TiAl-based intermetallics to steel 35CrMo using AgCuTi filler metal
Huijie et al. Vacuum brazing TiAl-based alloy to 40Cr steel using Ag-Cu-Zn filler metal
Song et al. Evaluation of TZM/ZrCp-W joint brazed with Ti-35Ni filler: microstructure and mechanical properties
Han et al. Effect of Cu66V34 filler thickness on the microstructure and properties of titanium/copper joint by electron beam welding
Barrena et al. Characterization of WC–Co/Ti6Al4V diffusion bonding joints using Ag as interlayer
Huijie et al. Microstructure and strength of the SiC/TiAl joint brazed with Ag-Cu-Ti filler metal
He et al. Microstructure and kinetics of induction brazing TiAl-based intermetallics to steel 35CrMo using AgCuTi filler metal
Winiowski et al. Brazing of titanium with aluminium alloys
Khorunov et al. Brazing of superalloys and the intermetallic alloy (γ-TiAl)