WO2017159637A1 - エポキシ化合物、硬化性組成物、硬化物、エポキシ化合物の製造方法および反応性希釈剤 - Google Patents

エポキシ化合物、硬化性組成物、硬化物、エポキシ化合物の製造方法および反応性希釈剤 Download PDF

Info

Publication number
WO2017159637A1
WO2017159637A1 PCT/JP2017/010040 JP2017010040W WO2017159637A1 WO 2017159637 A1 WO2017159637 A1 WO 2017159637A1 JP 2017010040 W JP2017010040 W JP 2017010040W WO 2017159637 A1 WO2017159637 A1 WO 2017159637A1
Authority
WO
WIPO (PCT)
Prior art keywords
curable composition
compound
monoepoxy compound
monoepoxy
cured product
Prior art date
Application number
PCT/JP2017/010040
Other languages
English (en)
French (fr)
Inventor
敦史 亀山
龍一 上野
央司 曾禰
鈴木　宏明
翔平 高田
隆史 關
Original Assignee
Ｊｘエネルギー株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2016188882A external-priority patent/JP6644659B2/ja
Priority claimed from JP2016188868A external-priority patent/JP6691855B2/ja
Application filed by Ｊｘエネルギー株式会社 filed Critical Ｊｘエネルギー株式会社
Priority to CN201780014232.4A priority Critical patent/CN109071477A/zh
Priority to US16/084,375 priority patent/US10995079B2/en
Priority to KR1020187024749A priority patent/KR102344209B1/ko
Priority to EP17766636.9A priority patent/EP3431470B1/en
Publication of WO2017159637A1 publication Critical patent/WO2017159637A1/ja

Abstract

以下の式（１）のモノエポキシ化合物、これを含んでなる硬化性組成物、その硬化物、該モノエポキシ化合物の製造方法、ならびに該モノエポキシ化合物を含んでなる反応希釈剤が開示される。式（１）のモノエポキシ化合物は、硬化性組成物に含有させたとき、硬化性組成物の耐熱性の低下およびこの硬化性組成物を硬化させた際の重量減少を防止しつつ、硬化性組成物の粘度を低下させることができる点で有用である。（式中、Ｒ１乃至Ｒ６はそれぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される。）

Description

エポキシ化合物、硬化性組成物、硬化物、エポキシ化合物の製造方法および反応性希釈剤 関連出願の参照
　本特許出願は、先に出願された日本国における特許出願である特願２０１６－４９７１２号（出願日：２０１６年３月１４日）、特願２０１６－１０７７２４号（出願日：２０１６年５月３０日）、特願２０１６－１２００１４号（出願日：２０１６年６月１６日）、特願２０１６－１８８８６８号（出願日：２０１６年月９日２７日）、および特願２０１６－１８８８８２号（出願日：２０１６年９月２７日）に基づく優先権の主張を伴うものである。この先の特許出願における全開示内容は、引用することにより本明細書の一部とされる。
　本発明は、エポキシ化合物、硬化性組成物、硬化物、エポキシ化合物の製造方法および反応性希釈剤に関する。
　ビスフェノールＡ型エポキシ樹脂等のエポキシ化合物を含んでなる代表的な液状硬化性組成物は、粘度が高く、その取り扱いには問題があった。液状硬化性組成物の低粘度化を目的として、硬化性組成物に溶剤を含有させることが行われているが、この方法では、硬化性組成物の硬化の際に溶剤が放出されてしまい、環境に悪影響を与えてしまうという問題があった。
　このような問題に鑑み、ブチルグリシジルエーテルや１，２－エポキシ－４－ビニルシクロヘキサン等のエポキシ化合物等を、反応性希釈剤として、液状硬化性組成物に含有させることが行われている。
　しかしながら、このようなエポキシ化合物を用いる方法では、硬化性組成物の粘度を十分に低下させることができない、硬化性組成物の耐熱性を過度に低下させてしまう、硬化性組成物を硬化させた際の重量減少率を増加させてしまう等の問題があった。
　一方、耐熱性、耐候性等の優れた硬化性組成物として脂環式エポキシ化合物の実用化が進んでいる。ここで、引用文献１（特開昭４９－１２６６５８号公報）には、特定のナフタレンタイプの骨格を持つ脂環式ジオレフィン化合物から製造された脂環式ジエポキシ化合物が開示されているが、これらの脂環式ジエポキシ化合物は針状結晶であり、固体であるため、液状硬化性組成物に用いることには適していない。
特開昭４９－１２６６５８号公報
　本発明は、上記問題に鑑みてなされたものであり、硬化性組成物に含有させたとき、硬化性組成物の耐熱性の低下およびこの硬化性組成物を硬化させた際の重量減少を防止しつつ、硬化性組成物の粘度を低下させることができるモノエポキシ化合物の提供をその目的とするものである。
　また、本発明者らは、このモノエポキシ化合物と光カチオン重合開始剤とを併用して硬化性組成物に含有させることにより、この硬化性組成物に活性エネルギー線を照射することにより硬化させた硬化物の密着性を飛躍的に向上させることができるということを見出した。本発明はかかる知見に基づくものであり、本発明の解決しようとする課題は、密着性に優れる硬化物を得ることのできる硬化性組成物を提供することである。
　さらに、本発明者らは、特定の構造を有する立体異性体を含むエポキシ化合物において、特定の立体異性体の割合を特定の数値以上とすることにより、硬化物の耐熱性を顕著に向上することができることをさらに知見した。本発明は、かかる知見に基づくものであり、硬化物の耐熱性を顕著に向上することのできるエポキシ化合物を提供することである。
　すなわち、本発明は以下の発明を包含する。
（１）下記式（１）：
Figure JPOXMLDOC01-appb-C000004
 （式中、Ｒ１乃至Ｒ６は、それぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される。）
で表される、モノエポキシ化合物。
（２）前記式（１）で表される化合物の立体異性体を含み、１３Ｃ－ＮＭＲ分析による、前記式（１）におけるノルボルナン骨格の橋頭位とビニル基とがトランスの関係にある立体異性体に由来するピーク面積の、化学シフト１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、６６％以上である、（１）に記載のモノエポキシ化合物。
（３）Ｒ１乃至Ｒ６は全て水素であり、ノルボルナン骨格の橋頭位とビニル基とがトランスの関係にある立体異性体が、下記化学式：
Figure JPOXMLDOC01-appb-C000005
 のいずれかで表される、（２）に記載のモノエポキシ化合物。
（４）前記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、６６％以上である、（１）に記載のモノエポキシ化合物。
（５）前記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲におけるピークのうち、低磁場側から１番目に生じるピークの面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、３５％以上である、（２）～（４）のいずれかに記載のモノエポキシ化合物。
（６）（１）～（５）のいずれかに記載のモノエポキシ化合物と、硬化剤、熱カチオン重合開始剤、および光カチオン重合開始剤からなる群より選択される１種とを含む、硬化性組成物。
（７）前記硬化剤が、フェノール化合物、アミン化合物、酸無水物系化合物およびアミド化合物からなる群より選択される１以上の硬化剤である、（６）に記載の硬化性組成物。
（８）前記熱カチオン重合開始剤が、芳香族スルホニウム塩系の熱カチオン重合開始剤、芳香族ヨードニウム塩系の熱カチオン重合開始剤、およびアルミニウム錯体系の熱カチオン重合開始剤からなる群から選択される、（６）に記載の硬化性組成物。
（９）前記光カチオン重合開始剤が、芳香族スルホニウム塩系の光カチオン重合開始剤である、（６）に記載の硬化性組成物。
（１０）前記モノエポキシ化合物と異なるその他のエポキシ化合物をさらに含む、（６）～（９）のいずれかに記載の硬化性組成物。
（１１）前記モノエポキシ化合物と異なるその他のエポキシ化合物が、グリシジルエーテル型エポキシド、グリシジルエステル型エポキシド、脂環式エポキシド、およびエポキシ樹脂からなる群から選択される、（１０）に記載の硬化性組成物。
（１２）前記硬化性組成物における、前記モノエポキシ化合物と、前記モノエポキシ化合物と異なるその他のエポキシ化合物との含有量比が、質量基準で、１：９９～７５：２５である、（１０）または（１１）に記載の硬化性組成物。
（１３）（６）～（１２）のいずれかに記載の硬化性組成物を硬化させる工程を含む、硬化物の製造方法。
（１４）（６）～（１２）のいずれかに記載の硬化性組成物の硬化物。
（１５）（１）に記載のモノエポキシ化合物を製造する方法であって、
　下記式（２）：
Figure JPOXMLDOC01-appb-C000006
 （式中、Ｒ１乃至Ｒ６は、それぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される。）
で表される化合物と、過酸とを反応させる工程を含んでなり、
　該過酸の使用量が、該式（２）で表される化合物１．００モルに対して、０．１０～１．８０モルであることを特徴とする、方法。
（１６）前記過酸が、過酸化水素または有機過酸である、（１５）に記載の方法。
（１７）（１）に記載のモノエポキシ化合物を少なくとも含む、反応性希釈剤。
　本発明によれば、硬化性組成物に含有させたとき、硬化性組成物の耐熱性の低下およびこの硬化性組成物を硬化させた際の重量減少を防止しつつ、硬化性組成物の粘度を低下させることができるモノエポキシ化合物を提供することができる。
　また、本発明によれば、密着性が飛躍的に向上された硬化物を得ることのできる硬化性組成物を提供することができる。
　さらに、本発明によれば、高い耐熱性を有する硬化物の作製が可能なモノエポキシ化合物を提供することができる。
図１は、実施例Ｉ１－１で合成したモノエポキシ化合物（Ａ）の１３Ｃ－ＮＭＲチャートを表す。 図２は、実施例ＩＩＩ１で合成したモノエポキシ化合物（Ａ－１）の１３Ｃ－ＮＭＲチャートを表す。 図３は、実施例ＩＩＩ１で合成したモノエポキシ化合物（Ａ－１）のガスクロマトグラフを表す。 図４は、実施例ＩＩＩ２で合成したモノエポキシ化合物（Ａ－２）の１３Ｃ－ＮＭＲチャートを表す。 図５は、実施例ＩＩＩ２で合成したモノエポキシ化合物（Ａ－２）のガスクロマトグラフを表す。 図６は、実施例ＩＩＩ４で合成したモノエポキシ化合物（Ａ－３）の１３Ｃ－ＮＭＲチャートを表す。 図７は、実施例ＩＩＩ４で合成したモノエポキシ化合物（Ａ－３）のガスクロマトグラフを表す。
１．定義
　本明細書において、配合を示す「部」、「％」等は特に断らない限り質量基準である。
　本明細書において、エポキシ当量とは、１当量のエポキシ基を含むモノエポキシ化合物の質量で定義され、ＪＩＳ　Ｋ７２３６に準じて測定することができる。
２．モノエポキシ化合物
（１）モノエポキシ化合物
　本発明のモノエポキシ化合物は、下記式（１）で表されるモノエポキシ化合物である。
Figure JPOXMLDOC01-appb-C000007
 （式中、Ｒ１乃至Ｒ６はそれぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される。）
　本発明のモノエポキシ化合物は、上記式（１）中、Ｒ１乃至Ｒ６はそれぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択されるが、該アルキル基が有する炭素数は、１～１０であることが好ましく、１～５であることがより好ましい。また、直鎖状のアルキル基であっても、分岐鎖状のアルキル基であってもよい。該アルコキシ基が有する炭素数は、１～１０であることが好ましく、１～５であることがより好ましい。
特に好ましくはＲ１乃至Ｒ６は水素である。
　上記式（１）で表される本発明のモノエポキシ化合物は、エポキシ当量が、１１０～１０００ｇ／ｅｑであることが好ましく、１５０～５００ｇ／ｅｑであることがより好ましく、１６０～３００ｇ／ｅｑであることがさらに好ましい。
（２）モノエポキシ化合物の製造方法
　上記式（１）を満たす本発明のモノエポキシ化合物は、下記式（２）で表される化合物と、過酸とを反応させる工程を含んでなる方法により得ることができる。
Figure JPOXMLDOC01-appb-C000008
 （式中、Ｒ１乃至Ｒ６は、それぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される。）
　本発明のモノエポキシ化合物の製造方法は、好ましくは、上記式（２）で表される化合物と、過酸とを反応させる工程を含んでなり、過酸の使用量が、上記式（２）で表される化合物１．００モルに対して、０．１０～１．８０モルであることを特徴とする。
　本発明のモノエポキシ化合物の製造にあたっては、上述の製造方法で得られたモノエポキシ化合物の純度が低い場合は、蒸留やカラムにより精製を行うことが好ましい。
　本発明のモノエポキシ化合物の製造に使用することのできる過酸としては、例えば、過ギ酸、過酢酸、過安息香酸、トリフルオロ過酢酸等の有機過酸や過酸化水素等が挙げられる。これらの中でも、過ギ酸、過酢酸や過酸化水素は、工業的に安価に入手可能であり、かつ安定性が高いため好ましい。
　本発明のモノエポキシ化合物の製造における過酸の使用量は、上記式（２）で表される化合物１．００モルに対して、０．１０～１．８０モルであることが好ましく、０．５０～１．５０モルであることがさらに好ましい。
　上記式（２）を満たす化合物は、５－ビニル－２－ノルボルネン（ＶＮＢ）と、１，３－ブタジエンとをディールズ・アルダー反応させることにより得ることができる。なお、ＶＮＢは、１，３－ブタジエンとシクロペンタジエンとをディールズ・アルダー反応させることにより得ることができる。
Figure JPOXMLDOC01-appb-C000009
（３）立体異性体を含んでなるモノエポキシ化合物
　上記式（１）で表されるモノエポキシ化合物におけるＲ１乃至Ｒ６が全て水素である場合、本発明のモノエポキシ化合物は、以下のような立体異性体を含んでなることが想定される。
Figure JPOXMLDOC01-appb-C000010
　ここで、本発明のモノエポキシ化合物の一つの実施態様として、１３Ｃ－ＮＭＲ分析による、上記式（１）におけるノルボルナン骨格の橋頭位とビニル基とがトランスの関係にある立体異性体に由来するピーク面積の、化学シフト１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、６６％以上であることを特徴とするものが好ましい。
　本発明のモノエポキシ化合物がこのような特徴を有することにより、これを含む硬化性組成物を硬化させた硬化物の耐熱性をよりよく向上させることができる。
　また、１３Ｃ－ＮＭＲ分析による、上記式（１）におけるノルボルナン骨格の橋頭位とビニル基とがトランスの関係にある立体異性体に由来するピーク面積の、化学シフト１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合は、７０％以上であることがより好ましい。
　上記式（１）で表されるモノエポキシ化合物におけるＲ１乃至Ｒ６が全て水素である場合、ノルボルナン骨格の橋頭位と、ビニル基とがトランスの関係にある立体異性体として以下の２つが挙げられる。
Figure JPOXMLDOC01-appb-C000011
　ここで、本発明のモノエポキシ化合物の他の一つの実施態様として、上記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、６６％以上であることを特徴とするものが好ましい。
　また、上記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、７０％以上であることを特徴とするものがより好ましい。
　また、上記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲におけるピークのうち、低磁場側から１番目に生じるピークの面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、３５％以上であることが好ましく、４０％以上であることがより好ましい。
　上記（２）に記載された製造方法により得られるモノエポキシ化合物を、分取蒸留することにより、１３Ｃ－ＮＭＲ分析による、上記式（１）で表されるモノエポキシ化合物におけるノルボルナン骨格の橋頭位とビニル基とがトランスの関係にある立体異性体に由来するピーク面積の、シフト値１４０～１４５ｐｐｍにおける総ピーク面積に対する割合を調整することができる。また、上記（２）に記載された製造方法により得られるモノエポキシ化合物を、分取蒸留することにより、上記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合を調整することができる。これらに限られず、例えば、シリカゲルクロマトグラフィーや液体クロマトグラフィーによっても、該割合を調整することができる。
（４）モノエポキシ化合物の有用性
　本発明のモノエポキシ化合物は、硬化性組成物に含有させたとき、硬化性組成物の耐熱性の低下およびこの硬化性組成物を硬化させた際の重量減少を防止しつつ、硬化性組成物を可塑化あるいは低粘度化することができる。そのため、缶、プラスチック、紙、木材等の様々なコーティング、インク、接着剤、シーリング剤、電気・電子材料、炭素繊維強化樹脂等の分野において好適に使用することができる。
　より具体的には、三次元造形材料、酸除去剤、家具コーティング、装飾コーティング、自動車下塗り、仕上げ塗り、飲料缶およびその他缶のコーティング、ＵＶ硬化型インク、光ディスク記録層の保護膜、カラーフィルター保護膜、光ディスク貼り合わせ用接着剤、光学材料用接着材、半導体素子のダイボンディング、有機ＥＬディスプレイのシール材、ＣＣＤ，赤外線センサー等の受光装置の封止材、ＬＥＤや有機ＥＬ等の発光装置の封止材、光配線板、光コネクタ、レンズ等の光学半導体関連部材、光導波路、フォトレジスト、強化ガラスや防犯ガラス等の複合ガラス等に好適に使用することができる。また、ポリマーを構成するモノマーや、シランカップリング剤前駆体としても有用である。
　また、本発明のモノエポキシ化合物は、反応性希釈剤の構成成分として好適に用いることができる。なお、本発明において、反応性希釈剤とは、エポキシ基を有する化合物を含むため、高い反応性を有するとともに、硬化性組成物の可塑化あるいは粘度調整（低下）することのできる添加剤である。
　さらに、上記式（１）で表されるモノエポキシ化合物と、光カチオン重合開始剤とを硬化性組成物に含有させることにより、これを活性エネルギー線により硬化させた硬化物の密着性を飛躍的に向上させることができる。また、本発明の硬化性組成物は、高い耐熱性を有する。
　さらに、硬化性組成物が上記「（３）立体異性体を含んでなるモノエポキシ化合物」の記載項目中に記載された好ましい実施態様のモノエポキシ化合物を含んでなることにより、この硬化性組成物を硬化させた硬化物の耐熱性をよりよく向上させることができる。硬化性組成物における該モノエポキシ化合物の含有量は、硬化性組成物１００質量部に対し、１～９０質量部であることが好ましく、５～７５質量部であることがより好ましい。該モノエポキシ化合物と熱カチオン重合開始剤とを組み合わせることにより、硬化物の耐熱性をより一層向上させることができる。さらに、硬化物の透明性を向上させることができる。
３．硬化性組成物
　本発明の硬化性組成物は、上記式（１）で表されるモノエポキシ化合物、硬化剤、熱カチオン重合開始剤、または光カチオン重合開始剤を含んでなることを特徴とする。また、本発明の硬化性組成物は、さらに、前記モノエポキシ化合物と異なるその他のエポキシ化合物を含んでなることを特徴とする。なお、本発明の硬化性組成物は、２種以上の上記式（１）で表されるモノエポキシ化合物を含んでいてもよい。
　本発明の硬化性組成物が上記式（１）で表されるモノエポキシ化合物を含んでなることにより、硬化性組成物の粘度を低下させることができる。また、硬化性組成物を硬化させた硬化物の耐熱性の低下およびこの硬化性組成物を硬化させた際に生じうる重量減少を抑制することができる。
　また、上記式（１）で表されるモノエポキシ化合物と、光カチオン重合開始剤とを硬化性組成物に含有させることにより、これを活性エネルギー線により硬化させた硬化物の密着性を飛躍的に向上させることができる。また、本発明の硬化性組成物は、高い耐熱性を有する。ここで、本発明の硬化性組成物中に、後述するような他の化合物が含まれてもよいが、硬化物の密着性という観点からは、本発明の硬化性組成物中に含まれる上記式（１）で表されるモノエポキシ化合物の含有量は、１～９０質量％であることが好ましく、５～７５質量％であることがより好ましい。
　さらに、本発明の硬化性組成物の好ましい一つの実施態様として、上記「（３）立体異性体を含んでなるモノエポキシ化合物」の記載項目中に記載された好ましい実施態様のモノエポキシ化合物と、硬化剤、熱カチオン重合開始剤、または光カチオン重合開始剤とを含んでなる。該硬化性組成物が該モノエポキシ化合物を含んでなることにより、この硬化性組成物を硬化させた硬化物の耐熱性をよりよく向上させることができる。硬化性組成物における該モノエポキシ化合物の含有量は、硬化性組成物１００質量部に対し、１～９０質量部であることが好ましく、５～７５質量部であることがより好ましい。
（１）硬化剤
　本発明の硬化性組成物に含有させることのできる硬化剤としては、酸無水物系硬化剤、アミン系硬化剤、フェノール系硬化剤および潜在性硬化剤等が挙げられる。
　酸無水物系硬化剤としては、ヘキサヒドロ無水フタル酸、メチルヘキサヒドロ無水フタル酸、テトラヒドロ無水フタル酸、メチルテトラヒドロ無水フタル酸、エンドメチレンテトラヒドロ無水フタル酸、メチルナジック酸無水物、メチルブテニルテトラヒドロ無水フタル酸、水素化メチルナジック酸無水物、トリアルキルテトラヒドロ無水フタル酸、シクロヘキサントリカルボン酸無水物、メチルシクロヘキセンジカルボン酸無水物、メチルシクロヘキサンテトラカルボン酸二無水物、無水マレイン酸、無水フタル酸、無水コハク酸、ドデセニル無水コハク酸、オクテニルコハク酸無水物、無水ピロメリット酸、無水トリメリット酸、アルキルスチレン－無水マレイン酸共重合体、クロレンド酸無水物、ポリアゼライン酸無水物、無水ベンゾフェノンテトラカルボン酸、エチレングリコールビスアンヒドロトリメリテート、グリセロールトリストリメリテート、グリセリンビス（アンヒドロトリメリテート）モノアセテート、ベンゾフェノンテトラカルボン酸、ポリアジピン酸無水物、ポリセバシン酸無水物、ポリ（エチルオクタデカン二酸）無水物、ポリ（フェニルヘキサデカン二酸）無水物、ヘット酸無水物、ノルボルナン－２，３－ジカルボン酸無水物等が挙げられる。
　アミン系硬化剤としては、ポリオキシエチレンジアミン、ポリオキシプロピレンジアミン、ポリオキシブチレンジアミン、ポリオキシペンチレンジアミン、ポリオキシエチレントリアミン、ポリオキシプロピレントリアミン、ポリオキシブチレントリアミン、ポリオキシペンチレントリアミン、ジエチレントリアミン、トリエチレンテトラミン、テトラエチレンペンタミン、ｍ－キシレンジアミン、トリメチルヘキサメチレンジアミン、２－メチルペンタメチレンジアミン、ジエチルアミノプロピルアミン、イソフォロンジアミン、１，３－ビスアミノメチルシクロヘキサン、ビス（４－アミノシクロヘキシル）メタン、ノルボルナンジアミン、１，２－ジアミノシクロヘキサン、ジアミノジフェニルメタン、メタフェニレンジアミン、ジアミノジフェニルスルフォン、Ｎ－アミノエチルピペラジン等が挙げられる。
　フェノール系硬化剤としては、キシリレン骨格含有フェノールノボラック樹脂、ジシクロペンタジエン骨格含有フェノールノボラック樹脂、ビフェニル骨格含有フェノールノボラック樹脂、フルオレン骨格含有フェノールノボラック樹脂、テルペン骨格含有フェノールノボラック樹脂、ビスフェノールＡノボラック、ビスフェノールＦノボラック、ビスフェノールＳノボラック、ビスフェノールＡＰノボラック、ビスフェノールＣノボラック、ビスフェノールＥノボラック、ビスフェノールＺノボラック、ビフェノールノボラック、テトラメチルビスフェノールＡノボラック、ジメチルビスフェノールＡノボラック、テトラメチルビスフェノールＦノボラック、ジメチルビスフェノールＦノボラック、テトラメチルビスフェノールＳノボラック、ジメチルビスフェノールＳノボラック、テトラメチル－４，４’－ビフェノールノボラック、トリスヒドロキシフェニルメタンノボラック、レゾルシノールノボラック、ハイドロキノンノボラック、ピロガロールノボラック、ジイソプロピリデンノボラック、１，１－ジ－４－ヒドロキシフェニルフルオレンノボラック、フェノール化ポリブタジエンノボラック、フェノールノボラック、クレゾール類ノボラック、エチルフェノール類ノボラック、ブチルフェノール類ノボラック、オクチルフェノール類ノボラック、ナフトール類ノボラック等が挙げられる。
　潜在性硬化剤としては、ジシアンジアミド、アジピン酸ジヒドラジド、セバシン酸ジヒドラジド、ドデカン二酸ジヒドラジド、イソフタル酸ジヒドラジド、ケチミン、イミダゾール化合物、ジヒドラジド化合物、アミンアダクト系潜在性硬化剤等が挙げられる。本発明の硬化性組成物は、上記したような硬化剤を１種または２種以上含んでいてもよい。
　本発明の硬化性組成物の好ましい実施態様においては、硬化剤が、酸無水物系硬化剤、アミン系硬化剤、フェノール系硬化剤および潜在性硬化剤からなる群より選択される１以上の硬化剤である。
　本発明の硬化性組成物における硬化剤の含有量は、使用する硬化剤の種類に応じ適宜変更することが好ましい。例えば、硬化剤として酸無水物系硬化剤、アミン系硬化剤またはフェノール系硬化剤を使用する場合、硬化性組成物全体のエポキシ基１当量に対して、０．５～１．５当量であることが好ましく、０．８～１．２当量であることがより好ましい。例えば、硬化剤として潜在性硬化剤を使用する場合、硬化性組成物１００質量部に対し、１～３０質量部であることが好ましく、５～２０質量部であることがより好ましい。
（２）硬化促進剤
　本発明の硬化性組成物は、硬化促進剤をさらに含んでいてもよい。硬化促進剤としては、例えば、トリフェニルホスフィン、トリフェニルベンジルホスホニウムテトラフェニルボレート、テトラブチルホスホニウムジエチルホスホロジチオエート、テトラフェニルホスホニウムブロマイド、テトラブチルホスホニウムアセテート、テトラ－ｎ－ブチルホスホニウムブロマイド、テトラ－ｎ－ブチルホスホニウムベンゾトリアゾレート、テトラ－ｎ－ブチルホスホニウムテトラフルオロボレート、テトラ－ｎ－ブチルホスホニウムテトラフェニルボレート、メチルトリフェニルホスホニウムブロマイド、エチルトリフェニルホスホニウムブロマイド、エチルトリフェニルホスホニウムアイオダイド、エチルトリフェニルホスホニウムアセテート、メチルトリ－ｎ－ブチルホスホニウムジメチルホスフェート、ｎ－ブチルトリフェニルホスホニウムブロマイド、ベンジルトリフェニルホスホニウムクロライド、テトラフェニルホスホニウムテトラフェニルボレート等のホスフィン類とその第四級塩、２－エチル－４－メチルイミダゾール、１，２－ジメチルイミダゾール、１－ベンジル－２－フェニルイミダゾール、２－メチルイミダゾール、２－フェニルイミダゾール、１－（２－シアノエチル）－２－エチル－４－メチルイミダゾール、２，４－ジアミノ－６－［２－メチルイミダゾリル－（１）］エチル－ｓ－トリアジン、２－フェニルイミダゾリン、２，３－ジヒドロ－１Ｈ－ピロロ［１，２－ａ］ベンズイミダゾール等のイミダゾール類、トリス（ジメチルアミノメチル）フェノール、ベンジルジメチルアミン、テトラブチルアンモニウムブロミド等の３級アミンとその第四級塩、１，８－ジアザビシクロ（５，４，０）ウンデセン－７、１，５－ジアザビシクロ（４，３，０）ノネン－５等の超強塩基性の有機化合物、オクチル酸亜鉛、ラウリン酸亜鉛、ステアリン酸亜鉛、オクチル酸錫等の有機カルボン酸金属塩、ベンゾイルアセトン亜鉛キレート、ジベンゾイルメタン亜鉛キレートおよびアセト酢酸エチル亜鉛キレート等の金属－有機キレート化合物、テトラ－ｎ－ブチルスルホニウム－ｏ，ｏ－ジエチルホスホロジチオネート等が挙げられる。本発明の硬化性組成物は、上記したような硬化促進剤を１種または２種以上含んでいてもよい。
　本発明の硬化性組成物における硬化促進剤の含有量は、硬化性組成物の総量１００質量部に対し、０．１～６質量部であることが好ましい。
（３）熱カチオン重合開始剤
　本発明の硬化性組成物に含有させることのできる熱カチオン重合開始剤としては、芳香族スルホニウム、芳香族ヨードニウム、芳香族ジアゾニウムおよびピリジニウムなどから選ばれる少なくとも１種のカチオンと、ＢＦ４ －、ＰＦ６ －、ＳｂＦ６ －、ＡｓＦ６ －、ＣＦ３ＳＯ３ －、（ＣＦ３ＳＯ２）２Ｎ－およびＢ（Ｃ６Ｆ５）４ －から選ばれる少なくとも１種のアニオンとから構成されるオニウム塩、アルミニウム錯体等の熱カチオン重合開始剤が挙げられる。
　芳香族スルホニウム塩系の熱カチオン重合開始剤としては、（２－エトキシ－１－メチル－２－オキソエチル）メチル－２－ナフタレニルスルホニウムヘキサフルオロアンチモネート、４－（メトキシカルボニルオキシ）フェニルベンジルメチルスルホニウムヘキサフルオロアンチモネート、４－アセトキシフェニルジメチルスルホニウムヘキサフルオロアンチモネート、４－ヒドロキシフェニルベンジルメチルスルホニウムヘキサフルオロアンチモネート、４－ヒドロキシフェニル（ｏ－メチルベンジル）メチルスルホニウムヘキサフルオロアンチモネート、４－ヒドロキシフェニル（α－ナフチルメチル）メチルスルホニウムヘキサフルオロアンチモネート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロアンチモネート、トリフェニルスルホニウムヘキサフルオロアンチモネート、ビス［４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル］スルフィドビスヘキサフルオロアンチモネート、ビス［４－（ジフェニルスルホニオ）フェニル］スルフィドビスヘキサフルオロアンチモネートなどのヘキサフルオロアンチモネート塩、（２－エトキシ－１－メチル－２－オキソエチル）メチル－２－ナフタレニルスルホニウムヘキサフルオロホスフェート、４－アセトキシフェニルベンジルメチルスルホニウムヘキサフルオロホスフェート、４－ヒドロキシフェニル（ｏ－メチルベンジル）メチルスルホニウムヘキサフルオロホスフェート、４－ヒドロキシフェニル（α－ナフチルメチル）メチルスルホニウムヘキサフルオロホスフェート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロホスフェート、トリフェニルスルホニウムヘキサフルオロホスフェート、ビス［４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル］スルフィドビスヘキサフルオロホスフェート、ビス［４－（ジフェニルスルホニオ）フェニル］スルフィドビスヘキサフルオロホスフェートなどのヘキサフルオロホスフェート塩、４－ヒドロキシフェニル（ｏ－メチルベンジル）メチルスルホニウムヘキサフルオロアルセネート、４－ヒドロキシフェニルベンジルメチルスルホニウムヘキサフルオロアルセネートなどのヘキサフルオロアルセネート塩、（２－エトキシ－１－メチル－２－オキソエチル）メチル－２－ナフタレニルスルホニウムテトラフルオロボレート、４－ヒドロキシフェニル（ｏ－メチルベンジル）メチルスルホニウムテトラフルオロボレート、４－ヒドロキシフェニルベンジルメチルスルホニウムテトラフルオロボレート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムテトラフルオロボレート、トリフェニルスルホニウムテトラフルオロボレート、ビス［４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル］スルフィドビステトラフルオロボレート、ビス［４－（ジフェニルスルホニオ）フェニル］スルフィドビステトラフルオロボレートなどのテトラフルオロボレート塩、４－ヒドロキシフェニル（ｏ－メチルベンジル）メチルスルホニウムトリフルオロメタンスルホン酸塩、４－ヒドロキシフェニルベンジルメチルスルホニウムトリフルオロメタンスルホン酸塩などのトリフルオロメタンスルホン酸塩、ジフェニル－４－（フェニルチオ）フェニルスルホニウムトリフルオロメタンスルホン酸塩などのトリフルオロメタンスルホン酸塩、４－ヒドロキシフェニル（α－ナフチルメチル）メチルスルホニウムビス（トリフルオロメタンスルホン）イミド、４－ヒドロキシフェニルベンジルメチルスルホニウムビス（トリフルオロメタンスルホン）イミドなどのビス（トリフルオロメタンスルホン）イミド塩、（２－エトキシ－１－メチル－２－オキソエチル）メチル－２－ナフタレニルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、４－（メトキシカルボニルオキシ）フェニルベンジルメチルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、４－ヒドロキシフェニル（ｏ－メチルベンジル）メチルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、４－ヒドロキシフェニル（α－ナフチルメチル）メチルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、４－ヒドロキシフェニルベンジルメチルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、トリフェニルスルホニウムテトラキス（ペンタフルオロフェニル）ボレート、ビス［４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル］スルフィドテトラキス（ペンタフルオロフェニル）ボレート、ビス［４－（ジフェニルスルホニオ）フェニル］スルフィドテトラキス（ペンタフルオロフェニル）ボレートなどのテトラキス（ペンタフルオロフェニル）ボレート塩等が挙げられる。
　芳香族ヨードニウム塩系の熱カチオン重合開始剤の具体例としては、フェニルヨードニウムヘキサフルオロホスフェート、ジフェニルヨードニウムヘキサフルオロアンチモネート、ジフェニルヨードニウムテトラフルオロボレート、ジフェニルヨードニウムテトラキス（ペンタフルオロフェニル）ボレート、ジフェニルヨードニウムヘキサフルオロホスフェート、ジフェニルヨードニウムトリフルオロメタンスルホン酸塩、ビス（ドデシルフェニル）ヨードニウムヘキサフルオロホスフェート、ビス（ドデシルフェニル）ヨードニウムヘキサフルオロアンチモネート、ビス（ドデシルフェニル）ヨードニウムテトラフルオロボレート、ビス（ドデシルフェニル）ヨードニウムテトラキス（ペンタフルオロフェニル）ボレート、４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムヘキサフルオロホスフェート、４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムヘキサフルオロアンチモネート、４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムテトラフルオロボレート、４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムテトラキス（ペンタフルオロフェニル）ボレート等が挙げられる。
　芳香族ジアゾニウム塩系の熱カチオン重合開始剤の具体例としては、フェニルジアゾニウムヘキサフルオロホスフェート、フェニルジアゾニウムヘキサフルオロアンチモネート、フェニルジアゾニウムテトラフルオロボレートおよびフェニルジアゾニウムテトラキス（ペンタフルオロフェニル）ボレート等が挙げられる。
　ピリジニウム塩系の熱カチオン重合開始剤の具体例としては、１－ベンジル－２－シアノピリジニウムヘキサフルオロホスフェート、１－ベンジル－２－シアノピリジニウムヘキサフルオロアンチモネート、１－ベンジル－２－シアノピリジニウムテトラフルオロボレート、１－ベンジル－２－シアノピリジニウムテトラキス（ペンタフルオロフェニル）ボレート、１－（ナフチルメチル）－２－シアノピリジニウムヘキサフルオロホスフェート、１－（ナフチルメチル）－２－シアノピリジニウムヘキサフルオロアンチモネート、１－（ナフチルメチル）－２－シアノピリジニウムテトラフルオロボレート、１－（ナフチルメチル）－２－シアノピリジニウムテトラキス（ペンタフルオロフェニル）ボレート等が挙げられる。
　アルミニウム錯体系の熱カチオン重合開始剤としては、アルミニウムのカルボン酸塩、アルミニウムアルコキシド、塩化アルミニウム、アルミニウム（アルコキシド）アセト酢酸キレート、アセトアセトナトアルミニウム、エチルアセトアセタトアルミニウム等が挙げられる。
　ホスホニウム塩系の熱カチオン重合開始剤としては、エチルトリフェニルホスホニウムヘキサフルオロアンチモネート、テトラブチルホスホニウムヘキサフルオロアンチモネート等が挙げられる。
　４級アンモニウム塩系の熱カチオン重合開始剤としては、Ｎ，Ｎ－ジメチル－Ｎ－ベンジルアニリニウムヘキサフルオロアンチモネート、Ｎ，Ｎ－ジエチル－Ｎ－ベンジルアニリニウムテトラフルオロボレート、Ｎ，Ｎ－ジメチル－Ｎ－ベンジルピリジニウムヘキサフルオロアンチモネート、Ｎ，Ｎ－ジエチル－Ｎ－ベンジルピリジニウムトリフルオロメタンスルホン酸、Ｎ，Ｎ－ジメチル－Ｎ－（４－メトキシベンジル）ピリジニウムヘキサフルオロアンチモネート、Ｎ，Ｎ－ジエチル－Ｎ－（４－メトキシベンジル）ピリジニウムヘキサフルオロアンチモネート、Ｎ，Ｎ－ジエチル－Ｎ－（４－メトキシベンジル）トルイジニウムヘキサフルオロアンチモネート、Ｎ，Ｎ－ジメチル－Ｎ－（４－メトキシベンジル）トルイジニウムヘキサフルオロアンチモネート等が挙げられる。
　本発明の硬化性組成物は、上記したような熱カチオン重合開始剤を１種または２種以上含んでいてもよい。
　本発明の硬化性組成物のさらに好ましい実施態様においては、前記熱カチオン重合開始剤が、芳香族スルホニウム塩系の熱カチオン重合開始剤、芳香族ヨードニウム塩系の熱カチオン重合開始剤、およびアルミニウム錯体系の熱カチオン重合開始剤からなる群から選択されることを特徴とする。
　本発明の硬化性組成物における熱カチオン重合開始剤の含有量は、使用する熱カチオン重合開始剤の種類に応じ適宜変更することが好ましい。例えば、熱カチオン重合開始剤を使用する場合、硬化性組成物１００質量部に対し、０．１～１５質量部であることが好ましく、０．３～７質量部であることがより好ましい。
（４）光カチオン重合開始剤
　本発明の硬化性組成物に含まれる光カチオン重合開始剤は、可視光線、紫外線、Ｘ線、電子線のような活性エネルギー線の照射によって、カチオン種又はルイス酸を発生させ、カチオン重合性化合物の重合反応を開始するものである。本発明の硬化性組成物に含まれる光カチオン重合開始剤としては、例えば、オニウム塩やメタロセン錯体、鉄－アレン錯体などの化合物を用いることができる。オニウム塩としては、芳香族スルホニウム塩、芳香族ヨードニウム塩、芳香族ジアゾニウム塩、芳香族ホスホニウム塩および芳香族セレニウム塩などが用いられ、これらの対イオンとしては、ＣＦ３ＳＯ３ －、ＢＦ４ －、ＰＦ６ －、ＡｓＦ６ －、およびＳｂＦ６ －などのアニオンが用いられる。これらの中でも、３００ｎｍ以上の波長領域でも紫外線吸収特性を有することから、硬化性に優れ、良好な機械強度や接着強度を有する硬化物を与えることができるため、芳香族スルホニウム塩系の光カチオン重合開始剤を使用することがより好ましい。また、本発明の硬化性組成物は、２種以上の光カチオン重合開始剤を含んでいてもよい。
　芳香族スルホニウム塩としては、ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロホスフェート、４，４’－ビス（ジフェニルスルホニオ）ジフェニルスルフィドビスヘキサフルオロホスフェート、４，４’－ビス〔ジ（β－ヒドロキシエトキシ）フェニルスルホニオ〕ジフェニルスルフィドビスヘキサフルオロアンチモネート、４，４’－ビス〔ジ（β－ヒドロキシエトキシ）フェニルスルホニオ〕ジフェニルスルフィドビスヘキサフルオロホスフェート、７－〔ジ（ｐ－トルイル）スルホニオ〕－２－イソプロピルチオキサントンヘキサフルオロアンチモネート、７－〔ジ（ｐ－トルイル）スルホニオ〕－２－イソプロピルチオキサントンテトラキス（ペンタフルオロフェニル）ボレート、４－フェニルカルボニル－４’－ジフェニルスルホニオ－ジフェニルスルフィドヘキサフルオロホスフェート、４－（ｐ－ｔｅｒｔ－ブチルフェニルカルボニル）－４’－ジフェニルスルホニオ－ジフェニルスルフィドヘキサフルオロアンチモネート、４－（ｐ－ｔｅｒｔ－ブチルフェニルカルボニル）－４’－ジ（ｐ－トルイル）スルホニオ－ジフェニルスルフィドテトラキス（ペンタフルオロフェニル）ボレート、ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロアンチモネート、トリフェニルスルホニウムトリフルオロメタンスルホン酸塩、ビス[４－（ジフェニルスルホニオ）フェニル]スルフィドビスヘキサフルオロアンチモネート、（４－メトキシフェニル）ジフェニルスルホニウムヘキサフルオロアンチモネート等が挙げられる。
　芳香族ヨードニウム塩としては、ジフェニルヨードニウムテトラキス（ペンタフルオロフェニル）ボレート、ジフェニルヨードニウムヘキサフルオロホスフェート、ジフェニルヨードニウムヘキサフルオロアンチモネート、ジ（４－ノニルフェニル）ヨードニウムヘキサフルオロホスフェート、（４－メトキシフェニル）フェニルヨードニウムヘキサフルオロアンチモネート、ビス（４－ｔ－ブチルフェニル）ヨードニウムヘキサフルオロホスフェート等が挙げられる。
　芳香族ジアゾニウム塩としては、ベンゼンジアゾニウムヘキサフルオロアンチモネート、ベンゼンジアゾニウムヘキサフルオロホスフェート、 ベンゼンジアゾニウムテトラフルオロボレート、４－クロロベンゼンジアゾニウムヘキサフルオロホスフェート等が挙げられる。
　芳香族ホスホニウム塩としては、ベンジルトリフェニルホスホニウムヘキサフルオロアンチモネート等が挙げられる。
　芳香族セレニウム塩としては、トリフェニルセレニウムヘキサフルオロホスフェート等が挙げられる。
　鉄－アレン錯体としては、キシレン－シクロペンタジエニル鉄（II）ヘキサフルオロアンチモネート、クメン－シクロペンタジエニル鉄（II）ヘキサフルオロホスフェート、キシレン－シクロペンタジエニル鉄（II）トリス（トリフルオロメチルスルホニル）メタナイド等が挙げられる。
　本発明の硬化性組成物における光カチオン重合開始剤の含有量は、硬化性組成物に含まれるモノエポキシ化合物１００質量部に対し、または硬化性組成物が、後述するその他のエポキシ化合物、後述するオキセタン化合物および／またはビニルエーテルを含む場合は、それらの総量１００質量部に対し、０．１～２０質量部であることが好ましく、０．３～１５質量部であることがより好ましい。光カチオン重合開始剤の含有量を上記数値範囲とすることにより、硬化物の耐熱性をより一層向上させることができる。また、硬化物の透明性をより向上させることができる。
（５）前記モノエポキシ化合物と異なるその他のエポキシ化合物
　本発明の硬化性組成物に含まれるその他のエポキシ化合物としては、上記式（１）で表されるモノエポキシ化合物以外の化合物であって、分子中にエポキシ基を１個以上、好ましくは２個以上有する化合物であり、このような化合物であれば特に限定されるものではない。
　本発明の硬化性組成物に含まれるその他のエポキシ化合物としては、例えば、グリシジルエーテル型エポキシド、グリシジルエステル型エポキシド、グリシジルアミン型エポキシドおよび脂環式エポキシド等が挙げられる。また、その他のエポキシ化合物は、グリシジルエーテル型エポキシド、グリシジルエステル型エポキシド、グリシジルアミン型エポキシドおよび脂環式エポキシド等が重合したエポキシ樹脂であってもよい。
　グリシジルエーテル型エポキシドとしては、ビスフェノールＡジグリシジルエーテル、ビスフェノールＦジグリシジルエーテル、ビスフェノールＳジグリシジルエーテル、テトラメチルビフェノールジグリシジルエーテル、水素化ビスフェノールＡジグリシジルエーテル、臭素化ビスフェノールＡジグリシジルエーテル等の二価フェノールのグリシジルエーテル、ジヒドロキシナフチルクレゾールトリグリシジルエーテル、トリス（ヒドロキシフェニル）メタントリグリシジルエーテル、テトラキス（ヒドロキシフェニル）エタンテトラグリシジルエーテル、ジナフチルトリオールトリグリシジルエーテル、フェノールノボラックグリシジルエーテル、クレゾールノボラックグリシジルエーテル、キシリレン骨格含有フェノールノボラックグリシジルエーテル、ジシクロペンタジエン骨格含有フェノールノボラックグリシジルエーテル、ビフェニル骨格含有フェノールノボラックグリシジルエーテル、テルペン骨格含有フェノールノボラックグリシジルエーテル、ビスフェノールＡノボラックグリシジルエーテル、ビスフェノールＦノボラックグリシジルエーテル、ビスフェノールＳノボラックグリシジルエーテル、ビスフェノールＡＰノボラックグリシジルエーテル、ビスフェノールＣノボラックグリシジルエーテル、ビスフェノールＥノボラックグリシジルエーテル、ビスフェノールＺノボラックグリシジルエーテル、ビフェノールノボラックグリシジルエーテル、テトラメチルビスフェノールＡノボラックグリシジルエーテル、ジメチルビスフェノールＡノボラックグリシジルエーテル、テトラメチルビスフェノールＦノボラックグリシジルエーテル、ジメチルビスフェノールＦノボラックグリシジルエーテル、テトラメチルビスフェノールＳノボラックグリシジルエーテル、ジメチルビスフェノールＳノボラックグリシジルエーテル、テトラメチル－４，４’－ビフェノールノボラックグリシジルエーテル、トリスヒドロキシフェニルメタンノボラックグリシジルエーテル、レゾルシノールノボラックグリシジルエーテル、ハイドロキノンノボラックグリシジルエーテル、ピロガロールノボラックグリシジルエーテル、ジイソプロピリデンノボラックグリシジルエーテル、１，１－ジ－４－ヒドロキシフェニルフルオレンノボラックグリシジルエーテル、フェノール化ポリブタジエンノボラックグリシジルエーテル、エチルフェノールノボラックグリシジルエーテル、ブチルフェノールノボラックグリシジルエーテル、オクチルフェノールノボラックグリシジルエーテル、ナフトールノボラックグリシジルエーテル、水素化フェノールノボラックグリシジルエーテル等の多価フェノールのグリシジルエーテル、エチレングリコールジグリシジルエーテル、プロピレングリコールジグリシジルエーテル、テトラメチレングリコールジグリシジルエーテル、１，６－ヘキサンジオールジグリシジルエーテル、シクロヘキサンジメチロールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、ポリプロピレングリコールジグリシジルエーテル等の二価アルコールのグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、グリセリントリグリシジルエーテル、ペンタエリスリトールテトラグリシジルエーテル、ソルビトールヘキサグリシジルエーテル、ポリグリセリンポリグリシジルエーテル等の多価アルコールのグリシジルエーテル、トリグリシジルイソシアヌレート等が挙げられる。
　グリシジルエステル型エポキシドとしては、グリシジルメタクリレート、フタル酸ジグリシジルエステル、イソフタル酸ジグリシジルエステル、テレフタル酸ジグリシジルエステル、シクロヘキサンジカルボン酸ジグリシジルエステル、トリメット酸トリグリシジルエステル等のカルボン酸のグリシジルエステルやグリシジルエステル型のポリエポキシド等が挙げられる。
　グリシジルアミン型エポキシドとしては、Ｎ，Ｎ－ジグリシジルアニリン、Ｎ，Ｎ－ジグリシジルトルイジン、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジルジアミノジフェニルメタン、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジルジアミノジフェニルスルホン、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジルジエチルジフェニルメタン等のグリシジル芳香族アミン、ビス（Ｎ，Ｎ－ジグリシジルアミノシクロヘキシル）メタン（Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジルジアミノジフェニルメタンの水素化物）、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジル－１，３－（ビスアミノメチル）シクロヘキサン（Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジルキシリレンジアミンの水素化物）、トリスグリシジルメラミン、トリグリシジル－ｐ－アミノフェノール、Ｎ－グリシジル－４－グリシジルオキシピロリドン等のグリシジル複素環式アミン等が挙げられる。
　脂環式エポキシドとしては、ビニルシクロヘキセンジオキシド、リモネンジオキシド、ジシクロペンタジエンジオキシド、ビス（２，３－エポキシシクロペンチル）エーテル、エチレングリコールビスエポキシジシクロペンチルエーテル、３，４－エポキシ－６－メチルシクロへキシルメチル　３’，４’－エポキシ－６’－メチルシクロヘキサンカルボキシレート、３，４－エポキシシクロへキシルメチル　３，４－エポキシシクロヘキサンカルボキシレート、３，４－エポキシ－１－メチルシクロへキシル　３，４－エポキシ－１－メチルヘキサンカルボキシレート、３，４－エポキシ－３－メチルシクロへキシルメチル　３，４－エポキシ－３－メチルヘキサンカルボキシレート、３，４－エポキシ－５－メチルシクロへキシルメチル　３，４－エポキシ－５－メチルシクロヘキサンカルボキシレート、２－（３，４－エポキシシクロへキシル－５，５－スピロ－３，４－エポキシ）シクロヘキサン－メタジオキサン、メチレンビス（３，４－エポキシシクロヘキサン）、（３，３’，４，４’－ジエポキシ）ビシクロヘキシル、２，２－ビス（ヒドロキシメチル）－１－ブタノールの１，２－エポキシ－（２－オキシラニル）シクロヘキサン付加物、テトラヒドロインデンジエポキシド等が挙げられる。本発明の硬化性組成物は、上記したようなその他のエポキシ化合物を１または２種以上含んでいてもよい。
　硬化物の耐熱性という観点からは、上記したその他のエポキシ化合物の含有量は、本発明の硬化性組成物に対して１～９９質量％であることが好ましく、５～９５質量％であることがより好ましい。
　本発明の硬化性組成物において、モノエポキシ化合物と、該モノエポキシ化合物と異なるその他のエポキシ化合物との含有量比は、質量基準で、１：９９～７５：２５であることが好ましく、５：９５～５０：５０であることがより好ましい。
　本発明の硬化性組成物の好ましい実施態様において、前記モノエポキシ化合物と異なるその他のエポキシ化合物はエポキシ樹脂である。
　本発明の硬化性組成物のさらに好ましい実施態様において、前記モノエポキシ化合物と異なるその他のエポキシ化合物が、グリシジルエーテル型エポキシド、グリシジルエステル型エポキシド、および脂環式エポキシドからなる群から選択されることを特徴とする。
（６）反応性希釈剤
　本発明の硬化性組成物は、低粘度化のために、反応性希釈剤をさらに含んでいてもよい。反応性希釈剤としては、例えば、実施例Ｉ１に記載された方法で調製されたモノエポキシ化合物（Ａ）、ブチルグリシジルエーテル、２－エチルヘキシルグリシジルエーテル、Ｃ１２－１３混合アルコールのグリシジルエーテル、１，２－エポキシ－４－ビニルシクロヘキサン等が挙げられる。硬化性組成物は、上記したような反応性希釈剤を１種または２種以上含んでいてもよい。反応性希釈剤の混合比率は、反応性希釈剤を含む硬化性組成物が所望の粘度となるように、適宜調整すればよい。
（７）オキセタン化合物
　本発明の硬化性組成物は、オキセタン化合物をさらに含んでいてもよい。オキセタン化合物としては、１，４－ビス［（３－エチル－３－オキセタニルメトキシ）メチル］ベンゼン、３－エチル－３－ヒドロキシメチルオキセタン、３－エチル－３－（フェノキシメチル）オキセタン、ジ［（３－エチル－３－オキセタニル）メチル］エーテル、３－エチル－３－（２－エチルヘキシルオキシメチル）オキセタン、３－エチル－３－（シクロヘキシルオキシメチル）オキセタン、フェノールノボラックオキセタン、１，３－ビス［（３－エチルオキセタン－３－イル）］メトキシベンゼン、オキセタニルシルセスキオキサン、オキセタニルシリケート、ビス［１－エチル（３－オキセタニル）］メチルエーテル、４，４’－ビス［（３－エチル－３－オキセタニル）メトキシメチル］ビフェニル、４，４’－ビス（３－エチル－３－オキセタニルメトキシ）ビフェニル、エチレングリコール（３－エチル－３－オキセタニルメチル）エーテル、ジエチレングリコールビス（３－エチル－３－オキセタニルメチル）エーテル、ビス（３－エチル－３－オキセタニルメチル）ジフェノエート、トリメチロールプロパンプロパントリス（３－エチル－３－オキセタニルメチル）エーテル、ペンタエリスリトールテトラキス（３－エチル－３－オキセタニルメチル）エーテル、フェノールノボラック型オキセタン等が挙げられる。本発明の硬化性組成物は、上記したようなオキセタン化合物を１種または２種以上含んでいてもよい。
　硬化物の耐熱性という観点からは、硬化性組成物におけるオキセタン化合物の含有量は、１～９０質量％であることが好ましく、５～８５質量％であることがより好ましい。
（８）ビニルエーテル化合物
　本発明の硬化性組成物は、ビニルエーテル化合物をさらに含んでいてもよい。ビニルエーテル化合物としては、例えば、メチルビニルエーテル、エチルビニルエーテル、プロピルビニルエーテル、ブチルビニルエーテルなどの単官能ビニルエーテル、エチレングリコールジビニルエーテル、ブタンジオールジビニルエーテル、シクロヘキサンジメタノールジビニルエーテル、シクロヘキサンジオールジビニルエーテル、トリメチロールプロパントリビニルエーテル、ペンタエリスリトールテトラビニルエーテル、グリセロールトリビニルエーテル、トリエチレングリコールジビニルエーテル、ジエチレングリコールジビニルエーテル等の多官能ビニルエーテル、ヒドロキシエチルビニルエーテル、ヒドロキシブチルビニルエーテル、シクロヘキサンジメタノールモノビニルエーテル、シクロヘキサンジオールモノビニルエーテル、９－ヒドロキシノニルビニルエーテル、プロピレングリコールモノビニルエーテル、ネオペンチルグリコールモノビニルエーテル、グリセロールジビニルエーテル、グリセロールモノビニルエーテル、トリメチロールプロパンジビニルエーテル、トリメチロールプロパンモノビニルエーテル、ペンタエリスリトールモノビニルエーテル、ペンタエリスリトールジビニルエーテル、ペンタエリスリトールトリビニルエーテル、ジエチレングリコールモノビニルエーテル、トリエチレングリコールモノビニルエーテル、テトラエチレングリコールモノビニルエーテル、トリシクロデカンジオールモノビニルエーテル、トリシクロデカンジメタノールモノビニルエーテル等の水酸基を有するビニルエーテル化合物およびアクリル酸２－（２－ビニロキシエトキシ）エチル、メタクリル酸２－（２－ビニロキシエトキシ）エチル等の異種の官能基を有するビニルエーテル等が挙げられる。本発明の硬化性組成物は、上記したようなビニルエーテル化合物を１種または２種以上含んでいてもよい。
　硬化物の耐熱性という観点からは、硬化性組成物におけるビニルエーテル化合物の含有量は、１～９０質量％であることが好ましく、５～８５質量％であることがより好ましい。
（９）水酸基を有する化合物
　本発明の硬化性組成物は、水酸基を有する化合物をさらに含んでいてもよい。硬化性組成物が、水酸基を有する化合物を含むことにより、硬化反応を緩やかに進行させることができる。水酸基を有する化合物としては、例えば、エチレングリコール、ジエチレングリコール、グリセリン等が挙げられる。本発明の硬化性組成物は、上記したような水酸基を有する化合物を１種または２種以上含んでいてもよい。
　硬化物の耐熱性という観点から、本発明の硬化性組成物における水酸基を有する化合物の含有量は、０．１～１０質量％であることが好ましく、０．２～８質量％であることがより好ましい。
（１０）その他の構成成分
　本発明の硬化性組成物は、溶剤をさらに含んでいてもよい。溶剤としては、例えば、メチルエチルケトン、酢酸エチル、トルエン、メタノールおよびエタノール等が挙げられる。
　本発明の硬化性組成物は、その特性を損なわない範囲において、各種添加剤を含んでいてもよい。添加剤としては、例えば、充填剤、シランカップリング剤、離型剤、着色剤、難燃剤、酸化防止剤、光安定剤および可塑剤、消泡剤、光安定剤、顔料や染料等の着色剤、可塑剤、ｐＨ調整剤、着色防止剤、艶消し剤、消臭剤、耐候剤、帯電防止剤、糸摩擦低減剤、スリップ剤、イオン交換剤等が挙げられる。
（１１）硬化性組成物の製造
　本発明の硬化性組成物の製造においては、当業者に広く知られた技術常識に従い、硬化性組成物にさらに含有させる成分、および硬化性組成物の調製方法を適宜選択することができる。
４．硬化物とその製造方法
　本発明の硬化物は、上述の本発明の硬化性組成物を硬化させることにより得られたものである。硬化性組成物の硬化の方法は特に限定されるものではないが、加熱または光照射により適宜行うことができる。
（１）硬化の条件
　加熱により、硬化性組成物を硬化させる場合、多段階的に硬化性組成物を加熱することが好ましい。これにより、硬化反応を十分に進めることができる。例えば、６０～１２０℃で１０～１５０分の一次加熱と、１３０～２００℃で６０～３００分の二次加熱とにより硬化反応を行うことができる。また、例えば、６０～１００℃で１０～１５０分の一次加熱と、１２０～１６０℃で１０～１５０分の二次加熱と、１８０～２５０℃で１０～１５０分の三次加熱とにより硬化反応を行うことができる。
　また、加熱により、硬化性組成物を硬化させる場合、本発明のモノエポキシ化合物の反応性の高さを考慮し、多段階的に硬化性組成物を加熱することが好ましい。これにより、硬化反応を十分に進めることができる。例えば、４０～７０℃で１０～１５０分の一次加熱と、７１～１００℃で１０～１５０分の二次加熱と、１０１～１４０℃で１０～１８０分の三次加熱と、１４１～１７０℃で１０～１５０分の四次加熱と、１７１～２２０℃で１０～１５０分の五次加熱とにより硬化反応を行うことができる。しかしながら、これに限定されるものではなく、モノエポキシ化合物の含有量、硬化性組成物に含まれるその他の化合物などの特性を考慮し、適宜変更して行うことが好ましい。
　さらに、可視光線、紫外線、Ｘ線、電子線のような活性エネルギー線の照射により硬化性組成物を硬化させる場合、硬化性組成物の組成に応じ、使用する活性エネルギー線種や条件を適宜変更することが好ましい。一つの実施態様において、照射強度と照射時間の積で表される積算光量が、１０～５０００ｍＪ／ｃｍ２となるように、紫外線を照射することがさらに好ましい。硬化性組成物への積算光量を上記数値範囲とすることにより、光カチオン重合開始剤由来の活性種を十分に発生させることができる。また、生産性を向上させることもできる。
（２）硬化物の用途
　本発明の硬化性組成物および硬化物の用途としては、具体的には、接着剤、粘着剤、金属、樹脂フィルム、ガラス、紙、木材等の基材上に塗布する塗料、半導体素子や有機薄膜素子（例えば、有機エレクトロルミネッセンス素子や有機薄膜太陽電池素子）の表面保護膜、ハードコート剤、防汚膜および反射防止膜等のコーティング剤、レンズ、プリズム、フィルター、画像表示材料、レンズアレイ、光半導体素子の封止材やリフレクター材料、半導体素子の封止材、光導波路、導光板、光拡散板、回折素子および光学用接着剤等の各種光学部材、注型材料、層間絶縁体、プリント配向基板用保護絶縁膜および繊維強化複合材料等の材料等が挙げられる。
５．反応性希釈剤
　本発明の反応性希釈剤は、上記式（１）で表されるモノエポキシ化合物を少なくとも含んでなる。
　また、本発明の反応性希釈剤は、前記モノエポキシ化合物と異なるその他のエポキシ化合物と混合することができ、この場合、上記式（１）で表されるモノエポキシ化合物と、該モノエポキシ化合物と異なるその他のエポキシ化合物との混合量比は、質量基準で、１：９９～７５：２５であることが好ましく、５：９５～５０：５０であることがより好ましい。
　モノエポキシ化合物と、その他のエポキシ化合物の混合量比を上記数値範囲とすることにより、混合物の粘度をより一層低下させることができると共に、これを硬化させた硬化物の耐熱性をより向上させることができる。
　本発明の好ましい一つの実施態様である本発明の態様Ｉは、以下の発明を包含する。
（１）下記式（１）：
Figure JPOXMLDOC01-appb-C000012
 （式中、Ｒ１乃至Ｒ６はそれぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される）
で表される、モノエポキシ化合物。
（２）（１）に記載のモノエポキシ化合物、該モノエポキシ化合物と異なるその他のエポキシ化合物、および硬化剤または熱カチオン重合開始剤を含んでなる、硬化性組成物。
（３）前記硬化性組成物における、前記（１）に記載のモノエポキシ化合物と、該モノエポキシ化合物と異なるその他のエポキシ化合物との含有量比が、質量基準で、１：９９～７５：２５である、（２）に記載の硬化性組成物。
（４）前記硬化剤が、フェノール化合物、アミン化合物、酸無水物系化合物およびアミド化合物からなる群より選択される１以上の硬化剤である、（２）または（３）に記載の硬化性組成物。
（５）前記モノエポキシ化合物と異なるその他のエポキシ化合物が、エポキシ樹脂である、（２）～（４）のいずれかに記載の硬化性組成物。
（６）前記モノエポキシ化合物と異なるその他のエポキシ化合物が、グリシジルエーテル型エポキシド、グリシジルエステル型エポキシド、および脂環式エポキシドからなる群から選択される、（２）～（４）のいずれかに記載の硬化性組成物。
（７）前記熱カチオン重合開始剤が、芳香族スルホニウム塩系の熱カチオン重合開始剤、芳香族ヨードニウム塩系の熱カチオン重合開始剤、およびアルミニウム錯体系の熱カチオン重合開始剤からなる群から選択される、（２）～（４）のいずれかに記載の硬化性組成物。
（８）（２）～（７）のいずれかに記載の硬化性組成物の硬化物。
（９）（１）に記載のモノエポキシ化合物の製造方法であって、
　下記式（２）：
Figure JPOXMLDOC01-appb-C000013
 （式中、Ｒ１乃至Ｒ６はそれぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される）
で表される化合物と、過酸とを反応させる工程を含んでなり、
　前記過酸の使用量が、下記式（２）で表される化合物１．００モルに対して、０．１０～１．８０モルであることを特徴とする、方法。
（１０）前記過酸が、過酸化水素または有機過酸である、（９）に記載の方法。
（１１）（２）～（７）のいずれかに記載の硬化性組成物を硬化させる工程を含む、硬化物の製造方法。
（１２）（１）に記載のモノエポキシ化合物を少なくとも含む、反応性希釈剤。
　本発明の態様Ｉによれば、硬化性組成物に含有させたとき、硬化性組成物の耐熱性の低下およびこの硬化性組成物を硬化させた際の重量減少を防止しつつ、硬化性組成物の粘度を低下させることができるモノエポキシ化合物を提供することができる。
　本発明の好ましい一つの実施態様である本発明の態様ＩＩは、以下の発明を包含する。
（１）下記式（１）で表されるモノエポキシ化合物：
Figure JPOXMLDOC01-appb-C000014
 （式中、Ｒ１乃至Ｒ６はそれぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される置換基を表す）
と、光カチオン重合開始剤とを含む、硬化性組成物。
（２）前記モノエポキシ化合物と異なるその他のエポキシ化合物をさらに含む、（１）に記載の硬化性組成物。
（３）前記硬化性組成物における、前記モノエポキシ化合物と、前記モノエポキシ化合物と異なるその他のエポキシ化合物との含有量比が、質量基準で、１：９９～７５：２５である、（２）に記載の硬化性組成物。
（４）前記モノエポキシ化合物と異なるその他のエポキシ化合物が、グリシジルエーテル型エポキシド、グリシジルエステル型エポキシド、および脂環式エポキシドからなる群から選択される、（２）または（３）に記載の硬化性組成物。
（５）前記光カチオン重合開始剤が、芳香族スルホニウム塩系の光カチオン重合開始剤である、（１）～（４）のいずれかに記載の硬化性組成物。
（６）（１）～（５）のいずれかに記載の硬化性組成物の硬化物。
　本発明の態様ＩＩによれば、密着性が飛躍的に向上された硬化物を得ることのできる硬化性組成物を提供することができる。
　本発明の好ましい一つの実施態様である本発明の態様ＩＩＩは、以下の発明を包含する。
（１）下記式（１）で表される化合物の立体異性体を含むモノエポキシ化合物であって、１３Ｃ－ＮＭＲ分析による、下記式（１）におけるノルボルナン骨格の橋頭位とビニル基とがトランスの関係にある立体異性体に由来するピーク面積の、化学シフト１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、６６％以上である、モノエポキシ化合物。
Figure JPOXMLDOC01-appb-C000015
 （式中、Ｒ１乃至Ｒ６はそれぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される）
（２）Ｒ１乃至Ｒ６は全て水素であり、ノルボルナン骨格の橋頭位と、ビニル基とがトランスの関係にある立体異性体が下記化学式で表される、（１）に記載のモノエポキシ化合物。
Figure JPOXMLDOC01-appb-C000016
 （３）前記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、６６％以上である、モノエポキシ化合物。
（４）前記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲におけるピークのうち、低磁場側から１番目に生じるピークの面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、３５％以上である、（１）～（３）のいずれかに記載のモノエポキシ化合物。
（５）（１）～（４）のいずれかに記載のモノエポキシ化合物と、熱カチオン重合開始剤、光カチオン重合開始剤、または硬化剤と、を含む硬化性組成物。
（６）前記硬化剤が、フェノール系硬化剤、アミン系硬化剤、酸無水物系硬化剤およびアミド系硬化剤からなる群より選択される１以上の硬化剤である、（５）に記載の硬化性組成物。
（７）（５）または（６）に記載の硬化性組成物の硬化物。
　本発明の態様ＩＩＩによれば、高い耐熱性を有する硬化物の作製が可能なモノエポキシ化合物を提供することができる。
　以下、実施例により、本発明をさらに詳細に説明するが、本発明がこれら実施例に限定されるものではない。
Ｉ．本発明の態様Ｉの実施例
Ｉ－１．実施例Ｉ１：モノエポキシ化合物（Ａ）の合成
（１）モノエポキシ化合物（Ａ）の合成（実施例Ｉ１－１）
　温度計、攪拌機、還流管、滴下装置を備えた反応容器に、下記式（３）で表されるジオレフィン化合物３１３２ｇ、トルエン３１３２ｇおよび酢酸ナトリウムを投入し、－５℃で攪拌しながら３８％過酢酸水溶液３７８３ｇを５時間かけて滴下した。そのまま－５℃で攪拌を継続し、１７時間反応を行った。
　次いで、１０％亜硫酸ナトリウム水溶液を用いて中和処理を行った後、分液操作を行った。圧力２ｈＰａ、塔底温度１３０～１４０℃で蒸留を行い、無色透明の液体２１０９ｇを得た。
　得られた液体は、図１で示す１３Ｃ－ＮＭＲスペクトルおよびＬＣ－ＭＳによる精密質量測定において、理論構造に相当する［Ｍ＋Ｈ］＋＝１９１．１４３９が得られたことから、上記式（１）を満たす目的のモノエポキシ化合物（Ａ）であることを確認した。
　なお、１３Ｃ－ＮＭＲスペクトルから、式（４）、式（５）で表される立体異性体がそれぞれ７５：２５の混合物であることが確認された。モノエポキシ化合物（Ａ）の粘度をＥ型粘度計を用いて測定したところ、１１．０ｍＰａ・ｓであった。
Figure JPOXMLDOC01-appb-C000017
Figure JPOXMLDOC01-appb-C000018
Figure JPOXMLDOC01-appb-C000019
（２）モノエポキシ化合物（Ａ）の合成（実施例Ｉ１－２）
　ねじ口試験管に、アパタイト０．２５ｇおよび（ＣｅｔｙｌＰｙ）９（ＮＨ４）［Ｈ２Ｗ１２Ｏ４２］を０．１７ｇを秤取り、よく混合した。これらの混合物に、下記式（３）で表されるジオレフィン化合物１．２１ｇ、３５％過酸化水素水１．０５ｇ、トルエン０．２０ｇを加えた。２０℃で６時間攪拌した後、反応混合物にトルエン１０ｍＬを加えてろ過を行い、酢酸エチル１００ｍＬを用いてろ液の分液抽出操作を行った。有機層を純水３０ｍＬ、飽和食塩水３０ｍＬで洗浄した。硫酸マグネシウムによって脱水操作を行った後、ロータリーエバポレーターで溶媒を留去した。カラムクロマトグラフィーで精製を行い、上記式（１）を満たす目的のモノエポキシ化合物（Ａ）０．５４ｇを得た。
Figure JPOXMLDOC01-appb-C000020
（３）モノエポキシ化合物（Ａ）の合成（実施例Ｉ１－３）
　温度計、攪拌機、還流管、滴下装置を備えた反応容器に、３５％過酸化水素６．４ｇ、Ｈ３ＰＷ１２Ｏ４０を０．３６ｇを投入し、６０℃で３０分撹拌した。４０℃で冷却した後、上記式（３）で表されるジオレフィン化合物８０．１１ｇ、セチルピリジニウムクロリド０．１３ｇ、クロロホルム５９６ｇを加えた。その後、４０℃で攪拌しながら３５％過酸化水素４４．８４ｇを滴下した後、４０℃で６時間反応を行なった。反応後、クロロホルム４５０ｇを用いて分液抽出操作を行った。有機層を１０％チオ硫酸ナトリウム水溶液３００ｍＬ、１０％炭酸ナトリウム水溶液３００ｍＬ、純水３００ｍＬで洗浄した。硫酸マグネシウムによって脱水操作を行った後、ロータリーエバポレーターで溶媒を留去した。圧力３ｈＰａ、塔底温度１４０～１６０℃で蒸留を行い、上記式（１）で表される目的のモノエポキシ化合物（Ａ）５０．１ｇを得た。
（４）式（６）で表されるジエポキシ化合物の合成（比較例Ｉ１－１）
　温度計、攪拌機、還流管、滴下装置を備えた反応容器に、下記式（３）で表されるジオレフィン化合物８．５ｇ、クロロホルム５０ｍＬを投入し、－５℃で攪拌しながら８％過安息香酸クロロホルム溶液１３０ｍＬを５時間かけて滴下した。そのまま－５℃で攪拌を継続し、反応を行った。
　次いで、５％水酸化ナトリウム水溶液を用いて中和処理を行った後、分液操作を行った。硫酸ナトリウムによって脱水操作を行った後、ロータリーエバポレーターで溶媒を留去した。圧力１ｈＰａで蒸留を行い、無色の固体として下記式（６）で表されるジエポキシ化合物５．８ｇを得た。
Figure JPOXMLDOC01-appb-C000021
Ｉ－２．実施例Ｉ２：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その１：エポキシ化合物（ＩＢ－１）および硬化剤との組合せ）
（１）実施例Ｉ２－１硬化性組成物の作製
　実施例Ｉ１－１で得られたモノエポキシ化合物（Ａ）を１３質量部、エポキシ化合物（ＩＢ－１）を１００質量部、硬化剤を９１質量部および硬化促進剤を２質量部配合し、硬化性組成物を作製した。
（２）比較例Ｉ２－１～Ｉ２－４
　硬化性組成物の組成を下記表Ｉ－１に示されるように変更した以外は、実施例Ｉ２－１と同様にして硬化性組成物を作製した。
（３）物性評価
（硬化性組成物の粘度）
　実施例および比較例において得られた硬化性組成物の粘度をＥ型粘度計を用いて測定した。なお、測定温度は、２５℃とした。測定結果を表Ｉ－１にまとめた。
（硬化性組成物の硬化物の重量減少率）
　実施例Ｉ２－１および比較例Ｉ２－１～Ｉ２－４において得られた硬化性組成物を、熱風循環オーブンにより、１００℃２時間、１６０℃４時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。重量減量率を以下のようにして算出し、表Ｉ－１にまとめた。
　重量減少率（％）＝（硬化性組成物の重量－硬化性組成物の硬化物の重量）／硬化性組成物の重量×１００
（硬化性組成物の硬化物の耐熱性）
　上記のようにして得た硬化物のガラス転移温度を、日立ハイテクサイエンス製示差走査熱量計ＤＳＣ７０２０により、３０～３００℃まで１０℃／ｍｉｎで昇温して測定し、硬化物の耐熱性とした。なお、ここでいうガラス転移温度は、ＪＩＳ　Ｋ７１２１「プラスチックの転移温度測定法」に記載されているうち「中点ガラス転移温度：Ｔｍｇ」に基づいて測定した。測定結果を表Ｉ－１にまとめた。
（総合評価）
　上記実施例および比較例において得られた硬化性組成物の総合評価を以下の評価基準に従い、評価した。評価結果を表Ｉ－１にまとめた。
○：粘度３００ｍＰａ・ｓ未満、重量減少率５％未満かつ耐熱性１４０℃以上
△：粘度３００ｍＰａ・ｓ未満、重量減少率５％未満かつ耐熱性１２０℃以上１４０℃未満
×：粘度３００ｍＰａ・ｓ以上、重量減少率５％以上および／または耐熱性１２０℃未満であり、実用上問題があった。
Figure JPOXMLDOC01-appb-T000022
（表Ｉ－１の説明）
　エポキシ化合物（ＩＢ－１）：ビスフェノールＡ型液状エポキシ樹脂、新日鉄住金化学製、商品名ＹＤ－１２８
ＩＣ－１：ブチルグリシジルエーテル（四日市合成製、商品名：ＤＹ－ＢＰ）
ＩＣ－２：２－エチルヘキシルグルシジルエーテル（四日市合成製、商品名：エポゴーセー２ＥＨ）
ＩＣ－３：Ｃ１２－１３混合アルコールのグリシジルエーテル（四日市合成製、商品名：エポゴーセーＥＮ）
硬化剤：メチルヘキサヒドロ無水フタル酸およびヘキサヒドロ無水フタル酸の混合物、新日本理化製、商品名：リカシッドＭＨ－７００
硬化促進剤：２－エチル－４－メチルイミダゾール、四国化成製、商品名：キュアゾール２Ｅ４ＭＺ
Ｉ－３．実施例Ｉ３：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その２：エポキシ化合物（ＩＢ－２）および硬化剤との組合せ）
（１）実施例Ｉ３－１
　実施例Ｉ１－１で得られたモノエポキシ化合物（Ａ）を１７質量部、エポキシ化合物（ＩＢ－２）を１００質量部、硬化剤を１２９質量部および硬化促進剤を２質量部を配合し、硬化性組成物を作製した。
（２）比較例Ｉ３－１～Ｉ３－４
　硬化性組成物の組成を下記表Ｉ－２に示されるように変更した以外は、実施例Ｉ３－１と同様にして硬化性組成物を作製した。
（３）物性評価
（硬化性組成物の粘度）
　実施例および比較例において得られた硬化性組成物の粘度を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－２にまとめた。
（硬化性組成物の硬化物の重量減少率）
　実施例Ｉ３－１および比較例Ｉ３－１～Ｉ３－４において得られた硬化性組成物を、熱風循環オーブンにより、１００℃２時間、１６０℃２時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。重量減量率を実施例Ｉ２－１と同様にして算出した。測定結果を表Ｉ－２にまとめた。
（硬化性組成物の硬化物の耐熱性）
　上記のようにして得た硬化物の耐熱性を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－２にまとめた。
（総合評価）
　上記実施例および比較例において得られた硬化性組成物の総合評価を以下の評価基準に従い、評価した。評価結果を表Ｉ－２にまとめた。
○：粘度７０ｍＰａ・ｓ未満、重量減少率５％未満かつ耐熱性２００℃以上
△：粘度７０ｍＰａ・ｓ未満、重量減少率５％未満かつ耐熱性１８０℃以上２００℃未満×：粘度７０ｍＰａ・ｓ以上、重量減少率５％以上および／または耐熱性１８０℃未満であり実用上問題があった。
Figure JPOXMLDOC01-appb-T000023
（表Ｉ－２の説明）
　エポキシ化合物（ＩＢ－２）：３’，４’－エポキシシクロヘキシルメチル　３，４－エポキシシクロヘキサンカルボキシレート、ダイセル製、商品名：セロキサイド２０２１Ｐ
Ｉ－４．実施例Ｉ４：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その３：エポキシ化合物（ＩＢ－１）および熱カチオン重合開始剤との組合せ）
（１）実施例Ｉ４－１
　実施例Ｉ１－１で得られたモノエポキシ化合物（Ａ）を４０質量部、エポキシ化合物（ＩＢ－１）を６０質量部および熱カチオン重合開始剤を１質量部配合し、硬化性組成物を作製した。
（２）比較例Ｉ４－１～Ｉ４－４
　硬化性組成物の組成を下記表Ｉ－３に示されるように変更した以外は、実施例Ｉ４－１と同様にして硬化性組成物を作製した。
（３）物性評価
（硬化性組成物の粘度）
　実施例および比較例において得られた硬化性組成物の粘度を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－３にまとめた。
（硬化性組成物の硬化物の重量減少率）
　実施例Ｉ４－１および比較例Ｉ４－１～Ｉ４－４において得られた硬化性組成物を、熱風循環オーブンにより、８０℃２時間、１２０℃２時間、１８０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。重量減量率を実施例Ｉ２－１と同様にして算出した。測定結果を表Ｉ－３にまとめた。
（硬化性組成物の硬化物の耐熱性）
　上記のようにして得た硬化物の耐熱性を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－３にまとめた。
（総合評価）
　上記実施例および比較例において得られた硬化性組成物の総合評価を以下の評価基準に従い、評価した。評価結果を表Ｉ－３にまとめた。
○：粘度３００ｍＰａ・ｓ未満、重量減少率５％未満かつ耐熱性１３０℃以上
△：粘度３００ｍＰａ・ｓ未満、重量減少率５％未満かつ耐熱性１１０℃以上１３０℃未満
×：粘度３００ｍＰａ・ｓ以上、重量減少率５％以上および／または耐熱性１１０℃未満であり、実用上問題があった。
Figure JPOXMLDOC01-appb-T000024
（表Ｉ－３の説明）
　ＩＣ－４：１，２－エポキシ－４－ビニルシクロヘキサン（ダイセル製、商品名：セロキサイド２０００）
　熱カチオン重合開始剤：芳香族スルホニウム塩、三新化学工業製、商品名：ＳＩ－８０Ｌ
Ｉ－５．実施例Ｉ５：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その４：エポキシ化合物（ＩＢ－２）および熱カチオン重合開始剤との組合せ）
（１）実施例Ｉ５－１
　実施例Ｉ１－１で得られたモノエポキシ化合物（Ａ）を５０質量部、エポキシ化合物（ＩＢ－２）を５０質量部および熱カチオン重合開始剤を１質量部配合し、硬化性組成物を作製した。
（２）比較例Ｉ５－１～Ｉ５－４
　硬化性組成物の組成を下記表Ｉ－４に示されるように変更した以外は、実施例Ｉ５－１と同様にして硬化性組成物を作製した。
（３）物性評価
（硬化性組成物の粘度）
　実施例および比較例において得られた硬化性組成物の粘度を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－４にまとめた。
（硬化性組成物の硬化物の重量減少率）
　実施例Ｉ５－１および比較例Ｉ５－１～Ｉ５－４において得られた硬化性組成物を、熱風循環オーブンにより、６０℃２時間、８０℃２時間、１２０℃１時間、１５０℃１時間、１８０℃１時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。重量減量率を実施例Ｉ２－１と同様にして算出した。測定結果を表Ｉ－４にまとめた。
（硬化性組成物の硬化物の耐熱性）
　上記のようにして得た硬化物の耐熱性を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－４にまとめた。
（総合評価）
　上記実施例および比較例において得られた硬化性組成物の総合評価を以下の評価基準に従い、評価した。評価結果を表Ｉ－４にまとめた。
○：粘度７０ｍＰａ・ｓ未満、重量減少率５％未満かつ耐熱性１５０℃以上
△：粘度７０ｍＰａ・ｓ未満、重量減少率５％未満かつ耐熱性１３０℃以上１５０℃未満×：粘度７０ｍＰａ・ｓ以上、重量減少率５％以上および／または耐熱性１３０℃未満であり実用上問題があった。
Figure JPOXMLDOC01-appb-T000025
Ｉ－６．実施例Ｉ６：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その５：各種エポキシ化合物および熱カチオン重合開始剤との組合せ）
（１）実施例Ｉ６－１～Ｉ６－６および比較例Ｉ６－１～Ｉ６－１２
　硬化性組成物の組成を、以下の成分を用いて表Ｉ－５～Ｉ－７に示されるように変更した以外は、実施例Ｉ２－１と同様にして、硬化性組成物を得た。
(i)エポキシ化合物（ＩＢ－２）
　３’，４’－エポキシシクロヘキシルメチル　３，４－エポキシシクロヘキサンカルボキシレート、ダイセル社製、商品名：セロキサイド２０２１Ｐを用いた。
(ii)エポキシ化合物（ＩＢ－４）
　フェノールノボラック型エポキシ樹脂、新日鉄住金化学社製、商品名：ＹＤＰＮ－６３８を用いた。
(iii)エポキシ化合物（ＩＢ－６）
　水素化ビスフェノールＡ型液状エポキシ樹脂、三菱化学社製、商品名：ＹＸ８０００を用いた。
(iv)エポキシ化合物（ＩＢ－９）
　シクロヘキサンジカルボン酸ジグリシジルエステル、東京化成工業社製試薬を用いた。
(v)エポキシ化合物（ＩＢ－１０）
　ビニルシクロヘキセンジオキシド、シグマアルドリッチ社製試薬を用いた。
(vi)エポキシ化合物（ＩＢ－１１）
　２，２－ビス（ヒドロキシメチル）－１－ブタノールの１，２－エポキシ－（２－オキシラニル）シクロヘキサン付加物、ダイセル社製、商品名：ＥＨＰＥ３１５０を用いた。
(vii)エポキシ化合物（ＩＢ－１２）
　（３，３’，４，４’－ジエポキシ）ビシクロへキシル、ダイセル社製、商品名：セロキサイド８０００を用いた。
(viii) モノエポキシ化合物（Ａ）
　実施例Ｉ１－１で得られたモノエポキシ化合物（Ａ）を用いた。
(ix)反応性希釈剤（ＩＣ－２）
　２－エチルヘキシルグリシジルエーテル、四日市合成社製、商品名：エポゴーセー２ＥＨを用いた。
(x)熱カチオン重合開始剤（ＩＥ－２）
　４－アセトキシフェニルジメチルスルホニウムヘキサフルオロアンチモネート、三新化学工業社製、商品名：ＳＩ－１５０Ｌを用いた。
（２）物性評価
（硬化性組成物の粘度）
　実施例および比較例において得られた硬化性組成物の粘度を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－５～Ｉ－７にまとめた。
（硬化性組成物の硬化物の重量減少率）
　上記のようにして得られた硬化性組成物を、以下の条件で加熱し、硬化物を得た。
(a)実施例Ｉ６－１
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１５０℃１時間、１８０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(b)実施例Ｉ６－２
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(c)実施例Ｉ６－３
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１５０℃１時間、１７０℃１時間、２１０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(d)実施例Ｉ６－４
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(e)実施例Ｉ６－５
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１７０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(f)実施例Ｉ６－６
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１３０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(a')比較例Ｉ６－１
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１５０℃１時間、１８０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(b')比較例Ｉ６－２
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１５０℃１時間、１８０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(c')比較例Ｉ６－３
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(d')比較例Ｉ６－４
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(e')比較例Ｉ６－５
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１５０℃１時間、１７０℃１時間、２１０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(f')比較例Ｉ６－６
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１５０℃１時間、１７０℃１時間、２１０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(g')比較例Ｉ６－７
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(h')比較例Ｉ６－８
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(i')比較例Ｉ６－９
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１７０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(j')比較例Ｉ６－１０
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１７０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(k')比較例Ｉ６－１１
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１３０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(l')比較例Ｉ６－１２
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１３０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
　上記のようにして得た硬化物の重量減量率を実施例Ｉ２－１と同様にして算出した。測定結果を表Ｉ－５～Ｉ－７にまとめた。
（硬化性組成物の硬化物の耐熱性）
　上記のようにして得た硬化物の耐熱性を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－５～Ｉ－７にまとめた。
（総合評価）
　上記実施例Ｉ６－１～Ｉ６－６および比較例Ｉ６－１～Ｉ６－１２において得られた硬化性組成物の総合評価を、表Ｉ－５～Ｉ－７にまとめた粘度、重量減少率および耐熱性の測定結果と、各実験区の実施例とその対応する比較例に共通に設定した表Ｉ－５～Ｉ－７に記載の粘度、重量減少率および耐熱性の基準値を用いて、以下の評価基準に従い総合評価を行った。評価結果を表Ｉ－５～Ｉ－７にまとめた。
評価基準
粘度の評価：硬化性組成物の粘度の各測定結果が各表の各実験区ごとに記載された基準値以下の場合に粘度の評価基準を満たすものとする。
重量減少率の評価：硬化物の重量減少率の各測定結果が各表の各実験区ごとに記載された基準値以下の場合に重量減少率の評価基準を満たすものとする。
耐熱性の評価：硬化物の耐熱性の各測定結果が各表の各実験区ごとに記載された基準値以上の場合に耐熱性の評価基準を満たすものとする。
総合評価：上の３つの評価基準の全てを満たす場合に総合評価を○と評価する。
Figure JPOXMLDOC01-appb-T000026
Figure JPOXMLDOC01-appb-T000027
Figure JPOXMLDOC01-appb-T000028
Ｉ－７．実施例Ｉ７：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その６：各種オキセタン化合物および熱カチオン重合開始剤との組合せ）
（１）実施例Ｉ７－１～Ｉ７－４および比較例Ｉ７－１～Ｉ７－８
　硬化性組成物の組成を、以下の成分を用いて表Ｉ－８およびＩ－９に示されるように変更した以外は、実施例Ｉ２－１と同様にして、硬化性組成物を得た。
(i)エポキシ化合物（ＩＢ－１）
　ビスフェノールＡ型液状エポキシ樹脂、新日鉄住金化学社製、商品名：ＹＤ－１２８を用いた。
(ii) モノエポキシ化合物（Ａ）
　実施例Ｉ１－１で得られたモノエポキシ化合物（Ａ）を用いた。
(iii)反応性希釈剤（ＩＣ－２）
　２－エチルヘキシルグリシジルエーテル、四日市合成社製、商品名：エポゴーセー２ＥＨを用いた。
(iv)オキセタン化合物（ＩＤ－１）
　１，４－ビス［（３－エチル－３－オキセタニルメトキシ）メチル］ベンゼン、東亞合成社製、商品名：アロンオキセタンＯＸＴ－１２１を用いた。
(v)オキセタン化合物（ＩＤ－２）
　３－エチル－３－ヒドロキシメチルオキセタン、東亞合成社製、商品名：アロンオキセタンＯＸＴ－１０１を用いた。
(vi)オキセタン化合物（ＩＤ－３）
　ジ［（３－エチル－３－オキセタニル）メチル］エーテル、東亞合成社製、商品名：アロンオキセタンＯＸＴ－２２１を用いた。
(vii)オキセタン化合物（ＩＤ－４）
　３－エチル－３－（２－エチルヘキシルオキシメチル）オキセタン、東亞合成社製、商品名：アロンオキセタンＯＸＴ－２１２を用いた。
(viii)熱カチオン重合開始剤（ＩＥ－２）
　４－アセトキシフェニルジメチルスルホニウムヘキサフルオロアンチモネート、三新化学工業社製、商品名：ＳＩ－１５０Ｌを用いた。
（２）物性評価
（硬化性組成物の粘度）
　実施例および比較例において得られた硬化性組成物の粘度を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－８およびＩ－９にまとめた。
（硬化性組成物の硬化物の重量減少率）
　上記のようにして得られた硬化性組成物を、以下の条件で加熱し、硬化物を得た。
(a)実施例Ｉ７－１
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、１４０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(b)実施例Ｉ７－２
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１５０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(c)実施例Ｉ７－３
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１３０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(d)実施例Ｉ７－４
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、１７０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(a')比較例Ｉ７－１
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、１４０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(b')比較例Ｉ７－２
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、１４０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(c')比較例Ｉ７－３
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１５０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(d')比較例Ｉ７－４
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１５０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(e')比較例Ｉ７－５
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１３０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(f')比較例Ｉ７－６
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１０℃１時間、１３０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(g')比較例Ｉ７－７
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、１７０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(h')比較例Ｉ７－８
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、１７０℃１時間、２２０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
　上記のようにして得た硬化物の重量減量率を実施例Ｉ２－１と同様にして算出した。測定結果を表Ｉ－８およびＩ－９にまとめた。
（硬化性組成物の硬化物の耐熱性）
　上記のようにして得た硬化物の耐熱性を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－８およびＩ－９にまとめた。
（総合評価）
　上記実施例Ｉ７－１～Ｉ７－４および比較例Ｉ７－１～Ｉ７－８において得られた硬化性組成物の総合評価を、表Ｉ－８およびＩ－９にまとめた粘度、重量減少率および耐熱性の測定結果と、各実験区の実施例とその対応する比較例に共通に設定した表Ｉ－８およびＩ－９に記載の粘度、重量減少率および耐熱性の基準値を用いて、以下の評価基準に従い総合評価を行った。評価結果を表Ｉ－８およびＩ－９にまとめた。
評価基準
粘度の評価：硬化性組成物の粘度の各測定結果が各表の各実験区ごとに記載された基準値以下の場合に粘度の評価基準を満たすものとする。
重量減少率の評価：硬化物の重量減少率の各測定結果が各表の各実験区ごとに記載された基準値以下の場合に重量減少率の評価基準を満たすものとする。
耐熱性の評価：硬化物の耐熱性の各測定結果が各表の各実験区ごとに記載された基準値以上の場合に耐熱性の評価基準を満たすものとする。
総合評価：上の３つの評価基準の全てを満たす場合に総合評価を○と評価する。
Figure JPOXMLDOC01-appb-T000029
Figure JPOXMLDOC01-appb-T000030
Ｉ－８．実施例Ｉ８：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その７：各種熱カチオン重合開始剤との組合せ）
（１）実施例Ｉ８－１～Ｉ８－４および比較例Ｉ８－１～Ｉ８－８
　硬化性組成物の組成を、以下の成分を用いて表Ｉ－１０およびＩ－１１に示されるように変更した以外は、実施例Ｉ２－１と同様にして、硬化性組成物を得た。
(i)エポキシ化合物（ＩＢ－１）
　ビスフェノールＡ型液状エポキシ樹脂、新日鉄住金化学社製、商品名：ＹＤ－１２８を用いた。
(ii) モノエポキシ化合物（Ａ）
　実施例Ｉ１－１で得られたモノエポキシ化合物（Ａ）を用いた。
(iii)反応性希釈剤（ＩＣ－２）
　２－エチルヘキシルグリシジルエーテル、四日市合成社製、商品名：エポゴーセー２ＥＨを用いた。
(iv)熱カチオン重合開始剤（ＩＥ－３）
　４－ヒドロキシフェニルベンジルメチルスルホニウムヘキサフルオロアンチモネート、三新化学工業社製、商品名：ＳＩ－１００Ｌを用いた。
(v)熱カチオン重合開始剤（ＩＥ－４）
　ビス［４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル］スルフィドビスヘキサフルオロアンチモネート、ＡＤＥＫＡ社製、アデカアークルズＳＰ－１７０を用いた。
(vi)熱カチオン重合開始剤（ＩＥ－５）
　ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロアンチモネート、サンアプロ社製、ＣＰＩ－１０１Ａを用いた。
(vii)熱カチオン重合開始剤（ＩＥ－６）
　４－メチルフェニル－４－（１－メチルエチル）フェニルヨードニウムテトラキス（ペンタフルオロフェニル）ボレート、東京化成工業社製試薬を用いた。
（２）物性評価
（硬化性組成物の粘度）
　実施例および比較例において得られた硬化性組成物の粘度を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－１０およびＩ－１１にまとめた。
（硬化性組成物の硬化物の重量減少率）
　上記のようにして得られた硬化性組成物を、以下の条件で加熱し、硬化物を得た。
(a)実施例Ｉ８－１
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１５℃１時間、１３０℃１時間、１９０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(b)実施例Ｉ８－２
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(c)実施例Ｉ８－３
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、８０℃１時間、１４０℃１時間、１８０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(d)実施例Ｉ８－４
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１４０℃１時間、１６０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(a')比較例Ｉ８－１
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１５℃１時間、１３０℃１時間、１９０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(b')比較例Ｉ８－２
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１１５℃１時間、１３０℃１時間、１９０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(c')比較例Ｉ８－３
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(d')比較例Ｉ８－４
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１２０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(e')比較例Ｉ８－５
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、８０℃１時間、１４０℃１時間、１８０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(f')比較例Ｉ８－６
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、８０℃１時間、１４０℃１時間、１８０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(g') 比較例Ｉ８－７
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１４０℃１時間、１６０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
(h') 比較例Ｉ８－８
　上記のようにして得られた硬化性組成物を、熱風循環オーブンにより、１４０℃１時間、１６０℃１時間、２４０℃２時間加熱することにより硬化させ、硬化性組成物の硬化物を得た。
　上記のようにして得た硬化物の重量減量率を実施例Ｉ２－１と同様にして算出した。測定結果を表Ｉ－１０およびＩ－１１にまとめた。
（硬化性組成物の硬化物の耐熱性）
　上記のようにして得た硬化物の耐熱性を実施例Ｉ２－１と同様にして測定した。測定結果を表Ｉ－１０およびＩ－１１にまとめた。
（総合評価）
　上記実施例Ｉ８－１～Ｉ８－４および比較例Ｉ８－１～Ｉ８－８において得られた硬化性組成物の総合評価を、表Ｉ－１０およびＩ－１１にまとめた粘度、重量減少率および耐熱性の測定結果と、各実験区の実施例とその対応する比較例に共通に設定した表Ｉ－１０およびＩ－１１に記載の粘度、重量減少率および耐熱性の基準値を用いて、以下の評価基準に従い総合評価を行った。評価結果を表Ｉ－１０およびＩ－１１にまとめた。
評価基準
粘度の評価：硬化性組成物の粘度の各測定結果が各表の各実験区ごとに記載された基準値以下の場合に粘度の評価基準を満たすものとする。
重量減少率の評価：硬化物の重量減少率の各測定結果が各表の各実験区ごとに記載された基準値以下の場合に重量減少率の評価基準を満たすものとする。
耐熱性の評価：硬化物の耐熱性の各測定結果が各表の各実験区ごとに記載された基準値以上の場合に耐熱性の評価基準を満たすものとする。
総合評価：上の３つの評価基準の全てを満たす場合に総合評価を○と評価する。
Figure JPOXMLDOC01-appb-T000031
Figure JPOXMLDOC01-appb-T000032
ＩＩ.本発明の態様ＩＩの実施例
ＩＩ－１．実施例ＩＩ１：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その１：エポキシ化合物（ＩＩＢ－１）および光カチオン重合開始剤（ＩＩＤ－１）との組合せ）
（１）実施例ＩＩ１－１
　硬化性組成物の作製
　上記のようにして得られたモノエポキシ化合物（Ａ）と、その他のエポキシ化合物（ＩＩＢ－１）と、光カチオン重合開始剤（ＩＩＤ－１）とを下記の組成となるように混合し、硬化性組成物を作製した。
＜硬化性組成物組成＞
・モノエポキシ化合物（Ａ）　　　２５質量部（実施例Ｉ１－１に記載された方法で製造されたモノエポキシ化合物）
・その他のエポキシ化合物（ＩＩＢ－１）　　　７５質量部（ビスフェノールＡ型液状エポキシ樹脂、新日鉄住金化学製、商品名：ＹＤ－１２８）
・光カチオン重合開始剤（ＩＩＤ－１）　　　１０質量部（芳香族スルホニウム塩：ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロホスフェートのプロピレンカーボネート５０％溶液、サンアプロ社製、商品名：ＣＰＩ－１００Ｐ）
（２）実施例ＩＩ１－２および実施例ＩＩ１－３
　モノエポキシ化合物（Ａ）およびその他のエポキシ化合物（ＩＩＢ－１）の含有量を表ＩＩ－１に示す量に変更した以外は、実施例ＩＩ１－１と同様にして硬化性組成物を得た。
（３）比較例ＩＩ１－１
　モノエポキシ化合物（Ａ）を１，２－エポキシ－４－ビニルシクロヘキサン（ダイセル社製、商品名：セロキサイド２０００）に変更した以外は、実施例ＩＩ１－１と同様にして硬化性組成物を作製した。
（４）比較例ＩＩ１－２および比較例ＩＩ１－３
　１，２－エポキシ－４－ビニルシクロヘキサンおよびその他のエポキシ化合物（ＩＩＢ－１）の含有量を表ＩＩ－１に示す量に変更した以外は、比較例ＩＩ１－１と同様にして硬化性組成物を得た。
（５）硬化性組成物の性能評価
＜密着性試験（剥離強度の測定）＞
　上記実施例ＩＩ１－１～ＩＩ１－３および比較例ＩＩ１－１～ＩＩ１－３において得られた硬化性組成物を、ＰＥＴフィルム（東洋紡社製、商品名：コスモシャインＡ４３００）上に５μｍ厚となるように塗布し、同様のＰＥＴフィルムとラミネートした。次いで、積算光量が、１，５００ｍＪ／ｃｍ２となるように紫外線光を室温（２３℃）で照射し、硬化性組成物を硬化させ、積層フィルムを得た。
　この積層フィルムから、長さ１５０ｍｍ、幅３０ｍｍの短冊状試験片を切り出し、東洋精機社製ストログラフＥ－Ｌにより９０度剥離強度（２３℃、剥離速度３００ｍｍ／ｍｉｎ）を測定した。測定結果を表ＩＩ－１にまとめた。なお、剥離強度が非常に高く、ＰＥＴフィルムの凝集破壊が生じたものについては測定不能と記載した。これは、接着力がＰＥＴフィルムの凝集力以上であるため、接着力が非常に優れることを意味する。
Figure JPOXMLDOC01-appb-T000033
ＩＩ－２．実施例ＩＩ２：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その２：エポキシ化合物（ＩＩＢ－１３）および光カチオン重合開始剤（ＩＩＤ－１）との組合せ）
（１）実施例ＩＩ２－１
　硬化性組成物の作製
　上記のようにして得られたモノエポキシ化合物（Ａ）と、その他のエポキシ化合物（ＩＩＢ－１３）と、光カチオン重合開始剤（ＩＩＤ－１）とを下記の組成となるように混合し、硬化性組成物を作製した。
＜硬化性組成物組成＞
・モノエポキシ化合物（Ａ）　　　５０質量部（実施例Ｉ１－１に記載された方法で製造されたモノエポキシ化合物）
・その他のエポキシ化合物（ＩＩＢ－１３）　　　５０質量部（（３，３’，４，４’－ジエポキシ）ビシクロへキシル、ダイセル社製、商品名：セロキサイド８０００）
・光カチオン重合開始剤（ＩＩＤ－１）　　　１０質量部（芳香族スルホニウム塩：ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロホスフェートのプロピレンカーボネート５０％溶液、サンアプロ社製、商品名：ＣＰＩ－１００Ｐ）
（２）実施例ＩＩ２－２
　モノエポキシ化合物（Ａ）およびその他のエポキシ化合物（ＩＩＢ－１３）の含有量を表ＩＩ－２に示す量に変更した以外は、実施例ＩＩ２－１と同様にして硬化性組成物を得た。
（３）比較例ＩＩ２－１
　モノエポキシ化合物（Ａ）を１，２－エポキシ－４－ビニルシクロヘキサンに変更した以外は、実施例ＩＩ２－１と同様にして硬化性組成物を作製した。
（４）比較例ＩＩ２－２
　１，２－エポキシ－４－ビニルシクロヘキサンおよびその他のエポキシ化合物（ＩＩＢ－１３）の含有量を表ＩＩ－２に示す量に変更した以外は、比較例ＩＩ２－１と同様にして硬化性組成物を得た。
（５）硬化性組成物の性能評価
＜密着性試験（剥離強度の測定）＞
　上記実施例ＩＩ２－１およびＩＩ２－２並びに比較例ＩＩ２－１およびＩＩ２－２において得られた硬化性組成物を、実施例ＩＩ１（５）に記載された方法に従い、積層フィルムを得て、剥離強度を測定した。測定結果を表ＩＩ－２にまとめた。なお、剥離強度が非常に高く、ＰＥＴフィルムの凝集破壊が生じたものについては測定不能と記載した。これは、接着力がＰＥＴフィルムの凝集力以上であるため、接着力が非常に優れることを意味する。
Figure JPOXMLDOC01-appb-T000034
ＩＩ－３．実施例ＩＩ３：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その３：各種エポキシ化合物および光カチオン重合開始剤（ＩＩＤ－１）との組合せ）
（１）実施例ＩＩ３－１～ＩＩ３－８および比較例ＩＩ３－１～ＩＩ３－８
　硬化性組成物の組成を、以下の成分を用いて表ＩＩ－３およびＩＩ－４に示されるように変更した以外は、実施例ＩＩ１－１と同様にして、硬化性組成物を得た。
(i)エポキシ化合物（ＩＩＢ－２）
　３’，４’－エポキシシクロヘキシルメチル　３，４－エポキシシクロヘキサンカルボキシレート、ダイセル社製、商品名：セロキサイド２０２１Ｐを用いた。
(ii)エポキシ化合物（ＩＩＢ－３）
　クレゾールノボラック型エポキシ樹脂、ＤＩＣ社製、商品名：Ｎ－６６０を用いた。
(iii)エポキシ化合物（ＩＩＢ－５）
　ビスフェノールＦ型液状エポキシ樹脂、新日鉄住金化学社製、商品名：ＹＤＦ－１７０を用いた。
(iv)エポキシ化合物（ＩＩＢ－６）
　水素化ビスフェノールＡ型液状エポキシ樹脂、三菱化学社製、商品名：ＹＸ８０００を用いた。
(v)エポキシ化合物（ＩＩＢ－８）
　テトラメチレングリコールジグリシジルエーテル、東京化成工業社製試薬を用いた。
(vi)エポキシ化合物（ＩＩＢ－９）
　シクロヘキサンジカルボン酸ジグリシジルエステル、東京化成工業社製試薬を用いた。
(vii)エポキシ化合物（ＩＩＢ－１１）
　２，２－ビス（ヒドロキシメチル）－１－ブタノールの１，２－エポキシ－（２－オキシラニル）シクロヘキサン付加物、ダイセル社製、商品名：ＥＨＰＥ３１５０を用いた。
(viii)エポキシ化合物（ＩＩＢ－１４）
　特開２０１２－１１６３９０号公報に記載された方法で製造されたテトラヒドロインデンジエポキシドを用いた。
(ix) モノエポキシ化合物（Ａ）
実施例Ｉ１－１に記載された方法で製造されたモノエポキシ化合物を用いた。
(x)１，２－エポキシ－４－ビニルシクロヘキサン
　１，２－エポキシ－４－ビニルシクロヘキサン、ダイセル社製、商品名：セロキサイド２０００を用いた。
(xi)光カチオン重合開始剤（ＩＩＤ－１）
　ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロホスフェートのプロピレンカーボネート５０％溶液、サンアプロ社製、ＣＰＩ－１００Ｐを用いた。
（２）硬化性組成物の性能評価
＜密着性試験（剥離強度の測定）＞
　上記実施例ＩＩ３－１～ＩＩ３－８および比較例ＩＩ３－１～ＩＩ３－８において得られた硬化性組成物を、実施例ＩＩ１（５）に記載された方法に従い、積層フィルムを得て、剥離強度を測定した。測定結果を表ＩＩ－３およびＩＩ－４にまとめた。なお、剥離強度が非常に高く、ＰＥＴフィルムの凝集破壊が生じたものについては測定不能と記載した。これは、接着力がＰＥＴフィルムの凝集力以上であるため、接着力が非常に優れることを意味する。
Figure JPOXMLDOC01-appb-T000035
Figure JPOXMLDOC01-appb-T000036
ＩＩ－４．実施例ＩＩ４：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その４：各種オキセタン化合物および光カチオン重合開始剤（ＩＩＤ－１）との組合せ）
（１）実施例ＩＩ４－１およびＩＩ４－２並びに比較例ＩＩ４－１およびＩＩ４－２
　硬化性組成物の組成を、以下の成分を用いて表ＩＩ－５に示されるように変更した以外は、実施例ＩＩ１－１と同様にして、硬化性組成物を得た。
(i)モノエポキシ化合物（Ａ）
　実施例Ｉ１－１に記載された方法で製造されたモノエポキシ化合物を用いた。
(ii)１，２－エポキシ－４－ビニルシクロヘキサン
　１，２－エポキシ－４－ビニルシクロヘキサン、ダイセル社製、商品名：セロキサイド２０００を用いた。
(iii)オキセタン化合物（ＩＩＣ－２）
　３－エチル－３－ヒドロキシメチルオキセタン、東亞合成社製、商品名：アロンオキセタンＯＸＴ－１０１を用いた。
(iv)オキセタン化合物（ＩＩＣ－３）
　ジ［（３－エチル－３－オキセタニル）メチル］エーテル、東亞合成社製、商品名：アロンオキセタンＯＸＴ－２２１を用いた。
(v)光カチオン重合開始剤（ＩＩＤ－１）
　ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロホスフェートのプロピレンカーボネート５０％溶液、サンアプロ社製、ＣＰＩ－１００Ｐを用いた。
（２）硬化性組成物の性能評価
＜密着性試験（剥離強度の測定）＞
　上記実施例ＩＩ４－１およびＩＩ４－２並びに比較例ＩＩ４－１およびＩＩ４－２において得られた硬化性組成物を、実施例ＩＩ１（５）に記載された方法に従い、積層フィルムを得て、剥離強度を測定した。測定結果を表ＩＩ－５にまとめた。
Figure JPOXMLDOC01-appb-T000037
ＩＩ－５．実施例ＩＩ５：モノエポキシ化合物（Ａ）を含む硬化性組成物の調製とその評価（その５：エポキシ化合物（ＩＩＢ－１）および各種光カチオン重合開始剤との組合せ）
（１）実施例ＩＩ５－１およびＩＩ５－２並びに比較例ＩＩ５－１およびＩＩ５－２
　硬化性組成物の組成を、以下の成分を用いて表ＩＩ－６に示されるように変更した以外は、実施例ＩＩ１－１と同様にして、硬化性組成物を得た。
(i)エポキシ化合物（ＩＩＢ－１）
　ビスフェノールＡ型液状エポキシ樹脂、新日鉄住金化学社製、商品名：ＹＤ－１２８を用いた。
(ii)モノエポキシ化合物（Ａ）
　実施例Ｉ１－１に記載された方法で製造されたモノエポキシ化合物を用いた。
(iii)１，２－エポキシ－４－ビニルシクロヘキサン
　１，２－エポキシ－４－ビニルシクロヘキサン、ダイセル社製、商品名：セロキサイド２０００を用いた。
(iv)光カチオン重合開始剤（ＩＩＤ－２）
　ジフェニル－４－（フェニルチオ）フェニルスルホニウムヘキサフルオロアンチモネート、サンアプロ社製、ＣＰＩ－１０１Ａを用いた。
(v)光カチオン重合開始剤（ＩＩＤ－３）
　ビス［４－（ジ（４－（２－ヒドロキシエトキシ））フェニルスルホニオ）フェニル］スルフィドビスヘキサフルオロアンチモネート、ＡＤＥＫＡ社製、アデカアークルズＳＰ－１７０を用いた。
（２）硬化性組成物の性能評価
＜密着性試験（剥離強度の測定）＞
　上記実施例ＩＩ５－１およびＩＩ５－２並びに比較例ＩＩ５－１およびＩＩ５－２において得られた硬化性組成物を、実施例ＩＩ１（５）に記載された方法に従い、積層フィルムを得て、剥離強度を測定した。測定結果を表ＩＩ－６にまとめた。なお、剥離強度が非常に高く、ＰＥＴフィルムの凝集破壊が生じたものについては測定不能と記載した。これは、接着力がＰＥＴフィルムの凝集力以上であるため、接着力が非常に優れることを意味する。
Figure JPOXMLDOC01-appb-T000038
ＩＩＩ.本発明の態様ＩＩＩの実施例
ＩＩＩ－１．実施例ＩＩＩ１：モノエポキシ化合物（Ａ－１）の合成
　温度計、攪拌機、還流管、滴下装置を備えた反応容器に、下記式（３）で表されるジオレフィン化合物３１３２ｇ、トルエン３１３２ｇおよび酢酸ナトリウムを投入し、－５℃で攪拌しながら３８％過酢酸水溶液３７８３ｇを５時間かけて滴下した。そのまま－５℃で攪拌を継続し、１７時間反応を行った。
　次いで、１０％亜硫酸ナトリウム水溶液を用いて中和処理を行った後、分液操作を行った。圧力２ｈＰａ、塔底温度１３０～１４０℃で蒸留を行い、無色透明の液体である、上記式（１）を満たすモノエポキシ化合物（Ａ－１）を２１０９ｇ得た。
　得られたモノエポキシ化合物（Ａ－１）を下記条件にて１３Ｃ－ＮＭＲ分析を行った。ノルボルナン骨格の橋頭位と、ビニル基とがトランスの関係にある立体異性体、すなわち下記式（４’）および（５’）で表される化合物に由来するピーク面積の、化学シフト１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合は、７７．０３％であった。モノエポキシ化合物（Ａ－１）のＮＭＲチャートを図２に表す。（ＮＭＲ分析条件）
測定機器：アジレント・テクノロジー社製ＤＤ２
プローブ：Ｏｎｅ
測定モード：完全デカップリング
積算回数：５１２
繰り返し時間：２．１３ｓ
測定時間：２５分
溶媒：重クロロホルム
温度：２３℃ 
内部標準：重クロロホルム
　図２のＮＭＲチャートによれば、モノエポキシ化合物（Ａ－１）の、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合は、７７．０３％であった。また、図２のＮＭＲチャートによれば、モノエポキシ化合物（Ａ－１）の、化学シフト１４０～１４２ｐｐｍの範囲において低磁場側から１番目に生じるピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合は、６１．４０％であった。
　また、モノエポキシ化合物（Ａ－１）について下記条件にてガスクロマトグラフィー分析を行った。モノエポキシ化合物（Ａ－１）のガスクロマトグラフを図３に示す。
（ガスクロマトグラフィー分析条件）
測定機器：アジレント・テクノロジー株式会社製Ａｇｉｌｅｎｔ６８５０シリーズ
カラム：ＨＰ－１、ジメチルポリシロキサン、長さ：６０．０ｍ、内径：２５０μｍ、膜厚：０．２５μｍ
キャリアガス：Ｎ２
流速：１．３ｍＬ／分
試料注入口温度：１４０℃
検出器温度：２５０℃
試料注入量：０．２μＬ
昇温条件：８０℃（３分間）、８０～１５０℃（１０℃／分）、１５０～２５０℃（５℃／分）、２５０℃（２０分間）
Figure JPOXMLDOC01-appb-C000039
Figure JPOXMLDOC01-appb-C000040
ＩＩＩ－２.実施例ＩＩＩ２：モノエポキシ化合物（Ａ－２）の合成
　温度計、攪拌機、還流管、滴下装置を備えた反応容器に、３５％過酸化水素を６．４ｇ、Ｈ３ＰＷ１２Ｏ４０を０．３６ｇ投入し、６０℃で３０分撹拌した。４０℃で冷却した後、上記式（３）で表されるジオレフィン化合物８０．１１ｇ、セチルピリジニウムクロリド０．１３ｇ、クロロホルム５９６ｇを加えた。その後、４０℃で攪拌しながら３５％過酸化水素４４．８４ｇを滴下した後、４０℃で６時間反応を行なった。反応後、クロロホルム４５０ｇを用いて分液抽出操作を行った。有機層を１０％チオ硫酸ナトリウム水溶液３００ｍＬ、１０％炭酸ナトリウム水溶液３００ｍＬ、純水３００ｍＬで洗浄した。硫酸マグネシウムによって脱水操作を行った後、ロータリーエバポレーターで溶媒を留去した。圧力３ｈＰａ、塔底温度１４０～１７０℃で蒸留を行い、塔底温度１６７℃で目的のモノエポキシ化合物（Ａ－２）４．９ｇを得た。
　得られたモノエポキシ化合物（Ａ－２）を上記条件にて１３Ｃ－ＮＭＲ分析を行った。ノルボルナン骨格の橋頭位と、ビニル基とがトランスの関係にある立体異性体に由来するピーク面積の、シフト値１４０～１４５ｐｐｍにおける総ピーク面積に対する割合は、６４．８９％であった。モノエポキシ化合物（Ａ－２）のＮＭＲチャートを図４に表す。
　図４のＮＭＲチャートによれば、モノエポキシ化合物（Ａ－２）の、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合は、６４．８９％であった。また、図４のＮＭＲチャートによれば、モノエポキシ化合物（Ａ－２）の、化学シフト１４０～１４２ｐｐｍの範囲において低磁場側から１番目に生じるピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合は、３１．０４％であった。
　また、モノエポキシ化合物（Ａ－２）について、上記同様ガスクロマトグラフィー分析を行った。モノエポキシ化合物（Ａ－２）のガスクロマトグラフを図５に示す。
Figure JPOXMLDOC01-appb-C000041
ＩＩＩ－３.実施例ＩＩＩ３：立体異性体含有率を変動させたモノエポキシ化合物と熱カチオン重合開始剤を含む硬化性組成物の調製とその評価（その１）
（実施例ＩＩＩ３－１）
　上記のようにして得られたモノエポキシ化合物（Ａ－１）、その他のエポキシ化合物（ＩＩＩＢ－１）および熱カチオン重合開始剤を下記の組成となるように混合し、硬化性組成物を得た。
＜硬化性組成物の組成＞
・モノエポキシ化合物（Ａ－１）　　　６０質量部
・その他のエポキシ化合物（ＩＩＩＢ－１）　　　４０質量部（３’，４’－エポキシシクロヘキシルメチル ３，４－エポキシシクロヘキサンカルボキシレート、ダイセル製、商品名：セロキサイド２０２１Ｐ）
・熱カチオン重合開始剤　　　１質量部（芳香族スルホニウム塩、三新化学工業社製、商品名：ＳＩ－８０Ｌ）
（実施例ＩＩＩ３－２）
　モノエポキシ化合物（Ａ－１）をモノエポキシ化合物（Ａ－２）に変更した以外は、実施例ＩＩＩ３－１と同様にして硬化性組成物を得た。
＜耐熱性評価＞
　上記実施例および比較例より得られた硬化性組成物を、熱風循環オーブンにより、６０℃にて２時間、８０℃にて２時間、１２０℃にて１時間、１５０℃にて１時間、１８０℃にて１時間加熱し、硬化物を得た。
　得られた硬化物のガラス転移温度を、ＳＩＩナノテクノロジー製示差走査熱量計ＤＳＣ７０２０により、３０～３００℃まで１０℃／ｍｉｎで昇温して測定し、硬化物の耐熱性とした。なお、ここでいうガラス転移温度は、ＪＩＳ　Ｋ７１２１「プラスチックの転移温度測定法」に記載されているうち「中間点ガラス転移温度：Ｔｍｇ」に基づいて測定した。測定結果を表ＩＩＩ－１にまとめた。
Figure JPOXMLDOC01-appb-T000042
ＩＩＩ－４.実施例ＩＩＩ４：モノエポキシ化合物（Ａ－３）の合成
　モノエポキシ化合物（Ａ－２）の合成時の蒸留において、塔底温度１５１℃で１２．６ｇの留分を得た（Ａ－３）。
　得られたモノエポキシ化合物（Ａ－３）を上記条件にて１３Ｃ－ＮＭＲ分析を行った。ノルボルナン骨格の橋頭位と、ビニル基とがトランスの関係にある立体異性体に由来するピーク面積の、シフト値１４０～１４５ｐｐｍにおける総ピーク面積に対する割合は、７２．３２％であった。モノエポキシ化合物（Ａ－３）のＮＭＲチャートを図６に表す。
　図６のＮＭＲチャートによれば、モノエポキシ化合物（Ａ－３）の、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合は、７２．３２％であった。また、図６のＮＭＲチャートによれば、モノエポキシ化合物（Ａ－３）の、化学シフト１４０～１４２ｐｐｍの範囲において低磁場側から１番目に生じるピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合は、４３．４５％であった。
　また、モノエポキシ化合物（Ａ－３）について、上記同様ガスクロマトグラフィー分析を行った。モノエポキシ化合物（Ａ－３）のガスクロマトグラフを図７に示す。
ＩＩＩ－５.実施例ＩＩＩ５：立体異性体含有率を変動させたモノエポキシ化合物と熱カチオン重合開始剤を含む硬化性組成物の調製とその評価（その２：その他のエポキシ化合物との組合せ）
（実施例ＩＩＩ５－１）
　上記のようにして得られたモノエポキシ化合物（Ａ－１）、その他のエポキシ化合物（ＩＩＩＢ－２）および熱カチオン重合開始剤を下記の組成となるように混合し、硬化性組成物を得た。
＜硬化性組成物の組成＞
・モノエポキシ化合物（Ａ－１）　　　４０質量部
・その他のエポキシ化合物（ＩＩＩＢ－２）　　　６０質量部（ビスフェノールＡ型液状エポキシ樹脂、新日鉄住金化学製、商品名ＹＤ－１２８）
・熱カチオン重合開始剤　　　１質量部（芳香族スルホニウム塩、三新化学工業社製、商品名：ＳＩ－８０Ｌ）
（実施例ＩＩＩ５－２）
　モノエポキシ化合物（Ａ－１）を下記のようにして合成したモノエポキシ化合物（Ａ－３）に変更した以外は、実施例ＩＩＩ５－１と同様にして硬化性組成物を得た。
（実施例ＩＩＩ５－３）
　モノエポキシ化合物（Ａ－１）をモノエポキシ化合物（Ａ－２）に変更した以外は、実施例ＩＩＩ５－１と同様にして硬化性組成物を得た。
＜耐熱性評価＞
　上記実施例および比較例より得られた硬化性組成物を、熱風循環オーブンにより、８０℃にて１時間、１２０℃にて２時間、１８０℃にて２時間加熱し、硬化物を得た。
　得られた硬化物のガラス転移温度を、実施例ＩＩＩ３－１同様測定した。測定結果を表ＩＩＩ－２にまとめた。
Figure JPOXMLDOC01-appb-T000043
ＩＩＩ－６.実施例ＩＩＩ６：立体異性体含有率を変動させたモノエポキシ化合物と酸無水系硬化剤を含む硬化性組成物の調製とその評価（その１）
（実施例ＩＩＩ６－１）
　上記のようにして得られたモノエポキシ化合物（Ａ－１）、その他のエポキシ化合物（ＩＩＩＢ－１）、酸無水物系硬化剤および硬化促進剤を下記の組成となるように混合し、硬化性組成物を得た。
＜硬化性組成物の組成＞
・モノエポキシ化合物（Ａ－１）　　　５０質量部
・その他のエポキシ化合物（ＩＩＩＢ－１）　　　１００質量部
・酸無水物系硬化剤　　　１５５質量部（４－メチルヘキサヒドロ無水フタル酸とヘキサヒドロ無水フタル酸との混合物、モノエポキシ化合物（Ａ－１）およびその他のエポキシ化合物（ＩＩＩＢ－１）１当量に対して、０．９当量相当、新日本理化社製、商品名：ＭＨ－７００）
・硬化促進剤　　　３質量部（２－エチル－４－メチルイミダゾール、四国化成社製、商品名：２Ｅ４ＭＺ）
（実施例６－２）
　モノエポキシ化合物（Ａ－１）をモノエポキシ化合物（Ａ－２）に変更した以外は、実施例（ＩＩＩ６－１）と同様にして硬化性組成物を得た。
＜耐熱性評価＞
　上記実施例および比較例より得られた硬化性組成物を、熱風循環オーブンにより、１００にて２時間、１６０℃にて２時間、２２０℃にて２時間加熱し、硬化物を得た。
　得られた硬化物のガラス転移温度を、実施例ＩＩＩ３－１同様測定した。測定結果を表ＩＩＩ－３にまとめた。
Figure JPOXMLDOC01-appb-T000044
ＩＩＩ－７.実施例ＩＩＩ７：立体異性体含有率を変動させたモノエポキシ化合物と酸無水系硬化剤を含む硬化性組成物の調製とその評価（その２：その他のエポキシ化合物との組合せ）
（実施例ＩＩＩ７－１）
　上記のようにして得られたモノエポキシ化合物（Ａ－１）、その他のエポキシ化合物（ＩＩＩＢ－２）、酸無水物系硬化剤および硬化促進剤を下記の組成となるように混合し、硬化性組成物を得た。
＜硬化性組成物の組成＞
・モノエポキシ化合物（Ａ－１）　　　５５．５質量部
・その他のエポキシ化合物（ＩＩＩＢ－２）　　　１００質量部
・酸無水物系硬化剤　　　１２５質量部
・硬化促進剤　　　３質量部
（実施例ＩＩＩ７－２）
　モノエポキシ化合物（Ａ－１）をモノエポキシ化合物（Ａ－２）に変更した以外は、実施例ＩＩＩ７－１と同様にして硬化性組成物を得た。
＜耐熱性評価＞
　上記実施例および比較例より得られた硬化性組成物を、熱風循環オーブンにより、１００にて２時間、１６０℃にて４時間加熱し、硬化物を得た。
　得られた硬化物のガラス転移温度を、実施例ＩＩＩ３－１同様測定した。測定結果を表ＩＩＩ－４にまとめた。
Figure JPOXMLDOC01-appb-T000045

Claims (17)

  1. 　下記式（１）：
    Figure JPOXMLDOC01-appb-C000001
     （式中、Ｒ１乃至Ｒ６は、それぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される。）
    で表される、モノエポキシ化合物。
  2. 　前記式（１）で表される化合物の立体異性体を含み、１３Ｃ－ＮＭＲ分析による、前記式（１）におけるノルボルナン骨格の橋頭位とビニル基とがトランスの関係にある立体異性体に由来するピーク面積の、化学シフト１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、６６％以上である、請求項１に記載のモノエポキシ化合物。
  3. 　Ｒ１乃至Ｒ６は全て水素であり、ノルボルナン骨格の橋頭位とビニル基とがトランスの関係にある立体異性体が、下記化学式：
    Figure JPOXMLDOC01-appb-C000002
     のいずれかで表される、請求項２に記載のモノエポキシ化合物。
  4. 　前記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲における総ピーク面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、６６％以上である、請求項１に記載のモノエポキシ化合物。
  5. 　前記式（１）で表される化合物の１３Ｃ－ＮＭＲ分析において、化学シフト１４０～１４２ｐｐｍの範囲におけるピークのうち、低磁場側から１番目に生じるピークの面積の、１４０～１４５ｐｐｍの範囲における総ピーク面積に対する割合が、３５％以上である、請求項２～４のいずれか一項に記載のモノエポキシ化合物。
  6. 　請求項１～５のいずれか一項に記載のモノエポキシ化合物と、硬化剤、熱カチオン重合開始剤、および光カチオン重合開始剤からなる群より選択される１種とを含む、硬化性組成物。
  7. 　前記硬化剤が、フェノール化合物、アミン化合物、酸無水物系化合物およびアミド化合物からなる群より選択される１以上の硬化剤である、請求項６に記載の硬化性組成物。
  8. 　前記熱カチオン重合開始剤が、芳香族スルホニウム塩系の熱カチオン重合開始剤、芳香族ヨードニウム塩系の熱カチオン重合開始剤、およびアルミニウム錯体系の熱カチオン重合開始剤からなる群から選択される、請求項６に記載の硬化性組成物。
  9. 　前記光カチオン重合開始剤が、芳香族スルホニウム塩系の光カチオン重合開始剤である、請求項６に記載の硬化性組成物。
  10. 　前記モノエポキシ化合物と異なるその他のエポキシ化合物をさらに含む、請求項６～９のいずれか一項に記載の硬化性組成物。
  11. 　前記モノエポキシ化合物と異なるその他のエポキシ化合物が、グリシジルエーテル型エポキシド、グリシジルエステル型エポキシド、脂環式エポキシド、およびエポキシ樹脂からなる群から選択される、請求項１０に記載の硬化性組成物。
  12. 　前記硬化性組成物における、前記モノエポキシ化合物と、前記モノエポキシ化合物と異なるその他のエポキシ化合物との含有量比が、質量基準で、１：９９～７５：２５である、請求項１０または１１に記載の硬化性組成物。
  13. 　請求項６～１２のいずれか一項に記載の硬化性組成物を硬化させる工程を含む、硬化物の製造方法。
  14. 　請求項６～１２のいずれか一項に記載の硬化性組成物の硬化物。
  15. 　請求項１に記載のモノエポキシ化合物を製造する方法であって、
    　下記式（２）：
    Figure JPOXMLDOC01-appb-C000003
     （式中、Ｒ１乃至Ｒ６は、それぞれ独立して、水素、アルキル基およびアルコキシ基からなる群より選択される。）
    で表される化合物と、過酸とを反応させる工程を含んでなり、
    　該過酸の使用量が、該式（２）で表される化合物１．００モルに対して、０．１０～１．８０モルであることを特徴とする、方法。
  16. 　前記過酸が、過酸化水素または有機過酸である、請求項１５に記載の方法。
  17. 　請求項１に記載のモノエポキシ化合物を少なくとも含む、反応性希釈剤。
PCT/JP2017/010040 2016-03-14 2017-03-13 エポキシ化合物、硬化性組成物、硬化物、エポキシ化合物の製造方法および反応性希釈剤 WO2017159637A1 (ja)