CN109535774A - 一种耐高温云母氧化铁颜料 - Google Patents
一种耐高温云母氧化铁颜料 Download PDFInfo
- Publication number
- CN109535774A CN109535774A CN201811379329.8A CN201811379329A CN109535774A CN 109535774 A CN109535774 A CN 109535774A CN 201811379329 A CN201811379329 A CN 201811379329A CN 109535774 A CN109535774 A CN 109535774A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- iron oxide
- mica
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温云母氧化铁颜料，它包括氧化铁红颗粒50‑54重量份、云母粉12‑16重量份、硅酸钠11‑15重量份、钛酸乙脂4‑8重量份、超耐磨炭黑2‑6重量份、碳钢纤维1‑3份、二丁酸二辛酯磺酸钠3‑5份、纳米碳化钨1‑3份、氧化锰粉末1‑3份、硫酸钡晶须2‑4份、一缩二乙二醇22‑26重量份等组分。本发明组分配制合理科学，制备的氧化铁颜料色度高、氧化稳定性强、耐候性好、流动性强，色相的变化少，分散性优异，特别是耐高温性能优异，耐热性好，能够满足200℃高温下性能稳定，具有广泛的应用前景。
Description
技术领域
本发明涉及颜料技术领域，尤其涉及一种耐高温云母氧化铁颜料。
背景技术
氧化铁颜料是涂料行业用量较大的颜料品种，也是涂料生 产线调色一体化系统的主要无机着色材料。氧化铁颜料是具有良好的分散性、优良的耐光及耐候性的一种颜料。氧化铁颜料主要指以铁的氧化物为基本物质的氧化铁红、铁黄、铁黑和铁棕四类着色颜料，其中以氧化铁红为主（大约占到氧化铁颜料的50%），用作防锈颜料的云母氧化铁以及用作磁性纪录材料的磁性氧化铁也属于氧化铁颜料的范畴。氧化铁是仅次于钛白的第二大无机颜料，也是第一大彩色无机颜料。在全部消费的氧化铁颜料中，70%以上是用化学合成方法制备的，称之为合成氧化铁。合成氧化铁由于其合成纯度高、粒径均匀整齐，且色谱广、颜色多、价廉、无毒，有优良的着色和应用性能，具有吸收紫外线等性能，因而广泛用于建材、涂料、塑料、电子、烟草、医药、橡胶、陶瓷、油墨、磁性材料、造纸等领域。
不过，氧化铁颜料的耐热性不够。比如：目前使用的聚乙烯、聚丙烯、苯乙烯聚合物、聚酰胺、聚烯烃、ABS等热塑性树脂等涂料在通常情况下需要将聚乙烯、聚丙烯、苯乙烯聚合物、聚酰胺、聚烯烃、ABS等热塑性树脂于200℃以上成型加工，200℃以上将难以使用氧化铁颜料。
因此，需要制备一种耐高温云母氧化铁颜料，具有氧化稳定、色度高、耐候性好、流动性强等，特别是耐高温方面具有显著性能。
发明内容
为克服上述不足，本发明提供一种耐高温云母氧化铁颜料。
本发明是采取以下技术方案来实现的：一种耐高温云母氧化铁颜料，它包括的组成原料按照重量份为：氧化铁红颗粒50-54重量份、云母粉12-16重量份、硅酸钠11-15重量份、钛酸乙脂4-8重量份、超耐磨炭黑2-6重量份、碳钢纤维1-3份、二丁酸二辛酯磺酸钠3-5份、纳米碳化钨1-3份、氧化锰粉末1-3份、硫酸钡晶须2-4份、一缩二乙二醇22-26重量份、醋酸钠溶液24-28重量份、卵磷脂4-6重量份、谷氨酸5-7重量份、硬脂酸钙2-4重量份以及惰性盐1-3重量份；
所述云母粉是通过将云母矿石经过破碎、研磨、沉淀、烘干、粉碎所得。
进一步地，本发明所述惰性盐是含有钠离子的碳酸盐。
进一步地，本发明它包括的组成原料按照重量份为：氧化铁红颗粒50重量份、云母粉12重量份、硅酸钠11重量份、钛酸乙脂4重量份、超耐磨炭黑2重量份、碳钢纤维1份、二丁酸二辛酯磺酸钠3份、纳米碳化钨1份、氧化锰粉末1份、硫酸钡晶须2份、一缩二乙二醇22重量份、醋酸钠溶液24重量份、卵磷脂4重量份、谷氨酸5重量份、硬脂酸钙2重量份以及惰性盐1重量份。
进一步地，本发明它包括的组成原料按照重量份为：氧化铁红颗粒52重量份、云母粉14重量份、硅酸钠13重量份、钛酸乙脂6重量份、超耐磨炭黑4重量份、碳钢纤维2份、二丁酸二辛酯磺酸钠4份、纳米碳化钨2份、氧化锰粉末2份、硫酸钡晶须3份、一缩二乙二醇24重量份、醋酸钠溶液26重量份、卵磷脂5重量份、谷氨酸6重量份、硬脂酸钙3重量份以及惰性盐2重量份。
进一步地，本发明它包括的组成原料按照重量份为：氧化铁红颗粒54重量份、云母粉6重量份、硅酸钠-15重量份、钛酸乙脂8重量份、超耐磨炭黑6重量份、碳钢纤维3份、二丁酸二辛酯磺酸钠5份、纳米碳化钨3份、氧化锰粉末3份、硫酸钡晶须4份、一缩二乙二醇26重量份、醋酸钠溶液28重量份、卵磷脂6重量份、谷氨酸7重量份、硬脂酸钙4重量份以及惰性盐3重量份。
进一步地，本发明所述云母粉是通过将云母矿石利用破碎机破碎过200目筛选、加上研磨成细粉，然后加入等量的去离子水搅拌均匀后，沉淀3h，过滤沉淀，再将沉淀在105℃烘箱中烘干，最后将烘干后的沉淀粉碎过200目筛所得。
综上所述本发明具有以下有益效果：本发明组分配制合理科学，制备的氧化铁颜料色度高、氧化稳定性强、耐候性好、流动性强，色相的变化少，分散性优异，特别是耐高温性能优异，耐热性好，能够满足200℃高温下性能稳定，具有广泛的应用前景。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
实施例1一种耐高温云母氧化铁颜料
一种耐高温云母氧化铁颜料，它包括的组成原料按照重量份为：氧化铁红颗粒50重量份、云母粉12重量份、硅酸钠11重量份、钛酸乙脂4重量份、超耐磨炭黑2重量份、碳钢纤维1份、二丁酸二辛酯磺酸钠3份、纳米碳化钨1份、氧化锰粉末1份、硫酸钡晶须2份、一缩二乙二醇22重量份、醋酸钠溶液24重量份、卵磷脂4重量份、谷氨酸5重量份、硬脂酸钙2重量份以及惰性盐1重量份；
所述云母粉是通过将云母矿石经过破碎、研磨、沉淀、烘干、粉碎所得。
作为本发明的优先方案，本发明所述惰性盐是含有钠离子的碳酸盐。
作为本发明的优先方案，本发明所述云母粉是通过将云母矿石利用破碎机破碎过200目筛选、加上研磨成细粉，然后加入等量的去离子水搅拌均匀后，沉淀3h，过滤沉淀，再将沉淀在105℃烘箱中烘干，最后将烘干后的沉淀粉碎过200目筛所得。
实施例2一种耐高温云母氧化铁颜料
一种耐高温云母氧化铁颜料，它包括的组成原料按照重量份为：氧化铁红颗粒52重量份、云母粉14重量份、硅酸钠13重量份、钛酸乙脂6重量份、超耐磨炭黑4重量份、碳钢纤维2份、二丁酸二辛酯磺酸钠4份、纳米碳化钨2份、氧化锰粉末2份、硫酸钡晶须3份、一缩二乙二醇24重量份、醋酸钠溶液26重量份、卵磷脂5重量份、谷氨酸6重量份、硬脂酸钙3重量份以及惰性盐2重量份；
所述云母粉是通过将云母矿石经过破碎、研磨、沉淀、烘干、粉碎所得。
作为本发明的优先方案，本发明所述惰性盐是含有钠离子的碳酸盐。
作为本发明的优先方案，本发明所述云母粉是通过将云母矿石利用破碎机破碎过200目筛选、加上研磨成细粉，然后加入等量的去离子水搅拌均匀后，沉淀3h，过滤沉淀，再将沉淀在105℃烘箱中烘干，最后将烘干后的沉淀粉碎过200目筛所得。
实施例3一种耐高温云母氧化铁颜料
一种耐高温云母氧化铁颜料，它包括的组成原料按照重量份为：氧化铁红颗粒54重量份、云母粉6重量份、硅酸钠-15重量份、钛酸乙脂8重量份、超耐磨炭黑6重量份、碳钢纤维3份、二丁酸二辛酯磺酸钠5份、纳米碳化钨3份、氧化锰粉末3份、硫酸钡晶须4份、一缩二乙二醇26重量份、醋酸钠溶液28重量份、卵磷脂6重量份、谷氨酸7重量份、硬脂酸钙4重量份以及惰性盐3重量份；
所述云母粉是通过将云母矿石经过破碎、研磨、沉淀、烘干、粉碎所得。
作为本发明的优先方案，本发明所述惰性盐是含有钠离子的碳酸盐。
作为本发明的优先方案，本发明所述云母粉是通过将云母矿石利用破碎机破碎过200目筛选、加上研磨成细粉，然后加入等量的去离子水搅拌均匀后，沉淀3h，过滤沉淀，再将沉淀在105℃烘箱中烘干，最后将烘干后的沉淀粉碎过200目筛所得。
以上所述是本发明的实施例，故凡依本发明申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。
Claims (6)
1.一种耐高温云母氧化铁颜料，其特征在于：它包括的组成原料按照重量份为：氧化铁红颗粒50-54重量份、云母粉12-16重量份、硅酸钠11-15重量份、钛酸乙脂4-8重量份、超耐磨炭黑2-6重量份、碳钢纤维1-3份、二丁酸二辛酯磺酸钠3-5份、纳米碳化钨1-3份、氧化锰粉末1-3份、硫酸钡晶须2-4份、一缩二乙二醇22-26重量份、醋酸钠溶液24-28重量份、卵磷脂4-6重量份、谷氨酸5-7重量份、硬脂酸钙2-4重量份以及惰性盐1-3重量份；
所述云母粉是通过将云母矿石经过破碎、研磨、沉淀、烘干、粉碎所得。
2.根据权利要求1所述的一种耐高温云母氧化铁颜料，其特征在于：所述惰性盐是含有钠离子的碳酸盐。
3.根据权利要求1所述的一种耐高温云母氧化铁颜料，其特征在于：它包括的组成原料按照重量份为：氧化铁红颗粒50重量份、云母粉12重量份、硅酸钠11重量份、钛酸乙脂4重量份、超耐磨炭黑2重量份、碳钢纤维1份、二丁酸二辛酯磺酸钠3份、纳米碳化钨1份、氧化锰粉末1份、硫酸钡晶须2份、一缩二乙二醇22重量份、醋酸钠溶液24重量份、卵磷脂4重量份、谷氨酸5重量份、硬脂酸钙2重量份以及惰性盐1重量份。
4.根据权利要求1所述的一种耐高温云母氧化铁颜料，其特征在于：它包括的组成原料按照重量份为：氧化铁红颗粒52重量份、云母粉14重量份、硅酸钠13重量份、钛酸乙脂6重量份、超耐磨炭黑4重量份、碳钢纤维2份、二丁酸二辛酯磺酸钠4份、纳米碳化钨2份、氧化锰粉末2份、硫酸钡晶须3份、一缩二乙二醇24重量份、醋酸钠溶液26重量份、卵磷脂5重量份、谷氨酸6重量份、硬脂酸钙3重量份以及惰性盐2重量份。
5.根据权利要求1所述的一种耐高温云母氧化铁颜料，其特征在于：它包括的组成原料按照重量份为：氧化铁红颗粒54重量份、云母粉6重量份、硅酸钠-15重量份、钛酸乙脂8重量份、超耐磨炭黑6重量份、碳钢纤维3份、二丁酸二辛酯磺酸钠5份、纳米碳化钨3份、氧化锰粉末3份、硫酸钡晶须4份、一缩二乙二醇26重量份、醋酸钠溶液28重量份、卵磷脂6重量份、谷氨酸7重量份、硬脂酸钙4重量份以及惰性盐3重量份。
6.根据权利要求1所述的一种耐高温云母氧化铁颜料，其特征在于：所述云母粉是通过将云母矿石利用破碎机破碎过200目筛选、加上研磨成细粉，然后加入等量的去离子水搅拌均匀后，沉淀3h，过滤沉淀，再将沉淀在105℃烘箱中烘干，最后将烘干后的沉淀粉碎过200目筛所得。