CN107227118A - 一种皮鞋鞋底粘合剂及其制备方法 - Google Patents
一种皮鞋鞋底粘合剂及其制备方法 Download PDFInfo
- Publication number
- CN107227118A CN107227118A CN201710441284.1A CN201710441284A CN107227118A CN 107227118 A CN107227118 A CN 107227118A CN 201710441284 A CN201710441284 A CN 201710441284A CN 107227118 A CN107227118 A CN 107227118A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- adhesive
- titanium dioxide
- bonding agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种皮鞋用鞋底粘合剂及其制备方法，该粘合剂按照重量份包括以下原料：白色胶水10~30份、羧甲基纤维素钠4~16份、钛白粉4~5份、聚氧化乙烯3~9份、天然粒子3~9份、群青15~25份、氯化钾3~9份、渗透剂JFC 4~8份、扩散剂1~9份、酐酪素1~3份、发泡剂3~10份、硬酸酯3~9份、软水30~35份。本发明提供的皮鞋鞋底粘合剂，低毒环保，是于环境友好型环保胶粘剂；粘合剂的原料易得，成本低廉；本发明采取的方法是减少胶粘剂中大分子材料的用量，增加天然粒子的用量，提高胶粘剂对鞋料的浸润性能。钛白粉耐候性强，使得胶水化学性质稳定，不易变性粘性降低。
Description
技术领域
本发明属于鞋具加工领域，具体涉及一种皮鞋鞋底粘合剂及其制备方法。
背景技术
鞋子有着悠久的发展历史，大约在5000多年前的仰韶文化时期，就出现了 兽皮缝制的最原始的鞋。鞋子是人保护脚不受伤的一种工具。最早人们为了克 服特殊情况下，不让脚难受或者受伤，就发明了毛皮鞋子。鞋子发展到现在，各种样式功能的鞋子随处可见。鞋子是人类生产生活中必不可少的生活用品，在社会发展过程中，由于鞋的制作材料、式样、用途越来越多，鞋的种类也开 始丰富起来，但是制鞋必不可少的是胶黏剂，目前大部分的胶粘剂还是溶剂型 胶黏剂，溶剂型胶黏剂是指天然橡胶、合成橡胶、合成树脂等高分子化合物溶 于有机溶剂(如甲苯、苯等)而制成的粘合剂，这类粘合剂固化靠溶剂的挥发。 溶剂型胶黏剂在生产操作施工和固化时会伴随着大量的溶剂挥发，造成严重的 环境污染和资源浪费，同时由于大部分有机溶剂对人体都有害，还会严重危害 使用生产人员的健康。综上所述，有必要设计出一种环保、无VOC的粘合剂。
发明内容
针对上述问题，本发明要解决的技术问题是提供一种皮鞋鞋底粘合剂及其制备方法，环保无毒，粘合效果好。
为实现上述目的，本发明的技术方案为：一种皮鞋用鞋底粘合剂，按照重量份包括以下原料：白色胶水10~30份、羧甲基纤维素钠4~16份、钛白粉4~5份、聚氧化乙烯3~9份、天然粒子3~9份、群青15~25份、氯化钾 3~9份、渗透剂JFC 4~8份、扩散剂1~9份、酐酪素1~3份、发泡剂3~10份、硬酸酯3~9份、软水30~35份。
优选地，所述天然粒子中包括以下重量份的组分：植物淀粉40～55份，甘油10～15份，聚乙烯35～45份。
优选地，所述白色胶水由以下重量份的物质组成：乙酸乙烯酯30~50份，乙二胺10~25份，聚苯乙烯3~15份。
优选地，所述扩散剂选自明胶、海藻胶、甲基纤维素、羟丙基甲基纤维素、聚乙烯醇、马来酸酐、苯乙烯或醋酸乙烯和聚丙烯酸盐中的一种或多种。
优选地，所述渗透剂JFC为硫酸化蓖麻油、烷基磺酸钠、烷基苯磺酸钠、烷基硫酸酯钠、仲烷基磺酸钠、仲烷基硫酸酯钠、a-烯基磺酸钠、烷基萘磺酸钠、琥珀酸烷基酯磺酸钠、胰加漂T、氨基磺酸钠、脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、聚醚、磷酸酯类化合物中的一种或几种。
一种皮鞋用鞋底粘合剂的制备方法，主要包括以下步骤：
步骤1：制备钛白粉水浊液，向装有软水的球磨罐中加入碱性溶液，使得碱性溶液与软水充分溶解，再向其加入钛白粉和扩散剂，搅拌让水将粉状材料湿润，并将磨罐封盖，放于球磨机上运转球磨2~4h，得到钛白粉水浊液；
步骤2：向胶浆搅拌机中依次加入白色胶水、羧甲基纤维素钠、聚氧化乙烯、天然粒子、群青、氯化钾、渗透剂JFC ，边加入边搅拌，搅拌时间30~90min，搅拌速度200~400r/min得到混合液；
步骤3：制备粘合剂，将步骤2得到的混合液加入到步骤1得到的钛白粉水浊液搅拌20~40min，然后加入酐酪素、发泡剂和硬酸酯，放入50~70℃的恒温箱中保温，使原料充分混合，从恒温箱中取出后冷却到常温即得皮鞋鞋底粘合剂。
优选地，所述步骤1中的碱性溶液为氢氧化钠溶液或者氢氧化钾溶液，其中氢氧化钠溶液的浓度为20~40%，氢氧化钾溶液的浓度为50~60%。
优选地，所述步骤3中的保温时间为2~4h。
本发明的有益效果在于：本发明提供的皮鞋鞋底粘合剂，低毒环保，是于环境友好型环保胶粘剂；粘合剂的原料易得，成本低廉；本发明采取的方法是减少胶粘剂中大分 子材料的用量，增加天然粒子的用量，提高胶粘剂对鞋料的浸润性能。钛白粉耐候性强，使得胶水化学性质稳定，不易变性粘性降低。并且渗透剂JFC对皮鞋鞋底的渗透浸润贡献较大，消除了皮鞋鞋底粘合剂对其表面张力，使得粘合剂轻易地从布面渗透进入布纹之中，形成一层胶粘剂浆体。该制备工艺简单易行，无污染，适用于工业化生产。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步的详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不限定本发明。
实施例1
一种皮鞋用鞋底粘合剂，按照重量份包括以下原料：白色胶水10份、羧甲基纤维素钠4份、钛白粉4份、聚氧化乙烯3份、天然粒子3份、群青15份、氯化钾 3份、渗透剂JFC 4份、扩散剂1份、酐酪素1份、发泡剂3份、硬酸酯3份、软水30份。
所述天然粒子中包括以下重量份的组分：植物淀粉40份，甘油10份，聚乙烯35份。
所述白色胶水由以下重量份的物质组成：乙酸乙烯酯30份，乙二胺10份，聚苯乙烯3份。
所述扩散剂选自明胶、海藻胶、甲基纤维素、羟丙基甲基纤维素、聚乙烯醇、马来酸酐、苯乙烯或醋酸乙烯和聚丙烯酸盐中的一种或多种。
所述渗透剂JFC为硫酸化蓖麻油、烷基磺酸钠、烷基苯磺酸钠、烷基硫酸酯钠、仲烷基磺酸钠、仲烷基硫酸酯钠、a-烯基磺酸钠、烷基萘磺酸钠、琥珀酸烷基酯磺酸钠、胰加漂T、氨基磺酸钠、脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、聚醚、磷酸酯类化合物中的一种或几种。
一种皮鞋用鞋底粘合剂的制备方法，主要包括以下步骤：
步骤1：制备钛白粉水浊液，向装有软水的球磨罐中加入碱性溶液，使得碱性溶液与软水充分溶解，再向其加入钛白粉和扩散剂，搅拌让水将粉状材料湿润，并将磨罐封盖，放于球磨机上运转球磨2h，得到钛白粉水浊液；
步骤2：向胶浆搅拌机中依次加入白色胶水、羧甲基纤维素钠、聚氧化乙烯、天然粒子、群青、氯化钾、渗透剂JFC ，边加入边搅拌，搅拌时间60min，搅拌速度300r/min得到混合液；
步骤3：制备粘合剂，将步骤2得到的混合液加入到步骤1得到的钛白粉水浊液搅拌30min，然后加入酐酪素、发泡剂和硬酸酯，放入60℃的恒温箱中保温，使原料充分混合，从恒温箱中取出后冷却到常温即得皮鞋鞋底粘合剂。
所述步骤1中的碱性溶液为氢氧化钠溶液或者氢氧化钾溶液，其中氢氧化钠溶液的浓度为20%，氢氧化钾溶液的浓度为50%。
所述步骤3中的保温时间为2h。
实施例2
一种皮鞋用鞋底粘合剂，按照重量份包括以下原料：白色胶水20份、羧甲基纤维素钠10份、钛白粉4份、聚氧化乙烯6份、天然粒子6份、群青20份、氯化钾 6份、渗透剂JFC 6份、扩散剂5份、酐酪素2份、发泡剂6份、硬酸酯6份、软水32份。
所述天然粒子中包括以下重量份的组分：植物淀粉45份，甘油12份，聚乙烯40份。
所述白色胶水由以下重量份的物质组成：乙酸乙烯酯40份，乙二胺15份，聚苯乙烯10份。
所述扩散剂选自明胶、海藻胶、甲基纤维素、羟丙基甲基纤维素、聚乙烯醇、马来酸酐、苯乙烯或醋酸乙烯和聚丙烯酸盐中的一种或多种。
所述渗透剂JFC为硫酸化蓖麻油、烷基磺酸钠、烷基苯磺酸钠、烷基硫酸酯钠、仲烷基磺酸钠、仲烷基硫酸酯钠、a-烯基磺酸钠、烷基萘磺酸钠、琥珀酸烷基酯磺酸钠、胰加漂T、氨基磺酸钠、脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、聚醚、磷酸酯类化合物中的一种或几种。
一种皮鞋用鞋底粘合剂的制备方法，主要包括以下步骤：
步骤1：制备钛白粉水浊液，向装有软水的球磨罐中加入碱性溶液，使得碱性溶液与软水充分溶解，再向其加入钛白粉和扩散剂，搅拌让水将粉状材料湿润，并将磨罐封盖，放于球磨机上运转球磨3h，得到钛白粉水浊液；
步骤2：向胶浆搅拌机中依次加入白色胶水、羧甲基纤维素钠、聚氧化乙烯、天然粒子、群青、氯化钾、渗透剂JFC ，边加入边搅拌，搅拌时间60min，搅拌速度300r/min得到混合液；
步骤3：制备粘合剂，将步骤2得到的混合液加入到步骤1得到的钛白粉水浊液搅拌30min，然后加入酐酪素、发泡剂和硬酸酯，放入60℃的恒温箱中保温，使原料充分混合，从恒温箱中取出后冷却到常温即得皮鞋鞋底粘合剂。
所述步骤1中的碱性溶液为氢氧化钠溶液或者氢氧化钾溶液，其中氢氧化钠溶液的浓度为30%，氢氧化钾溶液的浓度为55%。
所述步骤3中的保温时间为3h。
实施例3
一种皮鞋用鞋底粘合剂，按照重量份包括以下原料：白色胶水30份、羧甲基纤维素钠16份、钛白粉5份、聚氧化乙烯9份、天然粒子9份、群青25份、氯化钾 9份、渗透剂JFC 8份、扩散剂9份、酐酪素3份、发泡剂10份、硬酸酯9份、软水35份。
所述天然粒子中包括以下重量份的组分：植物淀粉55份，甘油15份，聚乙烯45份。
所述白色胶水由以下重量份的物质组成：乙酸乙烯酯50份，乙二胺25份，聚苯乙烯15份。
所述扩散剂选自明胶、海藻胶、甲基纤维素、羟丙基甲基纤维素、聚乙烯醇、马来酸酐、苯乙烯或醋酸乙烯和聚丙烯酸盐中的一种或多种。
所述渗透剂JFC为硫酸化蓖麻油、烷基磺酸钠、烷基苯磺酸钠、烷基硫酸酯钠、仲烷基磺酸钠、仲烷基硫酸酯钠、a-烯基磺酸钠、烷基萘磺酸钠、琥珀酸烷基酯磺酸钠、胰加漂T、氨基磺酸钠、脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、聚醚、磷酸酯类化合物中的一种或几种。
一种皮鞋用鞋底粘合剂的制备方法，主要包括以下步骤：
步骤1：制备钛白粉水浊液，向装有软水的球磨罐中加入碱性溶液，使得碱性溶液与软水充分溶解，再向其加入钛白粉和扩散剂，搅拌让水将粉状材料湿润，并将磨罐封盖，放于球磨机上运转球磨4h，得到钛白粉水浊液；
步骤2：向胶浆搅拌机中依次加入白色胶水、羧甲基纤维素钠、聚氧化乙烯、天然粒子、群青、氯化钾、渗透剂JFC ，边加入边搅拌，搅拌时间90min，搅拌速度400r/min得到混合液；
步骤3：制备粘合剂，将步骤2得到的混合液加入到步骤1得到的钛白粉水浊液搅拌40min，然后加入酐酪素、发泡剂和硬酸酯，放入70℃的恒温箱中保温，使原料充分混合，从恒温箱中取出后冷却到常温即得皮鞋鞋底粘合剂。
所述步骤1中的碱性溶液为氢氧化钠溶液或者氢氧化钾溶液，其中氢氧化钠溶液的浓度为40%，氢氧化钾溶液的浓度为60%。
所述步骤3中的保温时间为4h。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种皮鞋用鞋底粘合剂，其特征在于，按照重量份包括以下原料：白色胶水10~30份、羧甲基纤维素钠4~16份、钛白粉4~5份、聚氧化乙烯3~9份、天然粒子3~9份、群青15~25份、氯化钾 3~9份、渗透剂JFC 4~8份、扩散剂1~9份、酐酪素1~3份、发泡剂3~10份、硬酸酯3~9份、软水30~35份。
2.根据权利要求1所述的一种皮鞋用鞋底粘合剂，其特征在于，所述天然粒子中包括以下重量份的组分：植物淀粉40～55份，甘油10～15份，聚乙烯35～45份。
3.根据权利要求1所述的一种皮鞋用鞋底粘合剂，其特征在于，所述白色胶水由以下重量份的物质组成：乙酸乙烯酯30~50份，乙二胺10~25份，聚苯乙烯3~15份。
4.根据权利要求1所述的一种皮鞋用鞋底粘合剂，其特征在于，所述扩散剂选自明胶、海藻胶、甲基纤维素、羟丙基甲基纤维素、聚乙烯醇、马来酸酐、苯乙烯或醋酸乙烯和聚丙烯酸盐中的一种或多种。
5.根据权利要求1所述的一种皮鞋用鞋底粘合剂，其特征在于，所述渗透剂JFC为硫酸化蓖麻油、烷基磺酸钠、烷基苯磺酸钠、烷基硫酸酯钠、仲烷基磺酸钠、仲烷基硫酸酯钠、a-烯基磺酸钠、烷基萘磺酸钠、琥珀酸烷基酯磺酸钠、胰加漂T、氨基磺酸钠、脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、聚醚、磷酸酯类化合物中的一种或几种。
6.一种皮鞋用鞋底粘合剂的制备方法，其特征在于，主要包括以下步骤：
步骤1：制备钛白粉水浊液，向装有软水的球磨罐中加入碱性溶液，使得碱性溶液与软水充分溶解，再向其加入钛白粉和扩散剂，搅拌让水将粉状材料湿润，并将磨罐封盖，放于球磨机上运转球磨2~4h，得到钛白粉水浊液；
步骤2：向胶浆搅拌机中依次加入白色胶水、羧甲基纤维素钠、聚氧化乙烯、天然粒子、群青、氯化钾、渗透剂JFC ，边加入边搅拌，搅拌时间30~90min，搅拌速度200~400r/min得到混合液；
步骤3：制备粘合剂，将步骤2得到的混合液加入到步骤1得到的钛白粉水浊液搅拌20~40min，然后加入酐酪素、发泡剂和硬酸酯，放入50~70℃的恒温箱中保温，使原料充分混合，从恒温箱中取出后冷却到常温即得皮鞋鞋底粘合剂。
7.根据权利要求6所述的一种皮鞋鞋底粘合剂的制备方法，其特征在于，所述步骤1中的碱性溶液为氢氧化钠溶液或者氢氧化钾溶液，其中氢氧化钠溶液的浓度为20~40%，氢氧化钾溶液的浓度为50~60%。
8.根据权利要求6所述的一种皮鞋鞋底粘合剂的制备方法，其特征在于，所述步骤3中的保温时间为2~4h。