CN106693202A - Stone needle ear acupoint pressing beans and preparation method of stone needle ear acupoint pressing beans - Google Patents
Stone needle ear acupoint pressing beans and preparation method of stone needle ear acupoint pressing beans Download PDFInfo
- Publication number
- CN106693202A CN106693202A CN201611078134.0A CN201611078134A CN106693202A CN 106693202 A CN106693202 A CN 106693202A CN 201611078134 A CN201611078134 A CN 201611078134A CN 106693202 A CN106693202 A CN 106693202A
- Authority
- CN
- China
- Prior art keywords
- stone needle
- percent
- stone
- needle ear
- ear acupoint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses stone needle ear acupoint pressing beans and a preparation method of the stone needle ear acupoint pressing beans and belongs to the field of medical equipment. The stone needle ear acupoint pressing beans are prepared from the following raw materials in percentage by weight: 30 percent to 70 percent of stone needle, 10 percent to 30 percent of medical stone, 10 percent to 30 percent of clay, 5 percent to 20 percent of ceramic clay and 5 percent to 20 percent of calcined kaolin. According to the ear acupoint pressing beans prepared by the preparation method, the far infrared normal emittance is remarkably better than that of natural stone needles, and the hardness and surface roughness are closer to those of the natural stone needles; the stone needle ear acupoint pressing beans have better biological and physical effects and health-care effect on human bodies.
Description
Technical field
The present invention relates to a kind of stone needle ear pressure bean and preparation method thereof, belong to medical instruments field.
Background technology
The traditional Chinese medical science thinks that the vital organs of the human body of people can find corresponding position on ear, when human body is ill, often
There is reaction in related cave area on auricle, stimulates these corresponding reflecting points and acupuncture point, can play a part of to prevent and cure diseases,
These reflecting points and acupuncture point are exactly the ear acupuncture point.Auricular therapy is to stick the smooth small round shaped grain pressing ear in hard, surface on ear acupuncture point surface
Cave, it is a kind of simple therapy that imbedding needle is substituted on the basis of ear acupuncture point acupuncture needle method.Auricular therapy is treated some illnesss and can not only be received
To the same curative effect of acupuncture needle, imbedding needle, and the painless and noninvasive wound of safety, not few side effects, easy infection.Suitable for the elderly, children
Youngster, be afraid of that pin fears pain, far away, work and study are nervous can not daily go hospital admission person.This method can be used for various acute diseases
Anti-inflammatory, detumescence, analgesic, can treat various chronic diseases again, such as myopia, acne, hypertension, diabetes, enruesis, neurasthenia,
Insomnia etc., therefore welcome by many patients.
Mainly there are a three major types currently used for the pressing thing of auricular therapy, a class is vegetable seeds such as rapeseed, millet, green
Beans, radish seed, semen brassicae, Wang Anyi etc.；Two is Chinese medicine pill, such as Liushen Pills, antiphlogistic bezoar ball, YANHOU WAN, children
Infantile convulsion ball, benevolence pellet etc.；Three is polyphenyl pearl, magnetic bead.Vegetable seeds or traditional Chinese medicine pill make pelleting, the more difficult performance of medicinal ingredient of its own
Effect, effect is unstable, and magnetic bead is used as pressure beans, and its own health-care efficacy is not strong.
The main mine material composition of stone needle is calcite crystallite, and quality is fine and smooth, makes one to feel comfortably cool with human body friction.Simultaneously
Also there is sensing warming effect and infra-red radiation frequency band extremely wide, the biophysics beneficial to human body can be produced after being acted on human body
Effect, with temperature three-way meridian, the multiple efficacies such as the promoting flow of qi and blood circulation, refreshment and tranquilization have been widely used far-infrared textiles, control at present
The medicine equipments such as instrument, treatment patch are treated, but the far infrared normal emittance of natural stone needle is relatively low at present, causes properties of product to be owed
It is good.
The content of the invention
The purpose of the present invention is directed to defect present in prior art, there is provided a kind of stone needle ear pressure bean, the ear acupuncture point pressure
Beans have far infrared normal emittance higher, therefore with the preferably health care such as promotion microcirculation, temperature three-way meridian, promoting flow of qi and blood circulation
Effect.
Above-mentioned purpose is achieved through the following technical solutions：
A kind of ear pressure bean, it is prepared from the following raw materials in parts by weight：
Preferably, the weight proportion of the raw material is：
The present invention further provides the preparation method of the ear pressure bean, the method is comprised the following steps：
1) stone needle, medical stone, clay, ceramic clay, calcined kaolin were smashed into 200~400 eye mesh screens together and was mixed
Uniformly, then in mixed-powder add adhesive and stir be made softwood；
2) by extrusion-spheronizator on softwood, it is 1-5mm to use extrusion-spheronization to be made particle diameter, and heap density is 2-7g/ml
Spherical pellets；
3) spherical pellets are placed in 500 DEG C~800 DEG C kilns and are fired activation, come out of the stove after 1-5 hours, and drop naturally
Temperature；
4) obtained final product after polishing.
Preferably, described adhesive is the carboxymethylcellulose sodium solution that mass concentration is 0.1~2%.
The beneficial effects of the invention are as follows：The far infrared normal direction transmitting that the ear pressure bean that the present invention is provided is measured at 8~15 μm
Rate can advantageously promote microcirculation, temperature three-way meridian, the promoting flow of qi and blood circulation apparently higher than natural stone needle, to myopia, hypertension, sugar
The diseases such as urine disease, neurasthenia, insomnia have more preferable health-care effect.Simultaneously the present invention provide ear pressure bean hardness is moderate, table
Face is bright and clean, and usage comfort is good.
Specific embodiment
The present invention is described in detail below by way of specific embodiment.
Embodiment 1
A kind of ear pressure bean, it is prepared from the following raw materials in parts by weight：
Preparation method is as follows：
1) stone needle, medical stone, clay, ceramic clay, calcined kaolin are weighed by weight ratio, and 300 mesh sieves were smashed together
Net is simultaneously well mixed, and is then 0.5% carboxymethylcellulose sodium solution and stirs system to addition mass concentration in mixed-powder
Into softwood；
2) by extrusion-spheronizator on softwood, it is 3000 revs/min to control the rotating speed of spheronizator, and drying temperature is 80 DEG C, is made
Particle diameter is 3mm, and heap density is the spherical pellets of 4.5g/ml；
3) spherical pellets are placed in and activation is fired in 700 DEG C of kilns, come out of the stove after 3 hours, and Temperature fall；
4) add atoleine to be processed by shot blasting, obtain final product.
Embodiment 2
A kind of ear pressure bean, it is prepared from the following raw materials in parts by weight：
Preparation method is as follows：
1) stone needle, medical stone, clay, ceramic clay, calcined kaolin are weighed by weight ratio, and 200 mesh sieves were smashed together
Net is simultaneously well mixed, and is then that 2% carboxymethylcellulose sodium solution and stirring are made to addition mass concentration in mixed-powder
Softwood；
2) by extrusion-spheronizator on softwood, it is 5000 revs/min to control the rotating speed of spheronizator, and drying temperature is 60 DEG C, is made
Particle diameter is 5mm, and heap density is the spherical pellets of 7g/ml；
3) spherical pellets are placed in and activation is fired in 800 DEG C of kilns, come out of the stove after 1 hour, and Temperature fall；
4) add atoleine to be processed by shot blasting, obtain final product.
Embodiment 3
A kind of ear pressure bean, it is prepared from the following raw materials in parts by weight：
Preparation method is as follows：
1) stone needle, medical stone, clay, ceramic clay, calcined kaolin are weighed by weight ratio, and 400 mesh sieves were smashed together
Net is simultaneously well mixed, and is then 0.1% carboxymethylcellulose sodium solution and stirs system to addition mass concentration in mixed-powder
Into softwood；
2) by extrusion-spheronizator on softwood, it is 2000 revs/min to control the rotating speed of spheronizator, and drying temperature is 120 DEG C, system
It is 1mm into particle diameter, heap density is the spherical pellets of 2g/ml；
3) spherical pellets are placed in and activation is fired in 500 DEG C of kilns, come out of the stove after 5 hours, and Temperature fall；
4) add atoleine to be processed by shot blasting, obtain final product.
Embodiment 4
A kind of ear pressure bean, it is prepared from the following raw materials in parts by weight：
Preparation method is as follows：
1) stone needle, medical stone, clay, ceramic clay, calcined kaolin are weighed by weight ratio, and 300 mesh sieves were smashed together
Net is simultaneously well mixed, and is then that 1% carboxymethylcellulose sodium solution and stirring are made to addition mass concentration in mixed-powder
Softwood；
2) by extrusion-spheronizator on softwood, it is 4000 revs/min to control the rotating speed of spheronizator, and drying temperature is 75 DEG C, is made
Particle diameter is 3mm, and heap density is the spherical pellets of 5g/ml；
3) spherical pellets are placed in and activation is fired in 700 DEG C of kilns, come out of the stove after 3 hours, and Temperature fall；
4) add atoleine to be processed by shot blasting, obtain final product.
Test example
(the far infrared patch normal emittance based on Fourier infrared spectrograph is determined bibliography method, Li Fengguang etc., river
Southern medical research, the 6th phase of volume 24 in June, 2015) far infrared normal emittance of the detection ear pressure bean at 8~15 μm, detection
Temperature is 37 DEG C.The surface roughness and mohs hardness of ear pressure bean are also detected in addition.
It is simultaneously control with undressed natural stone needle, as a result see the table below：
The ear pressure bean far infrared normal emittance that can be seen that present invention preparation from above testing result is substantially better than day
Right stone needle, and hardness and surface roughness show there is more preferable effect of biophysics and guarantor to human body all close to natural stone needle
Strong effect.
Claims (4)
1. a kind of stone needle ear pressure bean, it is characterised in that be prepared from the following raw materials in parts by weight：
2. stone needle ear pressure bean as claimed in claim 1, it is characterised in that the weight proportion of the raw material is：
3. a kind of method for preparing stone needle ear pressure bean described in claim 1 or 2, it is characterised in that comprise the following steps：
1) stone needle, medical stone, clay, ceramic clay, calcined kaolin were smashed into 200~400 eye mesh screens together and were well mixed,
Then in mixed-powder add adhesive and stir be made softwood；
2) by extrusion-spheronizator on softwood, it is 1-5mm to use extrusion-spheronization to be made particle diameter, and heap density is the ball of 2-7g/ml
Shape piller；
3) spherical pellets are placed in 500 DEG C~800 DEG C kilns and are fired activation, come out of the stove after 1-5 hours, and Temperature fall；
4) obtained final product after polishing.
4. the preparation method of stone needle ear pressure bean as claimed in claim 3, it is characterised in that described adhesive is that mass concentration is
0.1~2% carboxymethylcellulose sodium solution.