CN106142753A - A kind of preparation method of high-strength V CM clad steel plate - Google Patents
A kind of preparation method of high-strength V CM clad steel plate Download PDFInfo
- Publication number
- CN106142753A CN106142753A CN201610504796.3A CN201610504796A CN106142753A CN 106142753 A CN106142753 A CN 106142753A CN 201610504796 A CN201610504796 A CN 201610504796A CN 106142753 A CN106142753 A CN 106142753A
- Authority
- CN
- China
- Prior art keywords
- upside
- layer
- downside
- chemical treatment
- steel plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the preparation method of a kind of high-strength V CM clad steel plate, including: substrate, it is provided with the first chemical treatment layer on the upside of substrate, is provided with the second chemical treatment layer on the downside of substrate, on the downside of the second chemical treatment layer, is provided with back of the body enamelled coating, the first adhesive layer it is provided with on the upside of first chemical treatment layer, it is provided with layer of PVC on the upside of first adhesive layer, is provided with the second adhesive phase on the upside of layer of PVC, on the upside of the second adhesive phase, is provided with pearl layer, it is coated with PET film layer on the upside of pearl layer, on the upside of PET film layer, is coated with PE film.Described substrate includes corrosion resistant plate, titanium steel plate it is provided with on the downside of corrosion resistant plate, it is provided with on the downside of titanium steel plate on the upside of downside zinc coat, corrosion resistant plate and is provided with upside zinc coat, on the downside of the zinc coat of downside, be provided with downside Aluminium Foil Package coating, on the upside of the zinc coat of upside, be provided with upside Aluminium Foil Package coating.Present configuration is reasonable, novel, and product with stable quality is easy to process, can improve working (machining) efficiency during use, and appearance looks elegant the most of the present invention, sense of touch are good, can be widely used in various home appliance panel.
Description
Technical field
The present invention relates to technical field of novel materials, the preparation method of a kind of high-strength V CM clad steel plate.
Background technology
Clad steel plate Application comparison in industry and life is extensive, and automobile, refrigerator, washing machine, top-grade furniture, kitchen set
Standby, industrial and civil buildings etc. is required for using, and the environment that clad steel plate uses is more and more special and more and more extensive,
Under certain special environment, clad steel plate and other parts Long contact time can occur the phenomenon of molecular migration, for
Under the traction of this molecular migration phenomenon, the development of clad steel plate industry will have the space of the most wide development.
It is heated poor-performing with the PVC of the VCM film product of pearlescent effect, if closing a little higher than process warm of plate temperature in membrane process
Degree, plate face is just easily generated the problem of appearance such as Pericarpium Citri tangerinae, because the scrappage that this defect causes this series products remains high always.
Summary of the invention
Technical problem solved by the invention is to provide the preparation method of a kind of high-strength V CM clad steel plate, to solve
The problem proposed in above-mentioned background technology.
Technical problem solved by the invention realizes by the following technical solutions: a kind of high-strength V CM clad steel plate bag
Include: substrate, on the upside of substrate, be provided with the first chemical treatment layer, on the downside of substrate, be provided with the second chemical treatment layer, the second chemical treatment layer
Downside is provided with back of the body enamelled coating, is provided with the first adhesive layer, is provided with layer of PVC on the upside of the first adhesive layer on the upside of the first chemical treatment layer,
It is provided with the second adhesive phase on the upside of layer of PVC, on the upside of the second adhesive phase, is provided with pearl layer, on the upside of pearl layer, be coated with PET film layer,
PE film it is coated with on the upside of PET film layer.
Described substrate includes corrosion resistant plate, is provided with titanium steel plate on the downside of corrosion resistant plate, be provided with on the downside of titanium steel plate downside zinc coat,
It is provided with upside zinc coat on the upside of corrosion resistant plate, is provided with downside Aluminium Foil Package coating on the downside of the zinc coat of downside, sets on the upside of the zinc coat of upside
There is upside Aluminium Foil Package coating.
The preparation method of a kind of high-strength V CM clad steel plate, comprises the following steps:
(1) by composite titanium steel plate on the downside of corrosion resistant plate, electroplate on the upside of zinc coat, corrosion resistant plate on the downside of plating on the downside of titanium steel plate
Upside zinc coat, Aluminium Foil Package coating on the downside of overlay film on the downside of the zinc coat of downside, Aluminium Foil Package coating on the upside of overlay film on the upside of the zinc coat of upside,
Form substrate；
(2) by substrate after pre-defat, defat and washing, roller coat potassium bichromate solution each to substrate front side and the back side,
I.e. substrate positive and negative has been respectively formed chemical treatment layer, the i.e. first chemical treatment layer and the second chemical treatment layer；
On the downside of (3) second chemical treatment layer, the solidification of roller coat epoxy coating is dried and is i.e. formed back of the body enamelled coating；At first chemistry
Form the first adhesive layer after the solidification of roller coat Polyester resin lacquer on the upside of reason layer, on the upside of the first adhesive layer, lay layer of PVC,
The second adhesive phase is formed after the solidification of roller coat Polyester resin lacquer on the upside of layer of PVC；
On the upside of (4) second adhesive phases, the solidification of roller coat pearl white Polyester resin lacquer is dried and is i.e. formed pearl layer, pearl layer
Upside is coated with PET film layer, is coated with PE film on the upside of PET film layer, and the backsize polyurethane binder in PE electron membrane solidifies
Rear formation PE film.
Further, described first chemical treatment layer, the thickness of the second chemical treatment layer are 2 μm-3 μm.
Further, the thickness of described substrate is 0.02-0.25mm.
Further, the thickness of described back of the body enamelled coating is 4 μm-8 μm.
Compared with prior art, the invention has the beneficial effects as follows: present configuration is reasonable, novel, product with stable quality adds
Work is convenient, can improve working (machining) efficiency during use, and appearance looks elegant the most of the present invention, sense of touch are good, can be widely used in various
Home appliance panel.
Accompanying drawing explanation
Fig. 1 is the structural representation of the present invention.
Fig. 2 is the board structure schematic diagram of the present invention.
Detailed description of the invention
In order to make realizing technological means, creation characteristic, reaching purpose and be easy to understand with effect of the present invention, knot below
Conjunction is specifically illustrating, and the present invention is expanded on further.
As shown in Figure 1 and Figure 2, the preparation method of a kind of high-strength V CM clad steel plate, including: substrate 1, set on the upside of substrate 1
There is the first chemical treatment layer 2, be provided with the second chemical treatment layer 3 on the downside of substrate 1, on the downside of the second chemical treatment layer 3, be provided with back of the body enamelled coating
8, it is provided with the first adhesive layer 4 on the upside of the first chemical treatment layer 2, is provided with layer of PVC 5 on the upside of the first adhesive layer 4, on the upside of layer of PVC 5
It is provided with the second adhesive phase 6, is provided with pearl layer 7 on the upside of the second adhesive phase 6, on the upside of pearl layer 7, is coated with PET film layer 9, PET
PE film 10 it is coated with on the upside of film layer 9.
Described substrate 1 includes corrosion resistant plate 11, is provided with titanium steel plate 12, is provided with down on the downside of titanium steel plate 12 on the downside of corrosion resistant plate 11
It is provided with upside zinc coat 14 on the upside of side zinc coat 13, corrosion resistant plate 11, on the downside of downside zinc coat 13, is provided with downside Aluminium Foil Package coating
15, it is provided with upside Aluminium Foil Package coating 16 on the upside of upside zinc coat 14.
The preparation method of a kind of high-strength V CM clad steel plate, comprises the following steps:
(1) by composite titanium steel plate on the downside of corrosion resistant plate, electroplate on the upside of zinc coat, corrosion resistant plate on the downside of plating on the downside of titanium steel plate
Upside zinc coat, Aluminium Foil Package coating on the downside of overlay film on the downside of the zinc coat of downside, Aluminium Foil Package coating on the upside of overlay film on the upside of the zinc coat of upside,
Form substrate；
(2) by substrate after pre-defat, defat and washing, roller coat potassium bichromate solution each to substrate front side and the back side,
I.e. substrate positive and negative has been respectively formed chemical treatment layer, the i.e. first chemical treatment layer and the second chemical treatment layer；
On the downside of (3) second chemical treatment layer, the solidification of roller coat epoxy coating is dried and is i.e. formed back of the body enamelled coating；At first chemistry
Form the first adhesive layer after the solidification of roller coat Polyester resin lacquer on the upside of reason layer, on the upside of the first adhesive layer, lay layer of PVC,
The second adhesive phase is formed after the solidification of roller coat Polyester resin lacquer on the upside of layer of PVC；
On the upside of (4) second adhesive phases, the solidification of roller coat pearl white Polyester resin lacquer is dried and is i.e. formed pearl layer, pearl layer
Upside is coated with PET film layer, is coated with PE film on the upside of PET film layer, and the backsize polyurethane binder in PE electron membrane solidifies
Rear formation PE film.
Concrete, described first chemical treatment layer, the thickness of the second chemical treatment layer are 2 μm-3 μm.
Concrete, the thickness of described substrate 1 is 0.02-0.25mm.
Concrete, the thickness of described back of the body enamelled coating is 4 μm-8 μm.
The preparation method of the present invention is:
Substrate carrying out defat and washing processes, be passivated processing at substrate positive and negative, the back side processes epoxy back of the body paint, then
Front is processed VCM film glue special, after glue curing, by hot laminating machine, VCM film is carried out laminating with substrate, then through steam
PE film is pasted after cooling.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.The claimed scope of the present invention by appending claims and
Its equivalent defines.
Claims (4)
1. a preparation method for high-strength V CM clad steel plate, its clad steel plate includes: substrate, it is characterised in that: on the upside of substrate
It is provided with the first chemical treatment layer, is provided with the second chemical treatment layer on the downside of substrate, on the downside of the second chemical treatment layer, is provided with back of the body enamelled coating, the
It is provided with the first adhesive layer on the upside of one chemical treatment layer, on the upside of the first adhesive layer, is provided with layer of PVC, on the upside of layer of PVC, be provided with second
Adhesive phase, is provided with pearl layer on the upside of the second adhesive phase, be coated with PET film layer, be coated with on the upside of PET film layer on the upside of pearl layer
PE film；Described substrate includes corrosion resistant plate, is provided with titanium steel plate on the downside of corrosion resistant plate, is provided with downside zinc coat, no on the downside of titanium steel plate
It is provided with upside zinc coat on the upside of rust steel plate, is provided with downside Aluminium Foil Package coating on the downside of the zinc coat of downside, is provided with on the upside of the zinc coat of upside
Upside Aluminium Foil Package coating, the preparation method of clad steel plate, comprise the following steps:
(1) by composite titanium steel plate on the downside of corrosion resistant plate, on the downside of titanium steel plate on the downside of plating on the upside of zinc coat, corrosion resistant plate on the upside of plating
Zinc coat, Aluminium Foil Package coating on the downside of overlay film on the downside of the zinc coat of downside, Aluminium Foil Package coating on the upside of overlay film on the upside of the zinc coat of upside, formed
Substrate；
(2) by substrate after pre-defat, defat and washing, roller coat potassium bichromate solution each to substrate front side and the back side, i.e. base
Plate positive and negative has been respectively formed chemical treatment layer, the i.e. first chemical treatment layer and the second chemical treatment layer；
On the downside of (3) second chemical treatment layer, the solidification of roller coat epoxy coating is dried and is i.e. formed back of the body enamelled coating；First chemical treatment layer
Form the first adhesive layer after the roller coat Polyester resin lacquer solidification of upside, on the upside of the first adhesive layer, lay layer of PVC, layer of PVC
The second adhesive phase is formed after the roller coat Polyester resin lacquer solidification of upside；
On the upside of (4) second adhesive phases, the solidification of roller coat pearl white Polyester resin lacquer is dried and is i.e. formed pearl layer, on the upside of pearl layer
It is coated with PET film layer, on the upside of PET film layer, is coated with PE film, shape after backsize polyurethane binder of PE electron membrane solidifies
Become PE film.
The preparation method of a kind of high-strength V CM clad steel plate the most according to claim 1, it is characterised in that: described first
Chemical treatment layer, the thickness of the second chemical treatment layer are 2 μm-3 μm.
The preparation method of a kind of high-strength V CM clad steel plate the most according to claim 1, it is characterised in that: described substrate
Thickness be 0.02-0.25mm.
The preparation method of a kind of high-strength V CM clad steel plate the most according to claim 1, it is characterised in that: described back of the body paint
The thickness of layer is 4 μm-8 μm.