CN105219188A - A kind of high temperature resistant weather-proof resin - Google Patents
A kind of high temperature resistant weather-proof resin Download PDFInfo
- Publication number
- CN105219188A CN105219188A CN201510598819.7A CN201510598819A CN105219188A CN 105219188 A CN105219188 A CN 105219188A CN 201510598819 A CN201510598819 A CN 201510598819A CN 105219188 A CN105219188 A CN 105219188A
- Authority
- CN
- China
- Prior art keywords
- high temperature
- temperature resistant
- proof resin
- resistant weather
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature resistant weather-proof resin, each component and weight percent content thereof respectively: acrylic resin 27-45%, glass fibre 10-20%, thinner 5-8%, auxiliary agent 1-5%, calcium carbonate 20-30%, fluorinated ethylene propylene 1-5%, silicon-dioxide 8-12%.The present invention is high temperature resistant, and weather resistance is good.
Description
Technical field
The present invention relates to technical field of polymer materials, particularly relate to a kind of high temperature resistant weather-proof resin.
Background technology
Along with the development of corrosion and protection and the raising of industrialization degree, the Application Areas of matrix material is also more and more wider, and applying working condition, medium becomes increasingly complex, and use temperature is also more and more higher, and the requirement of market to its performance is also more and more higher.
At present, domestic and international field adopts high-property resin composite material material more single, and cause product use temperature low, at high temperature ability to bear is poor, and weather resistance is poor.Therefore, traditional matrix material far can not meet the market requirement more and more higher to its performance.
Summary of the invention
Technical problem to be solved by this invention is, provide a kind of high temperature resistant weather-proof resin, high temperature resistant weather resistance is better.
In order to solve the problems of the technologies described above, the invention provides a kind of high temperature resistant weather-proof resin, each component and weight percent content thereof respectively:
Acrylic resin 27-45%,
Glass fibre 10-20%,
Thinner 5-8%,
Auxiliary agent 1-5%,
Calcium carbonate 20-30%,
Fluorinated ethylene propylene 1-5%,
Silicon-dioxide 8-12%.
Further, described thinner is N-BUTYL ACETATE and No. 200 solvent oils: the content of described N-BUTYL ACETATE and No. 200 solvent oils is than being 2:1.
Further, described auxiliary agent comprises flow agent and siccative, and flow agent is polyester resin change properties of organic silicon oxygen alkane and fluorin modified crylic acid ester, and siccative is triethylene diamine and dibutyl tin laurate.
Preferably, described content of glass fiber is 15%.
Preferably, described calcium carbonate content is 25%.
Preferably, described dioxide-containing silica is 10%.
Implement the present invention, there is following beneficial effect: the present invention is high temperature resistant, and weather resistance is better.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Test according to composition shown in table 1.
Table 1
| Composition | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Acrylic resin | 45 | 45 | 27 |
| Glass fibre | 10 | 15 | 20 |
| Thinner | 5 | 8 | 5 |
| Auxiliary agent | 5 | 1 | 1 |
| Calcium carbonate | 25 | 20 | 30 |
| Fluorinated ethylene propylene | 2 | 1 | 5 |
| Silicon-dioxide | 8 | 10 | 12 |
Wherein, described thinner is N-BUTYL ACETATE and No. 200 solvent oils, and the content of described N-BUTYL ACETATE and No. 200 solvent oils is than being 2:1.Described auxiliary agent comprises flow agent and siccative, and flow agent is polyester resin change properties of organic silicon oxygen alkane and fluorin modified crylic acid ester, and siccative is triethylene diamine and dibutyl tin laurate.
The effect of each embodiment is for shown in table 2.
Table 2
| Usefulness | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Glowing filament (850 DEG C of GWIT) | PASS | PASS | PASS |
| Glowing filament (950 DEG C of GWIT) | PASS | PASS | PASS |
| Weathering test | 1200 | 1200 | 1200 |
| Salt spray resistance is tested | 600 | 600 | 600 |
Implement the present invention, there is following beneficial effect: the present invention is high temperature resistant, and weather resistance is better.
It should be noted that, in this article, term " comprises ", " comprising " or its any other variant are intended to contain comprising of nonexcludability, thus make to comprise the process of a series of key element, method, article or device and not only comprise those key elements, but also comprise other key elements clearly do not listed, or also comprise by the intrinsic key element of this process, method, article or device.When not more restrictions, the key element limited by statement " comprising ... ", and be not precluded within process, method, article or the device comprising this key element and also there is other identical element.
To the above-mentioned explanation of the disclosed embodiments, professional and technical personnel in the field are realized or uses the present invention.To be apparent for those skilled in the art to the multiple amendment of these embodiments, General Principle as defined herein can without departing from the spirit or scope of the present invention, realize in other embodiments.Therefore, the present invention can not be restricted to these embodiments shown in this article, but will meet the widest scope consistent with principle disclosed herein and features of novelty.
Claims (6)
1. a high temperature resistant weather-proof resin, is characterized in that, each component and weight percent content thereof respectively:
Acrylic resin 27-45%,
Glass fibre 10-20%,
Thinner 5-8%,
Auxiliary agent 1-5%,
Calcium carbonate 20-30%,
Fluorinated ethylene propylene 1-5%,
Silicon-dioxide 8-12%.
2. high temperature resistant weather-proof resin as claimed in claim 1, is characterized in that, described thinner is N-BUTYL ACETATE and No. 200 solvent oils, and the content of described N-BUTYL ACETATE and No. 200 solvent oils is than being 2:1.
3. high temperature resistant weather-proof resin as claimed in claim 1, it is characterized in that, described auxiliary agent comprises flow agent and siccative, and flow agent is polyester resin change properties of organic silicon oxygen alkane and fluorin modified crylic acid ester, and siccative is triethylene diamine and dibutyl tin laurate.
4. high temperature resistant weather-proof resin as claimed in claim 1, is characterized in that, described content of glass fiber is 15%.
5. high temperature resistant weather-proof resin as claimed in claim 1, is characterized in that, described calcium carbonate content is 25%.
6. high temperature resistant weather-proof resin as claimed in claim 1, is characterized in that, described dioxide-containing silica is 10%.